BAM Dissertationsreihe
Filtern
Erscheinungsjahr
Dokumenttyp
- Dissertation (173)
Referierte Publikation
- nein (173)
Schlagworte
- Zerstörungsfreie Prüfung (7)
- Beton (6)
- Schweißen (5)
- Brandschutz (4)
- CFD (4)
- Ermüdung (4)
- Finite-Elemente-Methode (4)
- Holz (4)
- Simulation (4)
- Ultraschall (4)
Organisationseinheit der BAM
- 9 Komponentensicherheit (5)
- 7 Bauwerkssicherheit (4)
- 9.4 Integrität von Schweißverbindungen (4)
- 5 Werkstofftechnik (3)
- 5.3 Polymere Verbundwerkstoffe (3)
- 7.2 Ingenieurbau (2)
- 7.3 Brandingenieurwesen (2)
- 8 Zerstörungsfreie Prüfung (2)
- 3 Gefahrgutumschließungen; Energiespeicher (1)
- 3.1 Sicherheit von Gefahrgutverpackungen und Batterien (1)
158
Pentaerythrityltetranitrat (PETN), ein in jüngster Vergangenheit häufig von Terroristen verwendeter Sprengstoff, ist äußerst schwer zu detektieren. Ein verbesserter Antikörper gegen PETN wurde durch Anwendung des Konzepts des bioisosteren Ersatzes entwickelt,indem ein Nitroester durch einen Carbonsäurediester ersetzt wurde. Biostere Moleküle haben eine ähnliche Struktur wie die Referenzsubstanz und zeigen eine vergleichbare biologische Wirkung. Dieser Ansatz führte zu polyklonalen Antikörpern mit extrem guter Selektivität und Sensitivität. Die Nachweisgrenze des Enzyme-Linked Immunosorbent Assays (ELISAs) beträgt 0,15 μg/L. Der Messbereich des Immunassays liegt zwischen 1 und 1000 μg/L. Die Antikörper sind sowohl hinreichend pH-stabil als auch robust gegen Lösungsmittelzusätze. Das Antiserum könnte auch für Schnelltests, Biosensoren, Mikro-Arrays und andere analytische Methoden verwendet werden.
Für die Umweltanalytik von Trinitrotoluol (TNT) wurde eine Hochdruckflüssigkeitschromatographie (HPLC)-kompatible Affinitätssäule hergestellt. Druckbeständiges, poröses Glas hat sich als ein hervorragendes Trägermaterial herauskristallisiert. Um selektive anti-TNT-Antikörper für die Herstellung der Affinitätssäule aus den beiden verwendeten TNT-Seren zu isolieren, wurde eine Trennung an einer Dinitrophenyl-Affinitätssäule durchgeführt. Zur Optimierung der Immobilisierungsmethode wurden orangefarbene Dabsyl -Proteine synthetisiert und auf der Oberfläche gebunden. Die Färbung wurde als Indikator für die Immobilisierungsdichte verwendet. Wegen der hohen Affinitätskonstanten der polyklonalen anti-TNT-Antikörper der beiden Seren (5,1 bzw. 2,3∙109 L/mol) lässt sich TNT durch eine typische saure Elution der TNT-Affinitätssäule nur schwer eluieren. Aus diesem Grund wurde eine neuartige Elutionsmethode entwickelt, die irreversible, denaturierende, thermische Online -Elution.
Diese eröffnet ein weites Anwendungsfeld, da so Affinitäten, die klass ischerweise aufgrund zu hoher Bindungskonstanten zwischen Ligand und Rezeptor nicht für die Affinitätschromatographie genutzt werden können, für die Analytik besser handhabbar werden. Die maximale Kapazität einer im Rahmen dieser Arbeit hergestellten Affinitätssäule (64,8 μL) betrug 650 ng TNT bzw. 10 μg/mL Säulenvolumen.
Um die Immobilisierungsdichte der produzierten Affinitätssäulen zu bestimmen, wurde ein neues Verfahren entwickelt, da die üblichen spektroskopischen Proteinbestimmungsmethoden aufgrund der hohen unspezifischen Wechselwirkung mit dem Trägermaterial zur Proteinbestimmung nicht geeignet waren. Zur Quantifizierung von Proteinen oder Peptiden,die auf festen Trägern immobilisiert sind, wurde auf Grundlage einer HPLC-Trennung der aromatischen Aminosäuren Tyrosin (Tyr) und Phenylalanin (Phe) ohne vorherige Derivatisierung eine gegenüber der klassischen Aminosäureanalytik vereinfachte HPLC/UV-Methode entwickelt. Die Hydrolyse der Proteine und Peptide wurde durch Einsatz von Mikrowellentechnik beschleunigt, sodass nur 30 Minuten statt ca. 22 Stunden für das Standardprotokoll benötigt wurden, bei dem ein Hydrolyseröhrchen verwendet wird. Zur internen Kalibrierung wurden zwei Standardverbindungen, Homotyrosin (HTyr) und 4-Fluorphenylalanin (FPhe) verwendet. Die Nachweisgrenze (limit of detection, LOD) bei 215 nm ist sowohl für Tyr als auch für Phe 0,05 μM (~ 10 μg/L). Dieses neue Verfahren, das als Aromatische Aminosäureanalyse (Aromatic Amino Acid Analysis, AAAA) bezeichnet werden kann, wurde zur Proteinbestimmung von homogenen Proben mit Rinderserumalbumin (BSA) des Nationalen Instituts für Standards und Technologie der USA (NIST) validiert, wobei die Nachweisgrenze für Proteine mit 16 mg/L (~ 300 ng BSA) mit gängigen spektroskopischen Verfahren vergleichbar ist. Es liefert incl. der Hydrolysestufe eine verbesserte Genauigkeit mit einer relativen Standardabweichung von ca. 5%.
3
Angemessene Methoden zur Überprüfung von Bakterienpopulationen im Boden sind für die toxikologische Bewertung von Chemikalien, Bioziden und schadstoffbelasteten Böden besonders wichtig, da sie Auskünfte über die biologische Wirksamkeit eines Stoffes auf Organismen geben. Das Ziel der vorliegenden Arbeit bestand einerseits darin, molekularbiologische Methoden (Fluoreszenz in situ Hybridisierung) zur Analyse mikrobieller Populationen für den Lebensraum Boden zu etablieren. Anderseits sollte die Charakterisierung und funktionelle Beschreibung der mikrobiellen Bodenpopulation unter Biozideinfluss in zwei unterschiedlichen Modellsystemen (in Flüssigkulturen und Bodensystem) erfolgen. Seit einiger Zeit erfolgt eine Wandlung in der Holzschutzmittel-anwendung von metallhaltigen zu organisch basierten Wirkstoffen. Der Austrag und die Auswirkung von zwei organischen Holzschutzmittel-komponenten (Tebuconazol und Benzalkoniumchlorid) aus dem Holz in den Boden wurde zunächst mit Hilfe von Kultivierungstechniken und chemischen Analysen untersucht. Durch Bestimmung der koloniebildenden Einheiten (KBE) konnte eine Abschätzung über die Auswirkung der Biozide auf die Bodenbakterien gemacht werden. Die methodischen Einschränkungen und die Arbeitsintensität machte die Notwendigkeit für molekularbiologischer Methoden deutlich. Als zentrale molekularbiologische Methode wurde die Fluoreszenz in situ Hybridisierung (FISH) angewendet. Das Potential dieser Methode wurde zum einen an einem Modellsystem in Flüssigkulturen ("in vitro") getestet und zum anderen durch Etablierung einer Extraktionsmethode als Vorschritt der FISH- Technik für Bodensysteme anwendbar gemacht. Um zu verifizieren, inwieweit Biozide (besonders Tebuconazol und Benzalkoniumchlorid) auf unterschiedliche Bakteriengruppen wirken, wurde ein Modellsystem "in vitro" entwickelt. Anhand von ausgewählten Bakterienarten konnte gezeigt werden, dass mit Hilfe von FISH und einer "Färbe"- Methode (Live/Dead-Test) die Wirksamkeit der Biozide abgeschätzt werden kann. Es zeigte sich zum Beispiel, dass die Gram-Bakterien i.d.R. empfindlicher gegenüber Benzalkoniumchlorid waren als Gram-Bakterien. Die Untersuchungen an ausgewählten Reinkulturen und Mischkulturen erlaubten eine quantitative Abschätzung der Biozidauswirkungen und bieten ein Potential, Biozide vor ihrer Anwendung zu testen. Im Boden stören bzw. verhindern die Huminstoffe die Anwendung von FISH. Durch Etablierung einer Extraktionsmethode, bei der mit Hilfe von Polyvinylpyrrolidon (PVP) die Bakterienextrakte aufgereinigt werden, gelang es, die FISH-Technik auch für Bodensysteme anzuwenden. Es wurde ein zweites Modellsystem untersucht, bei dem die Populationänderung im Boden direkt durch FISH überprüft und gleichzeitig die Auswirkung der Biozide auf die Bodenfunktion anhand der Messung der Bodenatmung bestimmt wurde. Mit diesen Untersuchungen konnte gezeigt werden, dass bestimmte Bakteriengruppen bei toxischer Auswirkung von Tebuconazol und Benzalkoniumchlorid auf die Bodenatmung entweder prozentual im Boden zurückgingen (Gram-Bakterien mit niedrigen G+C- Gehalt durch Tebuconazolkontamination), oder andere Gruppen, einen gesteigerten Anteil in der Population zeigten (Proteobakterien der Subklasse Alpha und Gamma durch Benzalkoniumchlorid). Es war so möglich, durch FISH die Verteilung verschiedener phylogenetischer Gruppen mittels Einsatz spezifischer Oligonukleotidsonden im Boden zu untersuchen. Diese Untersuchungen sind geeignet, Bakterienarten mit möglichen hohen Abbaupotentialen zu finden. Anhand von verschiedenen Fallbeispielen von Verunreinigungen in Böden und Flüssigkulturen wurden die Möglichkeiten des Einsatzes von molekularbiologischen Methoden (besonders FISH) aufgezeigt.
149
Im Bauwesen werden Zugglieder aus Stahl in der Regel für Aussteifungsverbände, Abhängungen und Unterspannungen von Trägern verwendet. Die dafür verbauten, meist kreisförmigen Vollprofile dienen häufig der Stabilisierung des Tragwerks. Ein Versagen der Stahlzugglieder kann zu einem Einsturz der gesamten Konstruktion führen.
Unter Brandeinwirkung verlieren ungeschützte Stahlkonstruktionen aufgrund der schnellen Erwärmung frühzeitig ihre Tragfähigkeit. Durch den Einsatz reaktiver Brandschutzsysteme auf Stahlbauteilen kann deren Erwärmung verlangsamt und dadurch der Feuerwiderstand verbessert werden. Die Optik der oftmals filigranen Stahlzugglieder bleibt dabei im Wesentlichen unverändert.
Für die Anwendung reaktiver Brandschutzsysteme auf Stahlzuggliedern mit Vollquerschnitt gibt es derzeit in den allgemeinen bauaufsichtlichen Zulassungen keine Regelungen. Die an der Bundesanstalt für Materialforschung und –prüfung (BAM) durchgeführten experimentellen und numerischen Untersuchungen [35] sowie die darauf aufbauenden Erkenntnisse dieser Dissertation hinsichtlich des Verhaltens reaktiver Brandschutzsysteme auf Stahlzuggliedern mit Vollprofil bilden die Grundlage für eine Erweiterung des Anwendungsbereiches dieser Produkte. Eine Anwendung ist grundsätzlich möglich. Aufgrund der meist für Zugglieder eingesetzten filigranen Vollquerschnitte sowie der in Bezug auf die Tragfähigkeit fehlenden Umlagerungsmöglichkeit werden besonders hohe Anforderungen an die Wirksamkeit und Zuverlässigkeit von reaktiven Brandschutzsystemen gestellt. Anhand der Ergebnisse aus den Brandversuchen sowie theoretischer Betrachtungen ist festzustellen, dass das auf kreisförmigen, zugbeanspruchten Stahlprofilen aufgebrachte reaktive Brandschutzsystem aufgrund der notwendigen dreidimensionalen Ausdehnungsrichtung der höchst möglichen Beanspruchung ausgesetzt ist. Mit Hilfe von Leistungskriterien zur Bestimmung der Tragfähigkeit, welche im Rahmen der Dissertation entwickelt wurden, lassen sich die in Brandversuchen unter axialer Zugbeanspruchung getesteten Stahlzugglieder mit reaktiver Brandschutzbeschichtung in Feuerwiderstandsklassen einordnen.
Für die Beurteilung der thermischen Schutzwirkung des reaktiven Brandschutzsystems werden die Erwärmungsgeschwindigkeit, die maximale Stahltemperatur sowie die Rissbildung und das Rissheilungsvermögen der Beschichtung herangezogen. Die Brandversuche haben gezeigt, dass die Profilgeometrie, die Höhe der Trockenschichtdicke der Beschichtung, die Höhe der aufgebrachten Zugbeanspruchung sowie die Orientierungsrichtung der Zugglieder einen wesentlichen Einfluss auf die thermische Schutzwirkung des reaktiven Brandschutzsystems ausüben. Zudem stehen diese Faktoren in gegenseitiger Wechselwirkung. Durch Abstimmung der genannten Einflussgrößen lässt sich die Wirkung der Brandschutzbeschichtung optimieren. Durch die Vielzahl an reaktiven Brandschutzsystemen und die in den Produkten variierende chemische Zusammensetzung ist deren Aufschäumverhalten und thermische Schutzwirkung sehr unterschiedlich und kaum vorhersagbar. Die Wirksamkeit des reaktiven Brandschutzsystems ist daher für Grenzfälle des vom Hersteller definierten Anwendungsbereichs durch Brandversuche zu überprüfen. Empfehlungen zur Durchführung dieser Versuche sind im Forschungsbericht [35] beschrieben.
Bei Verwendung von kaltverformtem Blankstahl für Stahlzugglieder mit Vollprofil sind andere Hochtemperatureigenschaften als bei dem typischerweise für Träger und Stützen eingesetzten warmgewalztem Baustahl zu berücksichtigen. Kaltverformter Blankstahl weist gegenüber herkömmlichem Baustahl einen höheren Wärmeausdehnungskoeffizient und andere temperaturabhängige Abminderungsfaktoren für die Stahlfestigkeit auf. Die in experimentellen Untersuchungen für Blankstahl ermittelten Materialeigenschaften können für die Heißbemessung von Zuggliedern mit Vollprofil aus entsprechendem Material verwendet werden. In Kombination mit Temperaturdaten aus Brandversuchen lässt sich mittels eines auf der Grundlage der Finite-Elemente-Methode (FEM) entwickelten numerischen Berechnungsmodells das Trag- und Verformungsverhalten von Zuggliedern realitätsnah berechnen. Vergleiche zur Stablängsverformung von in Brandversuchen getesteten Zuggliedern zeigen eine hohe Übereinstimmung mit den Ergebnissen aus dem im Rahmen der Dissertation neu entwickelten Bemessungsmodell.
35
The behavior of amorphous polymers in contact with gas atmospheres is still an area of both fundamental scientific and applied industrial research. Applications range from the use as barrier materials or protective coatings to active layers in sensor applications (‘artificial nose’) and the large field of gas separation membranes. In all these applications, high concentrations of small penetrant molecules may lead to a plasticization of the polymer. This effect is utilized in processing applications, where supercritical carbon dioxide (CO2) can be used as a plasticizer.4 The phenomenon of penetrant induced plasticization of glassy polymers is also observed in gas separation membranes.5 In the process of natural gas sweetening, the CO2 content of the gas mixture is reduced by separation of the CO2 from the fuel gas methane (CH4) to avoid corrosion of pipelines and to enhance the fuel value. Solubility and diffusivity of the respective gas determine the separation performance of the membrane material, i.e., the permselectivity. Both parameters are connected to the internal structure of the polymer and its free volume. To achieve high throughputs, e.g. to enhance costeffectiveness, it is desirable to increase the CO2 solubility and mobility. However, the observed plasticization and the associated relaxations in the polymer matrix change its structure and free volume, and thereby affect the selectivity of the material.6 In addition, other properties of the polymer are influenced, e.g. a reduction of glass transition temperature,7 yield stress8 and creep compliance9 have been observed. The origin and mechanism of these structural relaxations are poorly understood, as are the factors that influence solubility and mobility of the plasticizing penetrant. This lack of knowledge leads to a development of new or optimized materials, which is in part determined by trial and error. A deeper understanding of the phenomena that accompany gas sorption on the molecular level is therefore needed to control material properties and enable a targeted design of functional materials. Therefore, in this work, laboratory experiments are combined with detailed atomistic molecular simulations. Modelling. In detailed atomistic molecular modeling, the interactions of an assembly of atoms, e.g. a polymer molecule, are calculated according to known physical laws. Several established analysis methods allow an indirect determination of certain properties of such assemblies, others can even be directly calculated.10 However, CPU-power limits both the size and the simulation time of such assemblies. The size of the simulated packing models used in this work (_ 5000 atoms) ranges among the larger models found in the literature. Forcefield based Molecular Dynamics (MD) simulations are calculated in femtosecond steps, but reliable results are usually not obtained until a nanosecond of net simulation time has been performed. Millions of interactions need to be calculated, making the time effort for these ‘virtual experiments’ comparable to laboratory experiments. However, increasing speed of single processors and the possibility of parallel processing will further reduce the evaluation times for such simulations in the future. The goal of computer simulations is therefore to establish reliable methods to predict material properties. Properties of new materials could then be assessed by simulations first and only the most promising materials need to be synthesized for further testing, reducing the expense of trial and error. Although some methods already exist to predict polymer/gas properties from simulations, which show well agreeing results in ideal circumstances, they frequently fail when applied to less moderate conditions, e.g., high penetrant concentrations, long time scales, large penetrants etc. The aforementioned gas induced plasticization of polymers presents such a case where the gap of time scales between experiment and available simulation time amounts to several orders of magnitude. The time scale of simulations is limited to a few nanoseconds and therefore it is not possible to directly simulate relaxations of the glassy matrix as they are observed experimentally. Experiments, on the other hand, yield results of the real macroscopic system, and though molecular details cannot be observed individually, the accumulated effects permit the analysis through models on a statistical or phenomenological basis. It is the aim of this work to survey new approaches of a combined analysis of experimental and modelling results and to establish, where possible, a convergence of boundary conditions or, alternatively, an identification and isolation of comparable aspects of these seemingly incompatible methods of research. To this effect, phenomenological models are utilized as a means of interpretation of experimental data as well as to construe modelling results.
61
Korrosionsprozesse und Aufkohlung von ferritisch-martensitischen Stählen in H2O-CO2 Atmosphären
(2010)
Ca. ein Viertel des in Deutschland emittierten CO2stammt aus fossil befeuerten Dampfkraftwerken, dessen Anteil es durch die Weiterentwicklung von CO2-Abtrennungstechnologien mit anschließender Speicherung in geologischen Formationen und durch die Gestaltung neuer CO2-armer Kraftwerksprozesse zu reduzieren gilt. Die hierzu in Deutschland laufenden Programme werden unter anderem innerhalb des COORETEC-Programms (CO2-Reduktions-Technologie-Programm) koordiniert [COR-04]. Allen CO2-Reduktionstechnologien ist gemein, dass die Erzeugung von speicherfähigem CO2 (Luftzerlegung zur Produktion von reinem Sauerstoff, der Separationsprozess von CO2 aus dem Rauchgas und das Komprimieren des CO2) energieaufwändig ist. Um eine CO2- Abtrennung aus den Rauchgasen und dessen Kompression wirtschaftlich zu machen, wird für kohlebefeuerte Kraftwerke eine Erhöhung des Wirkungsgrades der thermisch-elektrischen Energiewandlung angestrebt [KRA-06]. Der Wirkungsgrad ist das Verhältnis der gewonnenen elektrischen Leistung zur Wärme, die aus der Verbrennung eines Brennstoffes entsteht [DUB-90]. Er lasst sich für Dampfkraftwerke unter anderem erhöhen durch die Anhebung der Dampfparameter (Druck und Temperatur). Derzeit liegen die Dampfparameter im Bereich von 600°C und 250 bar Druck [VIS-00][VIS-06] und sollen auf 720 °C Dampftemperatur und 350 bar Druck angehoben werden [COR-99]. Eine Erhöhung des Wirkungsgrades des Grundkraftwerks ohne CO2-Abscheidung von 50 % oder mehr wird angestrebt, um eine CO2-Speicherung technisch und wirtschaftlich möglich machen [COR- 04]. Ein Ziel sind Dampfkraftwerke mit Oxyfuel-Verbrennung, bei denen die Abtrennung von CO2 nach dem Verbrennungsprozess stattfindet (post-combustion) [VAT-08]. Die Kohle wird mit reinem Sauerstoff an Stelle von Luft zu einem kohlendioxidangereicherten Rauchgas umgesetzt, aus denen sich nach der Kondensation des Wassers, der Entschwefelung und der Entstickung je nach Stickstoffanteil des Brennstoffs ein kohlendioxidreiches Gas generieren lasst. Je nach Kohle und Vorbehandlung der Kohlen variiert der CO2-Gehalt am Verbrennungsraumausgang (Boiler) zwischen 50 und 70 Vol %. Der Wasseranteil beträgt 16-25 Vol % und der überschüssige Sauerstoff ändert sich im Bereich von 2,5 und 4,5 Vol % [KAs-08-1][ KAs-08-2][BOI-09][CAU-09][STR-09]. Das gleiche Verbrennungsgas entsteht wahrend der druckgeladenen Wirbelschichtfeuerung mit reinem Sauerstoff [HON-09]. Für die Korrosionsuntersuchungen in dieser Arbeit wurde eine Gaszusammensetzung von 70 mol % Kohlendioxid und 30 mol % Wasserdampf genutzt. Ein Schaubild der von Vattenfall im September 2008 in Betrieb genommenen Oxyfuel-Pilotanlage ist in Abbildung 1-1 zu sehen. Wichtige Komponenten sind der gesamte Dampfkreislauf mit Dampfturbine, die Luftzerlegungsanlage zur Erzeugung von reinem Sauerstoff und der Kessel, in dem die eigentliche Verbrennung stattfindet, sowie die Entstaubung und Entschwefelung [VAT-08]. Eine weitere effiziente Technologie mit CO2-Abscheidung stellt der IGCC-Prozess (Integrated Gasification Combustion Cycle) dar. Er gehört zu den pre-combustion-Technologien, bei denen die Abscheidung des CO2 vor der Verbrennung stattfindet. An dieser Stelle sei auf die umfangreiche Literatur hingewiesen, in der IGCC-Prozesstechnik thematisiert wird. Die Entwicklung und die Eigenschaften der Werkstoffe spielen bei Erhöhung der Wirkungsgrade in Oxyfuel-Kraftwerken eine bedeutende Rolle, da sie erhöhten Dampfparametern und veränderten Rauchgaszusammensetzungen widerstehen müssen. Heute werden die Dampferzeugerrohre und Dampf führende Rohrleitungen in konventionellen Kohle befeuerten Dampfkraftwerken aus kriechfesten und korrosionsbeständigen Materialien gefertigt, die unter Kraftwerksbedingungen eine Lebensdauer von 100 000 h erreichen sollen [HAH-04][VIS-00][VIS-06][FUJ-92][ENN-07-2]. In Abhängigkeit von der Belastung werden für die verschiedenen Komponenten im Kraftwerk unterschiedliche Werkstoffe eingesetzt, welche optimiert für die anliegenden Bedingungen sind. Der Kessel (Verbrennungsraum) besteht aus einem Rohrsystem, die Membranwände genannt werden. Diese werden in mit Luft befeuerten Kraftwerken aus niedrig legierten Stahlen wie z.B. 13CrMo44 und T24 gefertigt. Sie werden maximal Temperaturen bis 525 °C ausgesetzt [ASM-96][VIS-00]. Innerhalb des Verbrennungsraumes sind Überhitzerrohre angeordnet, in denen Wasserdampf überhitzt und unter Druck gesetzt wird. Für Überhitzerrohre werden kriechresistente ferritisch-martensitische Stähle genutzt, welche sich durch eine hohe Festigkeit, hohe Bruchzähigkeit, Schweißbarkeit und im Vergleich zu austenitischen Stahlen geringen Wärmeausdehnungskoeffizienten auszeichnen [BEN- 02][VIS-00][VIS-06]. Die höchsten Einsatztemperaturen liegen für die ferritisch-martensitischen Stähle in Abhängigkeit ihrer Kriechfestigkeit heute bei maximal 620°C [VIS-00][VIS-06]. Typische Vertreter gehören zur Gruppe der hochwarmfesten Stahle 9-12 % Chrom-Stahle (z.B. X20CrMoV12-1, T91, T92) [BUR-06]. Die Anhebung der Dampfparameter Druck und Temperatur in Kombination mit der veränderten Rauchgaszusammensetzung im Oxyfuel-Kraftwerk haben einen unbekannten Einfluss auf die in Kraftwerken typischerweise eingesetzten kriech- und korrosionsresistenten Werkstoffe. In der vorliegenden Arbeit werden entsprechend den beschriebenen Bedingungen Temperaturen zwischen 500 und 650 °C, Drucke von 1, 30 und 80 bar und eine Gaszusammensetzung von 30 mol % H2O und 70 mol % CO2 auf verschiedene Stahle angewendet. Die Einflüsse der genannten Parameter sind Gegenstand dieser Arbeit.
69
Different amino group carrying surfaces, prepared by spin coating, self-assembly and plasma polymerization, were successfully investigated by XPS and NEXAFS. Amino groups were derivatized with the widely used primary amino group tags, PFB and TFBA, prior to analysis. Primary amino group quantification was then carried out according to the spectroscopic data. The gas-phase derivatization reactions of PFB and TFBA were also studied in order to understand their reaction behaviour, the spectral differences they cause and the time required for reaction completion. For the determination of maximum reaction yields of gas-phase surface derivatizations, a set of liquid-phase derivatization reactions was carried out. The selected amino compounds with a different degree of steric hindrance were reacted with PFB and TFBA. The yields (78-89%) were accepted as the upper limit of the gas- phase surface derivatizations. Thin films were prepared by spin coating of 4,4’-methylenebis(2,6-diethylaniline) on Si wafers and were reacted with the markers at 50ºC. The saturation time was found to be 15 min. for both reactions. XPS measurements showed the formation of a CF3 or C-F peak and a BE shift of the corresponding C=N group indicating a successful reaction. The NEXAFS results supported the XPS data by showing a sharp π*(C=N) resonance. The CF3 and C-F resonances were observed in the σ* region. The yields of the reactions were calculated from the component areas of the high resolution XP N1s spectra and from the [F]/[N] ratios. The surface amino groups were calculated from the stoichiometry and from the XP survey scans. The results were consistent with each other and showed a yield of 80-90% for PFB and 60-70% for TFBA. Self-assembled monolayers (SAMs) of different terminal groups were prepared and investigated with XPS and NEXAFS. The spectral properties of aliphatic and aromatic SAMs were compared to the reference surfaces of poly(allylamine) and 4,4’-methylenebis(2,6-diethylaniline) spin coated on Si wafers. NEXAFS was used to determine the orientation of SAMs. An angle resolved NEXAFS was applied at the C K-edge in order to prove a successful SAM deposition on Au. The intense peaks in the difference spectra are due to the polarization dependence in the orbital responsible for the NEXAFS resonance showing a successful bond/functional group orientation. The gas-phase surface derivatization of two amino terminated SAMs, 4-aminophenylbutane-1-thiolate and 11- amino-1-undecanethiol, were studied. 4-aminophenylbutane-1-thiolate was derivatized with TFBA whereas 11- amino-1-undecanethiol with PFB at room temperature for 90 min. The stoichiometrical data were compared to the atomic percentages obtained from the XPS spectra and the results were consistent with each other. The yields of the reactions (60-80%) were obtained from the high resolution N1s spectra. Since a certain number of spectra had to be acquired to reach reasonable S/N ratios, a considerable danger of beam damage in the NEXAFS measurements occurs. The potential radiation damage effects on the C and N K- edge of 11-amino-1-undecanethiol film on Au was studied. The spectral differences before and after 1 h radiation exposure were investigated. The intensities of resonances related to unsaturated species such as C=C and C=N were increased for the C K-edge spectra. The NEXAFS N K-edge spectra of 11-amino-1-undecanethiol film showed no significant irradiation effect. Plasma deposited allylamine samples were successfully investigated by XPS and NEXAFS. Primary amino group quantification on plasma deposited allylamine surfaces was carried out by derivatization after plasma deposition. TFBA and PFB showed side reactions when plasma polymerization was used. Due to the radical mechanisms, C- F bond cleavages followed by HF releases occurred resulting in a second peak formation in XP F1s spectra. PFB derivatized surfaces suffer more from the C-F bond cleavage since fluorinated aromatic molecules are highly susceptible to nucleophilic aromatic substitution. Potential X-ray beam damage of TFBA was studied by a 10 h XPS measurement and showed a fluorine degradation. Due to the short measurement times, X-ray beam damage can be neglected. Since HF release on the TFBA surfaces are lower in percentage, it was used as the marker reagent for the coupling reactions. A series of samples deposited at 20W, 0.5 duty cycle and 15 Pa were derivatized to determine the time required for saturation (90 min.). Plasma polymerized allylamine samples with different duty cycle, power and pressure values were prepared in order to study the effects of external plasma parameters on the primary amino group retention. The [CF3] area percentages, obtained from the high resolution XP C1s spectra, vs. plasma parameter variations were compared. Duty cycle, power and pressure variation experiments showed the same trend on amino group retention. The more the plasma conditions move from mild to hard, the more rearrangements occur on the surface. Milder plasma conditions promote the retention of amino groups originating from the allylamine monomer. QEA (Quantitative Elemental Analysis) and PFA (Peak Fit Analysis) methods were used for the quantification of surface amino groups, depending on the XPS data. The results of two data evaluation methods were compared by using a Youden plot showing no deviation. NEXAFS was used along with XPS in order to study plasma parameter effects on amino groups. As being sensitive against unsaturated moieties, NEXAFS was successfully applied to plasma deposited allylamine surfaces. An increase in fragmentation rate due to a variation in plasma parameters was followed by intensity changes in NEXAFS C K-edge spectra. An inter-laboratory comparison of hydroxyl group determination on plasma surfaces was carried out. Hydroxyl groups on polypropylene foil, treated with oxygen plasma at 100 W for 90 s, were coupled with TFAA. The surfaces were investigated with XPS and the [OH] amount on the surfaces was calculated by QEA and PFA methods showing a 33% deviation between the two methods. CD-XPS is applied successfully in order to determine different functional groups on the thin film surfaces. However, a validated derivatization procedure, which can be easily applied in each lab, should be established. The used hardware and the peak fitting procedures of XPS should be defined in detail for the validation. The sample inhomogeneity and the effects of beam damage play a role on the deviations of the results. The surface thickness should be optimized for consistency. By the derivatization reactions, the surface amino groups are successfully quantified. As the next step, the studied surfaces can be used for potential biological applications, such as coupling the available amino groups with DNA or stem cells.
58
Holz und eine Vielzahl von Holzschutzmitteln (HSM) werden im Bodenkontakt durch Eukaryonten und Prokaryonten bis zum Kohlenstoffdioxid abgebaut und zum Teil in mikrobielle Biomasse umgewandelt. Die Abbauprozesse eines HSMs, auf Basis von metallorganischem Kupfer-HDO, wurden im Rahmen dieser Arbeit durch die Verknüpfung chemischer und molekularbiologischer Techniken sowie 13C „Tracer“- Experimenten näher charakterisiert. Analysen mit sterilisiertem Boden ergaben, dass der Abbau von 13C- und 12C-Kupfer-HDO durch eine mikrobielle Gemeinschaft beschleunigt wurde. Durch Auswaschung aus geschütztem Holz können Teile des Biozids in geringen Konzentrationen in den Boden gelangen. Messungen der Biozidkonzentration mittels HPLC über die Zeit ergaben, dass das Kupfer-HDO innerhalb von wenigen Tagen im Boden abgebaut wurde. Ein Vergleich der Abbaugeschwindigkeiten zeigte, dass Kupfer-HDO als reines Biozid im Boden schneller abgebaut wird, als ein im Holz eingebetteter Bestandteil einer Holzschutzmittelformulierung. Die Analysen des respiratorisch entstandenen CO2, sowie der Veränderungen der mikrobiellen PLFA-Struktur in den Testansätzen mittels EA-IRMS- bzw. GC-C-IRMS erbrachten, dass das Kupfer-HDO sowohl anabolisch als auch katabolisch von der mikrobiellen Gemeinschaft metabolisiert wurde. Durch den Einsatz der SIP-PLFA-Technik wurde die mikrobielle Gemeinschaft charakterisiert. Mittels der Analyse des 13C-Werts in den PLFAs wurde nachgewiesen, dass der Abbau des Biozids hauptsächlich durch Gram negative Bakterien erfolgte. In den nur in geringem Maße vorhandenen Signaturfettsäuren von Pilzen und anderen Eukaryonten konnte demgegenüber keine Veränderung des 13C-Werts festgestellt werden. Dies deutet darauf hin, dass die Eukaryonten nicht am Abbau des Kupfer-HDOs beteiligt waren. Um die mikrobielle Sukzession in Bezug auf HSM zu charakterisieren, wurde die Zusammensetzung der mikrobiellen Lebensgemeinschaft auf der Oberfläche von Kupfer-HDO- und Kupfer-Amin-behandelten sowie unbehandelten Holzprüfkörpern im Bodenkontakt bestimmt. Zur Aufklärung der Bedeutung des Co- Biozids HDO für die mikrobielle Lebensgemeinschaft am Holz wurde dies durch ein anderes Amin ersetzt und unter der Bezeichnung Kupfer-Amin-HSM in den Untersuchungen eingesetzt. Mit Hilfe des Fingerabdruckverfahrens T-RFLP wurde die Zusammensetzung der bakteriellen Gemeinschaftsstruktur charakterisiert. In einem Ordinatensystem wurden die Veränderungen der bakteriellen Gemeinschaftsstruktur hinsichtlich der Faktoren Inkubationszeit und HSM visualisiert. Die statistische Auswertung der Datensätze ergab, dass sich die bakterielle Gemeinschaftstruktur zwischen dem Kupfer-Amin-basierten HSM signifikant von dem Kupfer-HDO-basierten HSM unterschieden. Im Verlauf der Inkubationszeit konnten in den einzelnen Testansätzen keine statistisch signifikanten Unterschiede detektiert werden. Die Gemeinschaftsstruktur der Eukaryonten wurde mittels des SSCP-Fingerabdruckverfahrens charakterisiert. Dazu wurde die DNA von abundanten operativen taxonomischen Einheiten (OTUs), welche sich über die Zeit und im Bezug auf die verschiedenen HSM besonders stark änderten, aus den Banden in den SSCP-Gelen isoliert, kloniert und sequenziert. Entgegen den Erwartungen, unter den Eukaryonten am Holz und im angrenzenden Boden eine große Anzahl an Pilzen detektieren zu können, zeigte sich, dass nur drei Pilze an der Sukzession der eukaryontischen Gemeinschaft von Bedeutung waren. So wurde der Weißfäule erregende Basidiomycet Sphaerobolus stellatus vor allem an den H2O-behandelten Kontrollprüfkörpern nachgewiesen. Auch der Moderfäule erregende Ascomycet Lecytophora multabilis wurde vermehrt in den Kontrollen nachgewiesen. Die eukaryontische Gemeinschaft wurde von unterschiedlichen Phyla, wie Alveolata, Disicicrista, Amoebozoa, Arthropoda oder Nematoda dominiert. Von keinem dieser Organismen war aus der Literatur bekannt, dass er in der Lage ist, Holz, HSM oder einzelne Bestandteile von HSM zu metabolisieren. Diese Organismen ernähren sich in der Mehrzahl bakterivor. Dies deutet darauf hin, dass sie weniger das Kupfer- HDO abbauen, als vielmehr den Bakterienrasen beweiden, der sich auf der Oberfläche des Holzes angesiedelt hat. Mit der vorliegenden Arbeit konnte erstmals eine direkte Verbindung zwischen Organismengruppen und dem Abbau des metallorganischen Biozids Kupfer-HDO hergestellt werden. Zusätzlich wurden die zeitlichen Veränderungen der mikrobiellen Lebensgemeinschaft in Abhängigkeit von Kupfer-HDO charakterisiert.
6
Modelling and simulation of light propagation in non-aged and aged step-index polymer optical fibres
(2005)
This thesis discusses theoretical and practical aspects of modelling of light propagation in non-aged and aged step-index polymer optical fibres (POFs). Special attention has been paid in describing optical characteristics of non-ideal fibres, scattering and attenuation, and in combining application-oriented and theoretical approaches. The precedence has been given to practical issues, but much effort has been also spent on the theoretical analysis of basic mechanisms governing light propagation in cylindrical waveguides. As a result a practically usable general POF model based on the raytracing approach has been developed and implemented. A systematic numerical optimisation of its parameters has been performed to obtain the best fit between simulated and measured optical characteristics of numerous non-aged and aged fibre samples. The model was verified by providing good agreement, especially for the non-aged fibres. The relations found between aging time and optimal values of model parameters contribute to a better understanding of the aging mechanisms of POFs.
79
Elastomerdichtungen finden als Bauteil oder Maschinenelement vielseitige Verwendung. Jedoch war trotz ihrer zentralen Bedeutung die untere Temperaturgrenze, bis zu der solche Dichtungen eingesetzt werden können, bisher nicht tiefgehend verstanden. Dieser Umstand erschwert die entsprechende notwendige sicherheitsrelevante Beurteilung. Mit der vorliegenden Arbeit ist deshalb das Ziel verfolgt worden, dass Materialverhalten repräsentativer Elastomerwerkstoffe in Abhängigkeit von der Temperatur zu verstehen und daraus dann abzuleiten, bis zu welcher Temperatur eine daraus hergestellte Dichtung unter Berücksichtigung der jeweiligen Einsatzbedingungen ihre Funktion noch sicher erfüllen kann. Ausgehend von der in der Literatur beschriebenen Aussage, dass eine Dichtung auch unterhalb der „Glasübergangstemperatur“ funktionsfähig ist, wurde der Einfluss des Glas-Gummi-Übergangs auf das Dichtungsversagen untersucht. Zunächst wurden dazu die Glasübergangstemperaturen an einer Vielzahl von Elastomeren mit gebräuchlichen Verfahren bestimmt, um diese mit dem Verhalten der Dichtung vergleichen zu können. Weiterhin wurde im Rahmen der Arbeit eine neue Charakterisierungsmethode des Tieftemperaturverhaltens von Elastomeren entwickelt, die die bisher für Dichtungen eingesetzte Normprüfung des Druckverformungsrests nachstellt. Mit dieser Methode ist im Vergleich zur Normprüfung jedoch eine deutlich schnellere und automatisierbare Untersuchung des Materialverhaltens gegeben. Darüber hinaus ist durch eine modellgestützte Auswertung eine Extrapolation der Messdaten auf zusätzliche Temperaturen möglich, wodurch der experimentelle Aufwand weiter reduziert wird. Zur temperaturabhängigen Charakterisierung des Versagensvorgangs an realen Bauteilen wurde deren Dichtverhalten mittels eines dafür entwickelten Versuchsstandes untersucht. Die festgestellte Abhängigkeit der Versagenstemperatur vom Verpressgrad konnte unter Verwendung der Ergebnisse aller angewandten Charakterisierungsmethoden für die hier untersuchten statisch beanspruchten Dichtungen erklärt werden. Zudem lassen sich aus dem mit Hilfe des Zeit-Temperatur- Superpositionsprinzips gewonnenen Informationen zur Zeitabhängigkeit der Materialeigenschaften auch Aussagen zum Verhalten von dynamisch beanspruchten Dichtungen ableiten. Mit dem Ergebnis der Arbeit zum Verständnis des Verhaltens von Elastomerdichtungen bei tiefen Temperaturen wird die gezielte Beurteilung und Auswahl von sicherheitsrelevanten Dichtsystemen in Zukunft vereinfacht.
59
Plasma chemical methods are well suited for introducing functional groups to the surface of chemically inert polymers such as polyolefins. However, a broad variety of functional groups is often formed. Unfortunately, for further chemical processing such as grafting of molecules for advanced applications a highly dense and monotype functionalized polyolefin surface is needed. Therefore, the main task was to develop a selective surface functionalization process, which forms preferably one type of functional groups at the surface in high and variable concentration. Amongst the novel plasma methods, the under-water plasma process (UWP) is one of most attractive to solve the problem of monotype functionalization. Such plasma is an efficient source of ions, electrons, UV-radiation, high frequency shock waves, radicals such as hydroxyl radical and reactive neutral molecules such as hydrogen peroxide, hydrogen and oxygen. It was found that underwater plasma and the closely related glow discharge electrolysis are interesting new methods for polymer surface functionalization. An effective modification into the topmost surface chemistry of polymer layer was observed by the collective effect of wet-chemistry, electrochemistry, atmospheric gas discharges, irradiation, and shock waves. Underwater capillary discharge was seen more effective in -OH functionalization and was largely seen as a flow dominated process because of the shock wave turbulences. Using such water-based plasma a fraction of 25-40% of all O-functional groups was produced as OH-groups in comparison to <10% OH produced in the oxygen low- pressure plasma. The exact concentration of the OH functionality was studied by TFAA gas phase derivatization and measuring the respective fluorine concentration by photoelectron spectroscopy (XPS). In contrast to established gas phase glow discharge processes, the water phase absorbs and therefore limits the particle and radiation energy and thus the energy input into the polymer. Extensive oxidation, degradation, cross-linking and radical formation in the polymer is more limited than under gas plasma exposure because of the liquid water environment, which moderates high energetic plasma species. The variety of plasma produced species in the water phase is also much smaller because of the limited reaction possibilities of the plasma with water. The possibility to admix a broad variety of chemical additives makes underwater plasma additionally highly attractive for the chemist. At last, the water removes all low-molecular weight oxidized products formed by plasma-induced polymer degradation. Hydrogen peroxide and the catalyst (Fe-ZSM5) should influence or increase the equilibrium concentration of OH radicals in the underwater process. It was supposed that these radicals play the most important role for OH functionalization of polyolefin surfaces. Hydrogen peroxide was believed to be the most prominent precursor for OH group formation in the UWP. The catalyst should modulate the steady state of OH group formation and recombination, and thus accelerate the functionalization. This was confirmed by an increased oxidation rate. Owing to the detection limit of XPS the C-O bond selectivity was defined as clearly resolvable subpeak within the C1s signal assigned to C-OH, C-O-C and other singly C-O bonded species. This bondamounts 47 C-O bonds/100 O atoms with pure UWP system and enhances to a maximum of the 81 C-O bonds/100 O atoms using the Fe-ZSM5 catalyst system. Therefore, this method exhibits a great progress for a start. However, after TFAA derivatization the fraction of desired OH groups could not be significantly increased. In the continuation acetic acid, acrylic acid, maleic and itaconic acid were used as additive monomers. The chemical selectivity in -COOH bond formation using bi-carboxylic additives was seen inferior. Acetic acid is not a chemically polymerizing monomer but it could polymerize by monomer/molecular fragmentation and recombination to a cross linked layer. The other monomers form preferably water-soluble polymers on a preferred chemical way. Only the fragmented fraction of these monomers could form an insoluble coating by cross linking to substrate. The XPS analysis was used to track the alterations in COO- bond percentage on the PP surface. To identify the -COOH groups on substrate surface unambiguously, which have survived the plasma polymerization process, the gas phase derivatization with trifluoroethanol was performed. A much higher yield in COOH groups was achieved using the glow discharge electrolysis and acrylic acid.
153
Die zerstörungsfreie Prüfung (ZfP) ist aus solchen Bereichen unseres Lebens nicht mehr wegzudenken, in denen Schäden mit hohen Folgekosten oder Gefährdungen von Menschenleben entstehen können (Beispiele: Transportwesen, Energieerzeugung, Chemieindustrie). In der Praxis kann ein Prüfsystem an seine Grenzen geraten, z.B. bei kleinen Defekten. Defekte mit kritischer Größe werden möglicherweise nicht detektiert. Daher müssen probabilistische Bewertungsverfahren das Prüfsystem beschreiben.
Es wird eine objektive Qualitätskennzahl gesucht, auf deren Basis die Anwendbarkeit der Prüfmethode definiert werden soll. Die Auffindwahrscheinlichkeit (engl. probability of detection - POD) erfüllt diese Anforderung. Die POD zeigt auf Basis des Zusammenhangs und der Streuung der Daten, ob das Verfahren für die Prüftätigkeit akzeptiert werden kann oder noch verbessert werden muss.
Das ursprüngliche POD-Verfahren wurde für quasi eindimensionale Defekte in dünnen Luftfahrtbauteilen entwickelt. In der industriellen Realität ist diese Bewertung ein Balanceakt zwischen Statistik und Durchführbarkeit: Die Prüfung soll mit realen Defektdaten für die spätere Produktion des Bauteils (bzw. wiederkehrende Wartungsprüfung) bewertet werden. Doch die notwendige Gegenüberstellung zwischen Schliffdaten, für die Erfassung der wahren Defektgröße von räumlich ausgeprägten Defekten und dem Signal eines ZfP-Systems stellt sich als herausfordernde und kostenintensive Aufgabe heraus. Sowohl die Aufstellung eines gemeinsamen Koordiantensystems als auch die Beschreibung und Angleichung der Daten stellen eine notwendige Vorarbeit dar. In dieser Arbeit wird ein mögliches Vorgehen entwickelt, dass im Weiteren eingesetzt werden kann. Während in der Literatur zum Thema POD häufig die Begrenzung des Einsatzes einer eindimensionalen POD (POD mit einem Defektparameter) für reale Defekte bereits erkannt wurde, soll außerdem in dieser Arbeit das Verfahren auf der Signalseite umfassender erweitert werden, um die Einbeziehung realer Defekte in die POD-Bewertung zu ermöglichen. Hierfür werden mit Hilfe dieser Arbeit zwei wesentliche Neuerungen in der POD-Bewertung eingeführt:
1. Die Anzeigenfläche wird als wichtiges Indiz zur Detektion in die Bewertung eingeführt. Dabei zeigt der Ansatz einer Observer-POD, bei dem der Detektierbarkeit eines Defekts beschrieben wird, eine Möglichkeit in die Bewertung zu erweitern. Jedoch wird die notwendige Datenanzahl die für eine Observer-POD selten mit Experimenten erreicht. Daher schlagen wir die Einführung eines Glättungsalgorithmus vor, um auch auf der Basis von wenigen Daten die Flächenabhängigkeit zu erfassen. Der Algorithmus wird hierbei durch simulierte Daten auf seine Funktionsfähigkeit überprüft, bevor er auf reale Defekte angewendet wird. Gleichzeitig helfen die simulierten Daten einen Vergleich zu den vorhergegangenen Ansätzen zu ermöglichen.
2. Darüber hinaus reichen die Daten der realen Defekte häufig nicht aus, um die statistische Forderung zu gewährleisten, so dass es notwendig, wird künstliche Defekte mit einzubeziehen. Deshalb sollen die vorhanden künstlichen Defekte in Form von Referenzdefekten mit einbezogen werden, um die statistische Grundlage zu erhöhen. Für die Prüfung von Referenzdefekten sind jedoch wichtige Einflussgrößen (z.B. Oberflächenrauhigkeit) nicht vorhanden. Wegen der unterschiedlichen Aussagekraft der Daten und zur Vermeidung einer zu optimistischen Abschätzung, ist eine einfache Mischung der Daten ausgeschlossen. Um realen Defekten eine Möglichkeit dafür zu schaffen, dass die Eigenschaften der realen Defekte angemessen auf das Ergebnis der Bewertung des Verfahrens Einfluss nehmen können, wird eine gewichtete Kombination der Defektdaten für die Bewertung vorgestellt. Das Vorgehen wird am Beispiel der radiographischen Prüfung einer elektronenstrahlgeschweißten Naht durchgeführt. Die Schweißnaht verbindet den Deckel zur Außenwand eines Kupferbehältern, der für die spätere Endlagerung von verbrauchten Brennstäben aus Kernkraftwerken entwickelt wurde. Die Messergebnisse stammen aus von der Firma Posiva Oy, dem zuständigen Unternehmen für die Endlagerung von verbrauchten Brennstäben aus Kernkraftwerken in Finnland. Hierbei stellt die POD-Bewertung ein wichtiges Element in der Gesamtrisikobewertung für das Endlagersystem dar.
164
Zur Bedarfsplanung von Feuerwehren in Städten in der Bundesrepublik Deutschland wurden im Jahr 1998 die Qualitätskriterien Hilfsfrist, Funktionsstärke und Erreichungsgrad für ein standardisiertes Schadensereignis erarbeitet. Das standardisierte Schadensereignis basiert auf Ergebnissen der O.R.B.I.T.-Studie aus dem Jahr 1978. Der dort dargestellte Rauchgas-temperaturverlauf für einen standardisierten Wohnungsbrand stellt Ergebnisse von Brandversuchen in einer Wohnung aus dem Jahr 1939 dar. Die zur Untersuchung herangezogenen Einrichtungsgegenstände bestanden dabei überwiegend aus cellulosehaltigen Materialien wie Holz und Papier. Die zunehmende Verwendung von Werkstoffen auf der Basis von Holz und Polymeren führt jedoch zu einer veränderten stofflichen Zusammensetzung von Einrichtungsgegenständen in Wohnungen. Im Rahmen der vorliegenden Dissertation wurde der Einfluss dieser veränderten stofflichen Zusammensetzung von gegenwärtigen Einrichtungsgegenständen auf den Verlauf von Raumbränden sowie auf die damit verbundene Stoff- und Energiefreisetzung während der Brandentstehungs- und Brandausbreitungsphase untersucht. Im Fokus der Untersuchung stand der Raum der Brandentstehung sowie ein angrenzender Raum.
Die Ergebnisse zeigen, dass gegenwärtige Einrichtungsgegenstände sowohl im Raum der Brandentstehung als auch in dem angrenzenden Raum zu höheren Rauchgastemperaturen und -konzentrationen führen. Grund hierfür sind neben den höheren Wärmefreisetzungsraten auch die höheren Stoffausbeuten der in den gegenwärtige Einrichtungsgegenständen verwendeten Materialzusammensetzungen. Vor diesem Hintergrund zeigt sich, dass sich die auf Basis der O.R.B.I.T.-Studie definierten Standards nicht mehr als Grundlage zur Bedarfsplanung von Feuerwehren eignen. Diese können mit Hilfe der vorliegenden Ergebnisse einer Prüfung unterzogen werden, um den veränderten Brandverläufen im Rahmen einer zukünftigen Bedarfsplanung gerecht zu werden.
104
Vereint unter dem Begriff Ingenieurmethoden haben Brandsimulationen Eingang in die Fortentwicklung des Baurechts gefunden und werden vermehrt zur Unterstützung von Brandschutzkonzepten und -nachweisen eingesetzt. Aktuelle Software verbindet Verbrennungsmodelle mit numerischer Strömungsmechanik und eignet sich so für die flexible Bearbeitung unterschiedlichster Fragestellungen. Darüber hinaus bieten erste Programme die Möglichkeit, Untermodelle zur Beschreibung des Feststoffabbrands bzw. der Pyrolyse von Brandlasten einzufügen. In der Polymerwissenschaft stellt die Untersuchung und Optimierung des Brandverhaltens einschließlich der Pyrolyse eine wichtige Aufgabe dar. Aufgrund des Brandrisikos ist die Verwendung polymerer Werkstoffe häufig eingeschränkt. Die Entwicklung flammgeschützter Materialien hat daher eine besondere Bedeutung und es existieren detaillierte Methoden zur Charakterisierung brandrelevanter Materialeigenschaften. Vor diesem Hintergrund zielt die vorliegende Arbeit darauf ab, die Potentiale und Herausforderungen der komplementären Nutzung von Brandsimulation und polymerwissenschaftlichen Methoden zu untersuchen. Hierfür wurden vier Brandszenarien ausgewählt: Der Brand in einem Einfamilienhaus in der Dimension Kubikdekameter (dam³), der Single Burning Item SBI Test in der Dimension Kubikmeter (m³), der Cone Kalorimeter Test in der Dimension Kubikdezimeter (dm³) und der UL 94 Test in der Dimension Kubikzentimeter (cm³). Die Brandszenarien werden zunächst ausführlich charakterisiert. Anschließend wird ein jeweils passendes Simulationsmodell erstellt und berechnet und die Berechnungsergebnisse werden mit den realen Ausprägungen verglichen. Schließlich werden die Simulationen, unterstützt durch eine Parameterstudie, bewertet. In den Untersuchungen zu den vier Brandszenarien werden durch die komplementäre Nutzung von Brandsimulation und Polymerwissenschaft belastbare numerische Berechnungen erarbeitet. Grundlage für die Ergebnisse sind die detaillierte Charakterisierung der brandrelevanten physikalischen und chemischen Eigenschaften der Werkstoffe und die damit verbundene Qualität der Eingabeparameter. Für das Brandszenario Einfamilienhaus wird der Brandverlauf in einer komplexen Geometrie mit unterschiedlichen Brandlasten realistisch berechnet. Für den SBI Test und den Cone Kalorimeter Test stehen die Wärmefreisetzungsrate bzw. die Massenverlustrate im Mittelpunkt der Simulation und zeigen eine hohe Übereinstimmung mit den experimentellen Ergebnissen. Für den vertikalen UL 94 Test werden darüber hinaus erstmals das komplexe Zusammenspiel von Pyrolyse, Verbrennung und Tropfverhalten simuliert und die unterschiedlichen Klassifizierungen und Zeitmaßstäbe übereinstimmend mit den Experimenten aus den Berechnungen abgeleitet. Anhand der Beispiele werden erweiterte Anwendungsbereiche von Brandsimulationen durch gezielte Nutzung der polymerwissenschaftlichen Kenntnisse aufgezeigt. Gleichzeitig weisen insbesondere die Untersuchungen zu den Brandszenarien Cone Kalorimeter Test und UL 94 Test auf den wertvollen Beitrag von Brandsimulationen für die Polymerwissenschaft hin. Durch Parametervariationen können aufbauend auf einem validierten Simulationsmodell zusätzliche Erkenntnisse über die Struktur-Eigenschaftsbeziehungen von Polymeren hinsichtlich des Brandverhaltens gewonnen werden, um die Entwicklung flammgeschützter Materialien zielführend zu unterstützen.
138
Das Radarverfahren ist ein schnelles bildgebendes Verfahren für die Untersuchung der inneren Struktur von Stahlbeton-Bauwerken und wird seit längerem erfolgreich für die zerstörungsfreie Untersuchung von Brückenbauwerken eingesetzt. Für die Rekonstruktion der Lage der Bewehrung reicht die Annahme einer homogenen Materialeigenschaft des Betons meistens aus.
Nähere Untersuchungen der empfangenen Streuungen der Radarwellen zeigen, dass neben der starken Streuung der Radarwellen an den metallischen Einbauteilen auch schwache Streuungen existieren. Diese schwachen Streuungen im Beton wurden nun erstmals in dieser Arbeit untersucht und können der Heterogenität des Betons zugeordnet werden. Die schwachen Streuungen entstehen durch den Permittivitätskontrast und die Geometrie der Gesteinskörnung im umgebenden Zementstein des Betons.
Im Rahmen dieser Arbeit wurden die schwachen Streuungen im Beton für unterschiedliche Gesteinskörnungen charakterisiert und der Einfluss des Wellenlängenbereichs der Radarwellen auf die Ergebnisse untersucht. Weiter zeigt die Arbeit, dass die Streuungen an der Gesteinskörnung einen wesentlichen Einfluss auf die maximale Eindringtiefe von Radarwellen in Beton haben.
123
A new safety characteristic named “dustiness” according to the German guideline VDI 2263 – part 9 is investigated. Dustiness describes the tendency of a powder to form airborne dust by a prescribed mechanical stimulus. Dusts often behave differently in a dust/air mixture or in the case of a dust explosion, even if they have comparable physical properties such as particle size and density. In order to look into the effects of dustiness on dust cloud Formation and explosion properties experiments and simulations in a 75 L vertical dust Dispersion glass tube apparatus were carried out. In a second step industrial-scale experiments were carried out in a 50 m³ silo.
Experiments showed that particle size and density are not the only factors which influence dustiness, since the chosen dusts with comparable densities and particle size distributions showed very different behavior in the flow. Other dust properties such as particle shape, specific surface area, humidity and agglomeration processes have an influence which can outweigh size and density. Preliminary explosion experiments showed that dustiness has an influence on the reduced explosion pressure and pressure rise in a vented 75 L test apparatus. In order to verify the results for applications in the process industries further tests with different settings were carried out in industrial-scale experiments. First dust concentration
measurements were done in order to evaluate the reproducibility of filling processes.
Experiments showed that single tests differed by 30 % and more from the average depending on dust sample and filling method. First explosion experiments with a worst-case
scenario in terms of high turbulence and homogenous dust distribution showed that the maximum reduced explosion pressures were well below the calculated values. Reduced
explosion pressures and rates of pressure rise of the hree tested dust were as their Explosion characteristics pmax and KSt let suggest.
The Euler/Lagrange and the Euler/Euler approaches were compared simulating dust/air mixtures. Especially sedimentation and the ability of the approaches to simulate the tendency of dust to stay airborne were investigated. The Euler/Lagrange approach is better
suited for simulating local dust concentrations, particle size distributions and particle forces.
With the Euler/Euler method it is possible to achieve fast solutions for one specified diameter.
The computational fluid dynamics code ANSYS CFX R14 was used for all simulations.
82
In der vorliegenden Arbeit wird die Online-Kopplung der Asymmetrischen Fluss- Feldflussfraktionierung (A4F) mit Kleinwinkelröntgenstreuung (SAXS) als leistungsfähiges analytisches Werkzeug vorgestellt und auf aktuelle Problemstellungen in der Nanopartikelanalytik wie auch auf Modellsysteme praxisrelevanter Polymere angewandt. Die A4F bietet die Möglichkeit, Suspensionen oder Lösungen von Teilchen ihrer Größe nach aufzutrennen. Bedingt durch das besondere Trennprinzip werden auf den Analyten nur minimale Scherkräfte wirksam, die im Gegensatz dazu bei anderen chromatographischen Methoden in erheblichem Maße auftreten können. Dies ermöglicht auch die Bearbeitung von diesbezüglich sehr empfindlichen Proben ohne dabei deren Integrität zu manipulieren. Die Kleinwinkelröntgenstreuung ermöglicht die zerstörungsfreie Untersuchung von Strukturmerkmalen in einer Größendomäne von etwa einem bis einhundert Nanometern. Durch die Kopplung mit A4F wird die Komplexität der ausgewählten Systeme maßgeblich verringert, die sonst aufgrund der sehr breiten Größenverteilungen der enthaltenen Teilchen schwer zu charakterisieren sind. Es konnten mit dieser Methodik detaillierte Aussagen über die Probenbeschaffenheit in Hinblick auf Teilchengestalt, -größenverteilung bzw. -konformation getroffen werden. Die Einbindung eines Dynamischen Lichtstreudetektors in den Kopplungsaufbau ließ noch weitergehende Aussagen zu. So wurde gezeigt, dass eine Nanopartikelsuspension sowohl hinsichtlich der Form, Größe und Größenverteilung der Nanopartikelkerne als auch der Stärke der Stabilisatorschicht in einem Online-Experiment charakterisiert werden kann. Diese Parameter sind wichtige Kenngrößen, die sowohl für die Funktionalität als auch Bioverfügbarkeit und Toxizität von Nanopartikeln maßgeblich sind und auf diese Weise zeitsparend und mit hoher Präzision erhalten werden konnten. Desweiteren wurde diese Kopplungsmethode erstmals auf verschiedene Polymersysteme wie Polyvinylpyrrolidon sowie starke und schwache Polyelektrolyte mit Erfolg angewendet. Durch die eingesetzte Größentrennung können Proben in einem sehr weiten Molmassenbereich fraktioniert werden, die häufig zu unerwünschten Wechselwirkungen in trägerbasierten Trennmethoden neigen. Durch die verwendete Röntgenstreuung konnten auch Strukturdetails kleiner Polymer- Größenfraktionen aufgelöst werden, die mit üblichen Standardverfahren nicht mehr zugänglich sind.
28
Bedingt durch die allgegenwärtige Notwendigkeit der Einsparung fossiler Brennstoffe steigt auch in der Kraftfahrzeugindustrie der Druck zur verstärkten Anwendung von intelligentem Leichtbau. Um dafür die bisher vornehmlich in der Luftfahrtindustrie eingesetzten, hochfesten β-Titanlegierungen für kostensensiblere Bereiche attraktiver zu machen, wurde die metastabile Legierung Ti-6,8Mo-4,5Fe-1,5Al (Handelsname: Timetal LCB) entwickelt. Ihr Einsatzschwerpunkt sind Strukturbauteile im Fahrwerksbereich von Kraftfahrzeugen. Die vorliegende Arbeit beschäftigt sich mit mechanischen Eigenschaften von Timetal LCB und sucht Hinweise für deren mikrostrukturelle Ursachen. Zu diesem Zweck wurden Proben aus für die Herstellung von Kraftfahrzeug-Fahrwerksfedern bestimmtem Draht dieses Materials entnommen und uniaxialen Zug- und Ermüdungsversuchen unterzogen. Dabei wurden sowohl Proben im Lieferzustand (gerollt im α+β-Gebiet und lösungsgeglüht) als auch im endwärmebehandelten Zustand (wie vor, plus 4 Stunden Laborwärmebehandlung bei 540°C) untersucht. Das mechanische Versuchsprogramm umfasste Zugversuche, uniaxiale Ermüdungsversuche im Zugschwellbereich (R = 0,1) in Spannungskontrolle und, erstmalig für dieses Material, gesamtdehnungsgeregelte uniaxiale Ermüdungsversuche, ebenfalls mit R = 0,1. Dabei wurden Versuche in Laboratmosphäre sowohl bei Raumtemperatur als auch unter 200°C bis zum Bruch durchgeführt und die erhaltenen Versuchsdaten ausgewertet. Zur Begutachtung der mikrostrukturellen Vorgänge wurden neben den üblichen licht- und rasterelektronenmikroskopischen Verfahren in größerem Umfang TEM-Untersuchungen unternommen. Die Auswertung der Zugversuchsdaten ergab ein nahezu ideal-plastisches Verhalten sowohl des lösungsgeglühten als auch des endwärmebehandelten Zustands. Bei 200°C Temperatur zeigte der endwärmebehandelte Zustand ein leichtes Verfestigungsverhalten bei reduzierter Steifigkeit und Zugfestigkeit. Die spannungsgeregelten Ermüdungsversuche ergaben leichtes zyklisches Entfestigungsverhalten ohne Sättigung und ausgeprägtes zyklisches Kriechen der endwärmebehandelten Proben bei Raumtemperatur. Versuche in Gesamtdehnungskontrolle hingegen zeigten nach kurzer Verfestigung Sättigung und konstantes Verhalten über die Rest-Versuchsdauer sowohl bei Raumtemperatur als auch bei 200°C bis hin zu Gesamt-Oberdehnungen von 2,5%, erst darüber zeigte sich kontinuierliche Entfestigung. Auffälligkeiten zeigten sich bei den Proben im Lieferzustand bei Raumtemperatur in Gesamtdehnungsregelung, wo das Verhalten der Spannungsantwort wie auch das Bruchverhalten für Versuche mit Gesamt-Oberdehnung von 3...4% stark von den übrigen Zuständen abwich. Als Ursache hierfür wird verformungsinduzierte α- Phasenausscheidung in Nanostruktur vorgeschlagen. Alle dehnungsgeregelten Versuche unterlagen ausgeprägter zyklischer Relaxation. Mit Hilfe der TEM wurden lamellare Substrukturen innerhalb der β-Phase des lösungsgeglühten Lieferzustands beobachtet. Ermüdungsbelastung führt zu weiterer Segmentierung dieser Lamellenstruktur. Im wärmebehandelten Zustand trägt die α-Phase den größten Teil der Verformung, erkennbar an ausgeprägten α-Subkornstrukturen in den ermüdeten Zuständen. Es wurden Hinweise auf Subkornrotation gefunden. Der Einfluss der Temperatur von 200°C bei der Versuchsführung ist mikrostrukturell minimal.
112
Austenitic welds and dissimilar welds are extensively used in primary circuit pipes and pressure vessels in nuclear power plants, chemical industries and fossil fuelled power plants because of their high fracture toughness, resistance to corrosion and creep at elevated temperatures. However, cracks may initiate in these weld materials during fabrication process or stress operations in service. Thus, it is very important to evaluate the structural integrity of these materials using highly reliable non- destructive testing (NDT) methods. Ultrasonic non-destructive inspection of austenitic welds and dissimilar weld components is complicated because of anisotropic columnar grain structure leading to beam splitting and beam deflection. Simulation tools play an important role in developing advanced reliable ultrasonic testing (UT) techniques and optimizing experimental parameters for inspection of austenitic welds and dissimilar weld components. The main aim of the thesis is to develop a 3D ray tracing model for quantitative evaluation of ultrasonic wave propagation in an inhomogeneous anisotropic austeniticweld material. Inhomogenity in the anisotropic weld material is represented by discretizing into several homogeneous layers. According to ray tracing model, ultrasonic ray paths are traced during its energy propagation through various discretized layers of the material and at each interface the problem of reflection and transmission is solved. The influence of anisotropy on ultrasonic reflection and transmission behaviour in an anisotropic austenitic weld material are quantitatively analyzed in three dimensions. Theultrasonic beam directivity in columnar grained austenitic steel material is determined three dimensionally using Lamb’s reciprocity theorem. The developed ray tracing model evaluates the transducer excited ultrasonic fields accurately by taking into account the directivity of the transducer, divergence of the ray bundle, density of rays and phase relations as well as transmission coefficients. The ray tracing model is able to determine the ultrasonic wave fields generated by a point source as well as finite dimension array transducers.
169
Die Werkstoffgruppe der Faser-Kunststoff-Verbunde (FKV) hat sich aufgrund ihrer hervorragenden Leichtbaueigenschaften unter anderem im Sportgerätebau, in der Luft- und Raumfahrt und in der Windenergieindustrie etabliert. Die so hergestellten Strukturen sind in der Regel nicht nur mechanischen Belastungen, sondern auch thermischen Lasten in einem breiten Temperaturspektrum ausgesetzt. Dennoch ist die Auswirkung des Temperatureinflusses bei einer Kombination von thermischer und mechanischer Last auf die Lebensdauer von Strukturen aus FKV bisher nur wenig untersucht.
Im Rahmen dieser Arbeit wird der Einfluss von Temperaturen zwischen 213 K und 343 K auf einen Glasfaser-Epoxidharz-Verbund experimentell untersucht. Das Material wird in diesem Temperaturbereich eingehend charakterisiert: Es werden sowohl die thermomechanischen Eigenschaften von Faser- und Matrixwerkstoff als auch die des Verbundes ermittelt. In einem weiteren Schritt wird dann der Einfluss der Temperatur auf die Schädigungsentwicklung im quasi-statischen Lastfall sowie unter schwingender Ermüdungsbeanspruchung bei verschiedenen FKV-Mehrschichtverbunden analysiert.
Basierend auf den experimentellen Daten wird ein Zusammenhang zwischen der Schädigung und der Anstrengung der Matrix innerhalb der Einzelschicht demonstriert. Die Matrixanstrengung wird mithilfe eines mikromechanischen Modells unter Berücksichtigung der thermomechanischen Eigenspannungen analytisch berechnet. Bei Querzugbeanspruchung kann gezeigt werden, dass eine Vorhersage der Schädigung in Abhängigkeit der Volumenänderungsenergie innerhalb der Matrix getroffen werden kann.
Mithilfe des Konzepts der Matrixanstrengung ist eine Vorhersage der Lebensdauer des Werkstoffs unter schwingender Ermüdungsbeanspruchung in Abhängigkeit der Einsatztemperatur möglich.
72
Die Erkenntnis, dass die Phasenumwandlung bei der Schweißeigenspannungsentstehung hochfester Stähle eine bedeutende Rolle spielt, gibt es bereits seit langer Zeit. Bisher existierten jedoch keine Ansätze, diesen Effekt praktisch zur Schweißeigen- spannungskontrolle zu nutzen. Neuartige Low Transformation Temperature (LTT) Legierungen bieten aufgrund ihrer charakteristischen chemischen Zusammensetzung die Möglichkeit, hochfeste Stähle auf deren Festigkeitsniveau zu fügen. Die martensitische Phasenumwandlung soll zudem eine gezielte Einstellung der Schweißeigenspannungen erlauben. Die im Schrifttum vorliegenden Untersuchungen zu diesem Thema sind zwar zahlreich, bieten jedoch nur wenige Erkenntnisse zur Wechselwirkung zwischen der Phasenumwandlung und den resultierenden Schweißeigenspannungen. Zur Klärung dieser Fragestellung wurde basierend auf Literaturauswertungen eine Matrix von LTT-Legierungen verwirklicht, welche hinsichtlich des Gefüges, der mechanischen Eigenschaften und der Umwandlungstemperaturen charakterisiert wurden. Weiterhin konnten im Rahmen dieser Arbeit erstmals In-situ-Beugungsexperimente während des Schweißens unter Anwendung energiedispersiver Methoden realisiert werden. Die Neukonzeption und Verwirklichung einer Schweißvorrichtung speziell für den Einsatz an Synchrotronstrahllinien ermöglichte die bislang einzigartige In-situ-Analyse der Umwandlungsvorgänge während des Schweißens mit LTT-Legierungen. Im Zuge dieser Experimente konnte neben den im Schweißgut vorherrschenden Umwandlungstemperaturen zusätzlich die Umwandlungskinetik dieser Legierungen ermittelt werden. Die Auswirkungen des Umwandlungsverhaltens wurden anhand der Eigenspannungsverteilungen in der Oberfläche variierender Probengeometrien analysiert. Die Ergebnisse verdeutlichen einerseits, dass die mittels der LTT-Legierungen angestrebte Eigenspannungskontrolle tatsächlich möglich ist. Dies zeigt sich insbesondere dann, wenn eine weitgehend freie Schrumpfung der Naht vorliegt. Mit zunehmender Schrumpfbehinderung ergibt sich jedoch eine Verschiebung des Eigenspannungsniveaus in den Zugbereich. Dies ist bei den hier betrachteten Legierungen vornehmlich in Nahtquerrichtung ausgeprägt. Dagegen ist das Eigenspannungsniveau in Nahtlängsrichtung nahezu unabhängig von den Schrumpfbedingungen. Anhand von Eigenspannungstiefengradienten ließ sich feststellen, dass sich die zusätzliche Schrumpfbehinderung in einer Parallelverschiebung des Eigenspannungsniveaus im Schweißgut äußert. Die Anwendung energiedispersiver Beugungsmethoden erlaubte zudem erstmals die Eigenspannungsermittlung in der parallel zum Martensit vorliegenden austenitischen Phase der LTT-Legierungen. Ergebnisse, die unter Laborbedingungen gewonnen werden, bedürfen zumeist der Überprüfung unter realen Fertigungsbedingungen. Zu diesem Zweck wurde ein Bauteilschweißversuch in einer speziellen Großprüfanalage durchgeführt. Unter konstruktiver Schrumpfbehinderung gelang es, die lastabbauende Wirkung eines spezifischen LTT-Schweißzusatzes anhand einer ausgeprägten Spannungsreduktion während des Schweißens zu belegen. Insgesamt wurde der Nachweis erbracht, dass das Konzept der Low Transformation Temperature (LTT) Legierungen zielführend ist und die nachgewiesene Austenit-Martensitumwandlung einen signifikanten Effekt auf das Eigenspannungsniveau ausübt.