TY - JOUR A1 - Langer, Christoph A1 - Prommesberger, Christian A1 - Ławrowski, Robert Damian A1 - Schreiner, Rupert A1 - Serbun, Pavel A1 - Müller, Günter A1 - Düsberg, Felix A1 - Hofmann, Martin A1 - Bachmann, Michael A1 - Pahlke, Andreas T1 - Field emission properties of p-type black silicon on pillar structures JF - Journal of Vacuum Science & Technology B N2 - Arrays of black silicon field emission pillar structures were fabricated on p-type silicon substrates. Two types of samples with the same number of pillars (arrays of 10 × 10) but different pillar heights (8 and 20 μm) were prepared as well as a black silicon reference sample without pillars. The field emission properties of these cathodes were investigated both by means of integral current-voltage measurements and by field emission scanning microscopy. Samples with a pillar height of 20 μm revealed onset fields as low as 6.4 V/μm, field enhancement factors up to 800, and emission currents up to 8 μA at an applied field of 20 V/μm. Due to the p-type material, a saturation of the emission current for fields above 11 V/μm was observed. This saturation leads to a stable operation with a current fluctuation of less than ±8%. It was found that samples with a pillar height of 20 μm showed improved emission characteristics compared to samples with a pillar height of 8 μm or without pillars. The voltage maps revealed an increased emission homogeneity after a “burn-in” sequence of the sample. The current map showed that a few of the pillars dominate the emission. Integral current stability measurements were performed under different vacuum pressures, in order to investigate altered emission behavior and a potential degradation of the emitters. At pressures above 10−6 mbar, the sample starts to degrade irreversibly. Nevertheless, even after a harsh treatment over 30 min at 5 × 10−5 mbar and at an applied field of 23 V/μm, the cathode was still operating, and did not fail during further operation over 20 h at 5 × 10−8 mbar and at an applied field of 28 V/μm. Y1 - 2016 U6 - https://doi.org/10.1116/1.4943919 VL - 34 IS - 2 ER - TY - JOUR A1 - Bachmann, Michael A1 - Dams, Florian A1 - Düsberg, Felix A1 - Hofmann, Martin A1 - Pahlke, Andreas A1 - Langer, Christoph A1 - Ławrowski, Robert Damian A1 - Prommesberger, Christian A1 - Schreiner, Rupert A1 - Serbun, Pavel A1 - Lützenkirchen-Hecht, Dirk A1 - Müller, Günter T1 - Extraction of the characteristics of current-limiting elements from field emission measurement data JF - Journal of Vacuum Science & Technology B N2 - In this contribution, the authors will present an algorithm to extract the characteristics of nonideal field emission circuit elements from saturation-limited field emission measurement data. The method for calculating the voltage drop on current-limiting circuit elements is based on circuit theory as well as Newton's method. Since the only assumption the authors make on the current-limiting circuit is a connection in series, this method is applicable to most field emission data showing saturation. To be able to determine the significance of any parameter output, the uncertainties of data and extracted parameters as well as the parameter correlations are fully taken into account throughout the algorithm. N-type silicon samples with varying external serial resistors are analyzed. All results show a good agreement to the nominal resistor values. Additionally, several p-type samples are analyzed, showing a diodelike behavior. The extracted current-limiting characteristics of the p-type samples are in good agreement with a pn-junction model. The stability of the emission current of the p-type samples is measured by constant voltage measurements and compared to the extracted current-limiting characteristics. The application of the algorithm to measurement data shows that the given algorithm is a valuable tool to analyze field emission measurement data influenced by nonemissive processes. Y1 - 2017 U6 - https://doi.org/10.1116/1.4971768 VL - 35 IS - 2 ER - TY - CHAP A1 - Langer, Christoph A1 - Hausladen, Matthias A1 - Prommesberger, Christian A1 - Ławrowski, Robert Damian A1 - Bachmann, Michael A1 - Düsberg, Felix A1 - Pahlke, Andreas A1 - Shamonin (Chamonine), Mikhail A1 - Schreiner, Rupert T1 - Field emission current investigation of p-type and metallized silicon emitters in the frequency domain T2 - International Vacuum Nanoelectronics Conference (IVNC), 31st, 2018, Kyoto, Japan N2 - We investigated two different field emitter arrays consisting of 10×10 p-type and 10×10 undoped Au-coated high aspect ratio silicon tips. The I-V characterization of the p-type sample showed a pronounced saturation for voltages higher than 500 V and a maximum emission current of 39 nA. The metallized sample revealed a FN-like emission up to several μA. The metallized and the p-type sample operating below the saturation region showed high current fluctuations of ±16%. Whereas, the metallized sample with current regulation and the p-type sample in the saturation yielded a current stability of ±0.4% and ±0.3%, respectively. Investigations in the frequency domain revealed the for field emission typical 1/f-noise. By operating in the saturation region (p-type sample) or using an emission current regulation (metallized sample) the noise level was reduced by at least 20 dB. Finally, the p-type sample was illuminated by a light emitting diode to increase and modulate the emission current in the saturation region. The emission current was increased by a factor of 3.7 to 145 nA. With this configuration we emulated an unstable emission behavior and evaluated the performance of our emission current regulation circuit. KW - field emission KW - field emitter array KW - silicon tip KW - current fluctuation KW - current stability KW - field emission noise Y1 - 2018 U6 - https://doi.org/10.1109/IVNC.2018.8520127 PB - IEEE ER - TY - JOUR A1 - Prommesberger, Christian A1 - Langer, Christoph A1 - Ławrowski, Robert Damian A1 - Schreiner, Rupert T1 - Investigations on the long-term performance of gated p-type silicon tip arrays with reproducible and stable field emission behavior JF - Journal of Vacuum Science & Technology B N2 - The authors report on the fabrication and characterization of p-type Si tip arrays with an integrated gate electrode for applications as field emission electron sources. After the reactive ion etching of the emitters, the combined thermal dry and wet oxidation was used for both the sharpening of the emitters and for the realization of an enhanced insulation layer. Au was evaporated in a self-aligned process as gate electrode. Arrays of 16 Si tips were fabricated with tip heights of about 3 μm and tip radii of about 20 nm with integrated gate electrode concentrically positioned ≈2 μm below the tip apex. Integral measurements with an additional anode showed improved field emission properties with a reproducible and stable emission behavior. A fast activation of the tips, low onset voltages of about 30 V, and moderate field emission currents up to 0.55 μA were noticed. The field emission parameters were calculated using the Fowler–Nordheim characteristics. A pronounced saturation regime was observed, and current fluctuations of less than ±1% were investigated for 30 min. Long-term measurements were carried out for a period of more than 8 h. In the first 6 h of operation, the authors observed a drift of the emission current from 0.35 to 0.55 μA caused by an increased emission surface. Y1 - 2017 U6 - https://doi.org/10.1116/1.4972519 VL - 35 IS - 1 ER - TY - CHAP A1 - Ławrowski, Robert Damian A1 - Hausladen, Matthias A1 - Schreiner, Rupert T1 - Individually Addressable Fully Integrated Field Emission Electron Source Fabricated by Laser Micromachining of Silicon T2 - 33rd International Vacuum Nanoelectronics Conference (IVNC): 6-10 July 2020, Lyon N2 - A cathode with individually addressable Si tips allows the observation of the activation procedure and emission behaviour of each field emission emitter at any time of the measurement. The cathode consists of an array of 2x2 conically shaped emitter structures, which were fabricated by laser micromachining and wet etching of a Si substrate bonded on a glass carrier. Using the same process, a Si extractions grid was fabricated and mounted onto the emitter. Integral field emission measurements were performed in a diode configuration in a vacuum chamber at pressures of about 10- 9 mbar. The emitters show an onset voltage between 200 V and 300 V. The emission current for each emitter on the cathode was regulated to a given value (1.0 μA, 2.5μA, 5.0μA) by an external regulating circuit and was recorded individually during the measurement. With such approach, the relation between the emission behaviour and the geometry of emitters can be studied in detail. In addition, the current stabilization of each emitters of an array can be investigated, which led to a current stability of better than 0.5%. Y1 - 2020 SN - 978-1-7281-9454-7 U6 - https://doi.org/10.1109/IVNC49440.2020.9203470 SP - 1 EP - 2 PB - IEEE ER - TY - CHAP A1 - Prommesberger, Christian A1 - Ławrowski, Robert Damian A1 - Langer, Christoph A1 - Mecani, Mirgen A1 - Huang, Yifeng A1 - She, Juncong A1 - Schreiner, Rupert ED - Tiginyanu (Ed.), Ion M. T1 - Field emission properties of ring-shaped Si ridges with DLC coating T2 - Proc. SPIE 10248, Nanotechnology VIII, 102480H (30 May 2017) N2 - We report on the fabrication and the emission characterization of single ring-shaped Si ridges with a coating of diamond-like carbon (DLC). The reactive ion etching and the subsequent inductively coupled plasma step were adjusted to realize ring-shaped Si ridges with a height of 7.5 μm respectively 15 μm and an apex radius of 20 – 25 nm. The samples were coated with a DLC layer (thickness ≈ 2 – 5 nm) by a filtered cathodic vacuum arc deposition system in order to lower the work function of the emitter and to improve the field emission characteristics. The field emission characterizations were done in diode configuration with cathode and anode separated by a 50 μm thick mica spacer. A higher emission current was carried out for the ring-shaped Si ridge in comparison to the point-shaped Si tips due to the increased emission area. The highest emission current of 0.22 μA at 1000 V was measured on a DLC-coated sample with the highest aspect ratio. No degradation of the emission current was observed in the plateau regime during a measurement period of 6 h. Finally, no decreasing performance of the field emission properties was found due to changes in the geometry or destructions. KW - Etching KW - Scanning electron microscopy KW - Silicon carbide KW - Carbon KW - Mica KW - Oxides Y1 - 2017 U6 - https://doi.org/10.1117/12.2265627 VL - 102480H PB - Society of Photo-Optical Instrumentation Engineers (SPIE) ER - TY - CHAP A1 - Ławrowski, Robert Damian A1 - Langer, Christoph A1 - Prommesberger, Christian A1 - Schreiner, Rupert T1 - Field emission from three-dimensional epitaxial grown GaN-microrods T2 - 29th International Vacuum Nanoelectronics Conference (IVNC), 2016, 11-15 July, Vancouver, BC, Canada N2 - A novel three-dimensional epitaxial technique allows on patterned substrates the realization of gallium nitride pillars, also known as nano- and microrods. The typical dimensions of the microrods are in the range of one micron for the radius of the hexagonal footprint and about 10 μm in height. The microrods consist of a semiconductor heterostructure with an n GaN core, a n-GaN shell, a p GaN shell and an intermediate quantum well layer. The field emission properties were investigated in diode configuration by integral field emission measurements in a vacuum chamber at pressures around 10 -9 mbar. The spacer was mica with a thickness of 50 μm. A metallized fine-meshed nitride grid (or a metallized Si-grid) was used as anode. A current of about 1 μA at a voltage of 1250 V (1750 V) was measured. An onset field of about 12.5 MV/m (20 MV/m) and field enhancement factors in the range of 200 to 500 (150 to 300) were found. The investigation with the fine-meshed grid showed an expected pronounced saturation region. KW - field emission KW - GaN KW - LED Y1 - 2016 U6 - https://doi.org/10.1109/IVNC.2016.7551477 SN - 2380-6311 SP - 87 EP - 88 PB - IEEE ER - TY - CHAP A1 - Prommesberger, Christian A1 - Langer, Christoph A1 - Ławrowski, Robert Damian A1 - Schreiner, Rupert T1 - Field emission from black silicon structures with integrated gate electrode T2 - 29th International Vacuum Nanoelectronics Conference (IVNC), 2016, 11-15 July, Vancouver, BC, Canada N2 - Black silicon structures with integrated gate electrode were realized by using an improved fabrication process. An enhanced insulation layer was achieved by a combination of dry and wet oxidation, and a gold layer was evaporated as gate electrode. The black silicon structures were prepared with a RIE/ICP etching process at room temperature. Arrays of 16 and 100 apertures with buried p-doped black silicon whiskers have been fabricated. These structures have an emitter height of approximately 1.5 μm with tip radii between 5 nm and 30 nm. The whiskers are surrounded by the gate electrode in a distance of 1.5 μm. Integral field emission measurements yielded an onset voltage of 92 V for 16 apertures and 60 V for 100 apertures for an emission current of 1 nA. Maximum emission currents up to 0.2 μA were observed for the array with 100 apertures at a cathode voltage of 200 V. Stability measurements showed a current fluctuation of ± 21% at a mean value of the emission current of 12 nA over a period of 30 minutes for 16 apertures with b-Si whiskers. KW - field emission KW - black silicon KW - integrated gate electrode Y1 - 2016 U6 - https://doi.org/10.1109/IVNC.2016.7551532 SN - 2380-6311 SP - 219 EP - 220 PB - IEEE ER - TY - CHAP A1 - Ławrowski, Robert Damian A1 - Langer, Christoph A1 - Prommesberger, Christian A1 - Schreiner, Rupert T1 - Microrods and microlines by three-dimensional epitaxially grown GaN for field emission cathodes T2 - International Vacuum Nanoelectronics Conference (IVNC), 30th, 2017, Regensburg N2 - The three-dimensional epitaxial technique allows the realization of gallium nitride lines in addition to the rods. To optimize the properties of GaN-based field emission cathodes further investigations and an improvement of the epitaxial process were performed. The microrods and microlines consist of a one-order higher n-doped gallium nitride in comparison to the gallium nitride layer on the sapphire substrate. The typical height of the microrods and -lines is about 5 μm. The field emission properties of these structures were investigated in diode configuration by integral field emission measurements at pressures below 10 -9 mbar. For the microrods (microlines) a voltage of 1100 V (2000 V) was measured for a field emission current of about 0.5 μA with an onset field of about 12 MV/m (24 MV/m). Furthermore, the field enhancement factors for microrods and -lines are in the range of 300 and 200, respectively. KW - field emission KW - GaN KW - LED KW - Gallium nitride KW - Epitaxial growth Y1 - 2017 U6 - https://doi.org/10.1109/IVNC.2017.8051576 SP - 130 EP - 131 PB - IEEE ER - TY - CHAP A1 - Bachmann, Michael A1 - Dams, Florian A1 - Düsberg, Felix A1 - Hofmann, Martin A1 - Pahlke, Andreas A1 - Langer, Christoph A1 - Ławrowski, Robert Damian A1 - Prommesberger, Christian A1 - Schreiner, Rupert T1 - Extraction of the characteristics of limiting elements from field emission measurement data T2 - 29th International Vacuum Nanoelectronics Conference (IVNC), 2016, 11-15 July, Vancouver, BC, Canada N2 - In this contribution we will present an algorithm to extract the characteristics of non-Fowler-Nordheim (FN) circuit elements from saturation limited field emission (FE) measurement data. The method for calculating the voltage drop on limiting circuit elements is based on circuit theory as well as Newton's method. Since no assumption on the limiting circuit is made, this method is applicable to any FE data showing saturation. To be able to determine the significance of any parameter output, the uncertainties of data and extracted parameters are fully taken into account throughout the algorithm. External serial resistors and a limiting p-doped substrate are analyzed, where the latter shows a diode-like behavior. Y1 - 2016 U6 - https://doi.org/10.1109/IVNC.2016.7551474 SN - 2380-6311 SP - 81 EP - 82 PB - IEEE ER - TY - CHAP A1 - Langer, Christoph A1 - Prommesberger, Christian A1 - Ławrowski, Robert Damian A1 - Schreiner, Rupert A1 - Huang, Yifeng A1 - She, Juncong T1 - Gated p-Si field emission cathode applied in an ionization vacuum gauge T2 - 29th International Vacuum Nanoelectronics Conference (IVNC), 2016, 11-15 July, Vancouver, BC, Canada N2 - A commercial Bayard-Alpert ionization vacuum gauge was equipped with a field emission electron source based on a cathode consisting of an array of 16 gated, p-doped, and DLC-coated Si-tips and characterized. An anode current of about 1.3 μA led to an ion current of 7 fA at 3×10 -7 mbar and 0.8 pA at 4×10 -5 mbar. Whereas at pressures higher than 4×10 -5 mbar the emission current of the electron source decreased, the ratio of ion and anode current remained linear. A nearly constant sensitivity of ~ 17 mbar -1 of the ionization vacuum gauge within the investigated pressure range was depicted. KW - field emission KW - field emitter array KW - Si KW - DLC KW - electron source KW - ionization vacuum gauge Y1 - 2016 U6 - https://doi.org/10.1109/IVNC.2016.7551500 SN - 2380-6311 SP - 145 EP - 146 PB - IEEE ER - TY - CHAP A1 - Bachmann, Michael A1 - Dams, Florian A1 - Düsberg, Felix A1 - Hofmann, Martin A1 - Pahlke, Andreas A1 - Langer, Christoph A1 - Ławrowski, Robert Damian A1 - Prommesberger, Christian A1 - Schreiner, Rupert T1 - Control of the electron source current T2 - International Vacuum Nanoelectronics Conference (IVNC), 30th, 2017, Regensburg N2 - A control circuit to stabilize the flux of electrons transmitted through an extractor electrode is presented. By controlling the emission current a fluctuation with a standard deviation of 0.015% is observed. However, the achievable stability of the transmitted electron current is limited due to a variation of the extraction grid current ratio showing a standard deviation of 4.33%. By regulating the difference of the emission current and the extraction grid current an improved stability of the transmitted electron current down to a standard deviation of 0.280% is observed. Even with operation at 2 × 10 -5 mbar a standard deviation of 0.558% is achieved. KW - Standards KW - Circuit stability KW - Power system stability KW - Current measurement KW - Voltage measurement KW - Electron sources KW - Stability analysis Y1 - 2017 U6 - https://doi.org/10.1109/IVNC.2017.8051550 SP - 66 EP - 67 PB - IEEE ER - TY - CHAP A1 - Ławrowski, Robert Damian A1 - Schreiner, Rupert A1 - Linghu, Shuangyi A1 - Gu, Fuxing T1 - Field Emission Behaviour of Single-Crystal Pd Nanowires T2 - 33rd International Vacuum Nanoelectronics Conference (IVNC): 6-10 July 2020, Lyon, France N2 - Single-crystal Pd nanowires with typically 100 nm diameters and lengths from several micrometers to tens of micrometers were grown on Al 2 O 3 substrates in a furnace with Ar atmosphere. Integral field emission measurements of such samples after Pd coating (~10 nm) were performed in a diode configuration with a 50 μm mica spacer in a vacuum chamber at pressures of about 10 -9 mbar. The IV measurement of the sample shows an integral emission current up to 2 μA at a voltage of 500 V (10 MV/m) and an onset voltage for a current of 1 nA of about 275 V. The corresponding Fowler-Nordheim plot show a linear behavior, like expected for a metal needle. Y1 - 2020 SN - 978-1-7281-9454-7 U6 - https://doi.org/10.1109/IVNC49440.2020.9203510 SP - 1 EP - 2 PB - IEEE ER - TY - CHAP A1 - Prommesberger, Christian A1 - Langer, Christoph A1 - Ławrowski, Robert Damian A1 - Schreiner, Rupert T1 - Benzocyclobutene as a novel integrated spacer material in a field emission electron source T2 - International Vacuum Nanoelectronics Conference (IVNC), 30th, 2017, Regensburg N2 - For the realization of a miniaturized field emission electron source we tested benzocyclobutene (BCB) as a new spacer material between cathode and anode. We fabricated black silicon emitters and characterized the emission behavior with an integrated 5 μm thin and large-area spacer of BCB. The integrated BCB layer allows the realization of a compact electron source with only two components consisting of a cathode with BCB and a grid. The comparison with other spacer materials like polyimide (25 μm thickness) or mica (50 μm thickness) revealed for the cathode with BCB a significantly reduced operational voltage of 240 V for a field emission current of 1 μA. KW - field emission KW - benzocyclobutene KW - integrated spacer KW - electron source KW - black silicon Y1 - 2017 U6 - https://doi.org/10.1109/IVNC.2017.8051605 SP - 192 EP - 193 PB - IEEE ER - TY - CHAP A1 - Ławrowski, Robert Damian A1 - Langer, Christoph A1 - Prommesberger, Christian A1 - Schreiner, Rupert T1 - Light emitting diodes based on three-dimensional epitaxial grown crystalline GaN rods T2 - 7. MikroSystemTechnik Kongress "MEMS, Mikroelektronik, Systeme", 23.-25. Oktober 2017, München Y1 - 2017 SN - 978-3-8007-4491-6 SP - 131 EP - 134 PB - VDE-Verlag CY - München ER - TY - JOUR A1 - Ławrowski, Robert Damian A1 - Hausladen, Matthias A1 - Buchner, Philipp A1 - Schreiner, Rupert T1 - Silicon Field Emission Electron Source With Individually Controllable Single Emitters JF - IEEE Transactions on Electron Devices N2 - An electron source with an array of individually controllable single tips allows the observation of each emitter current simultaneously as well as the measurement of the integral current. Furthermore, the initial activation process of the individual tips and current distribution of the source can be examined. The Si cathode consists of an array of 2 x 2 conically shaped emitter structures on a borosilicate glass substrate. The emitters were fabricated by laser micromachining and wet etching. Integral field emission (FE) measurements were performed in a diode configuration in a vacuum chamber at pressures of about 10(-9) mbar with a self-aligned Si extraction grid, due to adjustment pins. The total emission current was regulated to a predefined value (4.0, 10, 20, 40, and 50 mu A) by an external regulating circuit and recorded individually during the measurement. The onset voltage for a current of 1 nA varied between 320 and 430 V. The voltage conversion factor is in the range of 7.6 x 10(4) cm(-1) to 1.3 x 10(5) cm(-1). Constant currentmeasurementsover a longer periodof time (1800 values with a sample rate of 0.5 Hz) were performed and show a total current fluctuation less than 0.6% due to the regulation circuit. Despite the stable total current in regulated operation, it was observed that the individual emitters fluctuate up to 75% for low (similar to 10(-8) A) and 5% for high (similar to 10(-5) A) currents. KW - Current distribution KW - current limiters KW - electron emission KW - electron sources KW - silicon-on-insulator Y1 - 2021 U6 - https://doi.org/10.1109/TED.2021.3093374 VL - 68 IS - 8 SP - 4116 EP - 4122 PB - IEEE ER - TY - JOUR A1 - Bachmann, Michael A1 - Düsberg, Felix A1 - Pahlke, Andreas A1 - Edler, Simon A1 - Schels, Andreas A1 - Herdl, Florian A1 - Ławrowski, Robert Damian A1 - Schreiner, Rupert T1 - High current silicon nanowire field emitter arrays JF - Journal of Vacuum Science & Technology B N2 - Arrays of n-doped silicon nanowire field emitters with a high aspect ratio are realized by a novel dry etching technique. Compared to the high current silicon emitters in the literature, the manufacturing process is much simpler and requires only a single photolithography step and two dry etching steps. The cathodes realized with this method exhibit a total current of 20 mA from an active area of 4×4 mm2, which is significantly higher than that for most known structures made from silicon and also represents good performance in comparison with other emitter types, e.g., carbon nanotubes. In addition to characterization in ultrahigh vacuum, measurements at 10−5 mbar are performed and compared with our recent silicon emitters. Compared to these cathodes, the structures with the nanowires exhibit at least two orders of magnitude higher current-carrying capability. Y1 - 2022 U6 - https://doi.org/10.1116/6.0001639 VL - 40 IS - 1 PB - AIP Publishing ER - TY - JOUR A1 - Remskar, Maja A1 - Hüttel, Andreas K. A1 - Shubina, Tatiana V. A1 - Seabaugh, Alan A1 - Fathipour, Sara A1 - Ławrowski, Robert Damian A1 - Schreiner, Rupert T1 - Confinement Related Phenomena in MoS2 Tubular Structures Grown from Vapour Phase JF - Israel Journal of Chemistry N2 - We review recently discovered phenomena observed in the MoS2 tubular structures, which were synthesized by a lasting chemical transport reaction nearly at chemical equilibrium. Such MoS2 nanotubes are distinguished by low density of structural defects, thin walls and a high aspect ratio, which intrinsically provide a confined, edge-free geometry. Quantum confinement with single electron conductance was recorded and a bright exciton photoluminescence with appearance of whispering gallery modes was observed. In addition, the field-effect transistors and field emitters based on single MoS2 nanotubes were demonstrated. These discoveries revitalize research of MoS2 curved structures grown from vapour phase, which were reported several decades ago. Y1 - 2021 U6 - https://doi.org/10.1002/ijch.202100100 SN - 1869-5868 VL - 62 IS - 3-4 SP - 1 EP - 11 PB - Wiley ER - TY - CHAP A1 - Ławrowski, Robert Damian A1 - Bachmann, Michael A1 - Schreiner, Rupert T1 - Field Emission Arrays from Graphite Fabricated by Laser Micromachining T2 - 34th International Vacuum Nanoelectronics Conference (IVNC): 7/5/2021 - 7/9/2021, Lyon, France N2 - Arrays of 4x4 conical shaped emitters were directly structured by laser micromaching. Assembled as an electron source with a spacer and Si-grid, they were investigated by means of IV-measurement in ultra-high vacuum. The IV-measurements of the sample show integral emission currents up to 10 µA at a voltage of 1000 V (11 MV/m). Initially, an ideal FN-behaviour is noticeable. The deviation for higher voltage values in the FN-plot is caused by the change of the work function, which was proven by numerical calculations. KW - field emission array KW - graphite KW - laser micromachining Y1 - 2021 SN - 978-1-6654-2589-6 U6 - https://doi.org/10.1109/IVNC52431.2021.9600736 SP - 1 EP - 2 PB - IEEE ER - TY - CHAP A1 - Langer, Christoph A1 - Ławrowski, Robert Damian A1 - Prommesberger, Christian A1 - Dams, Florian A1 - Serbun, Pavel A1 - Bachmann, Michael A1 - Müller, Günter A1 - Schreiner, Rupert T1 - High aspect ratio silicon tip cathodes for application in field emission electron sources T2 - 2014 27th International Vacuum Nanoelectronics Conference (IVNC), 6-10 July 2014, Engelberg, Switzerland N2 - Precisely aligned arrays of sharp tip structures on top of elongated pillars were realized by using an improved fabrication process including an additional inductively-coupled-plasma reactive-ion etching step. Arrays of n-type and p-type silicon with 271 tips have been fabricated and investigated. Those structures have a total height of 5–6 µm and apex radii less than 20nm. Integral field emission measurements of the arrays yielded low onset-fields in the range of 8–12V=µm and field enhancement factors between 300 and 700. The I-E curves of n-type structures showed the usual Fowler-Nordheim behaviour, whereas p-type structures revealed a significant saturation region due to the limited number of electrons in the conduction band and a further carrier depletion effect caused by the pillar. The maximum integral current in the saturation region was 150 nA at fields above 30V=µm. An excellent stability of the emission current of less than ± 2% fluctuation was observed in the saturation region. For n-type Si a maximum integral current of 10 µA at 24V=µm and an average current stability with a fluctuation of ± 50% were measured. KW - Current measurement KW - Etching KW - FABRICATION KW - field emission KW - field emitter array KW - GEOMETRY KW - Iron KW - Sensor arrays KW - silicon KW - silicon tip Y1 - 2014 U6 - https://doi.org/10.1109/IVNC.2014.6894824 SP - 222 EP - 223 PB - IEEE ER -