@article{BleckDahlNonnetal., author = {Bleck, Wolfgang Peter and Dahl, Winfried and Nonn, Aida and Amlung, Lars and Feldmann, Markus and Sch{\"a}fer, Dirk and Eichler, Bj{\"o}rn}, title = {Numerical and experimental analyses of damage behaviour of steel moment connection}, series = {Engineering Fracture Mechanics}, volume = {76}, journal = {Engineering Fracture Mechanics}, number = {10}, doi = {10.1016/j.engfracmech.2009.03.004}, pages = {1531 -- 1547}, abstract = {Plastic design allows the exploitation of the full resistance of steel structures by taking advantage of stress-redistributions due to plastic strains exceeding the yield strain. Especially in seismic design the utilization of material reserves and the formation of plastic hinges play an important role. In devastating earthquakes in Northridge (USA) and Kobe (Japan) brittle fracture of welded connections in steel moment frames occurred prior to formation of plastic hinges and utilization of plastic material reserves. The subsequent research works resulted in improved design rules and recommendations for these kinds of failure. But to guarantee sufficient ductile performance of these connections also in the upper shelf region, plastic and earthquake resistant design rules should take into account degradation of strain capacity and toughness properties due to quasi static and especially seismic loading. In the scope of the current European project "Plastotough", the main objective is to derive quantified toughness design rules in the upper shelf based on the strain requirements opposed to strain capacities. This paper gives an overview over the research work in performance and shows recent results from experimental and numerical analyses performed within this project for monotonic and cyclic loading.}, language = {en} } @article{NonnDahlBleck, author = {Nonn, Aida and Dahl, Winfried and Bleck, Wolfgang Peter}, title = {Numerical modelling of damage behaviour of laser-hybrid welds}, series = {Engineering Fracture Mechanics}, volume = {75}, journal = {Engineering Fracture Mechanics}, doi = {10.1016/j.engfracmech.2007.10.015}, pages = {3251 -- 3263}, abstract = {The effect of laser-hybrid welds on deformation and failure behaviour of fracture mechanics specimens is investigated in order to provide quantitative prediction of damage tolerance and residual strength. The simulation of crack initiation and crack extension in hybrid welds is performed by applying GTN damage model. The identification of damage parameters requires combined numerical and experimental analyses. The tendency to crack path deviation during crack growth depends strongly on the constraint development at the interface between base and weld metal. In order to quantify the influence of local stress state on the crack path deviation, the initial crack location is varied. Finally, the results from fracture mechanics tests are compared to real component, beam-column-connection, with respect to fracture resistance.}, language = {en} } @inproceedings{NonnDahlBleck, author = {Nonn, Aida and Dahl, Winfried and Bleck, Wolfgang Peter}, title = {Damage Modelling and Safety Assessment of the Hybrid Welded Structures}, series = {5th German-Japanese Seminar "Materials, Processes and Components", Fraunhofer Institute for Mechanics of Materials, Freiburg, Germany}, booktitle = {5th German-Japanese Seminar "Materials, Processes and Components", Fraunhofer Institute for Mechanics of Materials, Freiburg, Germany}, language = {en} }