TY - CHAP A1 - Langer, Christoph A1 - Ławrowski, Robert Damian A1 - Prommesberger, Christian A1 - Dams, Florian A1 - Serbun, Pavel A1 - Bachmann, Michael A1 - Müller, Günter A1 - Schreiner, Rupert T1 - High aspect ratio silicon tip cathodes for application in field emission electron sources T2 - 2014 27th International Vacuum Nanoelectronics Conference (IVNC), 6-10 July 2014, Engelberg, Switzerland N2 - Precisely aligned arrays of sharp tip structures on top of elongated pillars were realized by using an improved fabrication process including an additional inductively-coupled-plasma reactive-ion etching step. Arrays of n-type and p-type silicon with 271 tips have been fabricated and investigated. Those structures have a total height of 5–6 µm and apex radii less than 20nm. Integral field emission measurements of the arrays yielded low onset-fields in the range of 8–12V=µm and field enhancement factors between 300 and 700. The I-E curves of n-type structures showed the usual Fowler-Nordheim behaviour, whereas p-type structures revealed a significant saturation region due to the limited number of electrons in the conduction band and a further carrier depletion effect caused by the pillar. The maximum integral current in the saturation region was 150 nA at fields above 30V=µm. An excellent stability of the emission current of less than ± 2% fluctuation was observed in the saturation region. For n-type Si a maximum integral current of 10 µA at 24V=µm and an average current stability with a fluctuation of ± 50% were measured. KW - Current measurement KW - Etching KW - FABRICATION KW - field emission KW - field emitter array KW - GEOMETRY KW - Iron KW - Sensor arrays KW - silicon KW - silicon tip Y1 - 2014 U6 - https://doi.org/10.1109/IVNC.2014.6894824 SP - 222 EP - 223 PB - IEEE ER - TY - CHAP A1 - Bieker, Johannes A1 - Roustaie, Farough A1 - Schlaak, H. F. A1 - Langer, Christoph A1 - Schreiner, Rupert T1 - Field emission characterization of in-situ deposited metallic nanocones T2 - 2017 30th International Vacuum Nanoelectronics Conference (IVNC), 10-14 July 2017, Regensburg, Germany N2 - An in-situ fabrication technique based on ion track etched template electrodeposition of metallic nanocones was used for the production of field emitter cathodes. Gold nanocones with a height of 24 microns, a base diameter between 3 to 4 microns and a tip diameter below 300 nanometers were deposited on a circular electrode with a diameter of 2.5 mm. The integral field emission (FE) measurements of samples with cone densities of 6 · 104 cones/cm2 (sample A) and 1 · 106 cones/cm2 (sample B) yielded in a maximum current of 37.5 μA at an applied field of 12.5 V/μm for sample A and 29.1 μA at 9.4 V/μm for sample B. The stability of emission current was investigated for over 48 hours and no degradation was observed. KW - CATHODES KW - Current measurement KW - FABRICATION KW - field emission KW - ion track template KW - Ions KW - Iron KW - nanocones KW - Vacuum technology KW - Voltage measurement Y1 - 2017 U6 - https://doi.org/10.1109/IVNC.2017.8051571 SP - 120 EP - 121 PB - IEEE ER - TY - CHAP A1 - Prommesberger, Christian A1 - Langer, Christoph A1 - Ławrowski, Robert Damian A1 - Muller, F. A1 - Dams, Florian A1 - Schreiner, Rupert A1 - Serbun, Pavel A1 - Müller, Günter T1 - Comparison of integral and local field-emission properties of Mo-coated p-Si tip arrays T2 - 2015 28th International Vacuum Nanoelectronics Conference (IVNC), 13-17 July 2015, Guangzhou, China N2 - Silicon tip arrays were fabricated by means of reactive ion etching followed by oxidation for final sharpening and molybdenum thin film coating. The field-emission (FE) properties of these Mo-coated p-Si tip arrays were systemically investigated by different measurement techniques. Integral measurements in diode configuration yielded a turn-on field (for 1 nA) of 22 V/μm and nearly stable FE currents up to 6.6 μA at 38 V/μm. The effective field enhancements factor extracted from the FN plots is about 180. Detailed investigations of these FE arrays were also performed by means of field emission scanning microscopy combined with electron microscopy. A rather limited efficiency of the tips (50% at 1500 V) and FE homogeneity (180 nA at 700 V) might be correlated with the varying morphology of the tips and the presence of oxides. Local I-V measurements of selected single tips revealed both activation and deactivation effects, which finally resulted in nearly reproducible I-V curves. Current stability measurements at a constant voltage showed rather large fluctuations (0.1-1 μA) of the FE current, which could be reduced up to 1.7% by using of a PID-regulated voltage source. SEM images showed unchanged tip shape after the current processing. KW - CATHODES KW - Coatings KW - Current measurement KW - field emission KW - Iron KW - Mo-coated KW - p-Si tip KW - Scanning electron microscopy KW - silicon KW - tip arrays KW - Vacuum technology Y1 - 2015 U6 - https://doi.org/10.1109/IVNC.2015.7225579 SP - 192 EP - 193 PB - IEEE ER - TY - CHAP A1 - Ławrowski, Robert Damian A1 - Langer, Christoph A1 - Prommesberger, Christian A1 - Schreiner, Rupert A1 - Mingels, S. A1 - Porshyn, V. A1 - Serbun, Pavel A1 - Müller, Günter T1 - Field emission from surface textured GaN with buried double-heterostructures T2 - 2015 28th International Vacuum Nanoelectronics Conference (IVNC), 13-17 July 2015, Guangzhou, China N2 - In this contribution we report on field emission (FE) cathodes based on thin-film LED-technology and surface texturing. The FE cathode can be used both as an n-GaN cathode with an electrical contact at the top side metallization as well as a pn-GaN diode contacting only the p-GaN layer at the bottom side of the structure. The local and integral FE properties of the textured surface of the LED structure were investigated. For n-GaN an integral emission current up to 1.0 μA at an electric field of 19 V/μm was achieved. The pn-GaN diode measurements showed an integral current saturation behavior with two orders of magnitude lower FE currents. Regulated voltage scans obtained by FE scanning microscopy revealed a well-distributed emission over the whole cathode area. Measurements under pulsed tunable laser illumination and moderate electric fields indicated charge carrier generation in the buried double-heterostructures at photon energies below 3.5 eV besides normal photoemission above 4.1 eV. KW - CATHODES KW - Current measurement KW - Electric fields KW - field emission KW - Gallium nitride KW - GaN KW - Iron KW - Light emitting diodes KW - photoemission KW - Surface texture Y1 - 2015 U6 - https://doi.org/10.1109/IVNC.2015.7225548 SP - 106 EP - 107 PB - IEEE ER - TY - CHAP A1 - Langer, Christoph A1 - Prommesberger, Christian A1 - Ławrowski, Robert Damian A1 - Müller, F. A1 - Schreiner, Rupert A1 - Serbun, Pavel A1 - Müller, Günter T1 - Enhanced field emission from p-doped black silicon on pillar structures T2 - 2015 28th International Vacuum Nanoelectronics Conference (IVNC), 13-17 July 2015, Guangzhou, China N2 - Aligned square arrays of black silicon (b-Si) on top of pillars were fabricated on p-type silicon substrate by a deep-etching step combined with a b-Si process. Two 10×10 arrays with pillar heights of 8 μm and 20 μm and one b-Si reference sample without pillars were investigated. Integral field emission (FE) measurements of the arrays yielded rather low onset-fields between 6.4 V/μm and 13.5 V/μm and field enhancement factors between 430 and 800. The I-V curves showed typical Fowler-Nordheim behavior for low fields, whereas a saturation region was observed at higher fields. The maximum integral current in the saturation region was 8 μA at a field of 20 V/μm. The stability of the emission current was investigated over 3 hours and revealed moderate fluctuations of ± 8% in the saturation region. Voltage scans showed well-aligned FE from nearly all pillars. KW - black silicon KW - CATHODES KW - Current measurement KW - Etching KW - FABRICATION KW - field emission KW - field emitter array KW - Iron KW - silicon KW - Vacuum technology Y1 - 2015 U6 - https://doi.org/10.1109/IVNC.2015.7225547 SP - 104 EP - 105 PB - IEEE ER - TY - CHAP A1 - Kleshch, Victor I. A1 - Serbun, Pavel A1 - Orekhov, Anton A1 - Lützenkirchen-Hecht, Dirk A1 - Obraztsov, Alexander N. A1 - Prommesberger, Christian A1 - Langer, Christoph A1 - Schreiner, Rupert A1 - Lutzenkirchen-Hecht, Dirk T1 - Field emission properties of p-type silicon tips decorated with tungsten nanoparticles T2 - 2017 30th International Vacuum Nanoelectronics Conference (IVNC), 10-14 July 2017, Regensburg, Germany N2 - An array of conical-shaped p-type silicon tips was fabricated by using reactive ion etching and sharpening oxidation. The apex of each tip was decorated by a tungsten hemispherical nanoparticle. Field emission properties of the tips were measured by a tungsten-needle anode positioned above the tip apex. Tips decorated with tungsten nanoparticles demonstrated a smaller saturation region in current-voltage characteristics compared to the pristine tips. An emission activation process, which consisted in sudden current increase at certain value of applied voltage, was observed for the decorated silicon tips. This behavior was explained by the formation of vertical protrusions extending from the metal particles revealed by scanning electron microscopy after field emission experiments. KW - Current measurement KW - field emission KW - Ions KW - Iron KW - metal nanoparticles KW - nanoparticles KW - p-type silicon KW - Scanning electron microscopy KW - silicon KW - Tungsten Y1 - 2017 U6 - https://doi.org/10.1109/IVNC.2017.8051580 SP - 138 EP - 139 PB - IEEE ER - TY - CHAP A1 - Schreiner, Rupert A1 - Langer, Christoph A1 - Prommesberger, Christian A1 - Mingels, S. A1 - Serbun, Pavel A1 - Müller, Güntner T1 - Field emission from surface textured extraction facets of GaN light emitting diodes T2 - 26th International Vacuum Nanoelectronics Conference (IVNC), 8-12 July 2013, Roanoke, VA, USA N2 - We report on the field emission properties of GaN LED surfaces. The textured extraction facet acts both as light scattering layer in order to increase the light extraction efficiency of the LED as well as nanostructured cathode surface for the field emission (FE) of electrons. The LED emits blue light with a peak wavelength of around 450 nm. The FE properties were investigated by a scanning microscope. Integral measurements as well as regulated voltage scans for 1 nA FE current over an area of 400 * 400 µm2were used to investigate both overall and local FE properties. A high number of well-distributed emitters with an average field enhancement factor ß of 85 and stable integral emission currents up to 100 µA at an electric field of   80 V/µm (Øanode= 880 µm) were found. Photo-field-emission spectroscopy (PFES) using a tunable pulsed laser revealed an enhanced photo absorption of the InGaN/GaN quantum well structures near the emission wavelength of the LED (<3.5 eV), whereas at high photon energies (>4.1 eV) photoemission from the GaN surface was observed. KW - Gallium nitride KW - Iron KW - Light emitting diodes KW - Cathodes KW - Surface texture KW - Surface waves KW - Photonics Y1 - 2013 U6 - https://doi.org/10.1109/ivnc.2013.6624721 PB - IEEE ER - TY - CHAP A1 - Serbun, Pavel A1 - Navitski, Aliaksandr A1 - Müller, Güntner A1 - Schreiner, Rupert A1 - Prommesberger, Christian A1 - Langer, Christoph A1 - Dams, Florian T1 - Scaling of the field emission current from B-doped Si-tip arrays T2 - 25th International Vacuum Nanoelectronics Conference (IVNC) ; Jeju, Korea (South), 09.07.2012 - 13.07.2012 N2 - We have fabricated a test chip with various hexagonal arrays of B-doped Si tips (height ~ 3 μm, apex radius <; 30 nm, number 1-4447, resistivity 4 Ωcm, 100 orientation) in triangular arrangement (pitch 10 μm, density 1.16×10 6 cm -2 ) in order to systematically investigate the field emission current scaling with the number N of tips. Regulated voltage scans for 1 nA revealed rather efficient emission from nearly all tips of the arrays at an average field of 15 V/μm. The expected current plateau was always obtained at fields around 20 V/μm, but its width strongly increased with N. In this carrier depletion range, the single tip provided a much higher stability (<; 5%) of the current (2-3 nA) than at lower (>; 50 %) and higher currents (>; 30%). Integral current measurements of the hexagonal arrays resulted in a statistically improved current stability (<; 1%) but only a weak increase of the total current with N 0.28 yet. These results will be discussed with respect to the remaining inhomogeneity of the tips. KW - Anodes KW - B-doped KW - boron KW - Current measurement KW - current scaling KW - electron field emission KW - elemental semiconductors KW - field emitter arrays KW - Iron KW - Nonhomogeneous media KW - silicon KW - Voltage control Y1 - 2012 SN - 978-1-4673-1984-3 SN - 978-1-4673-1983-6 SN - 978-1-4673-1982-9 U6 - https://doi.org/10.1109/IVNC.2012.6316965 SN - 2380-6311 SN - 2164-2370 SP - 1 EP - 2 PB - IEEE CY - Piscataway, N.J. ER - TY - CHAP A1 - Schreiner, Rupert A1 - Langer, Christoph A1 - Prommesberger, Christian A1 - Ławrowski, Robert Damian A1 - Dams, Florian A1 - Bachmann, Michael A1 - Düsberg, F. A1 - Hofmann, M. A1 - Pahlke, A. A1 - Serbun, Pavel A1 - Mingels, S. A1 - Müller, Günter T1 - Semiconductor field emission electron sources using a modular system concept for application in sensors and x-ray-sources T2 - 2015 28th International Vacuum Nanoelectronics Conference (IVNC), 13-17 July 2015, Guangzhou, China N2 - Semiconductor field emitters are suitable candidates for applications, which require a very stable field emission (FE) current and a high emission uniformity over the entire emission area. By using different materials and geometries, we are able to vary the FE characteristics within a wide range. Each specific application requires its own optimized design for the cathode as well as for the other parts of the FE electron source. To meet as many of these requirements as possible while using only a limited number of different prefabricated components, we established a modular system concept for our FE electron source. This allows the implementation of almost every cathode material. For first characterizations, we used gated p-type Si cathodes with 16 tips. We obtained stable FE currents of 0.4 μA for a grid-potential of 400 V and a gate potential of 100 V. Almost 100% of the electrons are emitted towards the grid-electrode. Parasitic leakage paths, as well as the electron emission towards the gate-electrode can be neglected. Approximately 10% of the electrons are transmitted through the grid and reach the external anode. This is in good agreement with the optical transmission through the grid-mesh. KW - Anodes KW - CATHODES KW - electron sources KW - GEOMETRY KW - Iron KW - Logic gates KW - semiconductor field emission KW - silicon Y1 - 2015 U6 - https://doi.org/10.1109/IVNC.2015.7225572 SP - 178 EP - 179 PB - IEEE ER - TY - CHAP A1 - Prommesberger, Christian A1 - Langer, Christoph A1 - Ławrowski, Robert Damian A1 - Dams, Florian A1 - Schreiner, Rupert A1 - Ławrowski, Robert Damian T1 - Gated p-Si field emitter arrays for sensor applications T2 - 2015 28th International Vacuum Nanoelectronics Conference (IVNC) N2 - We report on gated p-type Si-tip array cathodes for implementation into field emission electron sources for sensor applications. Arrays of 16 and 100 tips with tip heights of 3 μm and tip radii below 30 nm with integrated gate electrodes concentrically positioned 2 μm below the tip apexes were fabricated using an improved process, which leads to an enhanced isolation layer quality with sufficient breakdown field strengths and low leakage currents. Integral measurements with a fixed grid potential of 400 V showed emission currents up to 35 μA for 100 tips at a cathode voltage of 150 V and an almost negligible parasitic gate current. The array with 16 p-type Si-tips showed a significant stabilization of the emission current in the range of 0.3 - 0.4 μA, for cathode voltages between 90 V and 150 V. The current fluctuation in this saturation regime was measured for 10 minutes and a value of less than ± 1% was observed. No degradation of the cathode was found after 6 hours of operation at a constant cathode voltage of 100 V and a constant grid voltage of 400 V. KW - CATHODES KW - Current measurement KW - Current stabilization KW - field emission KW - integrated gate-electrode KW - Iron KW - Logic gates KW - semiconductor KW - Semiconductor device measurement KW - silicon KW - silicon tip array Y1 - 2015 U6 - https://doi.org/10.1109/IVNC.2015.7225567 SP - 164 EP - 165 PB - IEEE ER -