TY - JOUR A1 - Kravanja, Gaia A1 - Belyaeva, Inna A. A1 - Hribar, Luka A1 - Drevenšek‐Olenik, Irena A1 - Shamonin (Chamonine), Mikhail A1 - Jezeršek, Matija T1 - Laser Micromachining of Magnetoactive Elastomers as Enabling Technology for Magnetoresponsive Surfaces JF - Advanced Materials Technologies N2 - A simple method for structuring of the surface of a magnetoactive elastomer (MAE) on the tens of micrometers scale, which capabilities extend beyond conventional mold-based polymer casting, is reported. The method relies on the ablation of the material by absorption of nanosecond infrared pulses from a commercial laser. It is shown that it is possible to fabricate parallel lamellar structures with a high aspect ratio (up to 6:1) as well as structures with complex scanning trajectories. The method is fast (fabrication time for the 7 × 7 mm2 is about 60 s), and the results are highly reproducible. To illustrate the capabilities of the fabrication method, both orthogonal to the MAE surface and tilted lamellar structures are fabricated. These magnetosensitive lamellae can be easily bent by ±45° using an external magnetic field of about 230 mT. It is demonstrated that this bending allows one to control the sliding angle of water droplets in a great range between a sticky (>90°) and a sliding state (<20°). Perspectives on employing this fabrication technology for magnetosensitive smart surfaces in microfluidic devices and soft robotics are discussed. Y1 - 2021 U6 - https://doi.org/10.1002/admt.202101045 VL - 7 IS - 5 SP - 1 EP - 8 PB - Wiley ER - TY - JOUR A1 - Kravanja, Gaia A1 - Belyaeva, Inna A. A1 - Hribar, Luka A1 - Drevenšek‐Olenik, Irena A1 - Jezeršek, Matija A1 - Shamonin (Chamonine), Mikhail T1 - Tunable Drop Splashing on Magnetoactive Elastomers JF - Advanced Materials Interfaces N2 - The significant effect of an external dc magnetic field on the splashing behavior of ethanol drops impacting on the unstructured (flat) surface of soft magnetoactive elastomers (MAEs) is reported. The Weber number corresponding to the transition between the deposition and the splashing regime is reduced by ≈20% in a moderate magnetic field of ≈300 mT. Alongside this effect, a two-fold increase of the initial deceleration of the ejection sheet is observed for the softest sample. The main underlying mechanism for the observed phenomena is believed to be the magnetic-field-induced stiffening of the MAEs. Further possible mechanisms are magnetically induced changes in the surface roughness and magnetic-field-induced plasticity (magnetic shape memory effect). The potential application areas are magnetically regulable wetting and magneto-responsive surfaces for controlling the drop splashing. Y1 - 2021 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:898-opus4-24504 N1 - Corresponding author: Mikhail Shamonin VL - 8 IS - 11 SP - 1 EP - 7 PB - Wiley ER - TY - JOUR A1 - Lovšin, Matija A1 - Brandl, Dominik A1 - Glavan, Gašper A1 - Belyaeva, Inna A. A1 - Cmok, Luka A1 - Coga, Lucija A1 - Kalin, Mitjan A1 - Shamonin (Chamonine), Mikhail A1 - Drevenšek‐Olenik, Irena T1 - Reconfigurable Surface Micropatterns Based on the Magnetic Field-Induced Shape Memory Effect in Magnetoactive Elastomers JF - Polymers N2 - A surface relief grating with a period of 30 mu m is embossed onto the surface of magnetoactive elastomer (MAE) samples in the presence of a moderate magnetic field of about 180 mT. The grating, which is represented as a set of parallel stripes with two different amplitude reflectivity coefficients, is detected via diffraction of a laser beam in the reflection configuration. Due to the magnetic-field-induced plasticity effect, the grating persists on the MAE surface for at least 90 h if the magnetic field remains present. When the magnetic field is removed, the diffraction efficiency vanishes in a few minutes. The described effect is much more pronounced in MAE samples with larger content of iron filler (80 wt%) than in the samples with lower content of iron filler (70 wt%). A simple theoretical model is proposed to describe the observed dependence of the diffraction efficiency on the applied magnetic field. Possible applications of MAEs as magnetically reconfigurable diffractive optical elements are discussed. It is proposed that the described experimental method can be used as a convenient tool for investigations of the dynamics of magnetically induced plasticity of MAEs on the micrometer scale. KW - ADHESION KW - friction KW - magnetoactive elastomers KW - magnetorheological elastomer KW - optical diffraction KW - shape memory effect KW - surface microstructuring KW - TEMPERATURE Y1 - 2021 U6 - https://doi.org/10.3390/polym13244422 VL - 13 IS - 24 PB - MDPI ER -