TY - CHAP A1 - Langer, Christoph A1 - Prommesberger, Christian A1 - Ławrowski, Robert Damian A1 - Müller, F. A1 - Schreiner, Rupert A1 - Serbun, Pavel A1 - Müller, Günter T1 - Enhanced field emission from p-doped black silicon on pillar structures T2 - 2015 28th International Vacuum Nanoelectronics Conference (IVNC), 13-17 July 2015, Guangzhou, China N2 - Aligned square arrays of black silicon (b-Si) on top of pillars were fabricated on p-type silicon substrate by a deep-etching step combined with a b-Si process. Two 10×10 arrays with pillar heights of 8 μm and 20 μm and one b-Si reference sample without pillars were investigated. Integral field emission (FE) measurements of the arrays yielded rather low onset-fields between 6.4 V/μm and 13.5 V/μm and field enhancement factors between 430 and 800. The I-V curves showed typical Fowler-Nordheim behavior for low fields, whereas a saturation region was observed at higher fields. The maximum integral current in the saturation region was 8 μA at a field of 20 V/μm. The stability of the emission current was investigated over 3 hours and revealed moderate fluctuations of ± 8% in the saturation region. Voltage scans showed well-aligned FE from nearly all pillars. KW - black silicon KW - CATHODES KW - Current measurement KW - Etching KW - FABRICATION KW - field emission KW - field emitter array KW - Iron KW - silicon KW - Vacuum technology Y1 - 2015 U6 - https://doi.org/10.1109/IVNC.2015.7225547 SP - 104 EP - 105 PB - IEEE ER - TY - CHAP A1 - Serbun, Pavel A1 - Porshyn, Vitali A1 - Müller, Günter A1 - Lützenkirchen-Hecht, Dirk A1 - Prommesberger, Christian A1 - Langer, Christoph A1 - Ławrowski, Robert Damian A1 - Schreiner, Rupert T1 - Field emission behavior of single n- and p-type black Si pillar structures T2 - International Vacuum Nanoelectronics Conference (IVNC), 31st, 2018, Kyoto, Japan N2 - We have investigated the properties of single n- and p-type black silicon (b-Si) pillars with a height of 20 μ m under strong electric field and halogen lamp or laser illumination. For both type of b-Si pillar structures, I-V measurements revealed strong activation effects, which consisted in sudden current increases during the first up/down voltage sweeps. The maximum reproducible emission current from a single n-type b-Si pillar structure was about 15 μ A. A pronounced saturation region at 240 nA was observed for a single p-type b-Si pillar. The current fluctuation over time showed a standard deviation of 28% and 2.5% for n- and p-type single b-Si pillar structures, respectively. Optical switching under halogen lamp illumination resulted in at least 3 times higher saturation currents and showed a linear dependence of the FE current on the laser power. KW - field emission KW - black silicon KW - photoemission Y1 - 2018 U6 - https://doi.org/10.1109/IVNC.2018.8520292 PB - IEEE ER - TY - CHAP A1 - Serbun, Pavel A1 - Porshyn, Vitali A1 - Müller, Günter A1 - Mingels, Stephan A1 - Lützenkirchen-Hecht, Dirk A1 - Bachmann, Michael A1 - Düsberg, Felix A1 - Dams, Florian A1 - Hofmann, Martin A1 - Pahlke, Andreas A1 - Prommesberger, Christian A1 - Langer, Christoph A1 - Ławrowski, Robert Damian A1 - Schreiner, Rupert T1 - Field emission behavior of Au-tip-coated p-type Si pillar structures T2 - 29th International Vacuum Nanoelectronics Conference (IVNC), 2016, 11-15 July, Vancouver, BC, Canada N2 - Precisely aligned high-aspect-ratio (HAR) silicon tip arrays were fabricated using enhanced reactive ion etching with an inductively-coupled-plasma followed by a sharpening oxidation. A gold thin film was then sputtered only on the tips of the HAR structures. Field-emission (FE) properties from Au-coated HAR p-Si tip array cathodes have been systematically investigated by means of field emission scanning microscopy (FESM). A rather high efficiency of the HAR Si structures (71% at 550 V), but limited homogeneous FE with currents of 1-600 nA might be correlated with the varying geometry of the tips and the presence of oxides. I-V measurements of single Au-coated HAR emitters revealed activation effects and the saturation current region at 3 nA. An increase of the saturation current by 4 orders of magnitude was observed during 20 hours of conditioning at constant voltage, which finally resulted in nearly reproducible FN curves with a ß-factor of 473. An excellent stability of the emission current of less than 1 % was obtained during the additional long-time conditioning at constant voltage. Optical switching under halogen lamp illumination resulted in at least 2 times higher saturation currents and showed a linear dependence of the FE current on the light color temperature. KW - field emission KW - p-type Si-pillar array KW - surface oxide effects KW - photoemission Y1 - 2016 U6 - https://doi.org/10.1109/IVNC.2016.7551516 SN - 2380-6311 SP - 181 EP - 182 PB - IEEE ER - TY - CHAP A1 - Serbun, Pavel A1 - Porshyn, Vitali A1 - Lützenkirchen-Hecht, Dirk A1 - Prommesberger, Christian A1 - Langer, Christoph A1 - Ławrowski, Robert Damian A1 - Schreiner, Rupert T1 - Photosensitivity of single silicon high-aspect-ratio tips with different doping levels T2 - International Vacuum Nanoelectronics Conference (IVNC), 31st, 2018, Kyoto, Japan N2 - Photosensitivity of single lightly p-doped, highly p-doped, with an integrated p/n junction and intrinsic high-aspect-ratio (HAR) silicon tips was investigated in an ultra-high vacuum environment. The current-voltage characteristics (I-V) of the lightly doped p-type HAR tips showed a characteristic current saturation at around 10-12 nA, whereas the HAR Si tips with p/n junction showed similar saturation phenomena, however, at much smaller current values starting at ~20-30 pA. Optical switching under a halogen lamp illumination resulted in at least 2-4 times higher saturation currents and showed a linear dependence between the illumination power and the FE current, for both types of structures. In case of the highly p-doped HAR tips optical current switching effects, i. e. current saturation, were observed at rather low current levels 1-2 pA. Intrinsic HAR Si-tips showed relative unstable field emission behavior without a clear evidence of the photosensitivity. KW - field emission KW - Si p/n junction KW - p-type Si KW - photosensitivity Y1 - 2018 U6 - https://doi.org/10.1109/IVNC.2018.8520288 PB - IEEE ER - TY - CHAP A1 - Ławrowski, Robert Damian A1 - Langer, Christoph A1 - Prommesberger, Christian A1 - Schreiner, Rupert A1 - Mingels, Stephan A1 - Porshyn, Vitali A1 - Serbun, Pavel A1 - Müller, Günter T1 - Field emission from surface textured GaN with buried double-heterostructures T2 - 2015 28th International Vacuum Nanoelectronics Conference (IVNC), 13-17 July 2015, Guangzhou, China N2 - In this contribution we report on field emission (FE) cathodes based on thin-film LED-technology and surface texturing. The FE cathode can be used both as an n-GaN cathode with an electrical contact at the top side metallization as well as a pn-GaN diode contacting only the p-GaN layer at the bottom side of the structure. The local and integral FE properties of the textured surface of the LED structure were investigated. For n-GaN an integral emission current up to 1.0 μA at an electric field of 19 V/μm was achieved. The pn-GaN diode measurements showed an integral current saturation behavior with two orders of magnitude lower FE currents. Regulated voltage scans obtained by FE scanning microscopy revealed a well-distributed emission over the whole cathode area. Measurements under pulsed tunable laser illumination and moderate electric fields indicated charge carrier generation in the buried double-heterostructures at photon energies below 3.5 eV besides normal photoemission above 4.1 eV. KW - CATHODES KW - Current measurement KW - Electric fields KW - field emission KW - Gallium nitride KW - GaN KW - Iron KW - Light emitting diodes KW - photoemission KW - Surface texture Y1 - 2015 U6 - https://doi.org/10.1109/IVNC.2015.7225548 SP - 106 EP - 107 PB - IEEE ER - TY - CHAP A1 - Ławrowski, Robert Damian A1 - Langer, Christoph A1 - Schreiner, Rupert A1 - Sellmair, Josef T1 - Nano Emitters on Silicon Pillar Structures generated by a Focused Electron Beam Induced Deposition T2 - International Vacuum Nanoelectronics Conference (IVNC), 31st, 2018, Kyoto, Japan N2 - Nano emitters were deposited by focused electron beam induced deposition of Trimethyl-(methylcyclopentadienyl)platinum(IV) on top of silicon pillars. The nano emitters were exactly positioned in the center on the top of up to four pillars of a quadratic arranged array of sixteen pillars with a pitch of 50 μm. Integral field emission measurements were performed in a diode configuration with a 50 μm mica spacer in a vacuum chamber at pressures of about 10 -9 mbar. The Fowler-Nordheim plots show a linear behavior, like expected for an n-type silicon material and a metal needle. The I-V measurement of the most promising sample shows an integral emission current up to 2 μm at a voltage of 600 V (12 MV/m) and an onset voltage for a current of 1 nA of about 300 V. KW - field emission KW - nano emitter KW - focused electron beam induced deposition KW - MeCpPtMe3 Y1 - 2018 U6 - https://doi.org/10.1109/IVNC.2018.8520059 PB - IEEE ER -