@inproceedings{BiekerRoustaieSchlaaketal., author = {Bieker, Johannes and Roustaie, Farough and Schlaak, Helmut F. and Langer, Christoph and Schreiner, Rupert}, title = {Field emission characterization of in-situ deposited metallic nanocones}, series = {2017 30th International Vacuum Nanoelectronics Conference (IVNC), 10-14 July 2017, Regensburg, Germany}, booktitle = {2017 30th International Vacuum Nanoelectronics Conference (IVNC), 10-14 July 2017, Regensburg, Germany}, publisher = {IEEE}, doi = {10.1109/IVNC.2017.8051571}, pages = {120 -- 121}, abstract = {An in-situ fabrication technique based on ion track etched template electrodeposition of metallic nanocones was used for the production of field emitter cathodes. Gold nanocones with a height of 24 microns, a base diameter between 3 to 4 microns and a tip diameter below 300 nanometers were deposited on a circular electrode with a diameter of 2.5 mm. The integral field emission (FE) measurements of samples with cone densities of 6 · 104 cones/cm2 (sample A) and 1 · 106 cones/cm2 (sample B) yielded in a maximum current of 37.5 μA at an applied field of 12.5 V/μm for sample A and 29.1 μA at 9.4 V/μm for sample B. The stability of emission current was investigated for over 48 hours and no degradation was observed.}, language = {en} } @inproceedings{KnappLangerPrommesbergeretal., author = {Knapp, Wolfram and Langer, Christoph and Prommesberger, Christian and Lindner, Matthias and Schreiner, Rupert}, title = {Investigations of the transition from field electron emission to stable plasma discharge in a micro electron source at vacuum pressure}, series = {2017 30th International Vacuum Nanoelectronics Conference (IVNC), 10-14 July 2017, Regensburg, Germany}, booktitle = {2017 30th International Vacuum Nanoelectronics Conference (IVNC), 10-14 July 2017, Regensburg, Germany}, publisher = {IEEE}, doi = {10.1109/IVNC.2017.8051594}, pages = {166 -- 167}, abstract = {We report on the transition from field electron emission to plasma discharges. During an experiment with a miniaturized field emission electron source a plasma discharge accompanied by a luminous effect was observed. A novel graphical evaluation method was used to interpret and to compare the observed phenomenon.}, language = {en} } @inproceedings{SerbunPorshynMuelleretal., author = {Serbun, Pavel and Porshyn, Vitali and M{\"u}ller, G{\"u}nter and Mingels, Stephan and L{\"u}tzenkirchen-Hecht, Dirk and Bachmann, Michael and D{\"u}sberg, Felix and Dams, Florian and Hofmann, Martin and Pahlke, Andreas and Prommesberger, Christian and Langer, Christoph and Ławrowski, Robert Damian and Schreiner, Rupert}, title = {Field emission behavior of Au-tip-coated p-type Si pillar structures}, series = {29th International Vacuum Nanoelectronics Conference (IVNC), 2016, 11-15 July, Vancouver, BC, Canada}, booktitle = {29th International Vacuum Nanoelectronics Conference (IVNC), 2016, 11-15 July, Vancouver, BC, Canada}, publisher = {IEEE}, issn = {2380-6311}, doi = {10.1109/IVNC.2016.7551516}, pages = {181 -- 182}, abstract = {Precisely aligned high-aspect-ratio (HAR) silicon tip arrays were fabricated using enhanced reactive ion etching with an inductively-coupled-plasma followed by a sharpening oxidation. A gold thin film was then sputtered only on the tips of the HAR structures. Field-emission (FE) properties from Au-coated HAR p-Si tip array cathodes have been systematically investigated by means of field emission scanning microscopy (FESM). A rather high efficiency of the HAR Si structures (71\% at 550 V), but limited homogeneous FE with currents of 1-600 nA might be correlated with the varying geometry of the tips and the presence of oxides. I-V measurements of single Au-coated HAR emitters revealed activation effects and the saturation current region at 3 nA. An increase of the saturation current by 4 orders of magnitude was observed during 20 hours of conditioning at constant voltage, which finally resulted in nearly reproducible FN curves with a ß-factor of 473. An excellent stability of the emission current of less than 1 \% was obtained during the additional long-time conditioning at constant voltage. Optical switching under halogen lamp illumination resulted in at least 2 times higher saturation currents and showed a linear dependence of the FE current on the light color temperature.}, language = {en} } @inproceedings{PrommesbergerLangerŁawrowskietal., author = {Prommesberger, Christian and Langer, Christoph and Ławrowski, Robert Damian and Schreiner, Rupert}, title = {Field emission from black silicon structures with integrated gate electrode}, series = {29th International Vacuum Nanoelectronics Conference (IVNC), 2016, 11-15 July, Vancouver, BC, Canada}, booktitle = {29th International Vacuum Nanoelectronics Conference (IVNC), 2016, 11-15 July, Vancouver, BC, Canada}, publisher = {IEEE}, issn = {2380-6311}, doi = {10.1109/IVNC.2016.7551532}, pages = {219 -- 220}, abstract = {Black silicon structures with integrated gate electrode were realized by using an improved fabrication process. An enhanced insulation layer was achieved by a combination of dry and wet oxidation, and a gold layer was evaporated as gate electrode. The black silicon structures were prepared with a RIE/ICP etching process at room temperature. Arrays of 16 and 100 apertures with buried p-doped black silicon whiskers have been fabricated. These structures have an emitter height of approximately 1.5 μm with tip radii between 5 nm and 30 nm. The whiskers are surrounded by the gate electrode in a distance of 1.5 μm. Integral field emission measurements yielded an onset voltage of 92 V for 16 apertures and 60 V for 100 apertures for an emission current of 1 nA. Maximum emission currents up to 0.2 μA were observed for the array with 100 apertures at a cathode voltage of 200 V. Stability measurements showed a current fluctuation of ± 21\% at a mean value of the emission current of 12 nA over a period of 30 minutes for 16 apertures with b-Si whiskers.}, language = {en} } @inproceedings{LangerPrommesbergerŁawrowskietal., author = {Langer, Christoph and Prommesberger, Christian and Ławrowski, Robert Damian and Schreiner, Rupert and Huang, Yifeng and She, Juncong}, title = {Gated p-Si field emission cathode applied in an ionization vacuum gauge}, series = {29th International Vacuum Nanoelectronics Conference (IVNC), 2016, 11-15 July, Vancouver, BC, Canada}, booktitle = {29th International Vacuum Nanoelectronics Conference (IVNC), 2016, 11-15 July, Vancouver, BC, Canada}, publisher = {IEEE}, issn = {2380-6311}, doi = {10.1109/IVNC.2016.7551500}, pages = {145 -- 146}, abstract = {A commercial Bayard-Alpert ionization vacuum gauge was equipped with a field emission electron source based on a cathode consisting of an array of 16 gated, p-doped, and DLC-coated Si-tips and characterized. An anode current of about 1.3 μA led to an ion current of 7 fA at 3×10 -7 mbar and 0.8 pA at 4×10 -5 mbar. Whereas at pressures higher than 4×10 -5 mbar the emission current of the electron source decreased, the ratio of ion and anode current remained linear. A nearly constant sensitivity of ~ 17 mbar -1 of the ionization vacuum gauge within the investigated pressure range was depicted.}, language = {en} } @inproceedings{ŁawrowskiLangerPrommesbergeretal., author = {Ławrowski, Robert Damian and Langer, Christoph and Prommesberger, Christian and Schreiner, Rupert}, title = {Field emission from three-dimensional epitaxial grown GaN-microrods}, series = {29th International Vacuum Nanoelectronics Conference (IVNC), 2016, 11-15 July, Vancouver, BC, Canada}, booktitle = {29th International Vacuum Nanoelectronics Conference (IVNC), 2016, 11-15 July, Vancouver, BC, Canada}, publisher = {IEEE}, issn = {2380-6311}, doi = {10.1109/IVNC.2016.7551477}, pages = {87 -- 88}, abstract = {A novel three-dimensional epitaxial technique allows on patterned substrates the realization of gallium nitride pillars, also known as nano- and microrods. The typical dimensions of the microrods are in the range of one micron for the radius of the hexagonal footprint and about 10 μm in height. The microrods consist of a semiconductor heterostructure with an n GaN core, a n-GaN shell, a p GaN shell and an intermediate quantum well layer. The field emission properties were investigated in diode configuration by integral field emission measurements in a vacuum chamber at pressures around 10 -9 mbar. The spacer was mica with a thickness of 50 μm. A metallized fine-meshed nitride grid (or a metallized Si-grid) was used as anode. A current of about 1 μA at a voltage of 1250 V (1750 V) was measured. An onset field of about 12.5 MV/m (20 MV/m) and field enhancement factors in the range of 200 to 500 (150 to 300) were found. The investigation with the fine-meshed grid showed an expected pronounced saturation region.}, language = {en} } @inproceedings{PrommesbergerLangerŁawrowskietal., author = {Prommesberger, Christian and Langer, Christoph and Ławrowski, Robert Damian and Schreiner, Rupert}, title = {Benzocyclobutene as a novel integrated spacer material in a field emission electron source}, series = {International Vacuum Nanoelectronics Conference (IVNC), 30th, 2017, Regensburg}, booktitle = {International Vacuum Nanoelectronics Conference (IVNC), 30th, 2017, Regensburg}, publisher = {IEEE}, doi = {10.1109/IVNC.2017.8051605}, pages = {192 -- 193}, abstract = {For the realization of a miniaturized field emission electron source we tested benzocyclobutene (BCB) as a new spacer material between cathode and anode. We fabricated black silicon emitters and characterized the emission behavior with an integrated 5 μm thin and large-area spacer of BCB. The integrated BCB layer allows the realization of a compact electron source with only two components consisting of a cathode with BCB and a grid. The comparison with other spacer materials like polyimide (25 μm thickness) or mica (50 μm thickness) revealed for the cathode with BCB a significantly reduced operational voltage of 240 V for a field emission current of 1 μA.}, language = {en} } @inproceedings{ŁawrowskiLangerPrommesbergeretal., author = {Ławrowski, Robert Damian and Langer, Christoph and Prommesberger, Christian and Schreiner, Rupert}, title = {Microrods and microlines by three-dimensional epitaxially grown GaN for field emission cathodes}, series = {International Vacuum Nanoelectronics Conference (IVNC), 30th, 2017, Regensburg}, booktitle = {International Vacuum Nanoelectronics Conference (IVNC), 30th, 2017, Regensburg}, publisher = {IEEE}, doi = {10.1109/IVNC.2017.8051576}, pages = {130 -- 131}, abstract = {The three-dimensional epitaxial technique allows the realization of gallium nitride lines in addition to the rods. To optimize the properties of GaN-based field emission cathodes further investigations and an improvement of the epitaxial process were performed. The microrods and microlines consist of a one-order higher n-doped gallium nitride in comparison to the gallium nitride layer on the sapphire substrate. The typical height of the microrods and -lines is about 5 μm. The field emission properties of these structures were investigated in diode configuration by integral field emission measurements at pressures below 10 -9 mbar. For the microrods (microlines) a voltage of 1100 V (2000 V) was measured for a field emission current of about 0.5 μA with an onset field of about 12 MV/m (24 MV/m). Furthermore, the field enhancement factors for microrods and -lines are in the range of 300 and 200, respectively.}, language = {en} } @inproceedings{SerbunPorshynMuelleretal., author = {Serbun, Pavel and Porshyn, Vitali and M{\"u}ller, G{\"u}nter and L{\"u}tzenkirchen-Hecht, Dirk and Prommesberger, Christian and Langer, Christoph and Ławrowski, Robert Damian and Schreiner, Rupert}, title = {Field emission behavior of single n- and p-type black Si pillar structures}, series = {International Vacuum Nanoelectronics Conference (IVNC), 31st, 2018, Kyoto, Japan}, booktitle = {International Vacuum Nanoelectronics Conference (IVNC), 31st, 2018, Kyoto, Japan}, publisher = {IEEE}, doi = {10.1109/IVNC.2018.8520292}, pages = {1-2}, abstract = {We have investigated the properties of single n- and p-type black silicon (b-Si) pillars with a height of 20 μ m under strong electric field and halogen lamp or laser illumination. For both type of b-Si pillar structures, I-V measurements revealed strong activation effects, which consisted in sudden current increases during the first up/down voltage sweeps. The maximum reproducible emission current from a single n-type b-Si pillar structure was about 15 μ A. A pronounced saturation region at 240 nA was observed for a single p-type b-Si pillar. The current fluctuation over time showed a standard deviation of 28\% and 2.5\% for n- and p-type single b-Si pillar structures, respectively. Optical switching under halogen lamp illumination resulted in at least 3 times higher saturation currents and showed a linear dependence of the FE current on the laser power.}, language = {en} } @inproceedings{PrommesbergerLangerSchreiner, author = {Prommesberger, Christian and Langer, Christoph and Schreiner, Rupert}, title = {Stable and low noise field emission from single p-type Si-tips}, series = {International Vacuum Nanoelectronics Conference (IVNC), 31st, 2018, Kyoto, Japan}, booktitle = {International Vacuum Nanoelectronics Conference (IVNC), 31st, 2018, Kyoto, Japan}, publisher = {IEEE}, doi = {10.1109/IVNC.2018.8520018}, pages = {1-2}, abstract = {Single gated p-type Si-tips with two different tip radii were fabricated. An emission current of 2.40 μA was measured for the sharp-edged tip at a voltage of 170 V. In contrast, a stable and reproducible emission behavior was observed with an increased tip radius resulting in a pronounced saturation region between 90 V and 150 V, but merely an emission current of 0.55 μA at 150 V. More remarkable is the stable emission behavior with fluctuation of ± 4 \% during a measurement period of 30 minutes. The integral emission current in a homogeneous tip array (16 emitters) showed nearly the same I-V characteristics compared to the single tip and is therefore, most dominated by only a stable single tip in the array.}, language = {en} }