@article{HornbergerWitteHortetal., author = {Hornberger, Helga and Witte, Frank and Hort, Norbert and M{\"u}ller, Wolf-Dieter}, title = {Effect of fetal calf serum on the corrosion behaviour of magnesium alloys}, series = {Materials Science and Engineering B}, volume = {176}, journal = {Materials Science and Engineering B}, number = {29}, doi = {10.1016/j.mseb.2011.07.018}, pages = {1746 -- 1755}, abstract = {The corrosion behaviour of WE43 magnesium alloys using the mini cell system was studied. Voltammetry and impedance spectroscopy were applied to study on the one hand the effect of microstructure of the working electrode and on the other hand the effect of proteins in the electrolyte. Two types of alloy samples were produced (i) by permanent mould casting and (ii) by gas atomization followed by extrusion. The results showed that the microstructure was strongly influenced by the production process. The extruded samples showed an improved homogeneity of phase distribution compared with cast samples as it was aimed for. Due to increased homogeneity it was expected to find higher corrosion resistance. However, the electrochemical results are contradictory and suggest an additional phase in the extruded microstructure. Using energy dispersive X-ray spectroscopy (EDX) the secondary magnesium rare earths (RE) phase of extruded samples showed differing composition than of cast samples as well as additional oxide phases. After the samples were electrochemically investigated in cell medium with and without fetal calf serum (FCS), an impact of FCS was detected in voltammetry due to the length of the polarisation curve. As the tip of the mini cell in contact with the working electrode is small, developing gases tend to spread on the working electrode and break the contact of liquid to the counter electrode; which results in disrupting the current flow. This effect was more pronounced when rising the voltage and was found reduced when using electrolytes with FCS. Impedance spectra were slightly deformed by FCS, seen as a kinetic effect but not as a basic differing corrosion reaction. The insight into the effects of FCS was provided by the mini cell system as this system enables to collect entire series of measurements. In contrast of two single measurements, those series reflected the slight difference caused by FCS. The focus of the electrochemical corrosion study was set on the first half hour of immersion.}, language = {en} } @article{KloiberSchultheissSoteloetal., author = {Kloiber, Jessica and Schultheiß, Ulrich and Sotelo, Lamborghini and Sarau, George and Christiansen, Silke and Gavras, Sarkis and Hort, Norbert and Hornberger, Helga}, title = {Corrosion behaviour of electropolished magnesium materials}, series = {Materials Today Communications}, journal = {Materials Today Communications}, edition = {Journal Pre-proof}, publisher = {Elsevier}, doi = {10.1016/j.mtcomm.2023.107983}, url = {http://nbn-resolving.de/urn:nbn:de:bvb:898-opus4-68254}, abstract = {Although magnesium and its alloys are promising candidates as biodegradable implant materials, the tendency for localized corrosion mechanism in physiological environment limit their biomedical application. Electropolishing is an attractive strategy for improving the corrosion behaviour of metals, but it is still largely unexplored in magnesium materials. In this study, the characterization of electropolished surfaces of AM50 and pure magnesium was performed, focussing on their in vitro degradation behaviour in cell medium. Corrosion rates were evaluated using potentiodynamic polarisation. The surface morphology before and after the onset of corrosion was investigated by scanning electron microscopy and confocal laser scanning microscopy. The presented electropolishing process led to improved surface performances, observable by significantly lower corrosion rates (0.08 mm·year-1 in Dulbecco's modified Eagle's medium), lower arithmetical mean height (0.05 µm), lower water contact angle (25-35°) and lower micro hardness (35-50 HV 0.1) compared to mechanically and chemically treated surfaces. MgO/Mg(OH)2 could be detected on electropolished surfaces. The localized corrosion mode could be reduced, but not entirely prevented. Electropolishing shows great potential as post-treatment of magnesium-based components, but detailed tests of the long-term corrosion behaviour are an important area of future research.}, language = {en} }