@inproceedings{SerbunNavitskiMuelleretal., author = {Serbun, Pavel and Navitski, Aliaksandr and M{\"u}ller, G{\"u}ntner and Schreiner, Rupert and Prommesberger, Christian and Langer, Christoph and Dams, Florian}, title = {Scaling of the field emission current from B-doped Si-tip arrays}, series = {25th International Vacuum Nanoelectronics Conference (IVNC) ; Jeju, Korea (South), 09.07.2012 - 13.07.2012}, booktitle = {25th International Vacuum Nanoelectronics Conference (IVNC) ; Jeju, Korea (South), 09.07.2012 - 13.07.2012}, publisher = {IEEE}, address = {Piscataway, N.J.}, isbn = {978-1-4673-1984-3}, issn = {2380-6311}, doi = {10.1109/IVNC.2012.6316965}, pages = {1 -- 2}, abstract = {We have fabricated a test chip with various hexagonal arrays of B-doped Si tips (height ~ 3 μm, apex radius <; 30 nm, number 1-4447, resistivity 4 Ωcm, 100 orientation) in triangular arrangement (pitch 10 μm, density 1.16×10 6 cm -2 ) in order to systematically investigate the field emission current scaling with the number N of tips. Regulated voltage scans for 1 nA revealed rather efficient emission from nearly all tips of the arrays at an average field of 15 V/μm. The expected current plateau was always obtained at fields around 20 V/μm, but its width strongly increased with N. In this carrier depletion range, the single tip provided a much higher stability (<; 5\%) of the current (2-3 nA) than at lower (>; 50 \%) and higher currents (>; 30\%). Integral current measurements of the hexagonal arrays resulted in a statistically improved current stability (<; 1\%) but only a weak increase of the total current with N 0.28 yet. These results will be discussed with respect to the remaining inhomogeneity of the tips.}, language = {en} }