Angewandte Physik
Filtern
Erscheinungsjahr
- 2020 (65) (entfernen)
Dokumenttyp
- Vortrag (65) (entfernen)
Referierte Publikation
- nein (65)
Schlagworte
- Wasserstoff (4)
- Ageing (3)
- Compensation method (3)
- Heat pump (3)
- Load-based testing (3)
- Safety (3)
- Ageing Management (2)
- Alkali ions (2)
- Cladding Embrittlement (2)
- Convection coefficient (2)
- Corrosion (2)
- Energieeffizienz (2)
- Energieverbrauchskennzeichnung (2)
- Energy efficiency (2)
- Explosionsschutz (2)
- Extended Storage (2)
- Fatigue (2)
- Fire (2)
- Geothermal (2)
- Heat flux (2)
- Interim storage (2)
- Metal seal (2)
- Propane gas fire test facility (2)
- Reaction sintering (2)
- Ring Compression Test (2)
- Round robin test (2)
- Seasonal performance (2)
- Sicherheit (2)
- Sintering (2)
- Sintering additives (2)
- Spent Nuclear Fuel (2)
- Spent nuclear fuel (2)
- Thermoelectrics (2)
- Verteilte faseroptische Sensorik (2)
- Ökodesign (2)
- ADR (1)
- Acceptance rate (1)
- Additiver Fertigung (1)
- Adiabatic surface temperature (1)
- Ageing management (1)
- Aging management (1)
- Air Conditioners (1)
- Air conditioner (1)
- Akzeptanz (1)
- Alternative Antriebe (1)
- Ansys Autodyn (1)
- Approval (1)
- Auswirkungsbetrachtung (1)
- Automated manufacturing (1)
- Batch testing (1)
- Behälterversagen (1)
- Bergungsdruckgefäß (1)
- Biobrennstoff (1)
- Biomimetics (1)
- Buckling piles circular shells (1)
- CCUS (1)
- CFD (1)
- CO2-corrosion (1)
- Calcium cobaltite (1)
- Calcium manganate (1)
- Calorimetric test (1)
- Carbon Capture (1)
- Coefficient of performance (1)
- Component testing (1)
- Compression Set (1)
- Compression set (1)
- Computed Tomography (1)
- Copper (1)
- Crack detection (1)
- DAS (1)
- DPC (1)
- Damage characterization (1)
- Data Fusion (1)
- Deep foundations (1)
- Degradation (1)
- Design assessment of RAM packages (1)
- Digital Detector Arrays (1)
- Disposal (1)
- Drop tests (1)
- Druck-Volumen-Produkt (1)
- Druckbehälter (1)
- Drucker-Prager (1)
- Dynamic method (1)
- Dynamic test method (1)
- EU-Recht (1)
- Eigenspannungen (1)
- Encapsulations for damaged spent nuclear fuel (1)
- Energy Label (1)
- Energy label (1)
- Erdgas (1)
- Erdgasinfrastruktur (1)
- Explosion Limits (1)
- Explosion Protection (1)
- Explosion limits (1)
- Explosionsgrenzen (1)
- FAME (1)
- Fahrzeugbrand (1)
- Fatigue tests (1)
- Femtosecond laser ablation (1)
- Fibre break (1)
- Final disposal (1)
- Fire reference (1)
- Fragment (1)
- Fuel rod (1)
- Gas behaviour (1)
- Gefahrgutrecht (1)
- Gefahrguttransport (1)
- Glass fiber reinforced polymers (1)
- Glass transition (1)
- HR-CS-AAS (1)
- Heat Pumps (1)
- Heizöl (1)
- Hochfester Stahl (1)
- Hybrid laser arc welding (1)
- Hydrogen (1)
- IAEA (1)
- Ignition Source (1)
- Ignition energy (1)
- Ignition source (1)
- Impact (1)
- Infrastrukturmonitoring (1)
- Inspection (1)
- Internal shock absorber (1)
- Isotope analysis (1)
- KI (1)
- Kaltrisssicherheit (1)
- Kerntechnische Entsorgung (1)
- Kompetenzzentrum H2Safety@BAM (1)
- Konsequenzbegrenzung (1)
- Korrosion (1)
- Korrosionsschutz (1)
- Kühlmöbel (1)
- Künstliche Intelligenz (1)
- Künstliche Neuronale Netze (1)
- LCF (1)
- LNG (1)
- Laminography (1)
- Large scale fire testing (1)
- Laser ablation (1)
- Laser beam welding (1)
- Laser-induced periodic surface structures (LIPSS) (1)
- Laser-induced periodic surface structures, LIPSS (1)
- Lead (1)
- Leakage rate (1)
- Lebensdauervorhersage (1)
- Leitfaden (1)
- Lithium batteries (1)
- Lithiumbatterien (1)
- Load-Based Test Method (1)
- Low temperature (1)
- MSG-Schweißen (1)
- Machine Learning (1)
- Machine learning (1)
- Material properties and compatibility (1)
- Mean burst pressure (1)
- Mechanistic Modelling (1)
- Metal (1)
- Minimum Ignition Energy (1)
- Minimum burst ratio (1)
- Monte-Carlo Simulation (1)
- Monte-Carlo-Experiment (1)
- Multiscale model (1)
- New energy carriers (1)
- Notch stress approach (1)
- O-ring (1)
- Offshore geomechanics (1)
- Offshore wind energy (1)
- Offshore-Windenergieanlagen (1)
- Pipeline (1)
- Planar tomography (1)
- Polymer membranen (1)
- Population (1)
- Post-impact evaluation (1)
- Pressure Vessel (1)
- Production scatter (1)
- Propane (1)
- Radioaktives Material (1)
- Reduced volume method (1)
- Renewable energy (1)
- Ressourceneffizienz (1)
- Round Robin Test (1)
- Rubber seal (1)
- Rückbau (1)
- Safe handling (1)
- Safety Assessment (1)
- Safety assessment (1)
- Saline brine (1)
- Sample performance chart (1)
- Scarf repairs (1)
- Schwergas (1)
- Seal (1)
- Seal performance (1)
- Semiconductor (1)
- Sensors (1)
- Sequential analysis (1)
- Ship building (1)
- Sicherer Umgang (1)
- Sicherheitstechnische Eigenschaften (1)
- Silver precipitates (1)
- Silver-glass metallization paste (1)
- Silver-glass-metallization-paste (1)
- Simulation (1)
- Spent fuel behaviour (1)
- Statistische Bewertung (1)
- Steel (1)
- Steel structures (1)
- Stress relaxation (1)
- Structural stress approach (1)
- Störfall (1)
- Supermarktkälte (1)
- Surface functionalization (1)
- Synthesegas (1)
- Synthetic Gas (1)
- Testing (1)
- Transport (1)
- Transport and storage cask (1)
- Transport- und Lagerbehälter (1)
- Transportbehälter (1)
- Tubular X-joints (1)
- Type IV pressure vessels (1)
- UN-Modellvorschriften (1)
- Verteilte faseroptische akustische Sensorik (1)
- Viscosity (1)
- Volumenbegrenzung (1)
- Wasserstoffspeicher (1)
- Wasserstoffstrategie (1)
- Wilhelm Conrad Röntgen (1)
- Wind turbine blade shells (1)
- X-Ray (1)
- Zulassungspflichtige Versandstücke (1)
- Zustandsüberwachung (1)
- Zündenergie (1)
- Zündquellen (1)
- air conditioner (1)
- energy label (1)
- test method (1)
Organisationseinheit der BAM
- 3 Gefahrgutumschließungen; Energiespeicher (27)
- 7 Bauwerkssicherheit (11)
- 3.3 Sicherheit von Transportbehältern (10)
- 3.5 Sicherheit von Gasspeichern (9)
- S Qualitätsinfrastruktur (8)
- S.3 Ökodesign und Energieverbrauchskennzeichnung (8)
- 2 Prozess- und Anlagensicherheit (7)
- 2.1 Sicherheit von Energieträgern (7)
- 3.4 Sicherheit von Lagerbehältern (7)
- 5 Werkstofftechnik (7)
Eingeladener Vortrag
- nein (65)
Test methods for heat pumps
(2020)
The development within the offshore wind sector towards more powerful turbines combined with increasing water depth for new wind parks is challenging both the designer as well as the manufacturer of bottom fixed support structures. Besides XL-monopiles, the market developed an innovative and economic jacket support structure which is based on automatically manufactured tubular joints combined with standardized pipes. Besides the improvements for a serial manufacturing process the automatically welded tubular joints show a great potential in terms of fatigue resistance e.g. due to a smooth weld geometry without sharp notches. However, these benefits are not considered yet within the fatigue design process of automatically manufactured jacket substructures according to current standards due to the lack of suitable S-N curves. Therefore, 32 axial fatigue tests on single and double-sided automatically welded tubular X-joints have been performed to determine a new hot spot stress related S-N curve. Based on these constant amplitude fatigue tests a new S-N curve equal to a FAT 126 curve was computed which implicitly includes the benefits of the automatically welding procedure.
In Germany, spent nuclear fuel and vitrified high active waste is stored in dual purpose casks (DPC) at interim storage facilities. In order to ensure the transportability of the DPC to a final repository in future, the maintenance of the package design approval is realized. Therefore, the assessment of possible ageing effects during interim storage is necessary to ensure an evaluation of the transportability. The lecture presents BAM's current ageing evaluation concept in the field of trasnport law.
Outcomes of Three Large-Scale Fire Reference Tests Conducted in Propane Gas Fire Test Facility
(2020)
Packages for the transport of high-level radioactive material are designed to withstand severe accidents. Hypothetical severe accident conditions are defined in the IAEA Regulations for the Safe Transport of Radioactive Materials. One of these accident conditions is the thermal test, mainly consisting of a 30 minute fully engulfing 800°C pool fire or an equally severe fire test. The heat fluxes into the package depend substantially on the fire characteristics and the surface temperature of the package. Fire tests can be performed at BAM on a propane gas fire test facility. In order to investigate the heat fluxes over a wide range of surface temperatures in this test facility a fire reference package was designed for multiple use. The package represented the outer geometry of a specific transport cask for radioactive waste. The fire reference package is a closed steel sheet cylinder with a wall thickness of 10 mm, a length of 1500 mm and a diameter of 1050 mm. The package was instrumented with thermocouples and filled with heat resistant insulation material. Three open-air fire tests were performed in the BAM propane gas fire test facility. The flames exposure time period varied slightly for the fire tests. The wind direction as well as the wind speed were measured and changed between and during the tests. Test stand parameters such as wind shield location and propane gas volume flow were chosen constant for the three tests. The locally measured fire reference package steel sheet temperatures were used for the calculation of heat fluxes as function of time and surface temperature. The measured temperatures allowed further calculations. In a first approach effective fire characteristics of the propane gas fire, including the flame temperature, the fire convection coefficient and a radiation exchange coefficient mathematically describing the determined average heat flux over the surface temperature were calculated.
Packages for the transport of high-level radioactive material are designed to withstand severe accidents. Hypothetical severe accident conditions are defined in the IAEA Regulations for the Safe Transport of Radioactive Materials. One of these accident conditions is the thermal test, mainly consisting of a 30 minute fully engulfing 800°C pool fire or an equally severe fire test. The heat fluxes into the package depend substantially on the fire characteristics and the surface temperature of the package. Fire tests can be performed at BAM on a propane gas fire test facility. In order to investigate the heat fluxes over a wide range of surface temperatures in this test facility a fire reference package was designed for multiple use. The package represented the outer geometry of a specific transport cask for radioactive waste. The fire reference package is a closed steel sheet cylinder with a wall thickness of 10 mm, a length of 1500 mm and a diameter of 1050 mm. The package was instrumented with thermocouples and filled with heat resistant insulation material. Three open-air fire tests were performed in the BAM propane gas fire test facility. The flames exposure time period varied slightly for the fire tests. The wind direction as well as the wind speed were measured and changed between and during the tests. Test stand parameters such as wind shield location and propane gas volume flow were chosen constant for the three tests. The locally measured fire reference package steel sheet temperatures were used for the calculation of heat fluxes as function of time and surface temperature. The measured temperatures allowed further calculations. In a first approach effective fire characteristics of the propane gas fire, including the flame temperature, the fire convection coefficient and a radiation exchange coefficient mathematically describing the determined average heat flux over the surface temperature were calculated.
Composite pressure vessels (CPVs) are becoming the state of the art for storage for compressed hydrogen (CH2) in automotive applications. There is a strong interest of car manufacturers to use lightweight and less-costly gas storage units. In order to reduce the necessary amount of expensive carbon fibre, the nominal safety margins are becoming gradually smaller, pushing the limits of the regulations for type approval. At the same time, the total volume of these vessels increases to extend the range of the vehicles, increasing the consequences for worst-case scenarios like the rupture of the CPVs in service.
This presentation presents insights gained in the project “TAnk HYdrogen Automotive” (TAHYA). Its aim is to improve the safety of current regulations for type approval of pressure vessels for the use in hydrogen fueled vehicles, namely GTR No. 13 and ECE R 134.
For the assessment of safety, the probabilistic approach developed by division 3.5 of BAM is used. Monte-Carlo-Simulations were conducted leading to the identification of several weak spots, mainly found in the burst test and the batch test.
By changing the requirements for burst tests and the approach for batch tests, the identified weak spots can be strongly reduced.
State of the art and development perspectives of deep foundations for offshore wind converters
(2020)
This presentation provides an overview of the main geotechnical aspects associated with deep foundations in the context of offshore wind generation. The most common deep foundation typologies (large diameter monopiles and multipile typologies) as well as new trends under development (e.g. suction buckets) and their current limits will be briefly described. The talk concludes with a brief review of advanced topics not covered in classical pile design, such as hydromechanical coupling effects (pore pressure generation), cyclic accumulation of deformations, cyclic degradation of axial capacity or pile-setup gains.
This contribution provides current findings regarding materials susceptibility for CCUS applications. Basing on results gathered in 2 German long-term projects (COORAL and CLUSTER) suitable materials are introduced as well as dominating impurities of the CO2 stream and corrosion mechanisms. Investigations cover the whole CCUS process chain and provide the following recommendations for certain parts. Commercially available carbon steels are suitable for compression and pipelines as long as moisture content and impurities are limited (water 50 to 100 ppmv, SO2 and NO2 ca. 100 ppmv).
Corrosion rates increase with increasing water content (0.2 – 20 mm/a).
Condensation of acids and therefore droplet formation is always possible, even at low water contents.
A low SO2 content within the CO2-stream might be more important than a low water content.
Cr13-steels showed a general susceptibility to shallow pitting and pitting. So, they seem to be not suitable for CCUS applications.
Low alloyed steels showed better corrosion behavior (predictable uniform corrosion).
For direct contact with saline aquifer fluids only high alloyed steels shall be used.
Prediction of dynamic effects of reinforced concrete structures under impact loading is a technical challenge. This is a consequence of the great variability of the physical properties resulting from the wide adaptability of reinforced concrete and a consequence of the wide range of impact loading. Experiments and numerical investigations are normally used on a small scale to address the problem. In this paper, impact tests on reinforced conrete plates with the lateral dimensions of 1.5 m x 1.5 m and a thickness of 30 cm are presented. In bending reinforcement, besides the velocity two properties are varied, the diameter and the spatial distribution of the rebars. Experiments are performed at the Otto-Mohr-Laboratory of the Institute of Concrete Structures of the Technische Universit¨at Dresden. Due to the accelerated fall of the impactor the velocity ranges between 20 and 70 m/s. In addition to the measured quantities such as bearing forces, accelerations are also measured at 4 different positions on and under the plate, as well as the deflection at several positions. The measured data are used for the analysis of the damage form and the numerical examinations with the program Ansys Autodyn and the material model after Drucker-Prager. Numerical investigations support the tests, with detailed analysis of individual effects. These numerical computations and the planar tomographic investigations were carried out at BAM in Berlin. With the help of planar tomographic evaluation, the damaged structure is made visible and compared with the numerical results. Influences of the bending reinforcement are explained on the basis of damage evaluation in the local area and on selected measured values. In addition to the test evaluation, the tomographic and numerical methods are presented.
Since geothermal wells are a feasible energy source to replace fossil fuel supply, many technologies have been developed to take advantage of geothermal energy. Nevertheless, service conditions in geothermal facilities are in many cases extreme in terms of corrosion due to the chemical composition of hydrothermal fluids and temperatures. Therefore, materials selection based on preliminary material qualification is essential to guarantee a secure and reliable operation of the facilities. During operation of a geothermal research facility in Groß Schönebeck copper and lead effects have been found downhole. Occurring mechanisms and measures to prevent precipitation or scaling needed to be investigated as well as potential influences of such precipitates on corrosion resistance of metallic materials used for equipment.
This contribution deals with the evaluation of the corrosion behavior of carbon steel and corrosion resistant alloys in copper and/or lead containing artificial geothermal water, simulating the conditions in the Northern German Basin.
The behavior of these materials in an artificial geothermal water obtained by electrochemical measurements and exposure tests are presented. While carbon steel exhibits precipitation and deposition, higher alloyed material shows different response to such species and a higher resistance in saline geothermal water.
Basing on these results the suitability of the investigated corrosion resistant alloy is given for use in such conditions, whereas carbon steel creates difficulties due to its susceptibility to Cu- and Pb-precipitation.
An alternative method for lithium isotope amount ratio analysis is proposed by combining atomic absorption spectrometry with spectra data analysis by machine leaning. It is based on the well-known isotope shift of around 15 pm for the electronic transition at wavelength 670.7845 nm which can be measured by a high-resolution continuum source atomic absorption spectrometer (HR-CS-AAS). For isotope amount ratio analysis, a scalable three boosting machine learning algorithm (XGBoost) was employed and calibrated with a set of samples with a 6Li isotope amount fraction ranging from 99% to 6%. The absolute Li isotope amount fractions of these calibration samples were previously measured by multi-collector inductively coupled plasma mass spectrometry (MC-ICP-MS) and used as ab-initio data for the machine learning algorithm. Validation of the machine leaning model was performed with two standard reference materials (LSVEC and IRMM-016). The procedure was employed for the isotope amount ratio determination of a set of stock chemicals (Li2CO3, LiNO3, LiCl, LiOH, and LiF) as well as a BAM candidate LiMNC cathode reference material. Achieved uncertainties are one order of magnitude higher than those obtained by MC-ICP-MS. This precision and accuracy is nonetheless sufficient to resolve natural occurring variations in Lithium isotope ratios. Also, the LiMNC material was analyzed by HR-CS-AAS with and without matrix purification. The results are comparable within statistical error.
Hydrogen differs from most other flammable gases regarding the safety related properties. Mainly the minimum ignition energy (MIE) is particularly low and the burning velocity is particularly high. Hydrogen mixtures are formed in different hydrogen applications, for example if hydrogen is added to the existing natural gas grid, if synthetic gas (mixture of CO and H2) is produced or in biogas plants. Safety related properties of hydrogen mixtures were determined experimentally and are presented in this presentation. Moreover the accuracy of estimation methods for safety related properties of hydrogen mixtures is evaluated.”
Die Verwendung von Methoden des Maschinellen Lernens (ML) und der Künstlichen Intelligenz (KI) im Fachbereich 8.6 Faseroptische Sensorik wird dargestellt. Die vielfältigen Möglichkeiten, Machine Learning auf Basis Künstlicher Neuronaler Netze (ANN) für eine schnelle und effiziente Datenverarbeitung eizusetzen werden demonstriert. Hierfür werden Beispiele für die Anwendungszwecke Messgrößenberechnung, Entrauschen, Interpolation, Bildverarbeitung und Messdatenauswertung aufgezeigt.
Damaged spent nuclear fuel (DSNF) can be loaded in German dual-purpose casks (DPC) for transport and interim storage. Encapsulations are needed to guarantee a safe handling and a tight closure, separated from the package enclosure. These encapsulations shall be durable and leak-tight for a long storage period, because they are usually not accessible within periodical inspections of the DPC. Due to the general design of DPCs for standard fuel assemblies, specific requirements have to be considered for the design of encapsulations for DSNF to ensure the loading in existing package designs. Especially the primary lid system of a DPC is designed for maximum loads due to the internal impact of the content during drop test conditions. The main difference of encapsulations for damaged spent nuclear fuel is that they have usually a much higher stiffness than standard fuel assemblies. Therefore the design of an internal shock absorber, e.g. at the head of an encapsulation is required to reduce mechanical loads to the primary lid system during impacts.
BAM as part of the German competent authority system is responsible for the safety assessment of the mechanical and thermal package design, the release of radioactive material and the quality assurance of package manufacturing and operation. Concerning the mechanical design of the encapsulation BAM was involved in the comprehensive assessment procedure during the package design approval process. An internal shock absorber was developed by the package designer with numerical analyses and experimental drop tests. Experimental drop tests are needed to cover limiting parameters regarding, e.g. temperature and wall thickness of the shock absorbing element to enable a detailed specification of the whole load-deformation behavior of the encapsulation shock absorber.
The paper gives an overview of the assessment work by BAM and points out the main findings which are relevant for an acceptable design of internal shock absorbers. The physical drop tests were planned on the basis of pre-investigations of the applicant concerning shape, dimension and material properties. In advance of the final drop tests the possible internal impact behavior had to be analyzed and the setup of the test facility had to be validated. The planning, performance and evaluation of the final drop tests were witnessed and assessed by BAM. In conclusion it could be approved that the German encapsulation system for damaged spent nuclear fuel with shock absorbing components can be handled similar to standard fuel assemblies in existing package designs.
The aim of the work presented was the evaluation of corrosion resistance
of various materials in geothermal Waters as a base to create a catalogue of suitable materials for applications in (not only) German geothermal power plants.
Users shall be enabled to have a basis for designing such facilities. High alloyed corrosion resistant alloys are suitable and do not cause copper or lead deposition. They shall be chosen for future design of the piping system, either in massive or in cladded form, if crevices formation with non-metallic materials can be prevented!
Im DGMK-Projekt 780 wurde eine forcierte Prüfmethode entwickelt zur Bestimmung der Beständigkeit von metallenen Werkstoffen gegenüber Brennstoffen aus Mitteldestillaten und Gemischen aus Mitteldestillat und paraffinischen Kohlenwasserstoffen, die jeweils Fettsäuremethylester (FAME) als biogene Komponente enthalten. Bei der Prüfmethode werden Proben des Werkstoffes in einem speziellen Prüfmedien ausgelagert. Die Zusammensetzung von zwei Prüfmedien wurde im Vorhaben erarbeitet. Die Prüfmedien decken für den FAME-Anteil einen Bereich von bis zu 20 % (V/V) ab. Die Auslagerung kann bei geringem Aufwand unter Atmosphärendruck durchgeführt werden.
Die Eignung einer Auswahl von metallenen Werkstoffen und Polymerwerkstoffen, die für Versorgungsanlagen für Mitteldestillat relevant sind, wurde durch Auslagerung in folgenden nicht gealterten Brennstoffen bestimmt: Heizöl EL schwefelarm (B0), Heizöl EL schwefelarm mit 20 % (V/V) FAME (B20), FAME (B100) und hydriertes Pflanzenöl (HVO). Die Temperatur bei der Auslagerung betrug 50 °C für die metallenen Werkstoffe und 40 °C und 70 °C für die Polymerwerkstoffe. Die Ergebnisse der Beständigkeitsbewertung wurden in Beständigkeitslisten zusammengefasst. Die mit dem B20 erhaltenen Werkstoffbeständigkeiten gelten generell für Gemische aus Heizöl EL schwefelarm und FAME mit einem FAME-Gehalt bis zu 20 % (V/V). Sie sind auch auf Gemische aus Dieselkraftstoff und FAME mit einem FAME-Gehalt bis 20 %(V/V) übertragbar.
Die forcierte Prüfmethode kann insbesondere KMUs bei der Weiterentwicklung von bestehenden Produkten und der Entwicklung von neuen Produkten als ein kostengünstiger Schnelltest zur Überprüfung der Werkstoff- und Bauteilbeständigkeit gegenüber Mitteldestillaten mit hohem FAME-Anteil dienen. Sie kann für die Hersteller die Sicherheit erhöhen, dass Bauteile die Freigabeprüfungen der Bauaufsicht bestehen, wobei die Freigabe aber nur für Deutschland gültig ist.
Die Erkenntnisse des Forschungsvorhabens können in eine harmonisierte Europäischen Norm für alternative Brenn- und Kraftstoffe einfließen. Diese ist für die Bauteilhersteller die Voraussetzung für die Erschließung des europäischen Marktes.
Anwendungsfelder von verteilter faseroptischer akustischer Sensorik (DAS) werden anhand von früheren, gegenwärtigen und zukünftigen Projekten an der BAM vorgestellt und die Leistungsfähigkeit von DAS demonstriert. Die dargestellten Anwendungen sind Monitoring von Rohrleitungen, von Unterseekabeln, von Zügen und Gleisen, von Brücken, von Strassen und Verkehr, von Erdbebenauswirkungen in urbanen Gebieten, von Bohrlöchern im Kontext Erdgasspeicher und für Exploration und Monitoring von Untergründen für Geothermie-Anwendungen.
Understanding the failure mechanisms that lead to leakage of rubber seals at low temperatures is important. Rubber properties are highly temperature dependent. Changes in behaviour at low temperatures can result from the rubber-glass transition and for some rubbers by partial crystallisation. Experimental results on the low temperature behaviour of different rubber seals were discussed to help understand seal failure processes.
Wasserstoff unterscheidet sich hinsichtlich der sicherheitstechnischen Eigenschaften von anderen brennbaren Gassen, v.a. durch die sehr niedrige Mindestzündenergie und die sehr hohe Flammengeschwindigkeit. Durch Beimischung von Wasserstoff zum Erdgas ändern sich die sicherheitstechnischen Eigenschaften zum Teil in kritischer Richtung. Bis zu einem Wasserstoffanteil von 10 Mol-% im Erdgas ist aber keine wesentliche Anpassung der Maßnahmen für den Explosionsschutz erforderlich. Synthesgas ist ein weiteres Wasserstoffgemisch das in Zukunft vermutlich zunehmend relevant sein wird. Die beiden Komponenten Wasserstoff und Kohlenmonoxid haben zwar in mancher Hinsicht ähnliche sicherheitstechnische Eigenschaften unterscheiden sich aber auch sehr stark bzgl. der Mindestzündenergie und der Flammengeschwindigkeit.
High conductive silver-glass-metallization-pastes are key components in photovoltaics and advanced microelectronics. However, the underlying mechanisms of liquid phase sintering as silver dissolution, diffusion and reprecipitation are poorly understood so far.
In the current work, the influence of different network modifier in alkali-zinc-borate paste-glasses on liquid phase sintering of silver-glass-composites was studied. Therefore, silver-glass-composites containing 30 vol% glass were prepared, using low melting X2O-ZnO-B2O3 glasses with X = Na, Li, and Rb (NZB, LZB, and RZB). Glass transition temperature, viscosity, glass-silver wetting, crystallization and sintering behavior was studied by means of thermal analysis, dilatometry, heating microscopy and microscopy.
Similar glass transition temperatures of 450 °C (RZB), 460 °C (LZB) and 465 °C (NZB) were found by means of thermal analysis for glasses under study. Also, all glasses have a similar crystallization onset at about 550 °C, even though exhibiting with a different degree of crystallization.
Despite these similarities, however, the sintering behavior, measured in terms of area shrinkage, significantly differs for the composites. This finding indicates a different degree of silver dissolution. Assuming that dissolved silver reduces the viscosity, this effect could explain why glass crystallization starts at lower temperature in the composites. For example, the crystallization peak of LZB at 629 °C measured for pure glass powder compacts was decreased to 586 °C for the composite. Confirmatively, microstructure analyses indicate different degrees of silver dissolution, as e.g. revealed by different amount of silver precipitates within the residual glass phase, and reprecipitation. Best silver dissolution appeared for the RZB glass. Nevertheless, the final densification of RZB was retarded probably due to swelling and crystallization.
For the generation of renewable energy offshore wind farms play an important role. The majority of these wind generators are connected to steel foundation structures. Steady increasing power output of these wind turbines leads to new challenges as well for engineers of the related support structures. Caused by the high-cyclic loading of these structures by wind and waves fatigue plays a very important role. Besides the consideration of fatigue within the design process it is additionally an important topic and challenge to monitor the existing steel structures relating to potential fatigue cracks occurring during their lifetime. This plays a role for a fundamental understanding of mechanisms as investigated in testing but also for inspection in real structures.
Since the structures of the offshore wind generators are very large and in addition partially under water effective and reliable methods for fatigue crack detection are required. This contribution will present results of recent investigations on different crack detection methods applied on high-cycle fatigue tests on small welded steel samples as well as on welded steel components. The comparison of these measurements will show what are the advantages and disadvantages of the different methods and which method is potentially more suitable for the application on real offshore wind structures. It is outlined where challenges for detection methods exist.
Furthermore, in this context the resulting challenges for the execution of material testing especially caused by the increasing dimensions of wind energy converters will by exemplarily presented.
Das Thema Wasserstoff ist an der BAM seit mehr als hundert Jahren aktuell und steht auch gegenwärtig im Zentrum zahlreicher Forschungs- und Kooperationsaktivitäten. Mit der aktuellen Wasserstoff-Strategie der BAM werden wichtige Voraussetzungen dafür geschaffen, dass der Markthochlauf gelingt und die technische Sicherheit und Überwachung der Infrastrukturen und Anlagen gewährleistet ist – von der Erzeugung, über den Transport bis zur Speicherung und Bereitstellung von Wasserstoff als Energieträger der Zukunft.
Packages for the transport of high-level radioactive material are designed to withstand severe accidents. Hypothetical severe accident conditions are defined in the IAEA Regulations for the Safe Transport of Radioactive Materials.
One of these accident conditions is the thermal test, mainly consisting of a 30 minute fully engulfing 800°C pool fire or an equally severe fire test. The heat fluxes into the package depend substantially on the fire characteristics and the Surface temperature of the package.
Fire tests can be performed at BAM on a propane gas fire test facility. In order to investigate the heat fluxes over a wide range of surface temperatures in this test facility a fire reference package was designed for multiple use. The package represented the outer geometry of a specific transport cask for radioactive waste. The fire reference package is a closed steel sheet cylinder with a wall thickness of 10 mm, a length of 1500 mm and a diameter of 1050 mm. The package was instrumented with thermocouples and filled with heat resistant insulation material.
Three open-air fire tests were performed in the BAM propane gas fire test facility. The flames exposure time period varied slightly for the fire tests. The wind direction as well as the wind Speed were measured and changed between and during the tests. Test stand parameters such as wind shield location and propane gas volume flow were chosen constant for the three tests. The locally measured fire reference package steel sheet temperatures were used for the calculation of heat fluxes as function of time and surface temperature. The measured temperatures allowed further calculations. In a first approach effective fire characteristics of the propane gas fire, including the flame temperature, the fire convection coefficient and a Radiation exchange coefficient mathematically describing the determined average heat flux over the surface temperature were calculated.
Network modifier ions can decisively influence properties and structure of low melting alkali-zinc-borate glasses and thus cause complex effects on the liquid phase sintering of silver-glass metallization pastes. This effect was studied for X2O-ZnO-B2O3 (X = Li, Na, Rb) glasses for silver-glass metallization pastes. Viscosity and the glass transition temperature, Tg, were measured with rotational viscometry and dilatometry. Dried model pastes with 30 vol% LZB, NZB or RZB glass were prepared for sintering studies by means of heating microscopy measuring the silhouette area shrinkage of uniaxially pressed powder compacts during heating at 5 K/min. For comparison, the silhouette area shrinkage of pure glass and silver powder compacts were determined. Glass-silver wetting was investigated during heating of bulk glass cylinders placed on silver substrates. Glass RZB turned out to have the lowest viscosity among the glasses under study. Its glass transformation temperature, Tg, was found at 444 °C and it caused the lowest sintering onset for its glass and paste powder compacts. Slightly increased values of Tg were found for NZB and LZB (468 °C and 466 °C, respectively) and a slightly retarded sintering was found for both paste powder compacts. These results indicate that liquid phase sintering of silver-glass pastes under air atmosphere is mainly influenced by glass viscosity.
High power laser beam welding has been already introduced in ship building industry since last two decades and is characterized by higher performance as conventional arc welding technologies through its higher welding speed, penetration depth and therefore higher productivity. Moreover, high quality weld joints are achievable thanks to a stronger automatization degree and better repeatability of the process. A further advantage of the laser beam welding is a manufacturing of parts with very low distortion according to much lower heat input, so that rework amount can be reduced significantly. Nevertheless, there are still some unresolved problems limiting the range of application of the technology in part manufacturing within ship building industry, restricted by development and application of new materials or new design of ship vessels.
The present contribution deals with some novel aspects of laser beam welding technology allowing to widen this range significantly. One of the possibilities is to increase the weld seam thickness for single pass laser or laser-hybrid welding is to apply contactless EM-support system based on generation of the Lorentz force counteracting the liquid metal drop out. Also, application of laser-hybrid welding technology for welding novel materials like cold resistant steel X8Ni9 used for construction of LNG tanks brings technological and design advantages comparing to conventional welding technologies by using of a similar alloyed filler wire instead of expensive Ni-based filler material. Finally, it is shown how the application of computational techniques can be used to helps to improve the quality of laser welded joints and avoid the critical weld failure by optimization of the welding process parameters.
The irradiation of solids with high-intensity laser pulses can excite materials into extreme conditions, which then return to equilibrium via various structural and topographical relaxation mechanisms. Thus, ultrafast laser processing can manifest in various morphological surface transformations, ranging from direct contour shaping to large-area-surface functionalization through the generation of self-organized nano- and microstructures. The interaction mechanisms between semiconductors and metals with ultrashort laser pulses have been extensively studied using femtosecond laser sources, generating a general understanding of the main interaction mechanisms present during the processing of those materials. In the specific case of nanometer-scaled laser-induced periodic surface structures (LIPSS), however, the general explanation that fits all the experimental outcomes is still to be completed. The most accepted explanation consists in the interference of the incoming laser pulse with light scattered at the rough surface, e.g. via surface plasmon polaritons. Such scattering and interference effects generate a spatially modulated pattern of the absorbed optical energy featuring maxima and minima with periods very close to the laser irradiation wavelength, λ. One general criterion that allows to classify LIPSS in terms of their spatial periodicity (Λ) for normally incident radiation is the following: low spatial frequency for Λ≈λ, and high spatial frequency for Λ≪λ. In this way, the right combination of irradiation parameters (laser fluence, number of pulses per spot area unit and repetition rate) could be used to cover a wide size range that can ultimately be exploited for different applications in optics, biology, fluidics and tribology among others.
Nature has continuously inspired science when practical problems need to be solved in a functional and efficient way. The challenge for researchers usually consists in the transfer of such biological functionalities to diverse types of technical materials with the available processing technologies. In this regard, femtosecond laser-based approaches offer a large flexibility to modify virtually any material (metals, semiconductors and dielectrics), provide the ability to work under different environment conditions (air, vacuum or reactive atmospheres) and when combined with the proper optics, they offer exceptional spatial resolutions that could be used to mimic effectively very complex functionalities. In the particular case of surface processing, lasers have been proven feasible to functionalize materials by customizing its optical properties, chemical composition and surface morphology in a controllable way and in some cases at industrially relevant speeds. In this work, we present a selection of technical applications based on surface modifications in the form of laser-induced periodic surface structures (LIPSS) to tailor the material properties for utilization in optics, fluid transport, wetting control and tribology.
Nach der Reaktorkatastrophe in Fukushima 2011 hat die Bundesregierung beschlossen die Nutzung der Kernenergie bis zum Jahr 2022 zu beenden. Seitdem erfolgt der Rückbau und die Stilllegung der kerntechnischen Anlagen in Deutschland. Dieser Vortrag erörtert die Herausforderungen, die sich mit dem Transport und der Lagerung von Kernbrennstoffen ergeben und leitet daraus Anforderungen ab, die an Transportbehälter gestellt werden.
The stacking sequence of a real scale type IV pressure vessels has been found. Feasibility study of a multiscale model has been carried out by modifying the original stacking sequence. All of the results were displayed in a Sample Performance Chart (SPC), where different burst pressure in terms of mean and scatter had been found.
Polymers with intrinsic microporosity are promising candidates for the active separation layer in green gas separation membranes and as active materials for electronic applicatons. Here, by means of inelastic neutron scattering, the vibrational density of states (VDOS) and the molecular mobility were investigated for PIM-1, the prototypical polymer with intrinsic microporosity. The results are compared to data measured for a more conventional high-performance polyimide used in gas separation membranes (Matrimid).
The measured data show the characteristic low frequency excess contribution to the VDOS above the Debye sound wave level, generally known as the Boson peak in glass-forming materials. In comparison to the Boson peak of Matrimid, that of PIM-1 is shifted to lower frequencies. This shift is discussed considering the microporous, sponge-like structure of PIM-1 as providing a higher compressibility at the molecular scale than for conventional polymers.
Elastic fixed window scans were measured on a neutron backscattering spectrometer to have an overview about the molecular dynamics at a time scale of ca. 1 ns. The temperature dependence of the estimated mean squared displacement shows a step-like increase in the temperature range from 100 K to 250 K indicating the onset of some molecular mobility. The nature of this motional process was analysed in detail by quasielastic neutron scattering combining Time-of-Flight and backscattering where the data are discussed with regard to both the q- and the temperature dependence.
Die additive Verarbeitung hochfester Feinkornbaustähle mittels Wire Arc Additive Manufacturing (WAAM) ist ein komplexes, aber zugleich auch effizientes Verfahren, bei dem Werkstoff, Bauteilgeometrie und Schweißprozess gezielt aufeinander abgestimmt sein müssen. Ziel dieser Studie war es, einen Zusammenhang zwischen den Prozessparametern und der generierten Schichtgeometrie zu ermitteln. Dazu wurden definierte Referenzkörper mit einem robotergestützten Schweißsystem additiv gefertigt und hinsichtlich Schichthöhe, Wandstärke und Mikrostruktur analysiert. Fokus der Untersuchung waren sowohl konventionelle als auch für die WAAM-Fertigung speziell entwickelte hochfeste Schweißzusatzwerkstoffe. Die geometrischen Eigenschaften additiv gefertigter Bauteile lassen sich insbesondere durch die Faktoren Drahtvorschubgeschwindigkeit und Schweißgeschwindigkeit gezielt einstellen. Jedoch können diese Parameter nicht beliebig variiert werden, auch aufgrund der rheologischen Eigenschaften der Zusatzwerkstoffe. Zu hohe Streckenenergien führen zu lokalen Überhitzungen und Fehlstellen in der generierten Schicht. Undefinierte Fließ- und Erstarrungsvorgänge im überhitzten Bereich erschweren die maßhaltige Fertigung. Deshalb wird bei speziellen WAAM-Schweißdrähten das Fließverhalten gezielt modifiziert, sodass es über einen größeren Temperaturbereich hinweg konstant ist. Erst die Kenntnis über die komplexen Zusammenhänge zwischen den Prozessparametern und der Bauteilgeometrie ermöglicht die Erzeugung exakter Schichtmodelle für die additive Fertigung. Dies bildet die Grundlage für die Bearbeitung weiterer Fragestellungen auf dem Gebiet der additiven Fertigung mit hochfesten Zusatzwerkstoffen und insbesondere deren Anwendung in modernen hochfesten Bauteilen.
In the DECHEMA Virtual Talks, general aspects of the safety and acceptance of hydrogen technologies were presented. How can trust in new technologies be built when past accidents led to myths and fairy tales? The presentation does away with general prejudices and shows that handling hydrogen is neither more unsafe nor safer than handling other fuel gases. The basis for the safe handling of hydrogen is always a risk analysis.
Elastomer seals are used in many industrial applications due to their excellent mechanical properties at a wide range of temperatures. Their high versatility and recovery potential under several load conditions make them well suitable for the application in containers designed for transport, storage and/or disposal of radioactive materials. In containers for low and intermediate level radioactive waste, elastomer seals are used as barrier seals, and as auxiliary seals in storage and transportation casks (dual purpose casks) for heat generating radioactive waste, such as spent fuel and high-level waste. While a seal exchange at defined intervals is typical in many conventional applications, it is impossible or at least hard to perform when principles of minimization of radiation exposure have to be considered and prohibit an unnecessary cask handling. An extensive knowledge of the change of the elastomer’s properties during aging and the availability of reliable end-of-lifetime criteria to guarantee the permanent safe enclosure of the radioactive material is mandatory. As BAM is involved in most of the national cask licensing procedures and in the evaluation of cask-related long-term safety issues, great efforts have been already made and are still planned to scientifically support this task.
Compression stress relaxation and compression set were identified as key indicators of elastomer long-term performance and quantitatively investigated in comprehensive test programs. Among other representative types of elastomers, specimens made from ethylene propylene diene rubber (EPDM) were tested before, during and after aging to capture the most important of their complex mechanical properties.
In the presented study, exemplary results were used to simulate the compression stress relaxation and the compression set of elastomer O-rings during aging. Regarding the influence of temperature, the time temperature superposition principle is applied in the relaxation analysis of elastomer O-rings. The proposed model is implemented in the commercial finite element software ABAQUS/Standard® [1] with a sequential temperature displacement coupling. Numerical results match the experimental compression stress relaxation measurements well. The prediction of compression set values after long-term aging shows a relatively good agreement with the experimental results. Nevertheless, all input parameters derived from the specimen tests, additional assumptions concerning boundary conditions and modeling strategy are discussed with regard to the identified slight discrepancies.
The possibility to extend the finite element model to represent the O-ring seal’s ability to recover after a (fast) partial release is taken into account
Der Markt von LNG als Transportgut und als Kraftstoff ist seit Jahrzehnten kontinuierlich am Wachsen, wobei das Hauptanwendungsgebiet im Schiffsverkehr lag. LNG ist verflüssigtes Erdgas mit Hauptbestandteil Methan, das neben fossilen, aus erneuerbaren Quellen, wie synthetischen Methan oder Biogas, gewonnen werden kann. LNG hat als Kraftstoff sehr gute Eigenschaften dessen Potenzial als alternativer Kraftstoff zu Diesel im Schwerlast- und Fernverkehr gesehen wird. Dabei weist LNG gegenüber Diesel geringere Emissionen von CO2, Feinstaub, Stickoxiden und Lärm auf und hat gegenüber anderen erneuerbaren Energiespeichern wie CNG, Elektrobatterien oder Wasserstoff die höchste volumetrische und zweitgrößte gravimetrische Energiedichte. Neben seinen Vorteilen zu anderen erneuerbaren Energieträgern birgt LNG durch seine sehr niedrige Temperatur von bis zu 160°C und seiner Brennbarkeit aber auch neue Gefahren für Personen und Infrastrukturen.
Zur Bewertung von Gefahren und zur späteren Durchführung von Risikobewertungen bedarf es Methoden und Modellen deren Untersuchung Ziel des Forschungsprojekts war. Schwerpunkt der Untersuchung stellt die Freisetzung von LNG in Tunnel, mit sich anschließender Stoffausbreitung und verzögerter Zündung des Kraftstoff-Luftgemisches dar. Unfallszenarien mit Brandereignissen in Tunnel haben gezeigt, dass diese meist mit hohen Personen, Bauwerks und volkswirtschaftlichen Schäden verbunden sind. Des Weiteren zeigten Untersuchungen das von Gasexplosionen in Umschließungen wie sie ein Tunnel darstellt, mehr Gefahren ausgehen als von Gasexplosionen im Freifeld.
Im Vortrag werden die untersuchten Modelle und die aus dem Projekt gewonnenen Erkenntnisse für die Stoffausbreitung und Verbrennung der Gasphase von LNG in Umschließungen vorgestellt.
Understanding the mechanical behaviour of fuel cladding is decisive for an extended dry interim storage period beyond the currently licensed period of 40 years in Germany and subsequent handling, transport, and disposal considering normal and accidental conditions. Since fuel cladding acts as the first barrier for spent fuel, its integrity should be demonstrated to enable safe and secure discharge and handling options after interim storage and subsequent transportation in preparation of final disposal. An established method for characterizing cladding material is the Ring Compression Test (RCT), where a small, cylindrical sample of the cladding tube is subjected to a compressive load. This test is a laboratory representation of a fuel rod load case and has shown a high susceptibility to failure under the occurrence of radial hydrides. Certain hydride morphologies and low temperature might even lead to brittle fracture at very small loads. The BAM research project BRUZL (Fracture mechanical analysis of spent fuel claddings during long-term dry interim storage) aims to study the results of quasi-static RCTs and to establish numerical models to gain an in-depth understanding of the stress state during the experiments. Using a fracture mechanical approach, cases of sudden failure during the RCT procedure are used to characterize the material behaviour and establish a failure criterion. As an integral part of the project BRUZL, quasi-static Ring Compression Tests have been performed to identify all experimental details, which might be helpful for numerical modelling. Unirradiated samples of the cladding material ZIRLO® have been subjected to hydrogen charging and a thermo-mechanical treatment for radial hydride reorientation. Sample preparation, testing procedures, and analysis results are presented. A numerical model has been established and an elastic-plastic material model was derived from as-received RCT samples by inverse finite element analyses. Cohesive zone modelling has been implemented to reproduce sudden load drops during RCT. The project is funded by the Federal Ministry for Economic Affairs and Energy (BMWi) under contract no. 1501561.
An established method for characterizing cladding material is the Ring Compression Test (RCT), where a small, cylindrical sample of the cladding tube is subjected to a compressive load. This test is a laboratory representation of a fuel rod load case and has shown a high susceptibility to failure under the occurrence of radial hydrides. Certain hydride morphologies and low temperature might even lead to brittle fracture at very small loads. The BAM research project BRUZL (Fracture mechanical analysis of spent fuel claddings during long-term dry interim storage) aims to study the results of quasi-static RCTs and to establish numerical models to gain an in-depth understanding of the stress state during such experiments. Using a fracture mechanical approach, cases of sudden failure during the RCT procedure are used to characterize the material behaviour and establish a failure criterion.
As an integral part of the project BRUZL, quasi-static Ring Compression Tests have been performed to identify all experimental details, which might be helpful for numerical modelling. Unirradiated samples of the cladding material ZIRLO® have been subjected to hydrogen charging and a thermo-mechanical treatment for radial hydride reorientation. Sample preparation, testing procedures, and analysis results are presented. A numerical model has been established and an elastic-plastic material model was derived from as-received RCT samples by inverse finite element analyses. Cohesive zone modelling has been implemented to reproduce sudden load drops during RCT.
The project is funded by the Federal Ministry for Economic Affairs and Energy (BMWi) under contract no. 1501561.
Reaction sintering and sintering additives for cost-effective production of thermoelectric oxides
(2020)
Thermoelectric oxides attract much interest recently. Although their thermoelectric properties are inferior to non-oxides, they exhibit distinct advantages. Thermoelectric oxides are stable in air at higher temperatures, their raw materials are less toxic, and more abundant. To enhance attractivity of these materials for industrial applications, production costs need to be reduced.
Conventionally, the legs of thermoelectric generators are sintered from green bodies of previously synthesized powder. Reaction-sintering is a fabrication method without a powder synthesis step, as the final phase is formed during the sintering from a raw material mixture. Moreover, the reduction of chemical potential during reaction-sintering is effective as an additional driving force for sintering. We show that reaction-sintering increases the densification of CaMnO3 (n-type, Sm doped). Consequently, the electrical conductivities improved by about 100 % leading to superior power factors (PF = 230 µW/mK² for CaMnO3).
Another approach to reduce the production costs is to lower the sintering temperature by adding sinter additives. The addition of 4 wt% CuO to CaMnO3 lowers the sinter temperature from 1250 °C to 1050 °C. The achieved power factor PF = 264 µW/mK is more than two times higher as reported in literature for the same dopant.
Thermoelectric materials can convert waste heat directly into electrical power by utilizing the Seebeck effect. Calcium cobaltite (Ca3Co4O9, p-type) and calcium manganate (CaMnO3, n-type) are two of the most promising oxide thermoelectric materials. The performance of these materials is evaluated by the power factor PF = S²∙σ and the figure of merit ZT = (PF ∙ T) / κ, demanding high Seebeck coefficient S, high electrical conductivity σ and low thermal conductivity κ. The latter two are increasing with increasing relative sinter density. According to theory, the relative density of ceramics can be improved by increasing the driving force for sintering. This study investigates different approaches to increase the driving force for sintering of Ca3Co4O9 and CaMnO3 to improve densities and thermoelectric properties.
The following approaches were applied: minimizing the energy input during powder synthesis by calcination, fine milling of the powder, using reaction-sintering without a powder synthesis step, and adding a transient liquid phase by sinter additives.
All different approaches led to an increased densification and thus higher electrical conductivity and higher PF. Thermal conductivity increased as well but not to the same extent. E.g. reaction-sintering increased the densification of Ca3Co4O9 (p-type) and CaMnO3 (n-type). Consequently, the electrical conductivities improved by about 100 % for both oxides leading to superior power factors (PF = 230 µW/mK² for CaMnO3). Although the thermal conductivity increased as well by 8 %, the figures of merit (ZT) were significantly higher compared to conventionally sintered bars. The addition of 4 wt% CuO as a sinter additive to CaMnO3 lowers the sinter temperature from above 1250 °C to below 1100 °C and increases the relative density. Due to the increased density, both electrical conductivity and PF increased by more than 200 % even though the sintering temperature was 150 K lower.