The main subject of this work was the investigation of sintering behavior, microstructure, mechanical properties and biocompatibility of metal injection moulded (MIM) Ti-Nb alloys for biomedical applications. Commercially pure titanium (CP-Ti) samples were also fabricated by MIM as a reference. The sintering behavior of MIM Ti-Nb alloys was studied at first, in order to roughly determine the sintering parameters in the following investigations. Dilatometry was applied to investigate the linear shrinkage of MIM Ti-Nb samples from room temperature to 1500 °C at a heating rate of 3 °C/min under argon atmosphere. Various sintering parameters and Nb contents were used to investigate their influences on microstructure and mechanical properties of MIM Ti-Nb alloys by means of density measurements, optical microscopy (OM), X-ray diffraction (XRD), scanning electron microscopy (SEM) and mechanical testing. Transmission electron microscopy (TEM) and high energy X-ray diffraction (HEXRD) measurement were applied to investigate the nature and precipitation of the unexpected titanium carbide precipitates in MIM Ti-Nb alloys. Initial cell adhesion and cell proliferation assays of human umbilical cord perivascular cells (HUCPV) on MIM Ti-Nb alloys were performed for biocompatibility characterization. The results of this work show that MIM Ti-Nb and MIM CP-Ti samples have been successfully fabricated and the as-sintered samples show good shape retention without distortion compared to the green sample. The sintering process of MIM Ti-Nb alloys consists of three main steps – Ti-diffusion step, Ti-Nb-diffusion step and Matrix-diffusion step. With increasing sintering temperatures and time, MIM Ti-Nb alloys exhibit lower porosity and higher Young’s modulus. A higher Nb content in MIM Ti-Nb alloys leads to an increase of carbide area fraction and porosity. The three factors – Nb content, carbide area fraction and porosity – determine the mechanical properties of MIM Ti-Nb alloys. An increase of Nb content and amount of carbides as well as a lowered porosity lead to a higher tensile strength. A decrease of Young’s modulus can be expected with higher Nb content and porosity. A high amount of titanium carbides can result in very poor ductility, but annealing and quenching process can significantly improve the elongation by dissolving the carbides. MIM Ti-Nb alloys exhibit good biocompatibility, indicating their potential for implant applications.