@article{BartschBurgerGradetal., author = {Bartsch, Alexander and Burger, Moritz and Grad, Marius and Esper, Lukas and Schultheiß, Ulrich and Noster, Ulf and Schratzenstaller, Thomas}, title = {Enhancement of laser cut edge quality of ultra-thin titanium grade 2 sheets by applying an in-process approach using modulated Yb:YAG continuous wave fiber laser}, series = {Discover Mechanical Engineering}, journal = {Discover Mechanical Engineering}, number = {10}, publisher = {Springer}, doi = {10.1007/s44245-023-00018-3}, url = {http://nbn-resolving.de/urn:nbn:de:bvb:898-opus4-65647}, pages = {9}, abstract = {Titanium is used in many areas due to its excellent mechanical, biological and corrosion-resistant properties. Implants often have thin and filigree structures, providing an ideal application for fine cutting with laser. In the literature, the main focus is primarily on investigating and optimizing the parameters for titanium sheets with thicknesses greater than 1 mm. Hence, in this study, the basic manufacturing parameters of laser power, cutting speed and laser pulse of a 200 W modulated fiber laser are investigated for 0.15 mm thick grade 2 titanium sheets. A reproducible, continuous cut could be achieved using 90 W laser-power and 2 mm/s cutting-speed. Pulse pause variations between 85 and 335 μs in 50 μs steps and a fixed pulse width of 50 μs show that a minimum kerf width of 23.4 μm, as well as a minimum cut edge roughness Rz of 3.59 μm, is achieved at the lowest pulse pause duration. An increase in roughness towards the laser exit side, independent of the laser pulse pause duration, was found and discussed. The results provide initial process parameters for cutting thin titanium sheets and thus provide the basis for further investigations, such as the influence of cutting gas pressure and composition on the cut edge.}, language = {en} } @unpublished{GradHaagHahnetal., author = {Grad, Marius and Haag, Lydia and Hahn, Konstantin and Schultheiß, Ulrich and Esper, Lukas and Noster, Ulf}, title = {Influence of carbon content on the formation of TiC at diffusion bonded titanium-steel interface}, publisher = {Elsevier}, doi = {10.2139/ssrn.4261928}, abstract = {Hot pressing of pure Ti and various carbon steels in a temperature range of 950 - 1050 °C creates an up to 9 μm thick compound layer of TiC at the Ti/ steel interface. The calculation of the activation energy for layer formation is 126.5 - 136.7 kJ/mol, independent of the steels carbon content. As the carbon content of the steel increases, the layer thickness also increases, which provides enormous potential for the surface modification of Ti/ Ti-alloys.}, language = {en} } @unpublished{BurgerBartschGradetal., author = {Burger, Moritz and Bartsch, Alexander and Grad, Marius and Esper, Lukas and Schultheiß, Ulrich and Noster, Ulf and Schratzenstaller, Thomas}, title = {Enhancement of laser cut edge quality of ultra-thin titanium grade 2 sheets by applying in-process approach using modulated Yb:YAG continuous wave fibre laser}, doi = {10.21203/rs.3.rs-2520041/v1}, abstract = {Titanium is used in many areas due to its excellent mechanical, biological and corrosion-resistant properties. Implants often have thin and filigree structures, providing an ideal application for laser fine cutting. In literature, the main focus is primarily on investigating and optimizing the parameters for titanium sheet thicknesses greater than 1 mm. Hence, in this study, the basic manufacturing parameters of laser power, cutting speed and laser pulsing of a 200 W modulated fibre laser are investigated for 0.15 mm thick titanium grade 2 sheets. A reproducible, continuous cut could be achieved using 90 W laserpower and 2 cutting-speed. Pulse pause variations between 85-335 μs in 50 μs steps and fixed pulse duration of 50 μs show that a minimum kerf width of 23.4 μm, as well as a minimum cut edge roughness Rz of 3.59 μm, is achieved at the lowest pulse pause. An increase in roughness towards the laser exit side, independent of the laser pulse pause, was found and discussed. The results provide initial process parameters for cutting thin titanium sheets and thus provide the basis for further investigations, such as the influence of cutting gas pressure and composition on the cut edge.}, language = {en} } @article{GradSchultheissDiemaretal., author = {Grad, Marius and Schultheiß, Ulrich and Diemar, Andreas and Spieß, Lothar and Noster, Ulf}, title = {Preparation methodology for the microstructural characterization of diffusion layers in a titanium/steel composite}, series = {Practical Metallography}, volume = {61}, journal = {Practical Metallography}, number = {12}, publisher = {Walter de Gruyter GmbH}, issn = {2195-8599}, doi = {10.1515/pm-2024-0087}, url = {http://nbn-resolving.de/urn:nbn:de:bvb:898-opus4-78346}, pages = {938 -- 946}, abstract = {Hot pressing of titanium and carbon steel leads to the formation of a diffusion layer at the interface. Depending on the carbon content of the steel used, it either exclusively contains TiC or additional other phases. In the case of steel with a medium carbon concentration (0.67 wt.\% C), a pure TiC layer forms. A preparation methodology was developed to make statements about functional and microstructural properties of the respective layers such as layer thickness, porosity, or grain size. However, apart from the diffusion layer's microstructure, it also reveals the microstructure of the two base substrates. A comparison based on electron backscatter diffraction (EBSD) examinations yields similar results in terms of microstructure. A micrograph analysis based on the new preparation methodology also allows confirming the element distribution measurement by glow discharge optical emission spectroscopy (GDOES). The methodology therefore provides a way of quickly and reliably controlling the layer formation during the hot pressing process of titanium and carbon steel.}, language = {en} }