Filtern
Erscheinungsjahr
- 2012 (18) (entfernen)
Dokumenttyp
Sprache
- Englisch (18) (entfernen)
Schlagworte
- Laser beam welding (6)
- Lorentz force (4)
- Electromagnetic weld pool support (3)
- Marangoni stresses (3)
- Natural convection (3)
- Corrosion (2)
- Laser welding (2)
- Mechanical properties (2)
- Stainless steel (2)
- Stress reduction (2)
The residual stresses in narrow electron or laser beam welds with high stress gradients are decreased without any contact surfaces or additional equipment by applying the welding beam after welding in a defocused mode for heating the material regions in a certain distance from the weld on both sides. In case of electron beam application, the beam is positioned and focused by the electromagnetic coil with high frequency. In case of laser beam application a laser scanner optics enables fast positioning by an optomechanic beam deflection, while defocusing of the laser beam is obtained by increasing the distance between scanner optics and workpiece. Dependent on the component geometry and on the beam power different process parameters are used. The adjustable process parameters are the radius and the power of the defocused beam and the transversal and longitudinal distances between the welding and the defocused beam. The mechanism and the influence of the process parameters are investigated by FEM-simulation and a number of experiments on a ferritic steel S355J2+N with 5 mm thickness. FEM-simulation is used to reduce the matrix of process parameters for the experiments. The best experimental result shows a stress reduction of about 70%.
Simulation of an inductive weld pool support for deep penetration laser beam welding of metal parts
(2012)
three-dimensional laminar steady state numerical model was used to investigate the influence of an altemating current (ac) magnetic field during single pass high power laser beam keyhole welding of 20 mm thick aluminum. The three-dimensional heat transfer, fluid dynamics and electromagnetic field equations were solved with the commercial finite element package COMSOL Multiphysics. Dominant physical effects of the process were taken into account: Thermo-capillary (Marangoni) convection at the upper and lower weld pool surfaces, natural convection due to the gravity influence and the latent heat of solid-liquid phase transition. Simulations were conducted for several magnetic field strengths and it was found that the gravity drop-out associated with welding of thick plates due to the hydrostatie pressure can be prevented by the application of an ac magnetic field below the weld specimen of around 70 mT (rms) at an oscillation frequency of 450 Hz. The inductive support System allows for single-pass laser beam welding of thick aluminum plates. The flow pattem in the molten zone and the temperature distributions are significantly changed by the application of the electromagnetic forces in the weld pool.
Longitudinal residual stresses in beam welds ranging at the value of the local yield strength can diminish the lifespan of components. To extend the service life of welds special methods of welding residual stress reduction were developed earlier which are however not effective for beam welds in complex component geometries. Application of beam welding sources for postwelding heat treatment of components has become a flexible tool for reducing longitudinal stresses in beam welds. Such heat treatment in a specific transversal distance to the weld by a defocused beam results in huge stress reductions depending on the used process parameters. Experimental results for ferritic and austenitic steels reveal weld stress reductions to up to compressive stresses. For different materials and diverse material thicknesses special process parameter regions have to be used in this procedure. At a transmission component this procedure shows a stress reduction by >300 MPa.
Full penetration 15 kW Yb fibre laser butt welding of thick AlMg3 (AW 5754) plates was performed in PA position. A contactless inductive electromagnetic weld pool support system was used to prevent gravity dropout of the melt. The welding speed needed to achieve 20 mm penetration was ~0·5 m min-1. An ac power supply of ~244 W at 460 Hz was necessary to completely suppress gravity dropout of the melt and eliminate sagging of the weld pool root side surface. The oscillating magnetic field can suppress the Marangoni convection in the lower part of the weld pool. The system was also successfully used in the full penetration welding of 30 mm thick AlMg3 plates.
A three-dimensional laminar steady-state numerical model was developed to investigate the influence of an alternating current (ac) magnetic field during high-power full-penetration laser welding on the weld pool dynamics and weld cross section of a 20 mm thick aluminium plate in flat position. Three-dimensional heat transfer, fluid dynamics including phase transition and electromagnetic field partial differential equations were solved iteratively with the commercial finite element software COMSOL Multiphysics using temperature-dependent material properties up to evaporation temperature. Thermocapillary convection at the weld pool surfaces, natural convection and latent heat of solid–liquid phase transition were taken into account in this model. Solidification was modelled by the Carman–Kozeny equation for porous media morphology. The ac magnet was mounted on the root side of the weld specimen. The magnetic field was aligned perpendicular to the welding direction. The flow pattern in the melt and thus also the temperature distribution were significantly changed by the application of oscillating magnetic fields. It was shown that the application of an ac magnetic field to laser beam welding allows for a prevention of the gravity drop-out. The simulation results are in good qualitative agreement with the experimental observations.
A three-dimensional turbulent steady state numerical model was used to investigate the influence of a stationary magnetic field during partial penetration high power laser beam keyhole welding of thick aluminum parts. COMSOL Multiphysics was used to calculate the three-dimensional heat transfer, fluid dynamics and electromagnetic field equations. Thermo-capillary (Marangoni) convection at the upper weld pool surface, natural convection due to gravity and latent heat of solid-liquid phase transition were taken into account. It shows that the application of steady magnetic fields produces a braking Lorentz force in the melt based on the Hartmann effect. The flow pattern in the weld pool and also the temperature distribution and associated weld pool geometry thus change significantly. Convective flows in the melt can effectively be suppressed and the influence of thermo-capillary flow is diminished to a thin surface layer.
Electron beam plasma measurement was realised by means of DIABEAM system invented by ISF RWTH Aachen. The Langmuir probe method is used for measurement. The relative simplicity of the method and the possibility of dispersion of high power on the probe allow its application for the investigation of high-power electron beams. The key element of the method is a rotating thin tungsten wire, which intersects the beam transversely on its axis and collects part of the current by itself. The signals, which are registered in the DIABEAM as a voltage, were taken in the form of amplitude. The conversion of the probe current into the distribution along the beam radius was realised using the Abel's method. A voltage-current characteristic was built for the beam current. The local electron density as well as the electron temperature, the floating potential and the plasma potential were measured and calculated by means of this characteristic.
Thick-walled pipes made of steel are the basis of a large number of components in mechanical and installation engineering, e.g. for hydraulic components, in power station technology or in the petroleum industry. Particularly when strict positional and shape tolerances are demanded, the classical manufacturing process is chip-producing machining from the solid material. However, this is time-intensive and material-intensive. The laser/GMA hybrid processes with modern high-power lasers are a suitable alternative. With these processes, it is currently possible to weld components with a wall thickness up to approx. 15 mm with little distortion in one pass. However, in initial experiments, solidification cracks with longitudinal and vertical orientations in relation to the welding direction, so-called central line cracks, were established in welds on pipes. Within the framework of a research project, it was possible to determine the cause of the cracking and to find measures in order to avoid it. The technical boundary conditions could be complied with in this respect. The article gives an overview of the research project and the essential results.
In a repair process chain, damaged areas or cracks can be removed by milling and subsequently be reconditioned with new material deposition. The use of laser metal deposition has been investigated for this purpose. The material has been deposited into different groove shapes, using both stainless steel and Ti-6Al-4 V. The influence of welding parameters on the microstructure and the heat affected zone has been studied. The parameters have been modified in order to achieve low heat input and consequently low distortion as well as low metallurgical impact. Finally, an evaluation of the opportunities for an automatized repair process is made.