Institute
The aim of this work is to describe and explain the properties of defects in multicrystalline (mc) and thin-film solar silicon (Si). For this reason, investigations with scanning electron microscope methods were performed, namely cathodoluminescence (CL), electron beam induced current (EBIC), electron backscatter diffraction (EBSD) and transmission electron microscopy (TEM). Additionally, photoluminescence (PL) and reverse-biased electro luminescence (ReBEL) measurements were also conducted. Through correlation of PL, ReBEL and EBIC, it was possible to localize breakdown sites at mc-Si solar cells. Problems that occurred during the thin-film EBIC investigations could be demonstrated and explained. For the first time cross sectional EBIC investigations could be performed on thin-film silicon tandem cells. At mc-Si, it was possible to observe the oxygen related P-line next to the common D1-line luminescence at 10 K clearly distinguishable from each other at once. Furthermore, a hitherto not comprehensively discussed intense luminescence line at 0.93 eV could be described in detail. Through correlation of PL, CL, EBIC, EBSD, and TEM measurements, the origin of the now named Di luminescence at 0.93 eV is postulated to be in connection with Frank partial dislocations, with two energetic levels inside the band gap, one at 112±9 meV below the conduction band and the other at 93±10 meV above the valence band. Finally, it was attempted to explain the behavior of twin boundaries at temperatures below 30 K, where these show an enhanced collection efficiency in comparison to the surrounding grains. An alteration of the local “freeze out” temperature, possibly by a local band gap narrowing, is suggested as a reason. Another conceivable explanation is a breakdown of the diode potential at the grains.