The catalyst coated membrane represents the heart of a polymer electrolyte fuel cell (PEMFC) and is produced by directly applying a catalyst suspension on the membrane or a decal transfer foil. Understanding the rheology of catalyst inks is crucial to optimize the printed microstructure of the catalyst layer and hence the performance of the fuel cell. The suspension consists of platinum on carbon powder, ionomer dispersion (perfluorosulfonic acid ionomer) and solvents. Its rheology is directly affected by various material properties of all ink components. Therefore, measuring the flow curves represents a suitable tool for quality control at the beginning of the production line.
In this work, flatbed screen printing is evaluated regarding its capability to produce catalyst layers of PEM fuel cells. In the field of printed electronics, screen printing is regarded as robust and high-throughput coating technology. The possibility of in-plane structuring could be an additional degree of freedom, enabling more complex designs of catalyst layers in the future. In this study, process parameters are varied to investigate their effect on resulting layer thickness, homogeneity, and Pt-loading. With the usage of different screens, the Pt-loading can be adjusted. Additionally, two different pastes with and without water content are investigated. The catalyst paste without water showed a better process stability during printing and performed best under dry conditions (RH = 40%) and worst under wet conditions (RH = 100%) during electrochemical in-situ testing. Overall, the reproducibility of the CCM production process was verified. The viscosity of the catalyst paste with 19.55 wt% water in solvent was higher compared to the paste without water. Furthermore, a carbon paste (Pt-free) is developed in a similar viscosity range as the catalyst pastes. The main challenge of screen printing process development lies in the paste optimization to prevent evaporation effects over time, ensuring sufficient wetting of the paste on the substrate and sufficient fuel cell performance.