@inproceedings{MingelsPorshynSerbunetal., author = {Mingels, Stephan and Porshyn, Vitali and Serbun, Pavel and L{\"u}tzenkirchen-Hecht, Dirk and M{\"u}ller, G{\"u}nter and Prommesberger, Christian and Langer, Christoph and Schreiner, Rupert and Lutzenkirchen-Hecht, Dirk}, title = {Photo-enhanced field emission properties of p-doped black Si arrays}, series = {2016 29th International Vacuum Nanoelectronics Conference (IVNC), 11-15 July 2016, Vancouver, BC, Canada}, booktitle = {2016 29th International Vacuum Nanoelectronics Conference (IVNC), 11-15 July 2016, Vancouver, BC, Canada}, publisher = {IEEE}, doi = {10.1109/IVNC.2016.7551447}, pages = {1 -- 2}, abstract = {We have carried out systematic investigations of p-type black Si field emitter arrays under laser illumination. As expected the current-voltage characteristic revealed a strong saturation providing a high photosensitivity, which had a maximum on-off ratio of 43 at a maximum current of 13 μA. The saturation current was stable in the dark as well as under illumination with fluctuations <;0.7\%. Results from time-resolved measurements of the photo-sensitivity showed a rather fast response but a long decay time. Electron spectra in the dark and under laser illumination revealed the origin of the emission.}, language = {en} } @inproceedings{SchreinerLangerPrommesbergeretal., author = {Schreiner, Rupert and Langer, Christoph and Prommesberger, Christian and Mingels, Stephan and Serbun, Pavel and M{\"u}ller, G{\"u}nter}, title = {Field emission from surface textured extraction facets of GaN light emitting diodes}, series = {26th International Vacuum Nanoelectronics Conference (IVNC), 8-12 July 2013, Roanoke, VA, USA}, booktitle = {26th International Vacuum Nanoelectronics Conference (IVNC), 8-12 July 2013, Roanoke, VA, USA}, publisher = {IEEE}, doi = {10.1109/ivnc.2013.6624721}, abstract = {We report on the field emission properties of GaN LED surfaces. The textured extraction facet acts both as light scattering layer in order to increase the light extraction efficiency of the LED as well as nanostructured cathode surface for the field emission (FE) of electrons. The LED emits blue light with a peak wavelength of around 450 nm. The FE properties were investigated by a scanning microscope. Integral measurements as well as regulated voltage scans for 1 nA FE current over an area of 400 * 400 µm2were used to investigate both overall and local FE properties. A high number of well-distributed emitters with an average field enhancement factor ß of 85 and stable integral emission currents up to 100 µA at an electric field of   80 V/µm ({\O}anode= 880 µm) were found. Photo-field-emission spectroscopy (PFES) using a tunable pulsed laser revealed an enhanced photo absorption of the InGaN/GaN quantum well structures near the emission wavelength of the LED (<3.5 eV), whereas at high photon energies (>4.1 eV) photoemission from the GaN surface was observed.}, language = {en} } @inproceedings{NavitskiSerbunMuelleretal., author = {Navitski, Aliaksandr and Serbun, Pavel and M{\"u}ller, G{\"u}nter and Schreiner, Rupert and Dams, Florian}, title = {Efficient and reliable field emission from silicon tip arrays for miniaturized electron sources}, series = {2011 24th International Vacuum Nanoelectronics Conference ; 18-22 July 2011 Wuppertal}, booktitle = {2011 24th International Vacuum Nanoelectronics Conference ; 18-22 July 2011 Wuppertal}, publisher = {IEEE}, address = {Piscataway, NJ}, isbn = {978-3-00-035081-8}, issn = {2380-6311}, pages = {71 -- 72}, abstract = {Silicon-based cathodes with precisely aligned field emitter arrays (FEA) applicable for miniaturized electron sources were successfully developed and fabricated. The cathode chips contain about 3×105 Si tips/cm2 in a triangular array with a tip height of 2.5 μm, tip radius of 20 nm, and lateral distance between tips of 20 μm. Amazingly homogeneous and well-aligned field emission (FE) from all tips (i.e. 100\% efficiency) and maximum stable currents of typically 0.1 μA for p- and 0.6 μA for n-type Si were reproducibly achieved. Current-voltage characteristics of p-type Si tips exhibit the expected saturation at around 10 nA due to limited supply of electrons from a depletion layer, while the n-type Si tips show the usual FN behaviour. Additional coating of the Si tips with a 10 nm Au layer resulted in at least 5 times higher average FE current levels i.e. typically 3 μA but lead, however, to a 30\% increase of the onset voltage.}, language = {en} }