Historically, Ge is one of the oldest materials in the semiconductor industry and its (001) surface has been the subject of extensive investigations by photoelectron spectroscopy. I am going to challenge the predominant attribution of a semi-conducting nature of the Ge(001) surface in this thesis. My investigations reveal the presence of a Ge(001) surface state above the Fermi-level, occupied at room temperature. Employing time- and temperature-dependent angle-resolved photoelectron spectroscopy, I will demonstrate that the presence of this surface state is evidence for the conducting nature of the surface at room temperature.
Sparked by the remarkable properties of the GeSn-alloy and a trend towards Ge-Sn-related multiquantum well fabrication, I investigate the surface electronic structure of Ge(001) after adsorption and incorporation of Sn. With an in-depth analysis of surface core-level shifts, I will extend the growth model of the Sn wetting layer formation by also detailing structural changes in the subsurface region. At the same time, the modifications of the electronic structure will be detailed, observing the removal of the Ge(001) surface states, the creation of a new, Sn-related surface state and the initial stages of the Schottky barrier formation.
β-Ga2O3 is a transparent semi-conducting oxide that has sparked a lot of interest over the last decade, because it offers an ultra-wide band gap and high break down voltage. However, due to its monoclinic crystal structure, device fabrication is rather challenging and researchers are already looking into alternative materials. One of these candidates is ϵ-Ga2O3 and this work presents a combined study by photoelectron spectroscopy and ab initio calculations of its electronic structure. (Hard) X-rays reveal the impact of photoelectron recoil and the absence of a band bending to the surface, while the dispersion of experimentally determined valence states compares favorably with the calculations based on hybrid density-functional theory.
Another alternative to β-Ga2O3 could be ZnGa2O4 and I will present an investigation on the electronic structure of its (100) surface. Due to the novelty of ZnGa2O4 single-crystals, I am first going to explore the preparation of a clean and well-ordered surface by standard in-situ sputtering and annealing. I will show that already low annealing temperatures induce Zn-deficiency, leading to non-stoichiometric surfaces, further exacerbated by sputtering. By changing the sputtering parameters and the annealing conditions, the preparation of a surface with sufficient quality for subsequent investigations will be demonstrated. The results by photoemission techniques compare favorably with the expectations from theory and allowing the first fundamental insights into the surface electronic structure.
The chemical and electronic structure of the interfaces of kesterite-based and related absorber materials in thin-film solar cell device-relevant layer stacks have been investigated with x-ray based spectroscopic techniques (XPS, HAXPES, XAES, XES, and XAS). The analyzed materials are CZTS absorbers with their interfaces to the Mo back contact and to different Zn(O,S)-buffer layers, SnS absorbers with partly N-doped ZnO buffer layers, and 2 absorbers with (Cd,Zn)S buffer layers.
We find an unchanged CZTS surface in this series which has a profound effect on the ZnOS growth. Instead of a constant composition throughout the buffer thickness, we find S-rich material growing directly on the CZTS in the ALD process. The conduction band offset is found to be around -0.21(+-0.15) eV. The measured cliff is reduced by chemical interface modification towards a flat band alignment.
The interface effect during annealing at the CZTS back contact where MoS2 forms occurs even at low annealing temperatures below 500°C. Sn spectra of liftoff CZTS back sides, annealed on the Mo contact, resemble the precursor at all temperatures while Sn spectra of CZTS front sides are almost single phase after standard annealing. A TiN interlayer was effectively introduced to prevent reactions at the CZTS/Mo interface.
We find a strong impact of ALD deposited ZnO on oxidized SnS absorber surfaces, resulting in metallic Sn formation. In contrast, doped ZnO:N reduces the SnS much less agressively. The strong downwards bending for both ZnO and SnS at the ZnO/SnS junction that we find for undoped ZnO contact layers is drastically reduced if ZnO:N contact layers are used. The smaller cliff in the conduction band of 0.2 eV for ZnO:N/SnS makes this junction much more interesting for solar cell applications than the ZnO/SnS with a large cliff of 0.55 eV.
The chemical analysis of the (Cd,Zn)S:Ga/CuSbS2 reveals chemical interaction at the junction. We find an additional species on the high energy side of the Cu peak for all samples. The interface species can be explained with the changed buffer composition at the interface, particularly low S and Cd content and increased Ga concentration, and could also be affected by the presence of O and hydroxides. We find an upwards surface band bending of -0.15 eV for the bare absorber. At the junction, we see downwards band bending of up to 0.2(+-0.09) eV in the absorber and strong upwards band bending of -0.75(+-0.28) eV in the buffer. The junction is not an abrupt transition from one homogenious material to another. The buffer growth is strongly affected by the absorber. Also the electronic structure on both sides is significantly affected. We find a conduction band alignment with a large cliff of -1.3(+-0.3) eV.
This thesis focuses on the deposition of thin TiO₂ films on p-type Si using atomic layer deposition (ALD) technique, on the study of the electronic proprieties of the grown films and on the electrochemical characterization of TiO₂/Si photoelectrodes. The deposition parameters, electronic properties and electrochemical performance and stability of the TiO₂/Si samples are correlated.
The ALD technique is used to deposit TiO₂ with two different precursors namely Titanium isopropoxide and Titanium methoxide onto Si substrates. Laboratory as well as synchrotron based X-ray spectroscopy techniques are used to characterize these films. The growth quality of the TiO₂ ALD films is determined by analyzing X-Ray photoelectron spectroscopy (XPS) data in terms of stoichiometry, defect states and Ti³⁺:Ti⁴⁺ ratios. The ALD technique was modified with different heating arrangements to obtain various polymorphs of TiO₂.
The ALD and anatase TiO₂ films are characterized using synchrotron radiation to study their electronic properties and these films are compared with single crystal rutile TiO₂. X-ray absorption spectroscopy (XAS) and resonant photoelectron spectroscopy (res-PES) measurements are performed with synchrotron radiation. XAS measurements are used to determine the polymorphs as well as the electronic structure of TiO₂ Res-PES measurements are conducted at the O1s and Ti2p edges to study multiple hole Auger decay processes and polaronic and charge transfer states as well as to determine the electronic band gap of the TiO₂ layers. One of the main findings of this thesis is the determination of the partial density of states (pDOS) of O and Ti in the conduction and valence band. The combination of the pDOS and the band edge positions obtained from res-PES measurements are used to calculate the charge neutrality level of the TiO₂ polymorphs.
The photoelectrochemical measurements are conducted on bare-Si and TiO₂/Si photoelectrodes. The electrochemical performance of these photoelectrodes is studied in electrolytes having pH values ranging from 1 to 13. The deposition of TiO₂ on Si enhances the photoelectrochemical performance of the Si photoelectrode. The TiO₂ increases the stability of the photoelectrode in all electrochemical media over 12 hours of experimental condition. Moreover, it is also observed that the TiO₂/Si photoelectrode is less responsive to the pH value of the electrolyte. The electrochemical findings are explained on the basis of the electronic properties of the TiO₂ layer. The electronic band gap obtained from spectroscopic measurement and the photoelectrochemical measurements are used to explain the performance and stability of the TiO₂/Si photoelectrodes. The thesis also addresses the stability of Si microstructured photoelectrodes (SiMPs) prepared by an electrochemical method. The stability of the SiMPs deteriorates more rapidly than that one of the planar Si photoelectrode. However, using a protective ALD TiO₂ layer on these SiMPs the overall performance is even more enhanced than on the TiO₂/planar Si system.
In this thesis the detailed investigations concerning processing and stability of thin films including carbon species and their possible application as materials of a low dielectric constant (low k) are presented. In order to gather a complex information regarding the chemical, morphological and dielectric properties of the produced layer a combination of the spectroscopy: X-ray photoelectron spectroscopy (XPS), near edge X-ray absorption fine structure spectroscopy (NEXAFS) and Fourier transform infrared spectroscopy (FTIR), microscopy: atomic force microscopy (AFM) and electrical characterization: capacitance-voltage technique (CV) have been applied. The films deposited by means of variety of techniques have been described, ranging from evaporation, through spraying and dropping to spin-coating. Regarding the possible low-k application, a considerable attention has been paid to the hybrid organic-inorganic 3-aminopropyl-trimethoxysilane (APTMS) based composite materials enriched with carbon species coming from the following dopants: C60 fullerenes, [6,6]-phenyl-C61-butyric acid (PCBM), copper phthalocyanine (CuPc), and tris(dimethylvinylsilyloxy)-POSS (POSS). In the following thesis progressive steps leading to gradual decreasing of the resulting permittivity of the hybrid material is presented. As revealed by the performed investigations, the replacement of C60 within the APTMS based matrix by its better soluble derivative PCBM allows the increase of the concentration of the carbon species within the composite films. The introduction of POSS as an additional dopant gave the opportunity of increasing the resistance of the produced material against the ambient influence. With the excess of the POSS concentration an original fractal-shaped cluster formation has been observed. Finally, the dispersion of the properly chosen low concentration of CuPc and POSS molecules within the APTMS based matrix led to the fabrication of homogenous layer with an ultra-low dielectric constant of 1.8.
We have grown HfO2 on Si(001) by atomic layer deposition (ALD) using HfCl4, TEMAHf, TDMAHf and H2O as precursors. The early stages of the ALD were investigated with high-resolution photoelectron spectroscopy and x-ray absorption spectroscopy. We observed the changes occurring in the Si2p, O1s, Hf4f, Hf4d, and Cl2p (for HfCl4 experiment) core level lines after each ALD cycle up to the complete formation of two layers of HfO2. The investigation was carried out in-situ giving the possibility to determine the properties of the grown film after every ALD cycle or even after a half cycle. This work focused on the advantages of the in-situ approach in comparison to ex-situ experiments. The study provides to follow the evolution of the important properties of HfO2: contamination level, density and stoichiometry, and influence of the experimental parameters to the interface layer formation during ALD. Our investigation shows that the in-situ XPS approach for ALD gives much more information than ex-situ experiments.