Circumventing boundary effects while characterizing epoxy/copper interphases using nanoindentation
(2017)
Characterization of the size and mechanical properties of interphases is essential when designing multicomponent materials. When nanoindentation is used to investigate the size and mechanical properties of an interphase, a common challenge is that the indenter or the stress zone formed around it are often restricted by the reinforcement, making it difficult to distinguish the mechanical property variations caused by the interphase itself from those caused by the boundary effect. In this work, a testing system was developed that allows determining the indent affected zone and accounting for it in the interphase measurements of an epoxy/Cu system. Using finite element analysis, we confirmed the validity of the proposed system. Nanoindentation was used to investigate the Interphase between copper and two different epoxy systems; amine-cured and anhydride-cured. Nanoindentation results showed that a copper layer that is only 10 nm thick still exhibits a constriction effect on the indentations in its vicinity. The amine-cured epoxy did not show any sign of interphase existence using the introduced method. However,
a soft interphase with a thickness of ~1.7 μm was measured on theanhydride-cured epoxy. Furthermore, we show that the proposed system can be used to determine the interphase thickness as well as its relative mechanical properties regardless of the indentation depth.
This system can be further used for investigating other polymer/metal interphases to better understand the factors influencing them, thus helping engineer the interphase size and properties to enhance composite performance.
Viscoelastic properties of the interphase in fibre reinforced polymers - measurement and simulation
(1999)
Mapping Epoxy Interphases
(2005)
Characterization of the mechanical properties of interphases is essential when designing multicomponent materials such as fiber-reinforced matrices, protective coatings or multi-layered structures for integrated circuits. It can provide vital information about the durability of the finished product as a composite because failure is often initiated in the interfacial region induced by internal or external stress during fabrication or service. Nanoindentation is a powerful tool for investigating mechanical properties on the micro/nano scale. However, there are some challenges associated with conducting nanoindentation near interface regions. One main challenge is that the small thickness of the interphase region (typically 1-2µm) makes it difficult to apply several adjacent indents without overlap. Another issue is that the indentations are usually restricted by local reinforcement, and it becomes difficult to isolate the change in mechanical properties due solely to interphase formation. In this study we try to gauge the feasibility of nanoindentation for characterizing epoxy/Cu interphases. We develop a sample preparation method and optimize nanoindentation parameters in an attempt to avoid the restrictions mentioned above. Atomic force microscopy (AFM) and finite element analysis are employed as reference techniques to evaluate the effectiveness of our technique. We show the influence of preparation method and nanoindentaion parameters on measurements of interphase properties and how they relate the mentioned challenges.
Epoxy R-Glass Fiber-Reinforced Polymer (GFRP) composite plates were hydrothermally aged at 60 ◦C for 23, 75, and 133 days. The water content reached 0.97 wt%, 1.45 wt% and 1.63 wt%, respectively. The studied GFRP matrix was inert to hydrolysis or chain scission, allowing for investigation of irreversible changes in the fiber-matrix interphase due to hydrothermal aging upon re-drying. During each period, a subset of the specimens was removed from the water bath and dried in a chamber. The weight loss upon drying was explained with epoxy leaching (impurities), sizing-rich interphase hydrolysis, glass fiber surface hydrolysis, accumulated degradation products escaping, and water changing state from bound to free. The influence of hydrothermal aging on the fiber-matrix interfacial properties was investigated. Lower interfacial strength of hydrothermally aged (wet)
samples was attributed to plasticization of the epoxy, plasticization and degradation of the sizing-rich interphase (including formation of hydrolytic flaws), and hydrolytic degradation of the glass fiber surface. The kinetics of epoxy-compatible epoxysilane W2020 sizing-rich interphase hydrolysis provided an estimate of ca. 1.49%, 4.80%, and 8.49% of the total composite interphase degraded after 23, 75, and 133 days, respectively. At these conditions, the interface lost 39%, 48%, and 51% of its strength. Upon re-drying the specimens, a significant part of the interfacial strength was regained. Furthermore, an upward trend was observed, being 13%, 10% and 3% strength, respectively; thus, indicating a possibility of partial recovery of properties.