The presentation summarizes our recent results on the coupled electrochemical methods for high resolution corrosion studies. The combination of Scanning Electrochemical Microscopy (SECM) and multielectrode (MMA) based real-time corrosion monitoring was presented as a new method for achieving high time resolution in local electrochemical analysis. Correlative imaging by means of Atomic Force Microscopy (AFM) and Scanning Electron Microscopy (SEM) was demonstrated as a tool for the investigation of local corrosion processes initiated by the intermetallic particles (IMPs) on AA2024-T3 aluminium alloy.
Microbiologically influenced corrosion (MIC) on steel occurs where the presence and activity of microbes change the localized conditions on the surface of a metal substrate. For instance, metal reducing bacteria (MRB) are capable of utilizing metal compounds in the passive layer on stainless steel as electron acceptors during their metabolism. This weakening of the passive film not only leads to an acceleration of the general corrosion processes, but also increases the susceptibility of stainless steels to pitting corrosion. Even though the electron transfer mechanisms are not yet fully understood, recent research shows that the secretion of electron shuttles like flavins contribute significantly to the extracellular electron transfer (EET). Electron shuttle molecules like riboflavin (RB) or flavin mononucleotide (FMN) are secreted by MRB after the transition from planktonic to sessile mode and exist in the biofilm at low concentrations. Therefore, they are precise early phase indicators of bacterial settlement.
This project aims at clarifying the electrochemical interaction mechanisms of MRB with stainless steel surfaces, with a special focus on the role of the extracellular redox molecules. The analysis of corrosion processes as a function of chloride and flavin concentration have been performed by means of electrochemical methods. Due to the differences in their chemical structure, FMN and RB have shown significant differences in terms of their adsorption behavior and the stability of the formed films, which directly influences the electron transfer processes. Therefore, Electrochemical Quartz Crystal Microbalance (eQCM) studies have been performed on sputtered FeCr electrodes to investigate the adsorption/desorption kinetics of flavins.
The results of electrochemical studies are complemented by the analysis of the changes in the passive film chemistry and the chemical composition of the adsorbed films by means of Fourier Transform Infrared Reflection Absorption Spectroscopy (FT-IRRAS) and X-ray photoelectron spectroscopy (XPS). Changes in surface morphology have been investigated by means of Scanning Electron Microscopy (SEM) and Atomic Force Microscopy (AFM).The presentation will summarize our results on the degradation mechanisms of passive films on stainless steel surfaces in the presence of flavins and provide useful insights from a fundamental aspect for the understanding of the initial stages of microbiologically influenced corrosion.
Stainless steel AISI 304 surfaces were studied after a mild anodic polarization for oxide growth in the presence and absence of two derivatives of vitamin B2 (riboflavin and flavin mononucleotide) that can be secreted by metal‐reducing bacteria and act as a chelating agent for iron species. The alterations in oxide chemistry were studied by means of surface‐sensitive techniques such as X‐ray photoelectron spectroscopy and time‐of‐flight secondary ion mass spectrometry analysis. The complementary electrochemical characterization revealed a preferential growth of an oxide/hydroxide iron‐rich film that is responsible for an altered pit initiation and nucleation behavior. These findings suggest that as the corrosion behavior is determined by the interplay of the chemical and electronic properties, only a mild anodic polarization in the presence of redox‐active molecules is able to alter the chemical and electronic structure of the passive film formed on stainless steel AISI 304. This helps to achieve a profound understanding of the mechanisms of microbially influenced corrosion (MIC) and especially the possible effects of the redox‐active biomolecules, as they may play an important role in the corrosion susceptibility of stainless steel surfaces.
Biofilm formation and microbially influenced corrosion of the iron-reducing microorganism Shewanella putrefaciens were investigated on stainless steel surfaces preconditioned in the absence and presence of flavin molecules by means of XANES (X-ray absorption near-edge structure) analysis and electrochemical methods. The results indicate that biofilm formation was promoted on samples preconditioned in electrolytes containing minute amounts of flavins. On the basis of the XANES results, the corrosion processes are controlled by the iron-rich outer layer of the passive film. Biofilm formation resulted in a cathodic shift of the open circuit potential and a protective effect in terms of pitting corrosion. The samples preconditioned in the absence of flavins have shown delayed pitting and the samples preconditioned in the presence of flavins did not show any pitting in a window of −0.3- to +0.0-V overpotential in the bacterial medium. The results indicate that changes in the passive film chemistry induced by the presence of minute amounts of flavins during a mild anodic polarization can change the susceptibility of stainless steel surfaces to microbially influenced corrosion.