TY - CHAP A1 - Serbun, Pavel A1 - Porshyn, Vitali A1 - Lützenkirchen-Hecht, Dirk A1 - Prommesberger, Christian A1 - Langer, Christoph A1 - Ławrowski, Robert Damian A1 - Schreiner, Rupert T1 - Photosensitivity of single silicon high-aspect-ratio tips with different doping levels T2 - International Vacuum Nanoelectronics Conference (IVNC), 31st, 2018, Kyoto, Japan N2 - Photosensitivity of single lightly p-doped, highly p-doped, with an integrated p/n junction and intrinsic high-aspect-ratio (HAR) silicon tips was investigated in an ultra-high vacuum environment. The current-voltage characteristics (I-V) of the lightly doped p-type HAR tips showed a characteristic current saturation at around 10-12 nA, whereas the HAR Si tips with p/n junction showed similar saturation phenomena, however, at much smaller current values starting at ~20-30 pA. Optical switching under a halogen lamp illumination resulted in at least 2-4 times higher saturation currents and showed a linear dependence between the illumination power and the FE current, for both types of structures. In case of the highly p-doped HAR tips optical current switching effects, i. e. current saturation, were observed at rather low current levels 1-2 pA. Intrinsic HAR Si-tips showed relative unstable field emission behavior without a clear evidence of the photosensitivity. KW - field emission KW - Si p/n junction KW - p-type Si KW - photosensitivity Y1 - 2018 U6 - https://doi.org/10.1109/IVNC.2018.8520288 PB - IEEE ER -