Filtern
Erscheinungsjahr
Dokumenttyp
- Vortrag (17)
- Zeitschriftenartikel (6)
- Beitrag zu einem Tagungsband (2)
- Posterpräsentation (2)
- Dissertation (1)
- Sonstiges (1)
- Forschungsbericht (1)
Schlagworte
- Hydrogen (30) (entfernen)
Organisationseinheit der BAM
- 3 Gefahrgutumschließungen; Energiespeicher (10)
- 3.5 Sicherheit von Gasspeichern (10)
- 9 Komponentensicherheit (9)
- 2 Prozess- und Anlagensicherheit (6)
- 2.1 Sicherheit von Energieträgern (6)
- 9.0 Abteilungsleitung und andere (6)
- 8 Zerstörungsfreie Prüfung (4)
- 8.1 Sensorik, mess- und prüftechnische Verfahren (4)
- 9.4 Integrität von Schweißverbindungen (4)
- 1 Analytische Chemie; Referenzmaterialien (2)
Germany has concluded energy partnerships with various countries, including Japan. During the 3rd meeting of the Hydrogen Working Group, the strategic approach of both countries on developments of hydrogen guidelines, certification and safety was presented and discussed. BAM gave a presentation on important topics in the field of safety research and on safety-related issues along the value chain. Furthermore, the work program and selected projects of the competence center H2Safety@BAM were presented.
Competence Centre H2Safety@BAM – Safeguarding the Quality Infrastructure in the Hydrogen Economy
(2022)
Hydrogen is a central component of the energy transition and the European Green Deal for a climate-neutral Europe. To achieve the goals defined for 2050, the EU and the German government have developed a framework for action and are making long-term investments in research, development, and the rapid implementation of innovative hydrogen technologies.
With the Competence Centre "H2Safety@BAM", BAM is creating the safety-related prerequisites for the successful implementation of hydrogen technologies at national as well as European level.
To this end, BAM conducts research, testing and consulting in a holistic and inter-disciplinary manner under one roof – in the Competence Centre H2Safety@BAM. The activities of the competence centre focus on ensuring the safety of infra-structures, plants, and processes as well as innovative hydrogen transport and storage systems based on digital quality testing and the experimental testing of components and systems. It thus creates the prerequisites for the implementation and adaptation of legal framework conditions as well as for standardization. Closely related to this are investigations into the properties and compatibility of metallic materials and polymers as well as friction systems for the safe operation of components, plants, processes, and systems. This interdisciplinary and holistic approach is complemented by the development of gas analytics and suitable sensors, online measurements of gas properties in process control, test scenarios under real conditions as well as impact assessments of accidents and risk assessments and risk management systems derived from them. With its portfolio of tasks and competences, BAM builds trust in the safety and reliability of technical system solutions for hydrogen.
Die tribologischen Eigenschaften von graphitgefüllten Polyimiden gegen Stahl 100Cr6 wurden an Luft, im Hochvakuum (l0⁻ ³ Pa) und in Wasserstoffumgebung bei verschiedenen Drücken (10³ Pa, 10⁴ Pa und 10⁵ Pa) untersucht. Zwei unterschiedliche Polyimid-Typen wurden eingesetzt, wobei Typ und Menge des Graphits variiert wurden.
Die Experimente wurden bei 3,1 MPa Kontaktdruck und einer Gleitgeschwindigkeit von 0,2 m/s bzw. 1 m/s durchgeführt. Die verschlissenen Oberflächen und die Morphologie des Materialübertrags auf die Stahl-Gegenfläche wurden mittels Lichtmikroskopie, REM, TEM und FTIR untersucht. Die Untersuchung zeigt, dass sowohl die Matrix als auch der Graphitanteil einen deutlichen Einfluss auf das Reibverhalten von Verbundwerkstoffen in Wasserstoffumgehungen haben können.
Metals that are exposed to high pressure hydrogen gas may undergo detrimental failure by embrittlement. Understanding the mechanisms and driving forces of hydrogen absorption on the surface of metals is crucial for avoiding hydrogen embrittlement. In this study, the effect of stress-enhanced gaseous hydrogen uptake in bulk metals is investigated in detail. For that purpose, a generalized form of Sievert's law is derived from thermodynamic potentials considering the effect of microstructural trapping sites and multiaxial stresses. This new equation is parametrized and verified using experimental data for carbon steels, which were charged under gaseous hydrogen atmosphere at pressures up to 1000 bar. The role of microstructural trapping sites on the parameter identification is critically discussed.
H2Sense - Cost-effective and reliable Hydrogen Sensors for Facilitating the Safe Use of Hydrogen
(2016)
The H2SENSE (Cost-effective and reliable hydrogen sensors for facilitating the safe use of hydrogen) project promoted hydrogen primarily, but not exclusively, for its use as an alternative fuel. It brought together different stakeholders including sensor manufacturers, end-users, certification bodies and independent evaluators to ensure the optimum use of low-cost and reliable hydrogen sensors.
Project partners analysed sensor performance in real-life applications in industrial environments and identified increased requirements for sensors and for regulations, codes and standards. H2SENSE also facilitated the safe use and implementation of hydrogen as an alternative fuel by ensuring the correct use of effective hydrogen detection devices.
European scientists worked together with colleagues from the National Renewable Energy Laboratory (NREL) in Colorado, USA. They pooled their knowledge of developments in hydrogen sensor technology as well as deployment and commercialisation strategies. These benefits will be continued through trans-Atlantic inter-laboratory sensor testing programmes in which EU and US laboratories perform complementary tests and exchange results.
Der verstärkte Einsatz höherfester Stähle und Zusatzwerkstoffe erfordert ein vertieftes Verständnis der Zusammenhänge zwischen Schweißverfahren, Wärmeeinbringung, Abkühlbedingungen sowie den daraus resultierenden metallurgischen Vorgängen in der Schweißnaht und deren Umgebung. Nur aus dem Zusammenwirken aller Einflussfaktoren lassen sich Strategien ableiten, mit deren Hilfe die Festigkeitseigenschaften bzw. die Lebensdauer von Schweißkonstruktionen in einem Maße verbessert werden können, die den Einsatz höherfester Werkstoffe rechtfertigen und somit deren Leichtbaupotenzial voll ausgenutzt werden kann. Vorgestellt werden einige beispielhafte Untersuchungen an Schweißverbindungen aus höherfesten Feinkornbaustählen zu Interaktionen der Haupteinflussgrößen auf die Kaltrissbildung.----------------------------------------------------------------------------------------------------------------------------
The increased utilisation of higher-strength steels and filler materials necessitates more profound understanding of the connections between the welding process, the heat input, the cooling conditions and the resulting metallurgical processes in the weld and its surroundings. Strategies which help to improve the strength properties and service lives of welded structures to such an extent that the utilisation of higher-strength materials can be justified and their lightweight construction potential can thus be exploited to the full can only be derived from the interaction between all the influencing factors. Examples of a few investigations on welded joints between higher- strength fine-grained structural steels with regard to the interactions between the main variables influencing the cold cracking are presented in this article.
In the DECHEMA Virtual Talks, general aspects of the safety and acceptance of hydrogen technologies were presented. How can trust in new technologies be built when past accidents led to myths and fairy tales? The presentation does away with general prejudices and shows that handling hydrogen is neither more unsafe nor safer than handling other fuel gases. The basis for the safe handling of hydrogen is always a risk analysis.
Low-alloyed heat-resistant steels have a fundamental contribution to the currently applied steel grades in pressurized and temperature loaded components like membrane walls(water walls)or pressure vessels. Here, the main advantages of the low-alloy concept can be used in terms of superior high temperature mechanical properties, workability and decreased amounts of expensive alloy elements. The main challenge for the future is to further increase the power plant thermal efficiency independent of the type of power plant concept, i.e. fossil-fired or nuclear power plant, where the material selection can directly affect reduction of CO2 emissions.
In power plant design, welding is the most applied manufacturing technique in component construction. The necessary weld heat input causes metallurgical changes and phase transitions in the heat affected zone (HAZ) of the base materials and in the deposited weld metal. The weld joint can absorb hydrogen during welding or in later service - This absorption can cause degradation of mechanical properties of the materials, and in certain loading conditions, hydrogen-assisted cold cracks can occur. This cracking phenomenon can appear time delayed due to the temperature dependency of the hydrogen diffusion and
the presence of a “critical” hydrogen concentration. Additionally, each specific weld microstructure shows a certain hydrogen diffusion and solubility that contribute to susceptibility of the cracking phenomenon. Therefore hydrogen cannot be neglected as possible failure effect, which was identified recently in the case of T24 creep-resistant tubeto-tube weld joints. It is necessary to identify and assess the hydrogen effect in weld joints of low-alloyed steel grades for to improve further early detection of possible failures.
For each specific weld joint microstructure, it is necessary to separate the interdependencies between mechanical load and the hydrogen concentration. The
diffusivity and solubility must be considered to identify hydrogen quantities in the material at any given time. In this case, the effects of mechanical loading were dealt with independently. For the characterization of the mechanical properties, hydrogen charged tensile specimens were investigated for the base materials and thermally simulated HAZ
microstructures. The hydrogen diffusion was characterized with the permeation technique at room temperature and at elevated temperature ranges up to 400°C - It was investigated by interpreting the hydrogen effusion behavior with carrier gas hot extraction technique (CGHE). For realistic determination of the hydrogen diffusion coefficients, an improved
method was developed encompassing accelerated specimen heating and hydrogen determination via mass spectrometer (MS). Simultaneously, the corresponding temperature
dependent trapped and total hydrogen concentrations were determined.
The determined experimental results showed increased susceptibility to the hydrogen affected
degradation of the HAZ compared to the base material, which is independent of the investigated alloy composition. In particular, the martensitic coarse grain HAZ is the most susceptible microstructure to hydrogen-affected degradation. The results of the tensile
tests allowed the definition of consistent microstructure specific failure criteria (envelope curves) versus quantified hydrogen concentrations for the reactor pressure vessel 16MND5 steel (20MnMoNi-5-5) and the creep-resistant T24 steel (7CrMoVTiB10-10). The procedure of quantifying hydrogen concentrations in HAZ microstructures is novel and supports a new method of analysis for hydrogen degradation effects. Further investigations with the T22
steel (10CrMo9-10), as compared to the creep-resistant T24 steel (7CrMoVTiB10-10),
confirmed the beneficial effect of Vanadium as an alloying element to improve the resistance to degradation. In general, Mn-Mo-Ni base material grades show a higher resistance compared to Cr-Mo steels that do not include Vanadium alloying.
The investigations showed the decreased diffusion coefficient of the HAZ microstructure compared to the base material microstructure. This is caused by the stronger trapping effects that are present which simultaneously increase the hydrogen solubility as well. In
general, trapping effects above 100°C are negligible. It is noted that after testing the T24 grade, these trapping effects were observed above 100°C and must be considered. At elevated temperatures, the calculated hydrogen diffusion coefficients are sometimes greater than those in literature. This is primarily due to the unique applied specimen heating procedure resulting in a varied hydrogen effusion from the specimen.
The significance of the obtained results can be characterized in three perspectives. First, the direct comparison of the degradation was possible in terms of microstructure-specific hydrogen effects on the mechanical properties. Second, consistent failure criteria were established to quantify degradation vs. the hydrogen concentration. Third, the determination of more accurate hydrogen diffusion coefficients is now available.
From a scientific point of view, important contributions were made to further interpret the hydrogen effects on the macroscopic mechanical properties, with respect to the alloy composition and the microstructure. From a procedural standpoint, the mentioned deviation in the elevated temperature diffusion coefficients can be caused by the calculation method. This can be an explanation for the reported data scatter in the references.
In terms of an economic view, the presented experimental results contribute to a safe and reliable weld workability of the steel grades. Thus, the identified temperature levels of hydrogen trapping can be applied in the definition of minimum preheat, interpass or postheat temperatures. In addition, recommendations for suitable dehydrogenation heat treatment (DHT) procedures, with accurate temperature values and holding times, can be derived from these results. In the future, the application of the mechanical and diffusion data is intended to support numerical analysis methods to provide an improved prediction of hydrogen effects on material degradation in weld microstructures.
Welded components of P91 9% Cr steel demand for careful welding fabrication with necessary post weld heat treatment (PWHT). Before the PWHT, a hydrogen removal heat treatment is necessary for avoidance of hydrogen assisted cracking (HAC). In this context, the microstructure and temperature-dependent hydrogen diffusion is important, and reliable diffusion coefficients of P91 weld metal are rare. For that reason, the diffusion behavior of P91 multi-layer weld metal was investigated for as-welded (AW) and PWHT condition by electrochemical permeation experiments at room temperature and carrier gas hot extraction (CGHE) from 100 to 400 °C. Hydrogen diffusion coefficients were calculated, and the corresponding hydrogen
concentration was measured. It was ascertained that both heat treatment conditions show significant differences. At room
temperature the AW condition showed significant hydrogen trapping expressed by to seven times lower diffusion coefficients. A preferred diffusion direction was found in perpendicular direction expressed by high permeability. The CGHE experiments
revealed lower diffusion coefficients for the AW condition up to 400 °C. In this context, a hydrogen concentration of approximately 21 ml/100 g was still trapped at 100 °C. For that reason, a certain HAC susceptibility of as-welded P91 weld metal cannot
be excluded, and hydrogen removal should be done before PWHT.