@article{HuberHeindlSchlosseretal., author = {Huber, Lea and Heindl, Melanie and Schlosser, Marc and Pfitzner, Arno and Dawoud, Belal}, title = {On the Cycle Stability and Macroscopic Structure of Iron Oxide Pellets for Thermochemical Hydrogen Storage: Influence of Water Content during the Pelletizing Process}, series = {Applied Sciences}, volume = {13}, journal = {Applied Sciences}, number = {11}, publisher = {MDPI}, address = {16}, doi = {10.3390/app13116408}, abstract = {Hydrogen storage based on the repeated reduction and oxidation (redox) reactions of iron oxide/iron composites represents a promising technology. This work is dedicated to studying the influence of the amount of water added during the pelletizing process on the cycle stability and structure of iron oxide pellets. The storage composites were prepared from iron oxide (Fe2O3) and 10 wt.-\% support material (cement) with different amounts of water (18 and 33 wt.-\%) in a laboratory-scale pelletizing disk. To evaluate the cycle stability of the composites, the kinetics of the redox reactions were experimentally measured at 800 ∘ C in an atmosphere of 50\% N2 and 50\% H2 (reduction) or 50\% steam (oxidation), respectively. Moreover, the structure of the pellets was analyzed by micro-computed tomography scans. It turned out that pellets with higher water contents attained faster kinetics and a higher cycle stability. The sample with the least water content (18 wt.-\%) needed about 26 min and 19 min to reach a conversion rate of 80\% during the reduction and oxidation reactions of the sixth redox cycle, respectively. In contrast, the sample with the highest water content (33 wt.-\%) could achieve the same conversion rate after 18 min (reduction) and 13 min (oxidation) during the ninth redox cycle.}, language = {en} } @article{Schiek, author = {Schiek, Roland}, title = {Nonlinear refractive index in silica glass}, series = {Optical Materials Expres}, volume = {13}, journal = {Optical Materials Expres}, number = {6}, publisher = {Optica}, doi = {10.1364/ome.489520}, pages = {1727 -- 1740}, abstract = {The third-order nonlinear susceptibility of silica glass is measured via self-phase modulation in standard single mode fibers at a wavelength of 1550 nm. To minimize the influence of polarization state changes along the propagation only meter-long fibers were investigated. With pulse durations of picoseconds a quasi-instantaneous nonlinearity with ultrafast electronic and fast nuclear-vibration contributions produces under conditions of negligible dispersion a classic and clean nonlinear phase shift following exactly the shape of the pulse power. The complex pulse envelope was retrieved from frequency optical gating spectrograms. The nonlinear fiber parameter γ could be determined with an accuracy of 3.7 percent. Considering the mode field structure and the doping influence the nonlinear refractive index of silica glass as the fiber base material was found to be n 2 =2.22⋅10 -16 cm 2 W±6.0\% for picosecond-long pulses. Comparing nonlinear phase shifts from linear and circular polarized light a nuclear-vibration contribution to the cubic fiber nonlinearity of 25 percent was estimated.}, language = {en} } @article{RomanoEhrlich, author = {Romano, Marco and Ehrlich, Ingo}, title = {Classification of damping properties of fabric-reinforced flat beam-like specimens by a degree of ondulation implying a mesomechanic kinematic}, series = {Science and Engineering of Composite Materials}, volume = {31}, journal = {Science and Engineering of Composite Materials}, number = {1}, publisher = {Walter de Gruyter GmbH}, issn = {2191-0359}, doi = {10.1515/secm-2024-0019}, abstract = {In order to determine the influence of the ondulations in fabrics on the damping properties of fiber-reinforced plastics, the structural dynamic properties of fabric- and unidirectionally reinforced plastics are investigated. The free decay behavior of flat beam-like specimens is investigated under fixed-free boundary conditions. As the material damping is consistently higher in fabric-reinforced specimens compared to unidirectionally reinforced ones, a contribution of an additionally acting mesomechanic kinematic in fabric weaves is implied. Based on a degree of ondulation, it is possible to classify the enhancement of the material damping and determine the corresponding energy dissipation. The study provides valuable quantitative relations of the additional damping effect due to the mesomechanic kinematic. Compared to the unidirectionally reinforced material, plain weave enhances the material damping by 37…52\% at ˜OPL=0.0133 , whereas twill weave 2/2 enhances it by 31…40\% at ˜OT2=0.0098 . The consideration of the findings contributes to a deeper understanding of the visco-elastic dynamic behavior of fabric-reinforced plastics and allows further applications in research, development, and industry.}, language = {en} } @article{SteiningerGadererDawoud, author = {Steininger, Peter and Gaderer, Matthias and Dawoud, Belal}, title = {Assessment of the Annual Transmission Heat Loss Reduction of a Refurbished Existing Building with an Advanced Solar Selective Thermal Insulation System}, series = {Sustainability}, volume = {13}, journal = {Sustainability}, number = {13}, publisher = {MDPI}, address = {Basel}, doi = {10.3390/su13137336}, pages = {1 -- 19}, abstract = {A numerical parameter sensitivity analysis of the design parameters of the recently published solar selective thermal insulation system (SATIS) has been carried out to enhance its thermal and optical properties. It turned out that the insulation properties of SATIS can be effectively improved by reducing the length of the glass closure element. Increasing the area share of the light conducting elements (LCEs) and decreasing their length-to-diameter (L/D) ratio were identified as key parameters in order to increase the solar gain. Two SATIS variants were compared with the same wall insulation without SATIS in a yearly energetic performance assessment. The SATIS variant with 10 mm length of the closure element, 44.2\% area share of LCE, as well as front and rear diameters of 12 mm/9 mm shows an 11.8\% lower transmission heat loss over the heating period than the wall insulation without SATIS. A new methodology was developed to enable the implementation of the computed solar gains of SATIS in 1D simulation tools. The result is a radiant heat flow map for integration as a heat source in 1D simulation models. A comparison between the 1D and 3D models of the inside wall heat fluxes showed an integral yearly agreement of 98\%.}, language = {en} } @article{SindersbergerPremMonkman, author = {Sindersberger, Dirk and Prem, Nina and Monkman, Gareth J.}, title = {Structure formation in low concentration magnetoactive polymers}, series = {AIP advances}, volume = {9}, journal = {AIP advances}, number = {3}, publisher = {AIP Publishing}, doi = {10.1063/1.5079997}, abstract = {This paper concerns recent research into the autonomous formation of micro-structures in low carbonyl iron powder (CIP) concentration magneto active polymers (MAP). Higher concentrations of CIP show an isotropic distribution of magnetic filler throughout the entire sample, while autonomous structure formation is possible at mass concentrations lower than 3\%. The formation of micro-toroids commences as CIP concentration approaches 1\% wt. Further development of coherent rings with a defined order follow as CIP concentrations increase toward 2\% wt, whilst exceeding 3\% wt leads to the same isotropic distribution found in higher concentration MAP. Structured samples containing between 1\% wt and 3\% wt CIP were investigated using X-Ray tomography where solitary structures could clearly be observed. The ring structures represent microinductivities whose geometries can be manipulated during fabrication. In addition, these structures are magnetic field sensitive. This is not only relevant to applications in the GHz and THz areas but recent research has revealed implications for optical, thermal, acoustic and even chemical MAP sensors. (C) 2019 Author(s).}, language = {en} } @article{SternerBauer, author = {Sterner, Michael and Bauer, Franz}, title = {Power-to-X im Kontext der Energiewende und des Klimaschutzes in Deutschland}, series = {Chemie-Ingenieur-Technik}, volume = {92}, journal = {Chemie-Ingenieur-Technik}, number = {1-2}, publisher = {Wiley}, issn = {0009-286X}, doi = {10.1002/cite.201900167}, url = {http://nbn-resolving.de/urn:nbn:de:bvb:898-opus4-11669}, pages = {85 -- 90}, abstract = {Um den Einfluss verschiedener Power-to-X-Verfahren auf die Transformation des deutschen Energiesystems und das Erreichen der Klimaschutzziele zu {\"u}berpr{\"u}fen, wurde ein sektor{\"u}bergreifendes Energiesystemmodel entwickelt. Die daraus gewonnenen Ergebnisse zeigen: F{\"u}r eine erfolgreiche Energiewende ist der Einsatz von Power-to-X in Zukunft unverzichtbar. Vor allem in Bereichen und Sektoren, in denen hohe Energiedichten erforderlich und nur wenig andere Optionen zur Defossilisierung vorhanden sind, werden Power-to-X-Technologien zwingend notwendig.}, subject = {Power-to-Gas}, language = {de} } @article{ThemaBauerSterner, author = {Thema, Martin and Bauer, Franz and Sterner, Michael}, title = {Power-to-Gas: Electrolysis and methanation status review}, series = {Renewable and Sustainable Energy Reviews}, volume = {112}, journal = {Renewable and Sustainable Energy Reviews}, number = {7}, publisher = {Elsevier}, doi = {10.1016/j.rser.2019.06.030}, url = {http://nbn-resolving.de/urn:nbn:de:bvb:898-opus4-26238}, pages = {775 -- 787}, abstract = {This review gives a worldwide overview on Power-to-Gas projects producing hydrogen or renewable substitute natural gas focusing projects in central Europe. It deepens and completes the content of previous reviews by including hitherto unreviewed projects and by combining project names with details such as plant location. It is based on data from 153 completed, recent and planned projects since 1988 which were evaluated with regards to plant allocation, installed power development, plant size, shares and amounts of hydrogen or substitute natural gas producing examinations and product utilization phases. Cost development for electrolysis and carbon dioxide methanation was analyzed and a projection until 2030 is given with an outlook to 2050. The results show substantial cost reductions for electrolysis as well as for methanation during the recent years and a further price decline to less than 500 euro per kilowatt electric power input for both technologies until 2050 is estimated if cost projection follows the current trend. Most of the projects examined are located in Germany, Denmark, the United States of America and Canada. Following an exponential global trend to increase installed power, today's Power-to-Gas applications are operated at about 39 megawatt. Hydrogen and substitute natural gas were investigated on equal terms concerning the number of projects.}, language = {en} } @article{SternerHofrichterMeisingeretal., author = {Sterner, Michael and Hofrichter, Andreas and Meisinger, Alexander and Bauer, Franz and Pinkwart, Karsten and Maletzko, Annabelle and Dittmar, Felix and Cremers, Carsten}, title = {19 Import options for green hydrogen and derivatives - An overview of efficiencies and technology readiness levels}, series = {International Journal of Hydrogen Energy}, volume = {90}, journal = {International Journal of Hydrogen Energy}, publisher = {Elsevier}, issn = {0360-3199}, doi = {10.1016/j.ijhydene.2024.10.045}, url = {http://nbn-resolving.de/urn:nbn:de:bvb:898-opus4-77756}, pages = {1112 -- 1127}, abstract = {The import of hydrogen and derivatives forms part of many national strategies and is fundamental to achieving climate protection targets. This paper provides an overview and technical comparison of import pathways for hydrogen and derivatives in terms of efficiency, technological maturity and development and construction times with a focus on the period up to 2030. The import of hydrogen via pipeline has the highest system efficiency at 57-67 \% and the highest technological maturity with a technology readiness level (TRL) of 8-9. The import of ammonia and methanol via ship and of SNG via pipeline shows efficiencies in the range of 39-64 \% and a technological maturity of TRL 7 to 9 when using point sources. Liquid hydrogen, LOHC and Fischer-Tropsch products have the lowest efficiency and TRL in comparison. The use of direct air capture (DAC) reduces efficiency and TRL considerably. Reconversion of the derivatives to hydrogen is also associated with high losses and is not achievable for all technologies on an industrial scale up to 2030. In the short to medium term, import routes for derivatives that can utilise existing infrastructures and mature technologies are the most promising for imports. In the long term, the most promising option is hydrogen via pipelines.}, language = {en} } @article{KovalevBelyaevavonHofenetal., author = {Kovalev, Alexander and Belyaeva, Inna A. and von Hofen, Christian and Gorb, Stanislav and Shamonin (Chamonine), Mikhail}, title = {Magnetically Switchable Adhesion and Friction of Soft Magnetoactive Elastomers}, series = {Advanced Engineering Materials}, volume = {24}, journal = {Advanced Engineering Materials}, number = {10}, publisher = {WILEY-VCH}, doi = {10.1002/adem.202200372}, url = {http://nbn-resolving.de/urn:nbn:de:bvb:898-opus4-45283}, pages = {1 -- 8}, abstract = {Herein, the effect of an applied moderate (~240 mT) magnetic field on the work of adhesion (WoA) of mechanically soft (the shear modulus ~10 kPa) magnetoactive elastomer (MAE) samples with two different mass fractions (70 and 80 wt\%) of carbonyl iron powder (CIP) is concerned. The unfilled elastomer sample is used for comparison. Due to some sedimentation of filling particles, the concentration of inclusions in thin (~10 μm) subsurface layers is different. It is shown that the WoA increases (up to 1.8-fold) on the particle-enriched side (PES) in the magnetic field and its value is higher for higher filler concentration. On the particle-depleted side (PDS), WoA does not depend on particle concentration and on the magnetic field. Adhesion and friction are coupled in MAEs. No statistically significant difference in the friction coefficient, determined from the extended Amontons´ law, depending on sample side, CIP concentration, or presence of magnetic field is found. However, the PDS in the magnetic field demonstrates significantly higher critical shear stress compared to that for the PES or PDS in the absence of magnetic field. Correlations between different surface properties are discussed. Obtained results are useful for the development of magnetically controllable soft robots.}, language = {en} } @article{BartschBehamGebhardtetal., author = {Bartsch, Alexander and Beham, Daniela and Gebhardt, Jakob and Ehrlich, Ingo and Schratzenstaller, Thomas and Monkman, Gareth J.}, title = {Mechanical Properties of NdPrFeB Based Magnetoactive Bisphenol-Free Boron-Silicate Polymers}, series = {Journal of Nanomedicine and Nanotechnology}, volume = {14}, journal = {Journal of Nanomedicine and Nanotechnology}, number = {6}, publisher = {Walsh Medical Media}, issn = {2157-7439}, doi = {10.35248/2157-7439.23.14.705}, url = {http://nbn-resolving.de/urn:nbn:de:bvb:898-opus4-67425}, abstract = {Following a ban on many materials containing bisphenol-A, new bisphenol-free Boron silicates have been found as substitutes. The purpose of this study is to describe the mechanical properties of these bisphenol-free magnetoactive borosilicate polymers containing hard magnetic particles. Samples of 0\%, 33\% and 66\% by wt. were loaded for compression using a universal testing machine. The maximum forces occurring for different travel speeds were compared before and after post-magnetization treatments. The post-magnetization included 2 stages. In addition, the change in mechanical properties within 24 hours after the post-magnetization process was investigated. Furthermore, the influence of speed and particle content were investigated. In general, there is a correlation between the required compressive force and, the level of post-magnetization stress, the increase in travel speed and particle content in the boron silicate. Comparison of the non-post-magnetized and post-magnetized samples using two-tailed t-tests shows that the p-values for all weight fraction changes in NdPrFeB particles and travel speeds are less than 0.001. Also, a comparison between tests in which the traverse speed was varied also showed significant changes in the resulting compression forces. The same is valid for changes in the weight ratio of the NdPrFeB particles in the samples. For post-magnetized samples, no significant difference can be observed in the first 24 hours following magnetization. In summary, the material presents viscoelastic, plastic force-displacement behavior, which can be well recognized by its bi-linear curve shape. The investigation shows that borosilicate polymers based on NdPrFeB can have their mechanical behavior modified and controlled by post-magnetization processes. This opens new possibilities for many future applications.}, language = {en} } @article{GlavanBelyaevaShamoninChamonine, author = {Glavan, Gašper and Belyaeva, Inna A. and Shamonin (Chamonine), Mikhail}, title = {On the Piezomagnetism of Magnetoactive Elastomeric Cylinders in Uniform Magnetic Fields: Height Modulation in the Vicinity of an Operating Point by Time-Harmonic Fields}, series = {Polymers}, volume = {16}, journal = {Polymers}, number = {19}, doi = {10.3390/polym16192706}, abstract = {Soft magnetoactive elastomers (MAEs) are currently considered to be promising materials for actuators in soft robotics. Magnetically controlled actuators often operate in the vicinity of a bias point. Their dynamic properties can be characterized by the piezomagnetic strain coefficient, which is a ratio of the time-harmonic strain amplitude to the corresponding magnetic field strength. Herein, the dynamic strain response of a family of MAE cylinders to the time-harmonic (frequency of 0.1-2.5 Hz) magnetic fields of varying amplitude (12.5 kA/m-62.5 kA/m), superimposed on different bias magnetic fields (25-127 kA/m), is systematically investigated for the first time. Strain measurements are based on optical imaging with sub-pixel resolution. It is found that the dynamic strain response of MAEs is considerably different from that in conventional magnetostrictive polymer composites (MPCs), and it cannot be described by the effective piezomagnetic constant from the quasi-static measurements. The obtained maximum values of the piezomagnetic strain coefficient (∼102 nm/A) are one to two orders of magnitude higher than in conventional MPCs, but there is a significant phase lag (35-60°) in the magnetostrictive response with respect to an alternating magnetic field. The experimental dependencies of the characteristics of the alternating strain on the amplitude of the alternating field, bias field, oscillation frequency, and aspect ratio of cylinders are given for several representative examples. It is hypothesized that the main cause of observed peculiarities is the non-linear viscoelasticity of these composite materials.}, language = {en} } @article{GlavanKettlBrunhuberetal., author = {Glavan, Gašper and Kettl, Wolfgang and Brunhuber, Alexander and Shamonin (Chamonine), Mikhail and Drevenšek-Olenik, Irena}, title = {Effect of Material Composition on Tunable Surface Roughness of Magnetoactive Elastomers}, series = {Polymers}, volume = {11}, journal = {Polymers}, number = {4}, publisher = {MDPI}, address = {Basel}, doi = {10.3390/polym11040594}, pages = {1 -- 13}, abstract = {We investigated magnetic-field-induced modifications of the surface roughness of magnetoactive elastomers (MAEs) with four material compositions incorporating two concentrations of ferromagnetic microparticles (70 wt\% and 80 wt\%) and exhibiting two shear storage moduli of the resulting composite material (about 10 kPa and 30 kPa). The analysis was primarily based on spread optical reflection measurements. The surfaces of all four materials were found to be very smooth in the absence of magnetic field (RMS roughness below 50 nm). A maximal field-induced roughness modification (approximately 1 m/T) was observed for the softer material with the lower filler concentration, and a minimal modification (less than 50 nm/T) was observed for the harder material with the higher filler concentration. All four materials showed a significant decrease in the total optical reflectivity with an increasing magnetic field as well. This effect is attributed to the existence of a distinct surface layer that is depleted of microparticles in the absence of a magnetic field but becomes filled with particles in the presence of the field. We analyzed the temporal response of the reflective properties to the switching on and off of the magnetic field and found switching-on response times of around 0.1 s and switching-off response times in the range of 0.3-0.6 s. These observations provide new insight into the magnetic-field-induced surface restructuring of MAEs and may be useful for the development of magnetically reconfigurable elastomeric optical surfaces.}, language = {en} } @article{FoerstlSuessEnglertetal., author = {F{\"o}rstl, Nikolas and S{\"u}ß, Franz and Englert, Carsten and Dendorfer, Sebastian}, title = {Design of a reverse shoulder implant to measure shoulder stiffness during implant component positioning}, series = {Medical Engineering \& Physics}, volume = {121}, journal = {Medical Engineering \& Physics}, edition = {Journal Pre-proof}, publisher = {Elsevier}, doi = {10.1016/j.medengphy.2023.104059}, pages = {22}, abstract = {To avoid dislocation of the shoulder joint after reverse total shoulder arthroplasty, it is important to achieve sufficient shoulder stability when placing the implant components during surgery. One parameter for assessing shoulder stability can be shoulder stiffness. The aim of this research was to develop a temporary reverse shoulder implant prototype that would allow intraoperative measurement of shoulder stiffness while varying the position of the implant components. Joint angle and torque measurement techniques were developed to determine shoulder stiffness. Hall sensors were used to measure the joint angles by converting the magnetic flux densities into angles. The accuracy of the joint angle measurements was tested using a test bench. Torques were determined by using thin-film pressure sensors. Various mechanical mechanisms for variable positioning of the implant components were integrated into the prototype. The results of the joint angle measurements showed measurement errors of less than 5° in a deflection range of ±15° adduction/abduction combined with ±45° flexion/extension. The proposed design provides a first approach for intra-operative assessment of shoulder stiffness. The findings can be used as a technological basis for further developments.}, language = {en} } @article{BartschBurgerGradetal., author = {Bartsch, Alexander and Burger, Moritz and Grad, Marius and Esper, Lukas and Schultheiß, Ulrich and Noster, Ulf and Schratzenstaller, Thomas}, title = {Enhancement of laser cut edge quality of ultra-thin titanium grade 2 sheets by applying an in-process approach using modulated Yb:YAG continuous wave fiber laser}, series = {Discover Mechanical Engineering}, journal = {Discover Mechanical Engineering}, number = {10}, publisher = {Springer}, doi = {10.1007/s44245-023-00018-3}, url = {http://nbn-resolving.de/urn:nbn:de:bvb:898-opus4-65647}, pages = {9}, abstract = {Titanium is used in many areas due to its excellent mechanical, biological and corrosion-resistant properties. Implants often have thin and filigree structures, providing an ideal application for fine cutting with laser. In the literature, the main focus is primarily on investigating and optimizing the parameters for titanium sheets with thicknesses greater than 1 mm. Hence, in this study, the basic manufacturing parameters of laser power, cutting speed and laser pulse of a 200 W modulated fiber laser are investigated for 0.15 mm thick grade 2 titanium sheets. A reproducible, continuous cut could be achieved using 90 W laser-power and 2 mm/s cutting-speed. Pulse pause variations between 85 and 335 μs in 50 μs steps and a fixed pulse width of 50 μs show that a minimum kerf width of 23.4 μm, as well as a minimum cut edge roughness Rz of 3.59 μm, is achieved at the lowest pulse pause duration. An increase in roughness towards the laser exit side, independent of the laser pulse pause duration, was found and discussed. The results provide initial process parameters for cutting thin titanium sheets and thus provide the basis for further investigations, such as the influence of cutting gas pressure and composition on the cut edge.}, language = {en} } @article{SieglJungbauerGebhardtetal., author = {Siegl, Marco and Jungbauer, Bastian and Gebhardt, Jakob and Judenmann, Anna and Ehrlich, Ingo}, title = {Winding process of fibre-reinforced thermoplastic tubes with integrated tape production through in-situ roving impregnation and infrared consolidation}, series = {The International Journal of Advanced Manufacturing Technology}, volume = {135}, journal = {The International Journal of Advanced Manufacturing Technology}, number = {5-6}, editor = {Baeten, Somayeh}, publisher = {Springer Nature}, doi = {10.1007/s00170-024-14628-y}, url = {http://nbn-resolving.de/urn:nbn:de:bvb:898-opus4-77827}, pages = {2847 -- 2870}, abstract = {This paper introduces a novel method for producing fibre-reinforced thermoplastic tubes by integrating tape production and consolidation into a single operation. This innovation diverges from conventional methods by combining processes to reduce costs by using raw materials instead of organotapes, allowing customised material combinations and utilising residual heat from tape production. The new process uses carbon roving and molten low-viscosity PA6 granulates, processed through a new direct impregnation setup in siphon design. Key advancements include a high-speed impregnation module capable of up to 1 m/s with high-performance extruders, cost-effective infrared emitters for winding, and a powered consolidation unit with adjustable winding angles between ±65° and ±90°. Experiments demonstrate operational speeds of approximately 471 mm/min, with an optimal cross-winding speed of 354 mm/min due to the technical limitations of the laboratory extruder and IR emitter used. Based on the technical limitations of the current system, future improvements and methodological changes will be discussed.}, language = {en} } @article{KravanjaBelyaevaHribaretal., author = {Kravanja, Gaia and Belyaeva, Inna A. and Hribar, Luka and Drevenšek-Olenik, Irena and Jezeršek, Matija and Shamonin (Chamonine), Mikhail}, title = {Tunable Drop Splashing on Magnetoactive Elastomers}, series = {Advanced Materials Interfaces}, volume = {8}, journal = {Advanced Materials Interfaces}, number = {11}, publisher = {Wiley}, doi = {10.1002/admi.202100235}, url = {http://nbn-resolving.de/urn:nbn:de:bvb:898-opus4-24504}, pages = {1 -- 7}, abstract = {The significant effect of an external dc magnetic field on the splashing behavior of ethanol drops impacting on the unstructured (flat) surface of soft magnetoactive elastomers (MAEs) is reported. The Weber number corresponding to the transition between the deposition and the splashing regime is reduced by ≈20\% in a moderate magnetic field of ≈300 mT. Alongside this effect, a two-fold increase of the initial deceleration of the ejection sheet is observed for the softest sample. The main underlying mechanism for the observed phenomena is believed to be the magnetic-field-induced stiffening of the MAEs. Further possible mechanisms are magnetically induced changes in the surface roughness and magnetic-field-induced plasticity (magnetic shape memory effect). The potential application areas are magnetically regulable wetting and magneto-responsive surfaces for controlling the drop splashing.}, language = {en} } @misc{KrieglKravanjaHribaretal., author = {Kriegl, Raphael and Kravanja, Gaia and Hribar, Luka and Jezeršek, Matija and Drevenšek-Olenik, Irena and Shamonin (Chamonine), Mikhail}, title = {Characterization of Wetting Properties of Magnetoactive Elastomer Surfaces}, series = {Proceedings of the ASME Conference on Smart Materials, Adaptive Structures and Intelligent Systems (SMASIS) - 2023, September 11-13, 2023 Austin, Texas, USA}, journal = {Proceedings of the ASME Conference on Smart Materials, Adaptive Structures and Intelligent Systems (SMASIS) - 2023, September 11-13, 2023 Austin, Texas, USA}, publisher = {The American Society of Mechanical Engineers}, address = {New York, USA}, isbn = {978-0-7918-8752-3}, doi = {10.1115/SMASIS2023-110998}, abstract = {Commercially available contact angle (CA) measuring devices usually do not allow for the application of magnetic fields to the sample under test. A setup for measuring the CA of liquids on magnetosensitive surfaces has been developed specifically for investigating the surfaces of magnetoactive elastomers (MAEs). The addition of a programmable linear stage, which moves a permanent magnet, allows for fine control of the magnetic field applied to the MAE without the need for large and power-consuming electromagnets. Paired with a custom control and evaluation software, this measurement setup operates semiautomatically, limiting operator error and increasing precision, speed, as well as repeatability of static and dynamic CA measurements for different magnetoactive materials. The software is equipped with robust droplet fitting algorithms to avoid experimental challenges arising with soft magnetoactive materials, such as the curling of sample edges or diffuse non-reflective surfaces. Several application examples on MAE surfaces, both processed and unprocessed, are presented.}, language = {en} } @article{PangerlSukulRuecketal., author = {Pangerl, Jonas and Sukul, Pritam and R{\"u}ck, Thomas and Escher, Lukas and Miekisch, Wolfram and Bierl, Rudolf and Matysik, Frank-Michael}, title = {Photoacoustic trace-analysis of breath isoprene and acetone via interband- and Quantum Cascade Lasers}, series = {Sensors and Actuators: B. Chemical}, volume = {424}, journal = {Sensors and Actuators: B. Chemical}, publisher = {Elsevier}, doi = {10.1016/j.snb.2024.136886}, url = {http://nbn-resolving.de/urn:nbn:de:bvb:898-opus4-77024}, pages = {12}, abstract = {This research presents two laser-based photoacoustic approaches for analyzing exhaled breath isoprene and acetone. The integration of a PTR-ToF-MS as a reference device ensured the reliability and accuracy of the photoacoustic systems that is based on an ICL for isoprene and a QCL for acetone detection. The calibration yielded limits of detection of 26.9 ppbV and 1.7 ppbV, respectively, and corresponding normalized noise equivalent absorption coefficients (NNEAs) of 5.0E-9 Wcm 1Hz 0.5 and 4.9E-9 Wcm 1Hz 0.5. Laboratory as well as real breath sample measurements from alveolar breath revealed a robust system performance, with only one outlier within the static isoprene measurements. However, discrepancies emerged under dynamic breath sampling conditions, emphasizing the need for further optimization. Especially by knowing the dynamic nature and endogenous origin of exhaled isoprene our findings highlight the potential of breath analysis for non-invasive physio-metabolic and pathophysiological monitoring towards point-of-care devices}, language = {en} } @article{FrankeWagner, author = {Franke, Markus and Wagner, Marcus}, title = {Transient surrogate modeling of modally reduced structures with discontinuous loads and damping}, series = {Archive of Applied Mechanics}, volume = {94}, journal = {Archive of Applied Mechanics}, number = {5}, publisher = {Springer Nature}, doi = {10.1007/s00419-024-02601-w}, url = {http://nbn-resolving.de/urn:nbn:de:bvb:898-opus4-72834}, pages = {20}, abstract = {In this work, a surrogate model for structural, transient and discontinuously excited finite element method simulations is developed. This allows to reduce the computational effort of repeated calculations of identical models under different load cases. The architecture of the surrogate combines fully connected neural network layers with long short-term memory layers. For the reproduction of different damping ratios, a categorical variable is added to the continuous input data. Based on a recursive flow of the predicted data back to the input layer, long-term dependencies do not vanish due to short-input sequences. The system dimension is reduced by applying the model-order reduction technique for modal decomposition. The high accuracy of the surrogate and the reduction of computational costs are shown on an academic example of a cantilever beam and a real-world example of a robot. The advantages of our approach are illustrated in comparison with state-of-the-art surrogates for transient finite element analysis. By using the surrogate proposed in this study, oscillations due to discontinuous excitation of mechanical structures can be reproduced. For this purpose, only short-input sequences are necessary since the excitation of the oscillations does not have to be part of the input sequence during the whole duration of the oscillations. Due to the categorical variable for the damping ratio, the surrogate can account for the influence of different damping in parameter studies.}, language = {en} } @article{LindnerPipaKarpenetal., author = {Lindner, Matthias and Pipa, Andrei V. and Karpen, Norbert and Hink, R{\"u}diger and Berndt, Dominik and Foest, R{\"u}diger and Bonaccurso, Elmar and Weichwald, Robert and Friedberger, Alois and Caspari, Ralf and Brandenburg, Ronny and Schreiner, Rupert}, title = {Icing Mitigation by MEMS-Fabricated Surface Dielectric Barrier Discharge}, series = {Applied Sciences}, volume = {11}, journal = {Applied Sciences}, number = {23}, publisher = {MDPI}, address = {Basel}, doi = {10.3390/app112311106}, pages = {1 -- 17}, abstract = {Avoiding ice accumulation on aerodynamic components is of enormous importance to flight safety. Novel approaches utilizing surface dielectric barrier discharges (SDBDs) are expected to be more efficient and effective than conventional solutions for preventing ice accretion on aerodynamic components. In this work, the realization of SDBDs based on thin-film substrates by means of micro-electro-mechanical-systems (MEMS) technology is presented. The anti-icing performance of the MEMS SDBDs is presented and compared to SDBDs manufactured by printed circuit board (PCB) technology. It was observed that the 35 mu m thick electrodes of the PCB SDBDs favor surface icing with an initial accumulation of supercooled water droplets at the electrode impact edges. This effect was not observed for 0.3 mu m thick MEMS-fabricated electrodes indicating a clear advantage for MEMS-technology SDBDs for anti-icing applications. Titanium was identified as the most suitable material for MEMS electrodes. In addition, an optimization of the MEMS-SDBDs with respect to the dielectric materials as well as SDBD design is discussed.}, language = {en} }