TY - JOUR A1 - Burdin, Dmitrii A. A1 - Chashin, Dmitri V. A1 - Ekonomov, Nikolai A. A1 - Fetisov, Leonid Y. A1 - Fetisov, Yuri K. A1 - Shamonin (Chamonine), Mikhail T1 - DC magnetic field sensing based on the nonlinear magnetoelectric effect in magnetic heterostructures JF - Journal of physics D: Applied physics N2 - Recently, highly sensitive magnetic field sensors using the magnetoelectric effect in composite ferromagnetic-piezoelectric layered structures have been demonstrated. However, most of the proposed concepts are not useful for measuring dc magnetic fields, because the conductivity of piezoelectric layers results in a strong decline of the sensor's sensitivity at low frequencies. In this paper, a novel functional principle of magnetoelectric sensors for dc magnetic field measurements is described. The sensor employs the nonlinear effect of voltage harmonic generation in a composite magnetoelectric structure under the simultaneous influence of a strong imposed ac magnetic field and a weak dc magnetic field to be measured. This physical effect arises due to the nonlinear dependence of the magnetostriction in the ferromagnetic layer on the magnetic field. A sensor prototype comprising of a piezoelectric fibre transducer sandwiched between two layers of the amorphous ferromagnetic Metglas (R) alloy was fabricated. The specifications regarding the magnetic field range, frequency characteristics, and noise level were studied experimentally. The prototype showed the responsivity of 2.5 V mT(-1) and permitted the measurement of dc magnetic fields in the range of similar to 10 nT to about 0.4 mT. Although sensor operation is based on the nonlinear effect, the sensor response can be made linear with respect to the measured magnetic field in a broad dynamic range extending over 5 orders of magnitude. The underlying physics is explained through a simplified theory for the proposed sensor. The functionality, differences and advantages of the magnetoelectric sensor compare well with fluxgate magnetometers. The ways to enhance the sensor performance are considered. KW - composite KW - magnetic field sensors KW - magnetic heterostructures KW - magnetoelectric effect KW - nonlinear magnetostriction KW - Sensors KW - voltage harmonic generation Y1 - 2016 U6 - https://doi.org/10.1088/0022-3727/49/37/375002 VL - 49 IS - 37 PB - IOP Publishing ER - TY - JOUR A1 - Dechant, Eduard A1 - Fedulov, Feodor A1 - Chashin, Dmitri V. A1 - Fetisov, Leonid Y. A1 - Fetisov, Yuri K. A1 - Shamonin (Chamonine), Mikhail T1 - Low-frequency, broadband vibration energy harvester using coupled oscillators and frequency up-conversion by mechanical stoppers JF - Smart Materials and Structures N2 - The frequencies of ambient vibrations are often low (below 30 Hz). A broadband (3 dB bandwidth is larger than 10 Hz at an acceleration amplitude of 9.81 m s(-2)) vibration based energy harvester is proposed for transducing mechanical energy at such low frequencies into electrical energy. The mechanical setup converts low frequency mechanical vibrations into high frequency resonance oscillations of the transducer. This conversion is done by mechanical impacts on two mechanical stoppers. The originality of the presented design is that both low-frequency and high-frequency oscillators are permanently mechanically coupled. In the equivalent mechanical circuit, this coupling is achieved by connecting the ends of the stiff spring to both seismic masses, whereas one seismic mass (collison member) is also attached to the soft spring used as the constitutive element of a low-frequency oscillator. Further, both mechanical oscillators are not realized as conventional cantilever beams. In particular, the high frequency oscillator with the natural frequency of 340 Hz is a disc-shaped diaphragm with attached piezoelectric elements and a seismic mass. It is shown that it is possible to convert mechanical vibrations with acceleration amplitude of 9.81 m s(-2) in the region between approximately 7 and 25 Hz into electrical power larger than 0.1 mW with the maximum value of 0.8 mW. A simplified mathematical model based on piecewise linear coupled oscillators shows good agreement with experimental results. The ways to enhance the performance of the harvester and improve agreement with experiments are discussed. KW - broadband KW - efficiency KW - frequency up-conversion KW - low frequency KW - mechanical stoppers KW - Modeling KW - OUTPUT KW - Piezoelectric transducer KW - vibration energy harvesting Y1 - 2017 U6 - https://doi.org/10.1088/1361-665X/aa6e92 VL - 26 IS - 6 PB - IOP Publishing ER - TY - JOUR A1 - Burdin, Dmitrii A. A1 - Ekonomov, Nikolai A. A1 - Chashin, Dmitri V. A1 - Fetisov, Leonid Y. A1 - Fetisov, Yuri K. A1 - Shamonin (Chamonine), Mikhail T1 - Temperature Dependence of the Resonant Magnetoelectric Effect in Layered Heterostructures JF - Materials N2 - The dependence of the resonant direct magnetoelectric effect on temperature is studied experimentally in planar composite structures. Samples of rectangular shapes with dimensions of 5 mm x 20 mm employed ferromagnetic layers of either an amorphous (metallic glass) alloy or nickel with a thickness of 20-200 m and piezoelectric layers of single crystalline langatate material or lead zirconate titanate piezoelectric ceramics with a thickness of 500 m. The temperature of the samples was varied in a range between 120 and 390 K by blowing a gaseous nitrogen stream around them. It is shown that the effective characteristics of the magnetoelectric effectsuch as the mechanical resonance frequency f(r), the quality factor Q and the magnitude of the magnetoelectric coefficient (E) at the resonance frequencyare contingent on temperature. The interrelations between the temperature changes of the characteristics of the magnetoelectric effect and the temperature variations of the following material parametersYoung's modulus Y, the acoustic quality factor of individual layers, the dielectric constant epsilon, the piezoelectric modulus d of the piezoelectric layer as well as the piezomagnetic coefficients ((n)) of the ferromagnetic layerare established. The effect of temperature on the characteristics of the nonlinear magnetoelectric effect is observed for the first time. The results can be useful for designing magnetoelectric heterostructures with specified temperature characteristics, in particular, for the development of thermally stabilized magnetoelectric devices. KW - acoustic quality factor KW - composite structure KW - linear KW - magnetoelectric effect KW - magnetoelectric heterostructure KW - magnetostriction KW - nonlinear KW - piezoelectric KW - temperature dependence Y1 - 2017 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:898-opus4-32185 N1 - corresponding author: Mikhail Shamonin VL - 10 IS - 10 PB - MDPI ER - TY - JOUR A1 - Saveliev, Dmitry A1 - Fetisov, Leonid Y. A1 - Chashin, Dmitri V. A1 - Fetisov, Yuri K. A1 - Khon, Anastasia A1 - Shamonin (Chamonine), Mikhail T1 - Effects of ferromagnetic-material thickness on magnetoelectric voltage transformation in a multiferroic heterostructure JF - Smart Materials and Structures N2 - A magnetoelectric (ME) voltage transformer is fabricated on the basis of a ferromagnetic (FM)-piezoelectric (PE) heterostructure comprising two equally thick laminated layers of an amorphous FM alloy and a piezoceramic lead zirconate-titanate layer sandwiched between them. The structure, placed inside an excitation coil, is electrically poled and magnetized in the direction of the long axis. The primary voltage is applied to the coil and the secondary voltage is measured between the electrodes of the PE material. It is shown for the first time that the change in the total thickness of magnetic layers significantly influences the transformer ' s characteristics. At the largest total thickness of FM layers of 138 mu m, the open-circuit voltage transformation ratio K has a maximum value of about 20, and the power transfer efficiency eta at a matched resistive load of about 20 k omega reaches 45%. The variation of the control magnetic field in the range of 0-21.6 kA m(-1) makes it possible to change the voltage transformation ratio K from zero to the maximum value. A simple model allows one to calculate the dependence of the characteristics of the ME transformer on the frequency of the primary voltage, thickness of the FM layers, control magnetic field, and the load. KW - magnetoelectric effect KW - magnetostriction KW - multiferroic heterostructure KW - piezoelectric effect KW - voltage transformer Y1 - 2021 U6 - https://doi.org/10.1088/1361-665X/abf6c0 VL - 30 IS - 6 PB - IOP PUBLISHING ER - TY - JOUR A1 - Saveliev, Dmitri A1 - Chashin, Dmitri V. A1 - Fetisov, Leonid Y. A1 - Shamonin (Chamonine), Mikhail A1 - Fetisov, Yuri K. T1 - Ceramic-Heterostructure-Based Magnetoelectric Voltage Transformer with an Adjustable Transformation Ratio JF - Materials N2 - A voltage transformer employing the magnetoelectric effect in a composite ceramic heterostructure with layers of a magnetostrictive nickel–cobalt ferrite and a piezoelectric lead zirconate–titanate is described. In contrast to electromagnetic and piezoelectric transformers, a unique feature of the presented transformer is the possibility of tuning the voltage transformation ratio K using a dc magnetic field. The dependences of the transformer characteristics on the frequency and the amplitude of the input voltage, the strength of the control magnetic field and the load resistance are investigated. The transformer operates in the voltage range between 0 and 112 V, and the voltage transformation ratio K is tuned between 0 and 14.1 when the control field H changes between 0 and 6.4 kA/m. The power at the transformer output reached 63 mW, and the power conversion efficiency was 34%. The methods for calculation of the frequency response, and the field and load characteristics of the transformer are proposed. The ways to improve performance characteristics of magnetoelectric transformers and their possible application areas are discussed. KW - magnetoelectric effect KW - piezoelectric effect KW - voltage transformer KW - composite material KW - magnetostriction Y1 - 2020 U6 - https://doi.org/10.3390/ma13183981 VL - 13 IS - 18 SP - 1 EP - 13 PB - MDPI ER - TY - JOUR A1 - Fetisov, Yuri K. A1 - Chashin, Dmitri V. A1 - Saveliev, Dmitri A1 - Fetisov, Leonid Y. A1 - Shamonin (Chamonine), Mikhail T1 - Anisotropic Magnetoelectric Effect in a Planar Heterostructure Comprising Piezoelectric Ceramics and Magnetostrictive Fibrous Composite JF - Materials N2 - The direct magnetoelectric (ME) effect is investigated in a planar structure comprising mechanically coupled layers of a magnetostrictive fibrous composite (MFC) and a piezoelectric ceramics (lead zirconate titanate, PZT). The MFC is an array of Ni-wires with a diameter of 200 mu m that are aligned parallel to each other in a single layer. The wires are separated by a distance of 250 or 500 mu m and fixed in a polyamide matrix. The structure was placed in a tangential constant field H and was excited by an alternating magnetic field h parallel to H, while the voltage generated by the PZT layer was measured. The resulting field dependences of the magnetization M(H) and the magnetostriction lambda(H) were determined by the orientation of the field H in the plane of the structure and the distance between the Ni-wires. The ME coupling coefficient of the structure decreased from 4.8 to 0.25 V/A when the orientation of H was changed from parallel to perpendicular to Ni-wires. With an increase in the excitation field amplitude h, a nonlinear ME effect in the output voltage, namely frequency doubling, was observed. The frequency and field dependences of the efficiency of the ME transduction in the MFC-piezoelectric heterostructure are well described by the existing theory. KW - composite KW - frequency doubling KW - heterostructure KW - magnetoelectric effect KW - magnetostrictive fiber KW - piezoelectric ceramic material Y1 - 2019 U6 - https://doi.org/10.3390/ma12193228 N1 - Corresponding authors: Yuri Fetisov, Mikhail Shamonin VL - 12 IS - 19 SP - 1 EP - 13 PB - MDPI CY - Basel ER - TY - JOUR A1 - Kreitmeier, Florian A1 - Chashin, Dmitri V. A1 - Fetisov, Yuri K. A1 - Fetisov, Leonid Y. A1 - Schulz, Irene A1 - Monkman, Gareth J. A1 - Shamonin (Chamonine), Mikhail T1 - Nonlinear Magnetoelectric Response of Planar Ferromagnetic-Piezoelectric Structures to Sub-Millisecond Magnetic Pulses JF - Sensors N2 - The magnetoelectric response of bi- and symmetric trilayer composite structures to pulsed magnetic fields is experimentally investigated in detail. The structures comprise layers of commercially available piezoelectric (lead zirconate titanate) and magnetostrictive (permendur or nickel) materials. The magnetic-field pulses have the form of a half-wave sine function with duration of 450 µs and amplitudes ranging from 500 Oe to 38 kOe. The time dependence of the resulting voltage is presented and explained by theoretical estimations. Appearance of voltage oscillations with frequencies much larger than the reciprocal pulse length is observed for sufficiently large amplitudes (~1-10 kOe) of the magnetic-field pulse. The origin of these oscillations is the excitation of bending and planar acoustic oscillations in the structures. Dependencies of the magnetoelectric voltage coefficient on the excitation frequency and the applied magnetic field are calculated by digital signal processing and compared with those obtained by the method of harmonic field modulation. The results are of interest for developing magnetoelectric sensors of pulsed magnetic fields as well as for rapid characterization of magnetoelectric composite structures. Y1 - 2012 U6 - https://doi.org/10.3390/s121114821 N1 - Corresponding author: Mikhail Shamonin VL - 12 IS - 11 SP - 14821 EP - 14837 PB - MDPI CY - Basel ER - TY - CHAP A1 - Kreitmeier, Florian A1 - Schulz, Irene A1 - Monkman, Gareth J. A1 - Shamonin (Chamonine), Mikhail A1 - Fetisov, Yuri K. A1 - Chashin, Dmitri V. A1 - Fetisov, Leonid Y. T1 - Observation of Nonlinear Magnetoelectric Response to Magnetic Pulses in Layered Magnetostrictive-Piezoelectric Structures N2 - A detailed experimental study of the magnetoelectric response of planar bi- and symmetric trilayer composite structures to magnetic field pulses is reported. The structures consist of layers of commercially available piezoelectric (lead zirconate titanate) and magnetostrictive (permendur or nickel) materials. The magnetic-field pulses have the form of a half-wave sine function with duration of 450 μs and amplitude from 500 Oe up to 38 kOe. The measurement method is explained and the measured time dependence of the resulting voltage is presented. The most interesting case, when pulse amplitudes are sufficiently large (~ 1-10 kOe) and various types of acoustic oscillation with frequencies much larger than the reciprocal pulse length are excited in the structures, is considered. The dependencies of the magnetoelectric voltage coefficient on the excitation frequency and the applied magnetic field are calculated. By digital signal processing the results are compared with those obtained by the method of harmonic field modulation (HFM). The findings are of interest for developing magnetoelectric sensors for pulsed magnetic fields as well as for rapid characterization of magnetoelectric composite structures. T2 - Proceedings of 2012 21st IEEE ISAF held jointly with 11th IEEE ECAPD and IEEE PFM (ISAF/ECAPD/PFM), 9th-13th of July 2012, Aveiro, Portugal KW - composite materials KW - magnetoelectric effect KW - magnetoelectric sensors KW - magnetostriction KW - piezoelectricity KW - magnetic field pulse Y1 - 2012 U6 - https://doi.org/10.1109/ISAF.2012.6297739 PB - IEEE ER - TY - JOUR A1 - Hörner, Eduard A1 - Krykanov, Ivan M. A1 - Chashin, Dmitry V. A1 - Fetisov, Yury K. A1 - Fetisov, Leonid Y. A1 - Shamonin (Chamonine), Mikhail T1 - Magnetoelectric characteristics of cobalt-iron alloy–lead zirconate titanate bilayer planar structures JF - International Journal of Materials Research N2 - The characteristics of both direct and converse magnetoelectric (ME) interactions in bilayer composite structures comprising layers of a commercially available magnetostrictive permendur CoFe alloy and different piezoelectric PZT ceramics are investigated in detail by the method of harmonic field modulation. It is shown that, given the optimum DC magnetic bias field, a high piezomagnetic coefficient in the alloy leads to increased efficiency of ME interactions. The resonant behavior of frequency dependencies of the magnetoelectric voltage is explained by excitation of bending and planar mechanical oscillations in the structures. The results are of interest for developing highly sensitive AC magnetic field sensors and magnetoelectric transducers for energy harvesting from mechanical vibrations. KW - Composite materials KW - Magnetostriction KW - Piezoelectricity KW - Magnetically ordered materials KW - Magnetoelectric effect Y1 - 2012 U6 - https://doi.org/10.3139/146.110776 VL - 103 IS - 11 PB - De Gruyter ER - TY - JOUR A1 - Dechant, Eduard A1 - Fedulov, Feodor A1 - Fetisov, Leonid Y. A1 - Shamonin (Chamonine), Mikhail T1 - Bandwidth Widening of Piezoelectric Cantilever Beam Arrays by Mass-Tip Tuning for Low-Frequency Vibration Energy Harvesting JF - Applied Science N2 - Wireless sensor networks usually rely on internal permanent or rechargeable batteries as a power supply, causing high maintenance efforts. An alternative solution is to supply the entire system by harvesting the ambient energy, for example, by transducing ambient vibrations into electric energy by virtue of the piezoelectric effect. The purpose of this paper is to present a simple engineering approach for the bandwidth optimization of vibration energy harvesting systems comprising multiple piezoelectric cantilevers (PECs). The frequency tuning of a particular cantilever is achieved by changing the tip mass. It is shown that the bandwidth enhancement by mass tuning is limited and requires several PECs with close resonance frequencies. At a fixed frequency detuning between subsequent PECs, the achievable bandwidth shows a saturation behavior as a function of the number of cantilevers used. Since the resonance frequency of each PEC is different, the output voltages at a particular excitation frequency have different amplitudes and phases. A simple power-transfer circuit where several PECs with an individual full wave bridge rectifier are connected in parallel allows one to extract the electrical power close to the theoretical maximum excluding the diode losses. The experiments performed on two- and three-PEC arrays show reasonable agreement with simulations and demonstrate that this power-transfer circuit additionally influences the frequency dependence of the harvested electrical power. KW - array KW - BAND-PASS FILTERS KW - bandwidth KW - BIMORPH KW - Optimization KW - OUTPUT KW - PERFORMANCE KW - piezoelectric cantilever KW - POWER KW - vibration energy harvesting Y1 - 2017 U6 - https://doi.org/10.3390/app7121324 N1 - Corresponding Author: Mikhail Shamonin VL - 7 IS - 12 PB - MDPI ER - TY - JOUR A1 - Saveliev, Dmitry V. A1 - Belyaeva, Inna A. A1 - Chashin, Dmitri V. A1 - Fetisov, Leonid Y. A1 - Romeis, Dirk A1 - Kettl, Wolfgang A1 - Kramarenko, Elena Yu A1 - Saphiannikova, M. A1 - Stepanov, Gennady V. A1 - Shamonin (Chamonine), Mikhail T1 - Giant extensional strain of magnetoactive elastomeric cylinders in uniform magnetic fields JF - Materials N2 - Elongations of magnetoactive elastomers (MAEs) under ascending–descending uniform magnetic fields were studied experimentally using a laboratory apparatus specifically designed to measure large extensional strains (up to 20%) in compliant MAEs. In the literature, such a phenomenon is usually denoted as giant magnetostriction. The synthesized cylindrical MAE samples were based on polydimethylsiloxane matrices filled with micrometer-sized particles of carbonyl iron. The impact of both the macroscopic shape factor of the samples and their magneto-mechanical characteristics were evaluated. For this purpose, the aspect ratio of the MAE cylindrical samples, the concentration of magnetic particles in MAEs and the effective shear modulus were systematically varied. It was shown that the magnetically induced elongation of MAE cylinders in the maximum magnetic field of about 400 kA/m, applied along the cylinder axis, grew with the increasing aspect ratio. The effect of the sample composition is discussed in terms of magnetic filler rearrangements in magnetic fields and the observed experimental tendencies are rationalized by simple theoretical estimates. The obtained results can be used for the design of new smart materials with magnetic-field-controlled deformation properties, e.g., for soft robotics. KW - magnetostriction KW - magnetoactive elastomer KW - extensional strain KW - hysteresis KW - magnetomechanical effect KW - magnetodeformation Y1 - 2020 U6 - https://doi.org/10.3390/ma13153297 SN - 1996-1944 N1 - Corresponding author: Mikhail Shamonin VL - 13 IS - 15 SP - 1 EP - 17 PB - MDPI CY - Basel ER - TY - JOUR A1 - Saveliev, Dmitry V. A1 - Belyaeva, Inna A. A1 - Chashin, Dmitri V. A1 - Fetisov, Leonid Y. A1 - Shamonin (Chamonine), Mikhail T1 - Large Wiedemann effect in a magnetoactive elastomer JF - Journal of Magnetism and Magnetic Materials N2 - Large twists of a soft tube (hollow cylinder) in helical magnetic fields are presented for the first time. Such a phenomenon is usually denoted as the Wiedemann effect. The tube is fabricated from a soft magnetoactive elastomer material with the shear modulus of about 56 kPa. The composite material comprises 80 mass% of micrometer-sized iron particles embedded into a polydimethylsiloxane matrix. The circular magnetic field is generated by an electric current in a straight wire passing through the inner hole of the tube. The maximum value of approximately 350″/cm is observed in a longitudinal magnetic field of a few kA/m overlapped with a circumferential magnetic field of about 1.4 kA/m on the surface of the inner hole. A pronounced hysteresis in the dependence of the Wiedemann effect on the circular magnetic field is found. The ways to enhance the Wiedemann twist in magnetoactive elastomers are discussed. The observed large effect is promising for application in magnetic-field controlled torsional actuators, in particular for soft robotics. Y1 - 2020 U6 - https://doi.org/10.1016/j.jmmm.2020.166969 VL - 511 IS - October PB - Elsevier ER - TY - CHAP A1 - Shamonin (Chamonine), Mikhail A1 - Dechant, Eduard A1 - Fedulov, Feodor A1 - Fetisov, Leonid Y. T1 - Bandwidth optimization of piezoelectric cantilever beam arrays for harvesting energy from broadband, low-frequency mechanical vibrations T2 - INTERMATIC 2016, 21.–25.11.2016, Moskau Y1 - 2016 UR - https://elibrary.ru/item.asp?id=29382003 VL - 16 SP - 187 EP - 190 CY - Moskau ER - TY - JOUR A1 - Saveliev, Dmitry V. A1 - Glavan, Gašper A1 - Belan, Viktoria O. A1 - Belyaeva, Inna A. A1 - Fetisov, Leonid Y. A1 - Shamonin (Chamonine), Mikhail T1 - Resonant Magnetoelectric Effect at Low Frequencies in Layered Polymeric Cantilevers Containing a Magnetoactive Elastomer JF - Applied Sciences N2 - In this work, the resonance enhancement of magnetoelectric (ME) coupling at the two lowest bending resonance frequencies was investigated in layered cantilever structures comprising a magnetoactive elastomer (MAE) slab and a commercially available piezoelectric polymer multilayer. A cantilever was fixed at one end in the horizontal plane and the magnetic field was applied horizontally. Five composite structures, each containing an MAE layer of different thicknesses from 0.85 to 4 mm, were fabricated. The fundamental bending resonance frequency in the absence of a magnetic field varied between roughly 23 and 55 Hz. It decreased with the increasing thickness of the MAE layer, which was explained by a simple theory. The largest ME voltage coefficient of about 7.85 V/A was measured in a sample where the thickness of the MAE layer was ≈2 mm. A significant increase in the bending resonance frequencies in the applied DC magnetic field of 240 kA/m up to 200% was observed. The results were compared with alternative designs for layered multiferroic structures. Directions for future research were also discussed. KW - flexible composite KW - low frequency KW - magnetoactive elastomer KW - magnetoelectric effect KW - piezoelectric polymer Y1 - 2022 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:898-opus4-30637 N1 - corresponding authors: Dmitry V. Saveliev and Mikhail Shamonin VL - 12 IS - 4 SP - 1 EP - 13 PB - MPDI ER - TY - JOUR A1 - Saveliev, Dmitry V. A1 - Fetisov, Leonid Y. A1 - Chashin, Dmitri V. A1 - Shabin, P. A. A1 - Vyunik, D. A. A1 - Fedulov, Feodor A1 - Kettl, W. A1 - Shamonin (Chamonine), Mikhail T1 - Method of Measuring Deformations of Magnetoactive Elastomers under the Action of Magnetic Fields JF - Russian Technological Journal Y1 - 2019 U6 - https://doi.org/10.32362/2500-316x-2019-7-4-81-91 VL - 7 IS - 4 SP - 81 EP - 91 ER - TY - GEN A1 - Pershina, K. V. A1 - Saveliev, Dmitry V. A1 - Glavan, Gašper A1 - Chashin, Dmitri V. A1 - Belyaeva, Inna A. A1 - Fetisov, Leonid Y. A1 - Shamonin (Chamonine), Mikhail T1 - The voltage response of a structure comprising a magnetoactive-elastomer cylinder and a piezoelectric material to magnetic field step excitations T2 - The 4th International Baltic Conference on Magnetism (IBCM 2021) : Svetlogorsk, Russia August 29 - September 2, 2021 : Book of Abstracts Y1 - 2021 UR - http://smba.science/wp-content/uploads/2021/10/IBCM-2021-Book-of-Abstracts-5.pdf SP - 182 PB - Immanuel Kant Baltic Federal University, Kaliningrad, Russia ER -