Filtern
Dokumenttyp
- Vortrag (26)
Referierte Publikation
- nein (26)
Schlagworte
- MIC (26) (entfernen)
Organisationseinheit der BAM
- 4 Material und Umwelt (14)
- 4.1 Biologische Materialschädigung und Referenzorganismen (13)
- 6 Materialchemie (7)
- 6.2 Material- und Oberflächentechnologien (7)
- 1 Analytische Chemie; Referenzmaterialien (1)
- 1.1 Anorganische Spurenanalytik (1)
- 4.0 Abteilungsleitung und andere (1)
- 6.1 Oberflächen- und Dünnschichtanalyse (1)
- 9 Komponentensicherheit (1)
- 9.0 Abteilungsleitung und andere (1)
Eingeladener Vortrag
- nein (26) (entfernen)
The corrosion of stainless steel components is a problem of global scale, economically as well as in regards to the safety of industrial equipment and facilities. With microorganisms involved (microbial influenced corrosion, MIC), the problem becomes more complex. Iron reducing bacteria (IRB) for example accelerate the corrosion of iron based materials like stainless steel via the reduction of iron oxides in the passive layer. When co-cultivated with iron oxidizing bacteria, IRBs can induce deep, heterogeneously distributed pits on stainless steel surfaces. The analysis of localized corrosion – or pitting corrosion – is of great relevance since it can lead to unpredictable material failure. In general, macroscopic electrochemical methods are not capable of providing information about the spatial heterogeneity of a sample and thus need to be complemented by multi-electrode based techniques or scanning electrochemical methods.
The aim of this work is to develop methods for the analysis of localized corrosion, on stainless steel surfaces induced by IRB biofilms. The greatest challenge is to address the complexity of two heterogeneous systems at the metal/biofilm interface. First there is the variation in the passive layer composition and microstructure. Secondly, the microbial biofilm with its heterogeneous tree-dimensional structure resulting in local differential aeration cells and electrochemical parameters. To be able to differentiate between individual effects, artificial biofilms mimicking the physical properties of a natural biofilm are used in this study as model systems. This artificial biofilm is applied on a multi-electrode probe to identify local anodic sites during exposure experiments. The detailed analysis of active sites by means of scanning electrochemical microscopy (SECM) allows the investigation of local properties within the biofilm and its immediate vicinity.
The presented analytical approach delivers promising results in clarifying how localized corrosion of stainless steels develops chronologically and spatially in the presence of IRBs. Furthermore, our results on model systems provide the basis for the application of the methodology for the investigation of natural or multi-species biofilms in the future.
Presentation of the MIC-project (Microbially Induced Corrosion) within the focus area Materials of the BAM. Strategies, developments and innovations in the area of analytical tools, surface modifications, polymer stability and biofilm-enhanced deteriorations of materials in the context of microbially induced corrosion processes.
Microbiologically Influenced Corrosion (MIC) is a phenomenon that is increasingly becoming a problem
for the society. MIC describes the negative effects a material can experience due to the presence of
microorganisms. In Europe, several research groups/ other industrial stakeholders are already dealing with
MIC. Unfortunately, the discussions are fragmented and the exchange of information is limited. A true
transdisciplinary approach is hardly ever experienced, although this would be logical for this
material/biology related challenge.
USA, Canada and Australia have strong networks, and develop methods, prevention measures and
standards, which Europe is forced to use, since nothing similar exists for a network and combined
knowledge to design them according to european standards. This makes Europe extremely dependent and,
in some cases, the potential measures or standards cannot been used because the suggested solutions
are prohibited by European laws (e.g. use of biocides).
Therefore, it is important to initiate a new European MIC-network. Europe needs to combine the efforts as
experts in different fields and develop prevention measures according to the European rules, in close
cooperation with industry and plant operators and owners of critical infrastructure. This COST Action will
provide the necessary interaction and communication, knowledge sharing, training of personnel and of
researchers of different disciplines. This will bring Europe to a leading role in this process, bringing ideas on
an equal level with other nations, considering the values which are important for Europe and attitudes (e.g.environmental protection) and representing greater protection for people, property and the environment.
The main aim and objective of the Action is to , in the context of MIC-research/control, encourage a
fluent/synergistic collaboration/communication, closing the gap between materials scientists, engineers,
microbiologists, chemists and integrity managers to encourage sufficient interaction between academia and
industry. This Action will create a common MIC-Network, including the important stakeholders.
Microbiologically induced corrosion due to bacterial biofilms causes several problems in industrial systems, technical applications and in medicine. Prior to the formation of a biofilm on a substrate, planktonic cells attach on the surface. Hence, the properties of the surface play a key role in biofilm formation and are of great importance for the development of strategies to prevent bacterial attachment and biofilm formation.
This project aims at clarifying to which extent surface micro-/nanostructuring and chemical functionalization affects bacterial attachment and whether a synergistic combination of the two can be used to control bacterial adhesion. To answer these questions, model surfaces with regular patterns of 5-10 micrometers in size have been prepared, which provide distinct zones differing in terms of their chemistry or nano-roughness. This was achieved by micro contact printing of self-assembled monolayers with different functional groups and deposition of patterned ZnO nanorod arrays for studying the effect of surface chemistry and morphology, respectively. Typical contrasts studied were combinations of positively/negatively charged, hydrophobic/hydrophilic or flat/rough.
The attachment behavior of bacteria on tailored surfaces were studied in a flow chamber as a function of time. The strain Pseudomonas fluorescens SBW25 was chosen as a model organism. DNA-intercalating dyes such as Syto9 have a high affinity to adsorb on ZnO nanorods. To overcome this limitation a genetic modification was performed by introducing a gene which expresses a green fluorescent protein in P. fluorescens SBW25 enabling the quantitative evaluation of the flow chamber studies by means of fluorescence microscopy. Further analysis of the attachment behavior was performed by means of scanning electron microscopy.
The presentation will summarize the results of our systematic study on the role of individual parameters on bacterial attachment and highlight synergistic combinations, showing an inhibition or enhancing effect. As the investigations with model substrates enable a precise control of the surface parameters, this approach can be applied to different microorganisms and material systems to achieve a correlative description of bacterial adhesion on solid surfaces.
The presentation summarizes our recent results on the coupled electrochemical methods for high resolution corrosion studies. The combination of Scanning Electrochemical Microscopy (SECM) and multielectrode (MMA) based real-time corrosion monitoring was presented as a new method for achieving high time resolution in local electrochemical analysis. Correlative imaging by means of Atomic Force Microscopy (AFM) and Scanning Electron Microscopy (SEM) was demonstrated as a tool for the investigation of local corrosion processes initiated by the intermetallic particles (IMPs) on AA2024-T3 aluminium alloy.
Microbially influenced corrosion (MIC) of iron is usually attributed to sulfate-reducing microorganisms (SRM) which act upon the metal by the reactiveness of hydrogen sulfide, and by withdrawal of the available electrons in electrical contact with the metal. Methanogenic archaea can also cause MIC by directly withdrawing electrons from the iron surface for methanogenesis. However, the mechanistic details and kinetics of the overall process are poorly understood. Precipitation of siderite, a by-product of methanogenesis, (4Fe + 5HCO3 + 5H+ 4FeCO3 + CH4 + 3H2O) can lead to an insulating layer on the metal surface and lower the corrosion rate. Still, the extent of FeCO3 precipitation may be significantly influenced by environmental conditions such as pH and advective processes.
Microbiologically influenced corrosion (MIC) of iron is usually attributed to sulfate-reducing microorganisms (SRM) in offshore industries, such as the oil and gas pipelines, due to the high concentrations of sulfate in the seawater. SRM act upon the metal by the reactiveness of hydrogen sulfide (HS-), and by withdrawal of the available electrons (Fe --> Fe2+ + 2e-; E° = -0.47 V) in electrical contact with the metal (EMIC). However, methanogenic archaea can also cause MIC. Because they do not produce HS-, withdrawal of electrons may be their main corrosive mechanism; however, mechanistic details and kinetics of the overall process are poorly understood.
To investigate the corrosion potential of methanogens, we studied the EMIC methanogenic strains isolated from marine sediments (Methanobacterium-affiliated strain IM1) and crude oil tanks (Methanococcus maripaludis Mic1c10), in an in-house developed flow-through cell to simulate a fluctuating environment. A co-culture of M. maripaludis and D. alaskensis was also established to study the effect of syntrophic growth on metal corrosion that may occur in industrial pipelines. Results indicate that the rates of iron corrosion due to coupled methanogenesis (up to 0.4 mm/yr) are higher to that caused by the marine SRM Desulfovibrio alaskensis (0.15 mm/yr). Surface analyses of the metal showed severe pitting with high methane production. Genomic analysis of the EMIC methanogen M. maripaludis Mic1c10 will provide an insight on the mechanisms of MIC. Such knowledge and deeper understanding also from an electrokinetic point of view may not only provide further models in microbial electrophysiology, but also contribute to mitigation strategies in MIC
Microbiologically influenced corrosion (MIC) of iron is usually attributed to sulfate-reducing microorganisms (SRM) in offshore industries, such as the oil and gas pipelines, due to the high concentrations of sulfate in the seawater. SRM act upon the metal by the reactiveness of hydrogen sulfide (HS-), and by withdrawal of the available electrons (Fe --> Fe2+ + 2e-; E° = -0.47 V) in electrical contact with the metal (EMIC). However, methanogenic archaea can also cause MIC. Because they do not produce HS-, withdrawal of electrons may be their main corrosive mechanism; however, mechanistic details and kinetics of the overall process are poorly understood.
To investigate the corrosion potential of methanogens, we studied the EMIC methanogenic strains isolated from marine sediments (Methanobacterium-affiliated strain IM1) and crude oil tanks (Methanococcus maripaludis Mic1c10), in an in-house developed flow-through cell to simulate a fluctuating environment. A co-culture of M. maripaludis and D. alaskensis was also established to study the effect of syntrophic growth on metal corrosion that may occur in industrial pipelines. Results indicate that the rates of iron corrosion due to coupled methanogenesis (up to 0.4 mm/yr) are higher to that caused by the marine SRM Desulfovibrio alaskensis (0.15 mm/yr). Surface analyses of the metal showed severe pitting with high methane production. Genomic analysis of the EMIC methanogen M. maripaludis Mic1c10 will provide an insight on the mechanisms of MIC. Such knowledge and deeper understanding also from an electrokinetic point of view may not only provide further models in microbial electrophysiology, but also contribute to mitigation strategies in MIC
Microbiologically influenced corrosion (MIC) of iron is usually attributed to sulfate-reducing microorganisms (SRM) in oil and gas facilities. SRM act upon the metal by the re-activeness of hydrogen sulfide (HS-), and by withdrawal of the available electrons in electrical contact with the metal (EMIC). Methanogenic archaea (MA) can also cause MIC (Mi-MIC). Several MAs were identified to be corrosive by using elemental iron as the sole electron donor for methanogenesis, including Methanobacterium-affliated IM1 and Methanococcus maripaludis Mic1c10. Currently, low corrosion rates were reported for MA, possibly due to the formation of siderite (4Fe + 5HCO3- + 5H+ ® 4FeCO3 + CH4 + 3H2O). Since MA do not produce HS-, withdrawal of electrons may be their main corrosive mechanism; however, mechanistic details and kinetics of the overall process are poorly understood.
To investigate the corrosion potential of MA, we studied the EMIC methanogenic strains (IM1 and Mic1c10) individually or part of a syntrophic co-culture with SRM. Corrosion studies were conducted using an in-house developed flow-through system to simulate fluctuating environmental conditions. Results indicate that the rates of iron corrosion by MA (up to 0.4 mm/yr) are higher to that caused by the marine SRM Desulfovibrio alaskensis (0.15 mm/yr) and the co-culture (0.1 mm/yr). Scanning electron microscopy (SEM) images of the metal incubated with MA showed severe pitting corrosion. Genomic analysis of the EMIC MA was conducted to provide an insight on the possible cellular mechanisms that could be involved. Furthermore, low concentrations of MA-targeting biocides will be applied to EMIC MA in static and flow conditions to gain insights for possible mitigation strategies. Such knowledge and deeper understanding also from an electrokinetic point of view may not only provide further models in microbial electrophysiology, but also contribute to mitigation strategies in MIC.
Microbiologically influenced corrosion (MIC) of iron is usually attributed to sulfate-reducing microorganisms (SRM) in offshore industries, such as the oil and gas pipelines, due to the high concentrations of sulfate in the seawater. SRM act upon the metal by the reactiveness of hydrogen sulfide (HS-), and by withdrawal of the available electrons (Fe --> Fe2+ + 2e-; E° = -0.47 V) in electrical contact with the metal (EMIC). However, methanogenic archaea can also cause MIC. Because they do not produce HS-, withdrawal of electrons may be their main corrosive mechanism; however, mechanistic details and kinetics of the overall process are poorly understood.
To investigate the corrosion potential of methanogens, we studied the EMIC methanogenic strains isolated from marine sediments (Methanobacterium-affiliated strain IM1) and crude oil tanks (Methanococcus maripaludis Mic1c10), in an in-house developed flow-through cell to simulate a fluctuating environment. A co-culture of M. maripaludis and D. alaskensis was also established to study the effect of syntrophic growth on metal corrosion that may occur in industrial pipelines. Results indicate that the rates of iron corrosion due to coupled methanogenesis (up to 0.4 mm/yr) are higher to that caused by the marine SRM Desulfovibrio alaskensis (0.15 mm/yr). Surface analyses of the metal showed severe pitting with high methane production. Genomic analysis of the EMIC methanogen M. maripaludis Mic1c10 will provide an insight on the mechanisms of MIC. Such knowledge and deeper understanding also from an electrokinetic point of view may not only provide further models in microbial electrophysiology, but also contribute to mitigation strategies in MIC.
Introduction on BAM developments in the project “Microbially Induced Corrosion” (MIC) for new analytical tool, surface modifications and bacterial biofilm developments in the course of the ICBM-Colloquia at the Institut für Chemie und Biologie des Meeres (ICBM) of the Carl-von-Ossietzky-University in Oldenburg.
Microbially induced corrosion (MIC) is a severe cost and risk factor for the oil and gas industry, water heat- and cooling systems, waste water management, and infrastructural constructions. The industrial preventions management of MIC focuses on eliminating present microorganisms, which leads to the repeated and time-consuming application of biocides. However, biocides are often only minor effective for microorganisms that live protected from these agents in a biofilm matrix formed on material surfaces. In recent years, microbiologist have renewed our vision on the electrochemical processes underlying material corrosion induced by sulfate reducing bacteria, but the knowledge at the level of multispecies biofilm formation and the effects of material’s properties are still rather scarce.
Therefore, an interdisciplinary team of material scientists, chemists and microbiologists, established a MIC-research platform at the Federal Institute for Materials Research and Testing (BAM) to study the effects of material’s properties and biofilm formation on MIC. Using femtosecond laser pulse technology steel surfaces with defined nanostructures were manufactured. The test pieces were incubated using a flow-through chambers setup with different organisms relevant for biofilm studies. Our studies showed, that nanoscale structures severely affect the biofilm thickness and, hence, growth for health threatening organisms like E. coli and S. aureus, but also for MIC-relevant bacteria such as Fe(III)-reducing Shewanella spec.
Another aspect of the biofilm matrix is the establishment of microscale environments with conditions, such as anaerobic or acidic microenvironments, which promotes a diverse multispecies community. However, the detection and visualization of such small-scale microenvironments is rather challenging. Further, it could directly indicate the activity of microorganism influencing or inducing corrosion processes. Therefore, dye-stained nanoscale particles, bearing pH-responsive fluorophores at the surface, were developed to measure the pH at the biofilm’s surface and within the matrix using confocal laser scanning microcopy. The particles will be further advanced to measure other environmentally relevant parameters, including oxygen concentration, and concentrations of selected metal ions indicative of corrosion of e.g., materials used for water pipelines. In the future, our platform and its analytical tools will be employed to study the formation of biofilms in dependency of the respective support material, its surface properties like roughness, and the microbial community.
In dieser Präsentation wurden dem Beirat Umwelt die High-Lights und der weitere Ausblick des Foresight Process MIC vorgestellt. Im Fokus stehen hierbei insbesondere die neu angelaufenen Projekte:
COST Action Euro-MIC
MIC im Endlager
Hydrogen: MIC & Wasserstoffversprödung
Biorezeptivität von Betonoberflächen
Mitigation schwarze Pilze
WIPANO ResTest
Materials are key for our modern communities. In particular metals play important roles in all areas of our daily life - from building materials to high tech products.
Due to the increasing consumption of metals and corresponding waste production, an elevated release into the environment takes place. Furthermore, metals in direct contact with the environment undergo corrosion leading to a release into the (aquatic) environment. Thus, lifespan of products/buildings are substantially reduced – hence unnecessary economic costs arise. Thus, research in this regard is needed within the force field of metal/material - environment.
Evaluating the environmental impact of materials as well as developing “safe” materials, new analytical methods are highly needed. One promising powerful tool is single cell-ICP-ToF-MS for multi-elemental analysis on a single cell/organism level.
Within this presentation the concept, strength as well as challenge of single cell-ICP-MS are briefly introduced. Two application examples are presented: (i) assessing the environmental impact of metals and (ii) the impact of the environment on metal-based materials and the derivation of potential environmental-friendly material protection strategies. These applications highlight the strength of new analytical approaches to explore the durability and safety of newly developed materials. Thus, analytical chemistry is one corner stone to transformation of modern society into circular economy (CEco).
(i) Diatoms are located at the bottom of the food chain. Thus, toxicological relevant metals taken up by diatoms possibly accumulate within the food web causing harmful effects. Diatoms are common test system in ecotoxicology. To investigate potential metal uptake and effects, we developed an on-line single cell-ICP-ToF-MS approach for multi-elemental diatom analysis. Our approach is a new potential tool in ecotoxicological testing for metal-based materials.
(ii) Next to classical corrosion processes, microorganisms are responsible for so called microbially influenced corrosion (MIC). MIC is a highly unpredictable process relying on interaction pathways between cells and the metal surface. Sheding light on MIC processes and derivate potential protection strategies, we applied single cell-ICP-ToF-MS for MIC research on a single bacteria/archaea level. It turned out that microorganism are taking up particular metals from alloys - thus, single bacteria-ICP-ToF-MS will enable development of corrosion protection strategies.
Microbiologically influenced corrosion (MIC) is a highly unpredictable process involving a complex group of microorganisms, including sulfate-reducing bacteria and methanogens. Standard laboratory MIC testing using static serum bottle enrichments is an easy but limited method, offering poor resolution on the biomineralization process of corrosion products. An example of this is the presumed corrosion product siderite by corrosive methanogens (Mi-MIC). Previous publications reported siderite was the sole corrosion product of M. maripaludis using metal coupons incubated under stationary conditions.
However, the formation of siderite is closely related to the surrounding environmental conditions, i.e. pH, CO2 concentration, flow and temperature. Thus, siderite as the sole corrosion product of Mi-MIC remain inconclusive and questionable. To study Mi-MIC effectively, a novel versatile multiport flow-column corrosion monitoring system (MFC) was developed. MFC allows sectional corrosion rate determination under flow conditions using different types of material, inoculum and packing material. MFC offers great flexibility, ease of operation and accurate corrosion measurements that can be combined with many other techniques. Using MFC, we studied multiple strains of methanogens and compared it with sulfate-reducing bacteria under neutral and low pH conditions. It was revealed by MFC that corrosive methanogens have equally high corrosion potential as sulfate-reducing bacteria. Additionally, siderite is not the dominant nor sole corrosion product of Mi-MIC. Thus, effective corrosion monitoring and establishing standard laboratory practices, i.e. incorporating MFC as part of regular testing process, will provide deeper understanding of MIC. This will allow further microbial electrophysiology understandings, contributing to effective mitigation strategy development.
Microbiologically influenced corrosion (MIC) on steel occurs where the presence and activity of microbes change the localized conditions on the surface of a metal substrate. For instance, metal reducing bacteria (MRB) are capable of utilizing metal compounds in the passive layer on stainless steel as electron acceptors during their metabolism. This weakening of the passive film not only leads to an acceleration of the general corrosion processes, but also increases the susceptibility of stainless steels to pitting corrosion. Even though the electron transfer mechanisms are not yet fully understood, recent research shows that the secretion of electron shuttles like flavins contribute significantly to the extracellular electron transfer (EET). Electron shuttle molecules like riboflavin (RB) or flavin mononucleotide (FMN) are secreted by MRB after the transition from planktonic to sessile mode and exist in the biofilm at low concentrations. Therefore, they are precise early phase indicators of bacterial settlement.
This project aims at clarifying the electrochemical interaction mechanisms of MRB with stainless steel surfaces, with a special focus on the role of the extracellular redox molecules. The analysis of corrosion processes as a function of chloride and flavin concentration have been performed by means of electrochemical methods. Due to the differences in their chemical structure, FMN and RB have shown significant differences in terms of their adsorption behavior and the stability of the formed films, which directly influences the electron transfer processes. Therefore, Electrochemical Quartz Crystal Microbalance (eQCM) studies have been performed on sputtered FeCr electrodes to investigate the adsorption/desorption kinetics of flavins.
The results of electrochemical studies are complemented by the analysis of the changes in the passive film chemistry and the chemical composition of the adsorbed films by means of Fourier Transform Infrared Reflection Absorption Spectroscopy (FT-IRRAS) and X-ray photoelectron spectroscopy (XPS). Changes in surface morphology have been investigated by means of Scanning Electron Microscopy (SEM) and Atomic Force Microscopy (AFM).The presentation will summarize our results on the degradation mechanisms of passive films on stainless steel surfaces in the presence of flavins and provide useful insights from a fundamental aspect for the understanding of the initial stages of microbiologically influenced corrosion.
Melanins are organic pigments produced by most fungi. These organisms either fix these pigments in their cell wall or secrete them into their extracellular environment to protect themselves against an array of physicochemical stresses (e.g., UV irradiation, desiccation, ...). Melanin can adsorb metals like Fe. How this affects fungal uptake of Fe and deterioration of Fe-containing minerals and metals is however less known. To study this, we use the model fungi Knufia petricola A95, a rock-inhabiting fungus known to deteriorate minerals and have melanised cell walls, and Amorphotheca resinae, able to contaminate fuel tanks, secrete melanin and corrode metals. In K. petricola, we have deleted genes involved in melanin production and Fe uptake using CRISPR/Cas. Through comparison of the geochemical signatures of these gene deletion mutants with those of the wild type (WT), we explore the specific mineral/metal deterioration mechanisms of melanised fungi.
Fe isotope signatures of the biomass of melanin- and Fe uptake-deficient mutants of K. petricola revealed that Fe adsorbed either directly onto melanin or after being reduced by Fe reductases. Importantly, once adsorbed to melanin, Fe could not be mobilised and taken up into the cell: both the WT and its melanin-deficient mutant, previously grown at Fe replete conditions, showed similar growth at Fe deficient conditions.
Olivine dissolution experiments revealed that Fe oxidation inhibits dissolution. K. petricola was able to enhance dissolution when this inhibition is strongest (at pH 6) and prevented dissolution when this inhibition is weakest (at pH 4). The fungus therefore dissolves olivine by interacting with the oxidised Fe at the olivine surface. However, Fe uptake did not seem to be involved: mutants deficient in various Fe uptake mechanism dissolved olivine at the same rate as the WT. This indicates that Fe adsorption onto melanin might play a key role. This is also shown by K. petricola’s ability to enhance olivine dissolution even further if secreting a melanin precursor and A. resinae’s corrosion of carbon steel whilst secreting melanin. Combined, our results imply that the Fe adsorbed to melanin cannot be taken up but enables fungi to deteriorate Fe-containing substrates at a higher rate.
Bei dem Vortrag werden die potentiellen mikrobiologischen Einflüsse im Falle der Lagerung von Wasserstofflagerung in unterirdischen geologischen Formationen vorgestellt, die Zusammenarbeit mit internen und auch externen Partnern. Der Fokus liegt dabei auf UGF; anaerobe Umgebungen, Sulfate reduzierenden Bakterien, methanogenen Archaea, weiterleitenden Systeme und die Kombination der Untersuchung abiotisch/biotische