The Laves phase reinforced CoCrMoSi alloy system has emerged as a candidate material to protect the surface of components to withstand harsh environments under wear and/or corrosion. However, previous reports have raised some concerns and restricted a wider selection of iron-based substrates to be coated, especially limiting the carbon content. This work aims to outline the Laves - Carbides phases in the microstructure and its effect on the properties of T400 alloy deposited on GGG40 ductile iron. Dilution of 26 % ensured Laves formation either as primary or secondary, due to high-silicon substrate selected. Departing from 41 % dilution, the alloy changed to a completely carbide strengthened system. Therefore, for the lowest dilution the coatings hardness is dictated by Laves phase whereas, for higher ones, carbides are the most influent phases.
Fused filament fabrication allows for the additive manufacturing of complex geometries without requiring moulds. However, due to large air voids and poor layer adhesion, the mechanical properties of parts manufactured using fused filament fabrication lag behind those of parts manufactured using conventional techniques. A previous study found that the tensile strength and Young’s modulus of such parts could be increased by a heat-treatment process. However, large air voids were still present after annealing. This study, therefore, investigates the influence of a post-pressure-treatment process on the mechanical performance and the air void ratio of continuous glass fibre-reinforced polyamide 6 in the directions perpendicular to the fibres. Without the treatment, Young’s modulus on the plane parallel to the printing bed is eight times higher than Young’s modulus perpendicular to it. Annealing at 1 MPa homogenises the material and leads to a significant increase of both the tensile strength (55 MPa) and Young’s modulus (5 GPa). Increasing the pressure to 3 MPa only slightly increases the mechanical performance, whereas a further increase to 6 MPa causes no significant changes.
A high-power diode laser was used to generate single- and multi-bead coatings of Stellite™ 6 by coaxial laser cladding over flat grey cast iron (EN-GJLP-200) as a preliminary study to develop a wear and corrosion resistant coating for brake disks on a cost-effective substrate. In this article, we have focused on a detailed quantitative analysis of the effect of different laser powers (1.5, 2.0, 2.5, 3.0, 3.5, and 4.0 kW) on the bead geometry, dilution, microstructure, and hardness. Coatings dilution or composition depends directly on the laser power as well as bead geometry. The typical microstructure of the coatings comprises a solid solution of α (hcp)- and β (fcc)-Co with a dendritic structure as a metal matrix and an interdendritic lamellar eutectic, which contains predominantly β-Co, chromium carbides Cr7C3 and Cr23C6 as well as blocky tungsten carbide W2C. Coating hardness depends on the chemical composition and microstructure that is modified by the deposition parameters. Low laser power results in high carbide fraction and most refined microstructures, accounting for harder coatings.