@phdthesis{Mankovics2015, author = {Mankovics, Daniel}, title = {Luminescence investigation of bulk solar silicon and silicon thin films on glass substrate}, url = {http://nbn-resolving.de/urn:nbn:de:kobv:co1-opus4-35196}, school = {BTU Cottbus - Senftenberg}, year = {2015}, abstract = {The aim of this work is to study the optical properties of crystal defects in multicrystalline solar silicon and poly-/microcrystalline silicon thin films on glass substrate. First a setup for photoluminescence imaging on multicrystalline silicon solar wafers was developed. This system is suitable for detecting band-to-band luminescence as well as defect-related luminescence at room temperature on large-scale wafers at different stages of their processing. Spectroscopic photoluminescence investigations of multicrystalline silicon solar wafers indicated a new intense luminescence line at ≈ 0.91 eV at room temperature. The origin of this line is probably found in a specific grain boundary. Furthermore, luminescence in the region of 0.8 eV was investigated in detail, and it was found that probably oxygen is responsible for a peak at 0.77 eV at 80 K. Electroluminescence investigations at room temperature at both materials exhibit extended defect structures such as grain boundaries. Furthermore, it can be concluded that electroluminescence imaging in reverse bias mode indicate on serious breakdown points in solar cells, which can lead to destruction of solar cells and modules. By comparing defect-related and reverse bias electroluminescence images, a difference in the spatial distribution of defects emitting D1 radiation and defects emitting light under reverse bias beyond -12 V is detectable. In addition, there seems to be a correlation in the distribution of non-doping impurities and photoluminescence. Concerning this, vertical slabs of two silicon blocks were examined by means of Fourier-transform infrared spectroscopy and photoluminescence. A correlation of the distributions of interstitial oxygen and the band-to-band luminescence profiles could be found. Additionally, a correlation between D3/D4 luminescence profile and nitrogen distribution in the blocks was observed. Finally, the growth process, particularly the transition from amorphous to microcrystalline silicon by PECVD, was studied by combined photoluminescence and Raman investigations. Formation of silicon nano-grains was detected by means of photoluminescence and Raman spectroscopy.}, subject = {Silicon; Defects; Photoluminescence; Luminescence imaging; Silicon thin films; Silizium; Defekte; Photolumineszenz; Lumineszenz-Imaging; Silizium-D{\"u}nnfilme; Silicium; D{\"u}nnschichttechnik; Solarzelle; Fehleranalyse}, language = {en} } @phdthesis{Krause2015, author = {Krause, Christoph}, title = {Investigation of particular crystal defects in solar silicon materials using electron beam techniques}, url = {http://nbn-resolving.de/urn:nbn:de:kobv:co1-opus4-34846}, school = {BTU Cottbus - Senftenberg}, year = {2015}, abstract = {The aim of this work is to describe and explain the properties of defects in multicrystalline (mc) and thin-film solar silicon (Si). For this reason, investigations with scanning electron microscope methods were performed, namely cathodoluminescence (CL), electron beam induced current (EBIC), electron backscatter diffraction (EBSD) and transmission electron microscopy (TEM). Additionally, photoluminescence (PL) and reverse-biased electro luminescence (ReBEL) measurements were also conducted. Through correlation of PL, ReBEL and EBIC, it was possible to localize breakdown sites at mc-Si solar cells. Problems that occurred during the thin-film EBIC investigations could be demonstrated and explained. For the first time cross sectional EBIC investigations could be performed on thin-film silicon tandem cells. At mc-Si, it was possible to observe the oxygen related P-line next to the common D1-line luminescence at 10 K clearly distinguishable from each other at once. Furthermore, a hitherto not comprehensively discussed intense luminescence line at 0.93 eV could be described in detail. Through correlation of PL, CL, EBIC, EBSD, and TEM measurements, the origin of the now named Di luminescence at 0.93 eV is postulated to be in connection with Frank partial dislocations, with two energetic levels inside the band gap, one at 112±9 meV below the conduction band and the other at 93±10 meV above the valence band. Finally, it was attempted to explain the behavior of twin boundaries at temperatures below 30 K, where these show an enhanced collection efficiency in comparison to the surrounding grains. An alteration of the local "freeze out" temperature, possibly by a local band gap narrowing, is suggested as a reason. Another conceivable explanation is a breakdown of the diode potential at the grains.}, subject = {Defects; Silicon; EBIC; CL; Di luminescence; Defekte; Silizium; EBIC; CL; Di Lumineszenz; Solarzelle; Silicium; Zuverl{\"a}ssigkeit}, language = {en} }