Titanium and its alloys have been widely used as implant biomaterials due to their suitable combination of mechanical properties and biological compatibilities. At present, about 70-80% of implants are made of metallic biomaterials. Compared with magnesium alloys, stainless steel and cobalt alloys, titanium alloys have a higher specific strength, high corrosion resistance, and excellent biocompatibility. With research, Ti-Nb biomedical titanium alloys have been constantly developed. In the Ti-Nb alloy, the amount of Nb is usually from 16% to 42% (wt.%) which is about 10% to 30% (at.%). As reported, Mn as a trace element to the human body has the potential to be used in bio-materials. Therefore, this study aims at the partial replacement of Nb by Mn to reduce the costs, without deteriorating the mechanical properties. Moreover, it must be ensured good biocompatibility and corrosion resistance. This is the first investigated on Ti-Mn-Nb ternary alloys.
In this work, According to β single-phase field, Ti-xMn-yNb (x=4, 10, 16; y=2, 8, 14, at.%) alloys (arc-melted) have been fabricated. The Ti-Mn-Nb alloys are investigated by optical microscopy (OM), X-ray diffraction (XRD), hardness test, transmission electron microscopy (TEM) and mechanical testing. By screening study on alloy, Ti-10Mn-14Nb (at.%) (Ti-10Mn-23.7Nb (wt.%)) is the optimal alloy with tensile strength (760 MPa) and elongation (10.5%). After that, the Metal Injection Moulding (MIM) is used to prepare Ti-Mn-Nb alloys. The MIM method can greatly reduce the processing cost. MIM Ti-xMn-yNb (x=3, 4, 6; y=1, 2, 4, at.%), Ti-4Mn-14Nb and Ti-10Mn-14Nb alloys are fabricated. Among them, a very good combination of mechanical properties is achieved for MIM processed Ti-4Mn-2Nb (at.%) (Ti-4.5Mn-3.8Nb (wt.%)), namely a YS of 642 MPa, UTS of 725 MPa and high ductility of 16% elongation to fracture. With further investigations, when the yttrium content is 0.1% (at.%), the tensile strength of Ti-4Mn-2Nb-0.1Y (at.%) (Ti-4.5Mn-3.8Nb-0.18Y (wt.%)) is increased to 785 MPa while elongation of 12.9%. These mechanical properties already exceed Ti-6Al-4V (ASTM F2885 Grade 5 undensified).
In the in vitro evaluation, in comparison with MIM pure titanium, human osteoblasts MG63 adhered as well and proliferated on the surface of MIM Ti-Mn-Nb specimens. In the supernatant after cell culture, the Ti-Mn-Nb alloy shows similar osmolality and pH value results as MIM pure titanium. By LDH assay and DNA isolation, the MIM Ti-Mn-Nb alloys are not found to be toxic to MG63 cells.
In the study of corrosion resistance in Hanks’ balanced salt solution (HBSS) at 37 °C, the corrosion current densities as well as the impedance of MIM Ti-Mn-Nb alloys are all better than those of MIM pure titanium and even better than those of MIM Ti-6Al-4V alloy.