TY - JOUR A1 - Lautenschläger, Toni A1 - Leis, Alexander A1 - Dendorfer, Sebastian A1 - Palm, Christoph A1 - Schreiner, Rupert A1 - Langer, Christoph A1 - Prommesberger, Christian A1 - Ławrowski, Robert Damian A1 - Dams, Florian A1 - Bornmann, Benjamin A1 - Navitski, Aliaksandr A1 - Serbun, Pavel A1 - Müller, Günter A1 - Liebetruth, Thomas A1 - Kohlert, Dieter A1 - Pernsteiner, Jochen A1 - Schreier, Franz A1 - Heerklotz, Sabrina A1 - Heerklotz, Allwin A1 - Boos, Alexander A1 - Herwald, Dominik A1 - Monkman, Gareth J. A1 - Treiber, Daniel A1 - Mayer, Matthias A1 - Hörner, Eva A1 - Bentz, Alexander A1 - Shamonin (Chamonine), Mikhail A1 - Johansen, Søren Peter A1 - Reichel, Marco A1 - Stoll, Andrea A1 - Briem, Ulrich A1 - Dullien, Silvia A1 - Renkawitz, Tobias A1 - Weber, Tim A1 - Dendorfer, Sebastian A1 - Grifka, Joachim A1 - Penzkofer, Rainer A1 - Barnsteiner, K. A1 - Jovanovik, M. A1 - Wernecke, P. A1 - Vögele, A. A1 - Bachmann, T. A1 - Plötz, Martin A1 - Schliekmann, Claus A1 - Wels, Harald A1 - Helmberger, Paul A1 - Kaspar, Marcel A1 - Hönicka, M. A1 - Schrammel, Siegfried A1 - Enser, Markus A1 - Schmidmeier, Monika A1 - Schroll-Decker, Irmgard A1 - Haug, Sonja A1 - Gelfert, Verena A1 - Vernim, Matthias ED - Baier, Wolfgang T1 - Forschungsbericht 2012 T3 - Forschungsberichte der OTH Regensburg - 2012 Y1 - 2012 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:898-opus4-7834 CY - Regensburg ER - TY - JOUR A1 - Breuer, Janis A1 - Bachmann, Michael A1 - Düsberg, Felix A1 - Pahlke, Andreas A1 - Edler, Simon A1 - Langer, Christoph A1 - Prommesberger, Christian A1 - Ławrowski, Robert Damian A1 - Schreiner, Rupert A1 - Serbun, Pavel A1 - Lützenkirchen-Hecht, Dirk T1 - Extraction of the current distribution out of saturated integral measurement data of p-type silicon field emitter arrays JF - Journal of Vacuum Science and Technology B N2 - At the moment, only complicated techniques are known for the determination of array properties of field emitter arrays such as the number of active tips, the current distribution, or the individual tip radii. In this work, a method for extracting these parameters from integral measurement data is presented. A model describing the characteristics of a single emitter, including the saturation as a function of the applied voltage and the emitter radius, is developed. It is shown that experimental data of field emitter arrays can be represented as the sum of these functions and the characteristic parameters can be fitted to field emission data of an array. Using this method, the values of the radii as well as the parameters of distribution models can be determined directly. Analysis of experimental data from p-type Si emitter arrays shows that only 1–2% of the tips contribute significantly. Y1 - 2018 U6 - https://doi.org/10.1116/1.5035189 VL - 36 IS - 5 PB - AIP Publishing ER - TY - JOUR A1 - Langer, Christoph A1 - Prommesberger, Christian A1 - Ławrowski, Robert Damian A1 - Schreiner, Rupert A1 - Serbun, Pavel A1 - Müller, Günter A1 - Düsberg, Felix A1 - Hofmann, Martin A1 - Bachmann, Michael A1 - Pahlke, Andreas T1 - Field emission properties of p-type black silicon on pillar structures JF - Journal of Vacuum Science & Technology B N2 - Arrays of black silicon field emission pillar structures were fabricated on p-type silicon substrates. Two types of samples with the same number of pillars (arrays of 10 × 10) but different pillar heights (8 and 20 μm) were prepared as well as a black silicon reference sample without pillars. The field emission properties of these cathodes were investigated both by means of integral current-voltage measurements and by field emission scanning microscopy. Samples with a pillar height of 20 μm revealed onset fields as low as 6.4 V/μm, field enhancement factors up to 800, and emission currents up to 8 μA at an applied field of 20 V/μm. Due to the p-type material, a saturation of the emission current for fields above 11 V/μm was observed. This saturation leads to a stable operation with a current fluctuation of less than ±8%. It was found that samples with a pillar height of 20 μm showed improved emission characteristics compared to samples with a pillar height of 8 μm or without pillars. The voltage maps revealed an increased emission homogeneity after a “burn-in” sequence of the sample. The current map showed that a few of the pillars dominate the emission. Integral current stability measurements were performed under different vacuum pressures, in order to investigate altered emission behavior and a potential degradation of the emitters. At pressures above 10−6 mbar, the sample starts to degrade irreversibly. Nevertheless, even after a harsh treatment over 30 min at 5 × 10−5 mbar and at an applied field of 23 V/μm, the cathode was still operating, and did not fail during further operation over 20 h at 5 × 10−8 mbar and at an applied field of 28 V/μm. Y1 - 2016 U6 - https://doi.org/10.1116/1.4943919 VL - 34 IS - 2 ER - TY - JOUR A1 - Bachmann, Michael A1 - Dams, Florian A1 - Düsberg, Felix A1 - Hofmann, Martin A1 - Pahlke, Andreas A1 - Langer, Christoph A1 - Ławrowski, Robert Damian A1 - Prommesberger, Christian A1 - Schreiner, Rupert A1 - Serbun, Pavel A1 - Lützenkirchen-Hecht, Dirk A1 - Müller, Günter T1 - Extraction of the characteristics of current-limiting elements from field emission measurement data JF - Journal of Vacuum Science & Technology B N2 - In this contribution, the authors will present an algorithm to extract the characteristics of nonideal field emission circuit elements from saturation-limited field emission measurement data. The method for calculating the voltage drop on current-limiting circuit elements is based on circuit theory as well as Newton's method. Since the only assumption the authors make on the current-limiting circuit is a connection in series, this method is applicable to most field emission data showing saturation. To be able to determine the significance of any parameter output, the uncertainties of data and extracted parameters as well as the parameter correlations are fully taken into account throughout the algorithm. N-type silicon samples with varying external serial resistors are analyzed. All results show a good agreement to the nominal resistor values. Additionally, several p-type samples are analyzed, showing a diodelike behavior. The extracted current-limiting characteristics of the p-type samples are in good agreement with a pn-junction model. The stability of the emission current of the p-type samples is measured by constant voltage measurements and compared to the extracted current-limiting characteristics. The application of the algorithm to measurement data shows that the given algorithm is a valuable tool to analyze field emission measurement data influenced by nonemissive processes. Y1 - 2017 U6 - https://doi.org/10.1116/1.4971768 VL - 35 IS - 2 ER - TY - CHAP A1 - Langer, Christoph A1 - Ławrowski, Robert Damian A1 - Prommesberger, Christian A1 - Dams, Florian A1 - Serbun, Pavel A1 - Bachmann, Michael A1 - Müller, Günter A1 - Schreiner, Rupert T1 - High aspect ratio silicon tip cathodes for application in field emission electron sources T2 - 2014 27th International Vacuum Nanoelectronics Conference (IVNC), 6-10 July 2014, Engelberg, Switzerland N2 - Precisely aligned arrays of sharp tip structures on top of elongated pillars were realized by using an improved fabrication process including an additional inductively-coupled-plasma reactive-ion etching step. Arrays of n-type and p-type silicon with 271 tips have been fabricated and investigated. Those structures have a total height of 5–6 µm and apex radii less than 20nm. Integral field emission measurements of the arrays yielded low onset-fields in the range of 8–12V=µm and field enhancement factors between 300 and 700. The I-E curves of n-type structures showed the usual Fowler-Nordheim behaviour, whereas p-type structures revealed a significant saturation region due to the limited number of electrons in the conduction band and a further carrier depletion effect caused by the pillar. The maximum integral current in the saturation region was 150 nA at fields above 30V=µm. An excellent stability of the emission current of less than ± 2% fluctuation was observed in the saturation region. For n-type Si a maximum integral current of 10 µA at 24V=µm and an average current stability with a fluctuation of ± 50% were measured. KW - Current measurement KW - Etching KW - FABRICATION KW - field emission KW - field emitter array KW - GEOMETRY KW - Iron KW - Sensor arrays KW - silicon KW - silicon tip Y1 - 2014 U6 - https://doi.org/10.1109/IVNC.2014.6894824 SP - 222 EP - 223 PB - IEEE ER - TY - CHAP A1 - Prommesberger, Christian A1 - Langer, Christoph A1 - Ławrowski, Robert Damian A1 - Muller, F. A1 - Dams, Florian A1 - Schreiner, Rupert A1 - Serbun, Pavel A1 - Müller, Günter T1 - Comparison of integral and local field-emission properties of Mo-coated p-Si tip arrays T2 - 2015 28th International Vacuum Nanoelectronics Conference (IVNC), 13-17 July 2015, Guangzhou, China N2 - Silicon tip arrays were fabricated by means of reactive ion etching followed by oxidation for final sharpening and molybdenum thin film coating. The field-emission (FE) properties of these Mo-coated p-Si tip arrays were systemically investigated by different measurement techniques. Integral measurements in diode configuration yielded a turn-on field (for 1 nA) of 22 V/μm and nearly stable FE currents up to 6.6 μA at 38 V/μm. The effective field enhancements factor extracted from the FN plots is about 180. Detailed investigations of these FE arrays were also performed by means of field emission scanning microscopy combined with electron microscopy. A rather limited efficiency of the tips (50% at 1500 V) and FE homogeneity (180 nA at 700 V) might be correlated with the varying morphology of the tips and the presence of oxides. Local I-V measurements of selected single tips revealed both activation and deactivation effects, which finally resulted in nearly reproducible I-V curves. Current stability measurements at a constant voltage showed rather large fluctuations (0.1-1 μA) of the FE current, which could be reduced up to 1.7% by using of a PID-regulated voltage source. SEM images showed unchanged tip shape after the current processing. KW - CATHODES KW - Coatings KW - Current measurement KW - field emission KW - Iron KW - Mo-coated KW - p-Si tip KW - Scanning electron microscopy KW - silicon KW - tip arrays KW - Vacuum technology Y1 - 2015 U6 - https://doi.org/10.1109/IVNC.2015.7225579 SP - 192 EP - 193 PB - IEEE ER - TY - CHAP A1 - Langer, Christoph A1 - Prommesberger, Christian A1 - Ławrowski, Robert Damian A1 - Müller, F. A1 - Schreiner, Rupert A1 - Serbun, Pavel A1 - Müller, Günter T1 - Enhanced field emission from p-doped black silicon on pillar structures T2 - 2015 28th International Vacuum Nanoelectronics Conference (IVNC), 13-17 July 2015, Guangzhou, China N2 - Aligned square arrays of black silicon (b-Si) on top of pillars were fabricated on p-type silicon substrate by a deep-etching step combined with a b-Si process. Two 10×10 arrays with pillar heights of 8 μm and 20 μm and one b-Si reference sample without pillars were investigated. Integral field emission (FE) measurements of the arrays yielded rather low onset-fields between 6.4 V/μm and 13.5 V/μm and field enhancement factors between 430 and 800. The I-V curves showed typical Fowler-Nordheim behavior for low fields, whereas a saturation region was observed at higher fields. The maximum integral current in the saturation region was 8 μA at a field of 20 V/μm. The stability of the emission current was investigated over 3 hours and revealed moderate fluctuations of ± 8% in the saturation region. Voltage scans showed well-aligned FE from nearly all pillars. KW - black silicon KW - CATHODES KW - Current measurement KW - Etching KW - FABRICATION KW - field emission KW - field emitter array KW - Iron KW - silicon KW - Vacuum technology Y1 - 2015 U6 - https://doi.org/10.1109/IVNC.2015.7225547 SP - 104 EP - 105 PB - IEEE ER - TY - CHAP A1 - Ławrowski, Robert Damian A1 - Langer, Christoph A1 - Prommesberger, Christian A1 - Dams, Florian A1 - Serbun, Pavel A1 - Müller, Günter A1 - Schreiner, Rupert T1 - Spitzen- und Kantenemitter aus Silizium mit einem hohen Aspektverhältnis für Ionisationsgassensoren T2 - Mikrosystemtechnik als Schlüsseltechnologie der Systemintegration : 4. Landshuter Symposium Mikrosystemtechnik ; Tagungsband zum Symposium ; 12./13. März 2014, Hochschule Landshut N2 - Durch die Optimierung von reaktivem Ionenätzen mit induktiv gekoppeltem Plasma ist die Herstellung von verschiedenen Siliziumkathoden mit hoher Anisotropie und hohem Aspektverhältnis für Feldemissionsanwendungen möglich. Simulationen mit COMSOL Multiphysics untermauern das Potential von solchen Spitzen- und Kantenfeldemittern. Die Ergebnisse der Simulation zeigen einen zwei- bis sechsfach höheren Feldüberhöhungsfaktor der tiefgeätzten Strukturen im Vergleich zu identischen Emittern ohne zusätzliche Tiefenätzung. Feldemissionsmessungen bestätigen die Simulationsergebnisse. Der modifizierte Herstellungsprozess der Feldemitter ermöglicht somit einen zuverlässigen Betrieb von Feldemissionselektronenquellen bei kleineren makroskopischen Feldstärken. Außerdem weisen die Messungen des Emissionsstroms im Sättigungsbereich eine weitgehende Unabhängigkeit vom elektrischen Feld auf. Lokale Feldemissionsmessungen ergeben dadurch eine deutliche Stromstabilisierung, welche über große Feldstärkenbereiche konstant bleibt. Die Nutzung der HAR-Emitter (high aspect ratio) ist damit eine gute Voraussetzung für einen zuverlässigen Betrieb der Emissionskathoden bei kleinen Feldstärken für die Anwendung in Ionisationsgassensoren. KW - Emitter KW - Feldelektronenemission KW - Gassensor KW - Herstellung KW - Ionenemission KW - Silicium Y1 - 2014 SN - 978-3-9812696-5-9 SP - 28 EP - 35 PB - Cluster Mikrosystemtechnik CY - Landshut ER - TY - CHAP A1 - Serbun, Pavel A1 - Porshyn, Vitali A1 - Müller, Günter A1 - Lützenkirchen-Hecht, Dirk A1 - Prommesberger, Christian A1 - Langer, Christoph A1 - Ławrowski, Robert Damian A1 - Schreiner, Rupert T1 - Field emission behavior of single n- and p-type black Si pillar structures T2 - International Vacuum Nanoelectronics Conference (IVNC), 31st, 2018, Kyoto, Japan N2 - We have investigated the properties of single n- and p-type black silicon (b-Si) pillars with a height of 20 μ m under strong electric field and halogen lamp or laser illumination. For both type of b-Si pillar structures, I-V measurements revealed strong activation effects, which consisted in sudden current increases during the first up/down voltage sweeps. The maximum reproducible emission current from a single n-type b-Si pillar structure was about 15 μ A. A pronounced saturation region at 240 nA was observed for a single p-type b-Si pillar. The current fluctuation over time showed a standard deviation of 28% and 2.5% for n- and p-type single b-Si pillar structures, respectively. Optical switching under halogen lamp illumination resulted in at least 3 times higher saturation currents and showed a linear dependence of the FE current on the laser power. KW - field emission KW - black silicon KW - photoemission Y1 - 2018 U6 - https://doi.org/10.1109/IVNC.2018.8520292 PB - IEEE ER - TY - CHAP A1 - Serbun, Pavel A1 - Porshyn, Vitali A1 - Müller, Günter A1 - Mingels, Stephan A1 - Lützenkirchen-Hecht, Dirk A1 - Bachmann, Michael A1 - Düsberg, Felix A1 - Dams, Florian A1 - Hofmann, Martin A1 - Pahlke, Andreas A1 - Prommesberger, Christian A1 - Langer, Christoph A1 - Ławrowski, Robert Damian A1 - Schreiner, Rupert T1 - Field emission behavior of Au-tip-coated p-type Si pillar structures T2 - 29th International Vacuum Nanoelectronics Conference (IVNC), 2016, 11-15 July, Vancouver, BC, Canada N2 - Precisely aligned high-aspect-ratio (HAR) silicon tip arrays were fabricated using enhanced reactive ion etching with an inductively-coupled-plasma followed by a sharpening oxidation. A gold thin film was then sputtered only on the tips of the HAR structures. Field-emission (FE) properties from Au-coated HAR p-Si tip array cathodes have been systematically investigated by means of field emission scanning microscopy (FESM). A rather high efficiency of the HAR Si structures (71% at 550 V), but limited homogeneous FE with currents of 1-600 nA might be correlated with the varying geometry of the tips and the presence of oxides. I-V measurements of single Au-coated HAR emitters revealed activation effects and the saturation current region at 3 nA. An increase of the saturation current by 4 orders of magnitude was observed during 20 hours of conditioning at constant voltage, which finally resulted in nearly reproducible FN curves with a ß-factor of 473. An excellent stability of the emission current of less than 1 % was obtained during the additional long-time conditioning at constant voltage. Optical switching under halogen lamp illumination resulted in at least 2 times higher saturation currents and showed a linear dependence of the FE current on the light color temperature. KW - field emission KW - p-type Si-pillar array KW - surface oxide effects KW - photoemission Y1 - 2016 U6 - https://doi.org/10.1109/IVNC.2016.7551516 SN - 2380-6311 SP - 181 EP - 182 PB - IEEE ER - TY - CHAP A1 - Serbun, Pavel A1 - Porshyn, Vitali A1 - Lützenkirchen-Hecht, Dirk A1 - Prommesberger, Christian A1 - Langer, Christoph A1 - Ławrowski, Robert Damian A1 - Schreiner, Rupert T1 - Photosensitivity of single silicon high-aspect-ratio tips with different doping levels T2 - International Vacuum Nanoelectronics Conference (IVNC), 31st, 2018, Kyoto, Japan N2 - Photosensitivity of single lightly p-doped, highly p-doped, with an integrated p/n junction and intrinsic high-aspect-ratio (HAR) silicon tips was investigated in an ultra-high vacuum environment. The current-voltage characteristics (I-V) of the lightly doped p-type HAR tips showed a characteristic current saturation at around 10-12 nA, whereas the HAR Si tips with p/n junction showed similar saturation phenomena, however, at much smaller current values starting at ~20-30 pA. Optical switching under a halogen lamp illumination resulted in at least 2-4 times higher saturation currents and showed a linear dependence between the illumination power and the FE current, for both types of structures. In case of the highly p-doped HAR tips optical current switching effects, i. e. current saturation, were observed at rather low current levels 1-2 pA. Intrinsic HAR Si-tips showed relative unstable field emission behavior without a clear evidence of the photosensitivity. KW - field emission KW - Si p/n junction KW - p-type Si KW - photosensitivity Y1 - 2018 U6 - https://doi.org/10.1109/IVNC.2018.8520288 PB - IEEE ER - TY - CHAP A1 - Schreiner, Rupert A1 - Langer, Christoph A1 - Prommesberger, Christian A1 - Ławrowski, Robert Damian A1 - Dams, Florian A1 - Bachmann, Michael A1 - Düsberg, F. A1 - Hofmann, Martin A1 - Pahlke, Andreas A1 - Serbun, Pavel A1 - Mingels, Stephan A1 - Müller, Günter T1 - Semiconductor field emission electron sources using a modular system concept for application in sensors and x-ray-sources T2 - 2015 28th International Vacuum Nanoelectronics Conference (IVNC), 13-17 July 2015, Guangzhou, China N2 - Semiconductor field emitters are suitable candidates for applications, which require a very stable field emission (FE) current and a high emission uniformity over the entire emission area. By using different materials and geometries, we are able to vary the FE characteristics within a wide range. Each specific application requires its own optimized design for the cathode as well as for the other parts of the FE electron source. To meet as many of these requirements as possible while using only a limited number of different prefabricated components, we established a modular system concept for our FE electron source. This allows the implementation of almost every cathode material. For first characterizations, we used gated p-type Si cathodes with 16 tips. We obtained stable FE currents of 0.4 μA for a grid-potential of 400 V and a gate potential of 100 V. Almost 100% of the electrons are emitted towards the grid-electrode. Parasitic leakage paths, as well as the electron emission towards the gate-electrode can be neglected. Approximately 10% of the electrons are transmitted through the grid and reach the external anode. This is in good agreement with the optical transmission through the grid-mesh. KW - Anodes KW - CATHODES KW - electron sources KW - GEOMETRY KW - Iron KW - Logic gates KW - semiconductor field emission KW - silicon Y1 - 2015 U6 - https://doi.org/10.1109/IVNC.2015.7225572 SP - 178 EP - 179 PB - IEEE ER - TY - CHAP A1 - Ławrowski, Robert Damian A1 - Langer, Christoph A1 - Prommesberger, Christian A1 - Schreiner, Rupert A1 - Mingels, Stephan A1 - Porshyn, Vitali A1 - Serbun, Pavel A1 - Müller, Günter T1 - Field emission from surface textured GaN with buried double-heterostructures T2 - 2015 28th International Vacuum Nanoelectronics Conference (IVNC), 13-17 July 2015, Guangzhou, China N2 - In this contribution we report on field emission (FE) cathodes based on thin-film LED-technology and surface texturing. The FE cathode can be used both as an n-GaN cathode with an electrical contact at the top side metallization as well as a pn-GaN diode contacting only the p-GaN layer at the bottom side of the structure. The local and integral FE properties of the textured surface of the LED structure were investigated. For n-GaN an integral emission current up to 1.0 μA at an electric field of 19 V/μm was achieved. The pn-GaN diode measurements showed an integral current saturation behavior with two orders of magnitude lower FE currents. Regulated voltage scans obtained by FE scanning microscopy revealed a well-distributed emission over the whole cathode area. Measurements under pulsed tunable laser illumination and moderate electric fields indicated charge carrier generation in the buried double-heterostructures at photon energies below 3.5 eV besides normal photoemission above 4.1 eV. KW - CATHODES KW - Current measurement KW - Electric fields KW - field emission KW - Gallium nitride KW - GaN KW - Iron KW - Light emitting diodes KW - photoemission KW - Surface texture Y1 - 2015 U6 - https://doi.org/10.1109/IVNC.2015.7225548 SP - 106 EP - 107 PB - IEEE ER -