TY - JOUR A1 - Kofiani, Kirki A1 - Nonn, Aida A1 - Wierzbicki, Tomasz T1 - New calibration method for high and low triaxiality and validation on SENT specimens of API X70 JF - International Journal of Pressure Vessels and Piping N2 - The determination of the exact mechanical properties of material is essential for an optimal and safe design of linepipes. It is especially important for the prevention of over-engineering and the reliable assessment of complex accidental loading, such as extreme bending due to loss of buoyancy of support, or abrupt ground movement. Currently, the focus of research in offshore deepwater installations and linepipes is towards pre-cracked structures with high triaxiality stress states and complex loading histories. At the same time, low triaxiality stress states must be correctly studied in order to represent shear dominated failure in pipes. A comprehensive experimental and numerical program was undertaken to determine the mechanical properties of the traditional API X70 grade of steel. The material was characterized for anisotropic plasticity, fracture initiation and uncracked ductility for various states of stress. The same material was also used for pre-cracked fracture toughness assessment. The experimental program included flat and round specimens. The first type of tests on flat butterfly-shaped, central hole, notched and circular disk specimens; were selected to address the low stress triaxiality range. Tests on round notched bar specimens and SENT fracture mechanics tests extended the characterization and verification process to higher stress triaxiality values. This program covered a wide range of stress conditions and demonstrated their effect on the material resistance to crack extension. Each test conducted was numerically simulated using solid finite element models, matching the exact geometric and loading history features. The numerical simulation provided information on the local stress and strain fields around the location of the potential or existing cracks. Based on the above hybrid experimental/numerical technique tailored for pipe applications, the MMC fracture model was calibrated. The model relates the material ductility not only to stress triaxiality but also to the Lode parameter. The predictive capabilities of the MMC were then evaluated in the case of SENT testing, used extensively in the pipeline industry. It was shown that the present fracture model calibration can describe fracture behavior of SENT experiments. KW - Ductile fracture KW - SENT tests KW - Offshore API grade KW - X70 KW - Modified Mohr – Coulomb model KW - Triaxiality and Lode angle dependence Y1 - 2013 U6 - https://doi.org/10.1016/j.ijpvp.2013.07.004 VL - 111-112 SP - 187 EP - 201 ER - TY - CHAP A1 - Kofiani, Kirki A1 - Nonn, Aida A1 - Wierzbicki, Tomasz A1 - Kalwa, Christoph A1 - Walters, Carey T1 - Experiments and fracture modeling of high-strength pipelines for high and low stress triaxiality T2 - 22nd International Society of Offshore and Polar Engineering 2012 (ISOPE 2012), Rhodes, Greece, June 2012 N2 - This paper provides results from a comprehensive study on mechanical characterization of high-strength pipeline steel, grade X100 using experimental and numerical methods. The material was characterized for anisotropic plasticity, fracture initiation for various states of stress, (pre-cracked) fracture toughness and uncracked ductility. The experimental program included tests on flat butterfly-shaped, central hole, notched and circular disk specimens for low stress triaxiality levels; as well as tests on round notched bar specimens and SENT fracture mechanics tests, for high values of stress triaxiality. This program covered a wide range of stress conditions and demonstrated its effect on the material resistance. Parallel to the experimental study, detailed numerical investigations were carried out to simulate all different experimental tests. Using an inverse method, a 3-parameter calibration was performed on the Modified Mohr-Coulomb (MMC) fracture model. Subsequently, the predictive capabilities of the MMC were evaluated by the comparison to the fracture toughness tests results, used extensively in the pipeline industry. The capabilities of the MIT fracture model have been demonstrated on an example of high strength offshore steel, X100. The outcome of this study was not only to provide, the overall characterization of the fracture behavior of this material as an example, but also to present the methodology on how to use the MMC model as a practical tool in pipeline design. Y1 - 2012 ER -