Sapphire is a robust and wear-resistant material. However, efficient and high-quality micromachining is still a challenge. This contribution demonstrates and discusses two novels, previously unreported approaches for femtosecond laser-based micromachining of rotational-symmetric sapphire workpieces, whereas both methods are in principal hybrids of laser scanning and laser turning or laser lathe. The first process, a combination of a sequential linear hatch pattern in parallel to the workpiece’s main axis with a defined incremental workpiece rotation, enables the fabrication of sapphire fibers with diameters of 50 µm over a length of 4.5 mm. Furthermore, sapphire specimens with a diameter of 25 µm over a length of 2 mm can be fabricated whereas an arithmetical mean height, i.e., Sa parameter, of 281 nm is achieved. The second process combines a constant workpiece feed and orthogonal scanning with incremental workpiece rotation. With this approach, workpiece length limitations of the first process are overcome and sapphire fibers with an average diameter of 90 µm over a length of 20 cm are manufactured. Again, the sapphire specimen exhibits a comparable surface roughness with an average Sa value of 249 nm over 20 cm. Based on the obtained results, the proposed manufacturing method paves an innovative and flexible, all laser-based way towards the fabrication or microstructuring of sapphire optical devices, and thus, a promising alternative to chemical processes.
While sapphire is one of the most durable materials, its properties entail that high-precision machining, especially in the sub-millimeter regime, is still challenging. This contribution demonstrates and discusses novel femtosecond laser-based micromachining approaches for the fabrication of rotational-symmetric sapphire workpieces, specifically the generation of optical fibers by means of laser lathe of sapphire rods and the practical realization of windmill fibers. In addition, volume refractive index modification in planar sapphire substrates is presented to induce photonic crystal waveguides. The micromachined structures are comprehensively examined with respect to geometric fidelity, surface roughness, refractive index modification, and potential optical waveguiding properties. All micromachining approaches are done by means of frequency-doubled or frequency-tripled femtosecond laser radiation. Different laser optical setups including laser scanning head, spatial beam profilers including a spatial light modulator and axial rotatory movement of the specimen are employed for micro structuring and in-depth refractive index modifications. In particular for laser lathe, a sophisticated scanning pattern, in combination with an incremental axial rotatory movement of the specimen, allows for the precise diameter reduction of sapphire rods with 250 µm diameter to fibers with outer diameters of 25 µm. By supporting the workpiece with a V-groove fixture, multi-mode fibers with lengths up to 20 cm can be processed with an average surface roughness of 250 nm. Additionally, an adapted ablation scanning sequence enables the first practical demonstration of sapphire windmill fibers. Furthermore, using a spatial light modulator allows for the adaption of the laser propagation properties as to enable volume refractive index modifications with free-form arrangement. Hexagonal patterns of refractive index modifications surrounding a pristine waveguide core are fabricated and single-mode waveguiding at 1550 nm is verified. Finally, the possibility of integrating Bragg gratings into this photonic waveguide type is demonstrated
We report on the fabrication of rotationally symmetrical geometries with ultrashort laser pulses impinging the constant rotating workpiece tangentially. This particular micro machin-ing of geometry is referred to as laser turning, upon which the laser beam is, in general, orient-ed perpendicularly to the rotational axis and tangentially to the work piece. The target geome-try is realized by moving the constantly rotating specimen according to the specified geometry along the focused laser spot. In contrast to mechanical turning, laser turning induces a mini-mized amount of lateral forces through friction that might deteriorate the geometry. In this study, laser turning is examined for stellite as a function of pulse energy and pulse length in the range between 240 fs and 10 ps. Shorter pulse lengths and higher pulse energies increase the achievable ablation rate, while in the pulse length regime of below 1 ps lower roughness is achieved. With a maximum ablation rate of 1.27 mm³/min and a minimum roughness of 0.17 µm, laser turning combines both, fast processing and high surface quality.
Laser turning with ultra-short laser pulses provides the possibility of manufacturing rotationally symmetric geometries, even of hard to machine materials as fused silica, down to a micrometer scale. In this laser micro machining approach, the laser beam is oriented perpendicularly to the rotational axis and tangentially to the material, whereas the target geometry is realized by moving the constantly rotating specimen according to the specified geometry under the focused laser spot. Due to the fric-tion-less laser ablation it is possible to realize a turning process in fused silica without the use of a contacting tool and therefore without causing mechanical tensions in the work piece. The processing head focuses the laser to a calculated spot size of 18 μm in diameter and the applied processing gas pressure assists in removing the ablated material. In this study, femto-second laser turning of fused silica with a diameter of 3.7 mm is investigated. The influence of the applied pulse energy is stated and the use of a trepanning optic during the turning process is characterized. Furthermore, compre-hensive parameter studies in order to optimize roughness and to find the maximum achievable abla-tion rate are shown. Limited by the mechanical speed of the rotational axis, the highest feasible abla-tion rate is 19.5 mm³/min. A roughness of Ra 0.65 μm are demonstrated.
We report on a comprehensive micromachining study of rotationally symmetric parts using femtosecond laser. A
laser turning process with tangential impingement of the laser radiation complemented by a trepanning optics is
implemented as to accomplish a true laser lathe micromachining approach. With the objective of optimized
ablation rate and reduced surface roughness, the influence of pulse energy, feed rate, trepanning diameter and
angular beam incidence, respectively, is investigated for processing stellite rods. We find the smallest feasible
feature sizes of 8.5 μm in diameter and smoothest surfaces with an arithmetic average of the roughness profile as
low as 0.18 μm. The surface roughness, however, appears to be limited by the occurrence of laser induced periodic
surface structures provoked by the femtosecond laser radiation. Furthermore, the variation of the fluence
in accordance to the incidence on a curved surface is discussed and the heat input into the material is examined
through a longitudinal cross section.
This article discusses the process of the laser turning of rotational symmetric, cylindrical components using ultrashort laser pulses with respect to the geometrical conditions and the resulting energy distribution during the laser turning process. As a result, process predictions and potential process optimizations are feasible. Particular attention is drawn to the laser spot formation on the cylindrical surface of the work piece in conjunction with the positioning of the laser beam relative to the rotation axis of the specimen. Based on fundamental calculations and experimental results, an optimum processing strategy is discussed, whereat the use of a trepanning optic in the laser turning process and the forming of a particular surface structure is additionally being issued.