TY - JOUR A1 - Dikra, Bouras A1 - Fellah, Mamoun A1 - Barille, Regis A1 - Weiß, Sabine A1 - Samad, Mohammed Abdul A1 - Alburaikan, Alhanouf A1 - Khalifa, Hamiden Abd El-Wahed A1 - Obrosov, Aleksei T1 - Improvement of photocatalytic performance and sensitive ultraviolet photodetectors using AC-ZnO/ZC-Ag2O/AZ-CuO multilayers nanocomposite prepared by spin coating method T1 - Verbesserung der photokatalytischen Leistung empfindlicher Ultraviolett-Photodetektoren unter Verwendung von AC-ZnO/ZC-Ag2O/AZ-CuO-Multilayer-Nanokompositen abgeschieden durch Rotationsbeschichtung JF - Journal of science: advanced materials and devices N2 - Morphological and optical properties of a multilayer film (CAZO/CZAO/ZACO) prepared by spin-coating method and deposited on a glass substrate were evaluated. The study was initially carried out for each layer, individually and then as a multilayer subsequently. Structural properties using X-ray diffraction (XRD), energy-dispersive X-ray spectroscopy (EDS), infrared spectra (IR) and X-ray photoelectron Spectroscopy (XPS) showed the presence of three phases of zinc, copper and silver oxides at different levels. The CZAO sample observed with scanning electron microscope (SEM) showed an excellent porous surface with a large deformation in the multilayer configuration. Doping with zinc and copper in the silver crystal lattice improved the crystal structure and reduced the optical energy gap, thus increasing the optical absorbance and refractive index. The dielectric constants and showed an increase in the optical polarization values for lower photonic energies. The maximum degradation rate for photocatalysts of methylene blue was 89 % for a 5-h exposure period with CAZO/CZAO/ZACO while it reached 71 % for the CZAO sample during the same time period. The sensitivity of samples to light proved that the presence of ultraviolet radiation increases the number of holes trapped by oxygen ions and causes more free electrons and contribute to a better production of photocurrent than in darkness. N2 - Die morphologischen und optischen Eigenschaften eines mehrlagigen Films (CAZO/CZAO/ZACO), der im Rotationsbeschichtungsverfahren hergestellt und auf ein Glas-Substrat aufgebracht wurde, wurden bewertet. Die Studie wurde zunächst für jede Schicht einzeln und anschließend als Multilagenbeschichtung durchgeführt. Die strukturellen Eigenschaften mittels Röntgenbeugung (XRD), energiedispersiver Röntgenspektroskopie (EDS), Infrarotspektren (IR) und Röntgenphotoelektronenspektroskopie (XPS) zeigten das Vorhandensein von drei Phasen aus Zink-, Kupfer- und Silberoxiden auf verschiedenen Ebenen. Die mit dem Rasterelektronenmikroskop (REM) untersuchte CZAO-Probe zeigte eine ausgezeichnete poröse Oberfläche mit einer großen Verformung in der Multischichtkonfiguration. Die Dotierung des Silberkristallgitters mit Zink und Kupfer verbesserte die Kristallstruktur und verringerte die optische Energielücke, wodurch sich die optische Absorption und der Refraktionsindex erhöhten. Die Dielektrizitätskonstanten und die optischen Polarisationswerte stiegen bei niedrigeren Photonenergien an. Die maximale Abbaugeschwindigkeit der Photokatalysatoren für Methylenblau betrug 89 % bei einer 5-stündigen Belichtungszeit mit CAZO/CZAO/ZACO, während sie bei der CZAO-Probe im gleichen Zeitraum 71 % erreichte. Die Lichtempfindlichkeit der Proben beweist, dass das Vorhandensein von ultravioletter Strahlung die Anzahl der von Sauerstoffionen eingefangenen Löcher erhöht und mehr freie Elektronen verursacht, die zu einer besseren Produktion von Photostrom beitragen als bei Dunkelheit. KW - Multilayer CAZO/CZAO/ZACO KW - Photocatalysis KW - Photodetector KW - Nanostructures KW - Nanocomposites KW - Multilagenbeschichtung CAZO/CZAO/ZACO KW - Rotationsbeschichtung KW - Photokatalyse KW - Nanostrukturen KW - Nanokompositen KW - Nanokomposit KW - Mehrschichtsystem KW - Beschichtung KW - Fotokatalyse KW - Photodetektor Y1 - 2023 U6 - https://doi.org/10.1016/j.jsamd.2023.100642 SN - 2468-2179 VL - 9 IS - 1 PB - Elsevier CY - Amsterdam ER - TY - JOUR A1 - Obrosov, Aleksei A1 - Fallah, Mamoun A1 - Hezil, Naouel A1 - Bouras, Dikra A1 - Bouchareb, Nabila A1 - Perez Larios, Alejandro A1 - El-Hiti, Gamal A. A1 - Weiß, Sabine T1 - Investigating the effect of Zr content on electrochemical and tribological properties of newly developed near β-type Ti-alloys (Ti–25Nb-xZr) for biomedical applications T1 - Untersuchung der Auswirkung des Zr-Gehalts auf die elektrochemischen und tribologischen Eigenschaften neu entwickelter β-naher Ti-Legierungen (Ti-25Nb-xZr) für biomedizinische Anwendungen JF - Journal of Science: Advanced Materials and Devices N2 - In order to create alloys with exceptional properties for orthopedic uses, this study focuses on the impact of zirconium (Zr) content on the structural, electrochemical, and tribological qualities of nanostructured Ti–25NbxZr [x = 5, 10, 15, 20, 25, and 30 atomic (at.) %] alloys. The structural evolution was investigated using XRD and SEM techniques. The mechanical characteristics of the produced alloys, including Vickers hardness and Young’s modulus, were measured. In addition, the corrosion tests were performed using the OCP, EIS, and PD methods in Ringer’s solution within the independent pH range at 37°C. A ball-on-disc tribometer was used to investigate the tribological behavior of the alloys under various loads and wet conditions using the Ringer solution. It has been verified that Zr content (at. %) in the alloys had an impact on their morphologies, structural evolution, and mechanical characteristics. According to the morphological analysis, the particle and crystallite size decreases with increasing Zr content. Young’s modulus and Vickers hardness show the same tendency. The EIS data demonstrated that a single passive film formed on the alloy surfaces, and the addition of Zr enhanced the corrosion resistance of the passive films. The polarization curves demonstrate that the alloys had low corrosion current densities and large passive areas without the passive films disintegrating. Likewise, the inclusion of Zr resulted in a reduction in the corrosion and passive current density values. All of these results suggested that the titanium alloys exhibit a more noble electrochemical activity caused by Zr. From the tribological perspective, it was found that the friction coefficient of the alloys reduced with increasing Zr content. N2 - Um Legierungen mit außergewöhnlichen Eigenschaften für orthopädische Anwendungen zu schaffen, konzentriert sich diese Studie auf die Auswirkungen des Zirkonium (Zr)-Gehalts auf die strukturellen, elektrochemischen und tribologischen Eigenschaften von nanostrukturierten Ti-25NbxZr [x = 5, 10, 15, 20, 25 und 30 Atom-(at.) %] Legierungen. Die strukturelle Entwicklung wurde mit XRD- und SEM-Techniken untersucht. Die mechanischen Eigenschaften der hergestellten Legierungen, einschließlich der Vickershärte und des Elastizitätsmoduls, wurden gemessen. Darüber hinaus wurden die Korrosionstests mit den Methoden OCP, EIS und PD in Ringerlösung im unabhängigen pH-Bereich bei 37°C durchgeführt. Mit einem Kugel-Scheiben-Tribometer wurde das tribologische Verhalten der Legierungen unter verschiedenen Belastungen und nassen Bedingungen in Ringerlösung untersucht. Es wurde nachgewiesen, dass der Zr-Gehalt (in %) in den Legierungen einen Einfluss auf ihre Morphologie, strukturelle Entwicklung und mechanischen Eigenschaften hat. Die morphologische Analyse ergab, dass die Partikel- und Kristallitgröße mit zunehmendem Zr-Gehalt abnimmt. Elastizitätsmodul und Vickershärte zeigen die gleiche Tendenz. Die EIS-Daten zeigten, dass sich auf den Legierungsoberflächen ein einziger Passivfilm bildete, und der Zusatz von Zr erhöhte die Korrosionsbeständigkeit der Passivfilme. Die Polarisationskurven zeigen, dass die Legierungen niedrige Korrosionsstromdichten und große passive Flächen aufwiesen, ohne dass sich die Passivfilme auflösten. Ebenso führte der Zusatz von Zr zu einer Verringerung der Korrosions- und Passivstromdichtewerte. Alle diese Ergebnisse deuten darauf hin, dass die Titanlegierungen eine edlere elektrochemische Aktivität aufweisen, die durch Zr verursacht wird. Aus tribologischer Sicht wurde festgestellt, dass der Reibungskoeffizient der Legierungen mit zunehmendem Zr-Gehalt abnahm. KW - Ti-Nb-Zr alloys KW - Nanobiomaterials KW - Tribological behavior KW - Ringer's solution KW - Biomedical applications KW - Ti-Nb-Zr-Legierungen KW - Nanowerkstoffe KW - Tribologisches Verhalten KW - Ringerlösung KW - Biomedizinische Anwendungen KW - Biomedizin KW - Nanostrukturiertes Material KW - Titanlegierung KW - Zirconium Y1 - 2024 U6 - https://doi.org/10.1016/j.jsamd.2024.100695 SN - 2468-2179 VL - 9 IS - 2 PB - Elsevier CY - Amsterdam ER -