Limited process control can cause metallurgical defect formation and inhomogeneous relative density in laser powder bed fusion manufactured parts. This study shows that process monitoring, based on optical melt-pool signal analysis is capable of tracing relative density variations: Unsupervised machine learning, applied to cluster multiple-slice monitoring data, reveals characteristic patterns in this noisy time-series signal, which can be co-registered with geometrical positions in the build part. For cylindrical 15–5 PH stainless steel specimens, manufactured under constant process parameters and post-analyzed by µ-computer tomography, correlations between such patterns and an increased local relative density at the edge have been observed. Finite element method (FEM) modeling of thermal histories at exemplary positions close to the edge suggest pre-heating effects caused by neighboring laser scan trajectories as possible reasons for the increased melt pool intensity at the edge.
We report on the laser ablation of cyclic olefin copolymer using an amplified ultrashort pulsed laser in the ultraviolet spectral range. In addition to a high ablation depth per laser-structured layer up to 74 μm at a fluence of 22 J cm−2, an excellent mean roughness 𝑅𝑎
of laser-patterned surfaces down to 0.5 μm is demonstrated. Furthermore, with increasing fluence, increasing ablation efficiencies up to 2.5 mm3 W−1 min−1 are determined. Regarding the quality of the ablation, we observed steep ablation flanks and low debris formation, though for fluences above 10.5 J cm−2 the formation of troughs was observed, being attributed to multiple reflections on the ablation flanks. For comparison, laser ablation was performed under identical conditions with an infrared laser wavelength. The results highlight that UV ablation exhibits significant advantages in terms of ablation efficiency, surface roughness and quality. Moreover, our results show that a larger UV focus spot accelerates the ablation process with comparable quality, paving the way for high-power UV ultrashort pulsed lasers towards an efficient and qualitative tool for the laser machining of cyclic olefin copolymer. The production of complex microfluidics further underlines the suitability of this type of laser.