@article{GradZentgrafSchultheissetal., author = {Grad, Marius and Zentgraf, Jan and Schultheiss, Ulrich and Esper, Lukas and Diemar, Andreas and Noster, Ulf and Spiess, Lothar}, title = {Effect of Carbon Content on the Phase Composition, Microstructure and Mechanical Properties of the TiC Layer Formed in Hot-Pressed Titanium-Steel Composites}, series = {Metals}, volume = {14}, journal = {Metals}, number = {9}, publisher = {MDPI AG}, issn = {2075-4701}, doi = {10.3390/met14090959}, url = {http://nbn-resolving.de/urn:nbn:de:bvb:898-opus4-74617}, abstract = {During the hot pressing of pure titanium and different carbon steels in a temperature range of ϑ = 950-1050 °C, a compound layer up to dL≈10 μm thick is formed at the titanium-steel interface. With a higher carbon content of the used steel, the layer thickness increases. The carbon concentration within the layer is in the range of stoichiometry for TiC. Apart from TiC, no other phases can be detected by X-ray diffraction (XRD) measurements inside the formed layer. The calculation of the activation energy for the TiC layer formation is Q = 126.5-136.7 kJ mol-1 and is independent of the carbon content of the steel. The resulting microstructure has a grain size gradient, wherein the mechanical properties, such as hardness and Young's modulus, are almost constant. Statistical analysis using Response Surface Methodology (RSM) indicates that the carbon content of the steel has the most significant influence on layer thickness, followed by annealing temperature and annealing time. By selecting the appropriate carbon steel and the subsequent removal of the steel, it is possible to produce targeted TiC layers on titanium substrates, which holds enormous potential for this material in wear-intensive applications.}, language = {en} } @article{BartschBurgerGradetal., author = {Bartsch, Alexander and Burger, Moritz and Grad, Marius and Esper, Lukas and Schultheiß, Ulrich and Noster, Ulf and Schratzenstaller, Thomas}, title = {Enhancement of laser cut edge quality of ultra-thin titanium grade 2 sheets by applying an in-process approach using modulated Yb:YAG continuous wave fiber laser}, series = {Discover Mechanical Engineering}, journal = {Discover Mechanical Engineering}, number = {10}, publisher = {Springer}, doi = {10.1007/s44245-023-00018-3}, url = {http://nbn-resolving.de/urn:nbn:de:bvb:898-opus4-65647}, pages = {9}, abstract = {Titanium is used in many areas due to its excellent mechanical, biological and corrosion-resistant properties. Implants often have thin and filigree structures, providing an ideal application for fine cutting with laser. In the literature, the main focus is primarily on investigating and optimizing the parameters for titanium sheets with thicknesses greater than 1 mm. Hence, in this study, the basic manufacturing parameters of laser power, cutting speed and laser pulse of a 200 W modulated fiber laser are investigated for 0.15 mm thick grade 2 titanium sheets. A reproducible, continuous cut could be achieved using 90 W laser-power and 2 mm/s cutting-speed. Pulse pause variations between 85 and 335 μs in 50 μs steps and a fixed pulse width of 50 μs show that a minimum kerf width of 23.4 μm, as well as a minimum cut edge roughness Rz of 3.59 μm, is achieved at the lowest pulse pause duration. An increase in roughness towards the laser exit side, independent of the laser pulse pause duration, was found and discussed. The results provide initial process parameters for cutting thin titanium sheets and thus provide the basis for further investigations, such as the influence of cutting gas pressure and composition on the cut edge.}, language = {en} } @article{EsperSchultheissGradetal., author = {Esper, Lukas and Schultheiss, Ulrich and Grad, Marius and Noster, Ulf and Bund, Andreas}, title = {Application of the Hull Cell for Identifying Electropolishing Parameters to Adjust Surface Morphology in Additive Manufacturing}, series = {ECS Advances}, volume = {4}, journal = {ECS Advances}, number = {4}, publisher = {The Electrochemical Society}, issn = {2754-2734}, doi = {10.1149/2754-2734/ae184f}, url = {http://nbn-resolving.de/urn:nbn:de:bvb:898-opus4-86295}, pages = {9}, abstract = {Additively processed materials are increasingly used to manufacture customized parts, e.g. medical implants. Implant surfaces often require a smooth finish, which can be achieved by post-processing and well-defined process parameters. In this study, the effects of electropolishing of metal parts produced by laser powder bed fusion are investigated using Hull cell experiments and a three-electrode setup. Current density voltage curves were measured with the three-electrode setup to identify the regimes for electropolishing. Subsequently different constant-currents were applied and Hull cell experiments were conducted. The surface roughness (Sz, Sa) and the mass removal were analysed. Surface morphologies were assessed using laser scanning and scanning electron microscopy. A reduction of the initial surface roughness of more than 90\% to Sa \< 0.3 μm has been achieved. Considering the passed electrical charge during electropolishing, results from Hull cell experiments are systematically correlated with current-controlled electropolishing. This approach enables the precise tailoring of polishing parameters to achieve surfaces with defined roughness. Furthermore, the study demonstrates the suitability of Hull cells in determining electropolishing parameters for additive materials and highlights their contribution to post-processing in additive manufacturing.}, language = {en} }