Angewandte Physik
Filtern
Dokumenttyp
- Vortrag (61) (entfernen)
Referierte Publikation
- nein (61) (entfernen)
Schlagworte
- Hydrogen (17)
- Wasserstoff (12)
- Welding (11)
- Hydrogen assisted cracking (10)
- Mikrolegierungseinfluss (7)
- Hochfester Feinkornbaustahl (6)
- Schweißen (6)
- WEZ-Erweichung (6)
- Diffusion (5)
- Gaseous hydrogen (5)
Organisationseinheit der BAM
- 9.0 Abteilungsleitung und andere (61) (entfernen)
The presentation gives an overview of BAM's activities on processing influences and application properties of MPEAs in the form of joined and machined high and medium entropy alloys (CoCrFeMnNi and CoCrNi). In the case of welding, the focus is on defect-free welded joints with sufficient mechanical properties. In the case of machining, the focus is on the possible influence on the surface quality of the materials through adequate milling parameters. In addition, the hydrogen absorption and diffusion properties as well as the electrochemical corrosion behavior are fundamentally examined.
This presentation describes the usability of the hollow tensile specimen technique for in-situ material testing in a hydrogen atmosphere.
In addition, the presentation provides an outlook on the methodology for investigating the suitability of pipeline steels and their weld seams for hydrogen operation.
As energy carrier of the future, green hydrogen can make a decisive contribution to a sustainable energy supply. Particularly important is the decarbonization of heavy industry. Therefore, a reliable supply of hydrogen must be guaranteed. A hydrogen pipeline grid can achieve this purpose. In Europe concrete plans for a hydrogen pipeline grid already exist, as the so called “European Hydrogen backbone”. As building a completely new pipeline grid is economically not justifiable, a dual-way strategy of repurposing natural gas (NG) pipelines and newly built pipelines is intended. Long distance pipeline grids require regular maintenance and repairs. For natural gas (NG) pipelines in-service welding is state of the art. Concepts such as hot-tapping (drilling into pressurized pipelines) and “stoppling” (sealing off pipeline sections after installing bypasses or pressure relieves) allow the repair of damaged pipeline sections or the installation of new branches without shutting the pipeline down, which in most cases isn’t possible from an economic standpoint. The EIGA 121/14 guideline already pointed out in 2014 that “a hydrogen hot-tap shall not be considered a routine procedure”. This shows that the determination of the transferability of these repair concepts to hydrogen pipelines is of utmost importance. Due to the degrading effects of hydrogen on mechanical proper-ties, commonly referred to as “hydrogen embrittlement” it is necessary to understand and investigate the occurring effects. In the special case of repair welding on in-service hydrogen pipelines an increased hydro-gen uptake due to a large heat input and microstructural changes in the material needs to be considered. Therefore, material degradation must be investigated to determine whether modifications of repair procedures are necessary to ensure a reliable and safe hydrogen transportation via pipelines. For this reason, this paper gives an overview on existing weld repair concepts and its risks and limitations in terms of hydrogen absorption and possible embrittlement effects when transferred to hydrogen pipelines. The complexity lies in a large variety of materials (low alloyed steels), pipeline diameters and corresponding welded joints. The material compatibility of materials in used (repurposed NG-pipelines) and new condition must be investigated. Particularly for repurposed/used pipelines the effect of a pre-matured/corroded inner surface and sometimes insufficient documentation of the material “history” needs to be considered. An overview on ongoing and completed R&D-projects with respect to repair concepts for hydrogen pipelines and hydrogen effects on pipeline materials is given. The focus hereby lies on possible methods of material testing and modeling. Its current difficulties, limits and possible solution will be discussed.
Contemporary steels creep-resistant steels like the 13CrMoV9-10 are used as thick plates e.g., for applications in hydrocrackers. The large plate thickness requires high efficiency welding processes like submerged arc welding (SAW) and a mandatory post weld heat treatment (PWHT). The PWHT-parameters stem from a combination of empirical knowledge and traditional experiments on free shrinking (FS) welds. In that connection, the formation of so-called stress-relief cracking (SRC) must be anticipated. The SRC susceptibility of a welded component is a complex combination and interaction of com-ponent specific, thermal, and metallurgical factors. Many of which have to date not been conclusively researched. For example, it is well known that SRCs develop during PWHT due to formation and growth of carbides on prior austenite grain boundaries, resulting in a significant hardness increase (secondary hardening) and toughness decrease. This leads to a high SRC susceptibility of the coarse grain heat-affected zone (CGHAZ) of the last weld bead during PWHT. This is intensified in case of high residual stresses from the component-specific, structurally induced stiffness. In combination with multi-layer welding this leads to a multiaxial stress distribution. Nonetheless, the combined effect of PWHT and high-residual stresses on the SRC formation is merely unknown. For that reason, this study presents the effect of different heating rates in conjunction with a certain component stiffness. For that reason, SAW joints of 13CrMoV9-10 steel were investigated under FS and defined external restraint condition.
Zur Umsetzung der wasserstoffbasierten Energiewende ist eine zuverlässige Transportinfrastruktur unverzichtbar. Hierfür ist die Nutzung großer Teile des vorhandenen Erdgasnetzes vorgesehen. Im Rahmen von Reparatur- und Wartungsarbeiten ist das Schweißen im Betrieb an Erdgaspipelines Stand der Technik. In Verbindung mit Wasserstoff wirft diese Technik jedoch Fragen der Materialverträglichkeit auf. Das im Vortrag vorgestellte Projekt H2SuD leistet Beiträge zur Aufklärung des Einflusses von Reparaturschweißprozessen auf die Wasserstoffaufnahme und Degradation im Betrieb befindlicher H2 Gasleitungen. Ein Schwerpunkt des Vortrages liegt auf der im Projekt erarbeiteten Prüfmethode für Modellversuche, mit denen der Einfluss von Schweißen im Betrieb an Pipelines auf die Wasserstoffaufnahme getestet wird. Die Durchführung erster Versuche und dabei erzielte Ergebnisse werden präsentiert.
Mikrolegierungselemente wie Nb und Ti sind entscheidend für die erwünschte mechanische Festigkeit von vergüteten Feinkornbaustählen mit einer Nennstreckgrenze von ≥ 690 MPa. Aktuelle Spezifikationen geben lediglich Obergrenzen für die chemische Zusammensetzung vor, allerdings können geringfügige Abweichungen erhebliche Auswirkungen auf die mechanischen Eigenschaften haben. Die Vorhersage der Schweißbarkeit und Integrität von Schweißverbindungen stellt aufgrund der variierenden Zusammensetzung und Mikrostrukturen Herausforderungen dar. Unerwünschte Effekte wie Erweichung der Wärmeeinflusszone (WEZ) oder Verfestigung können auftreten. Um dies zu untersuchen, wurden verschiedene Mikrolegierungsrouten mit variierenden Ti- und Nb-Gehalten an Laborschmelzen erforscht. Die Basis jeder Route entsprach der üblichen S690QL in Zusammensetzung und Wärmebehandlung. Dreilagenschweißungen wurden mittels Metallaktivgasschweißens (MAG) durchgeführt, um kritische Gefügebereiche zu identifizieren. Die Analyse konzentrierte sich auf Phasenumwandlungen während der Abkühlung und metallurgisches Ausscheidungsverhalten. Die mechanischen Eigenschaften der Schweißnähte wurden durch Zugversuche ermittelt. Die Ergebnisse zeigen einen bedeutenden Einfluss der Mikrolegierungsroute und Schweißwärmezufuhr auf die Ausscheidungskinetik, trotz insgesamt guter Schweißbarkeit der Werkstoffe.
Mikrolegierungselemente, wie Nb und Ti, sind für die signifikante Festigkeitssteigerung von vergüteten, hochfesten Feinkornbaustählen mit einer Nominalstreckgrenze ≥ 690 MPa unerlässlich. Normvorgaben zur chemischen Zu-sammensetzung geben dabei nur obere Grenzwerte für die Hersteller vor. Weiterhin wirken sich bereits kleine Abweichungen in der Legierungsroute teilweise drastisch auf die mechanischen Eigenschaften aus. Somit wird eine adäquate Vorhersage der Schweißeignung und der Integrität der Schweißverbindung aufgrund der variierenden Mikrogefüge erschwert bis unmöglich.
Die Nb-mikrolegierte Güte weist im Vergleich zur Ti-mikrolegierten Güte eine bessere Anlassbeständigkeit auf. Eine divergente Phasenverteilung in den äußeren Zonen der WEZ der Fülllagen erklärt die unterschiedliche Härteverteilung in der WEZ der drei untersuchten Legierungen und die markanten Unterschiede der Kerbschlagzähigkeit. Die quasistatischen Querzugversuche mittels DIC zeigten ein divergentes lokales Dehnungsverhalten auf. Die Ti-mikrolegierte Stahlsorte zeigt ein signifikanten lokales Dehnungsverhalten in der WEZ, wobei hier sich aufgrund der hohen metallurgischen Kerbwirkung Makrostützeffekte während des plastischen Fließens in der WEZ auftreten.
Der Einsatz von hochfesten niedriglegierten Stählen (HSLA) ist in vielen Industriesektoren, wie dem allgemeinen Bauwesen, Offshore Strukturen, Mobilkranbau usw. unumgänglich geworden. Die steigende Nachfrage an Stählen mit einer hohen Festigkeit und gleichzeitig hervorragenden Zähigkeit stellt ein ökonomisches und ökologisches Potential dieser Stähle in Vordergrund. Aktuell gültige Normvorgaben (EN ISO 10025-6) geben den Stahlherstellern Vorgaben bezüglich der chemischen Zusammensetzung, um die geforderten mechanischen Eigenschaften erreichen zu können. Die Legierungsrouten variieren jedoch von Hersteller zu Hersteller. In Betracht der Schweißeignung dieser Stähle zeigt sich das Problem, dass diese bereits bei geringen Nb- und Ti-Mikrolegierungsunterschieden im Grundwerkstoff ein divergentes metallurgisches Verhalten in der Wärmeeinflusszone (WEZ) aufweisen.
In diesem Vortrag werden die schweiß-metallurgischen Unterschiede zwischen verschieden mikrolegiertem hochfestem Feinkornbaustahl S690QL thematisiert. Zur Prüfung der Schweißnahtfestigkeit wurden mittels eines instrumentierten DIC (ARAMIS) Systems Querzugversuche an Schweiß-Querflachzugproben durchgeführt.
In the course of tomorrow's hydrogen-based energy transition, the construction of the corresponding infrastructure will play a central role. The majority of materials used to date are typically welded for component fabrication. In that context, steels are widely applied and can be prone to hydrogen embrittlement. This includes the classical delayed cold cracking during welding processing as well as embrittlement phenomena during operation. For the evaluation of any hydrogen effect on, for example, the mechanical properties of a welded metallic material, the hydrogen content must be precisely determined. In the case of welds, for example, according to ISO 3690, this is the isothermal carrier gas hot extraction (CGHE). CGHE is based on accelerated hydrogen degassing due to thermal activation of hydrogen at elevated temperatures. In addition to the pure quantification of hydrogen, thermal desorption analysis (TDA) with varied heating rates can be used to determine and evaluate the bonding state at microstructural defects in the material. For both techniques, experimental and measurement influences have to be considered, which have a great effect on the result. For CGHE, for example, ISO 3690 suggests different sample geometries as well as minimum extraction times. The present study summarizes results and experiences of numerous investigations with different sample temperatures and geometries (ISO 3690 type B and cylindrical TDA samples) regarding: the influence of the sample surface (polished/welded), measurement accuracies depending on the sample volume as well as the insufficient monitoring of the effect of the PI controller on the extraction temperature. In particular, a deviating extraction temperature to the set temperature, can significantly falsify the measurement results. Based on the results, methods are shown to quickly reach the desired extraction temperature without having to physically interfere with the measurement equipment. This serves to substantially improve the reliability of hydrogen measurement through increased signal stability and accelerated hydrogen desorption. In general, an independent temperature measurement with dummy samples for the selected heating procedure is advisable to exclude possible unwanted temperature influences already before the measurement. In addition (and way more important), the methods described can be transferred directly to industrial applications.
Multi-principal element alloys (MPEAs) are innovative materials that have attracted extensive research attention within the last decade. MPEAs are characterized by a solid solution of equiatomic metallic elements. Depending on the number of elements, they are also referred as high entropy alloys (HEAs with n ≥ 4 elements like CoCrFeMnNi) and medium-entropy alloys (MEA with n = 3 elements CoCrNi). Depending on the alloy concept, MPEAs show exceptional properties in terms of mechanical performance or corrosion resistance at extreme environments. In that connection, hydrogen and its challenges for the most metallic materials gets more and more important. MPEAs are candidate materials for the substitution of conventional materials like austenitic stainless steels e.g., at very high-pressure up to 1000 bar. Those pressures are typically reached in valves or compressors for refueling of tanks with operational pressure of 700 bar. So far, the susceptibility of HEA/MEAs to hydrogen assisted cracking (if any) and the especially the underlying hydrogen uptake and diffusion was not within the scientific scope and not investigated in detail yet. For that reason, we focused on the hydrogen absorption the characterization of the hydrogen diffusion and trapping at elevated temperatures in a CoCrFeMnNi-HEA (each element with 20 at.-%) and CoCrNi-MEA, each element with 33.3 at.-%). As reference grade, the commercially available austenitic stainless steel AISI 316L was investigated. High-pressure hydrogen charging was conducted at different pressures in autoclave environment with maximum value of 1,000 bar. Thermal desorption analysis (TDA) via carrier gas hot extraction with coupled mass spectrometry was used with a max. heating rate of 0.5 K/s up to 650 °C. The measured desorption spectra of the different samples were deconvoluted into a defined number of individual peaks. The individually calculated peak temperatures allowed the definition of activation energies for predominant trap sites in the respective materials as well as the percentage share of the totally absorbed hydrogen concentration. The results present for the first time the complex interaction of both MPEAs and high-pressure hydrogen charging. A deconvolution of four peaks was selected and a main desorption peak was identified the dominant hydrogen trap containing the biggest share of the absorbed hydrogen concentration. The chemical composition an austenitic phase of both MPEAs is responsible for delayed hydrogen diffusion and strong, but mostly reversible, trapping. The comparison with the 316L samples showed significantly higher activation energies in the MPEAs, whereas hydrogen was also trapped at very high extraction temperatures. The absorbed maximum hydrogen concentration at 1,000 bar was 130 ppm for the CoCrFeMnNi-HEA, 50 ppm for the CoCrNi-MEA and 80 ppm for the 316L. It is interesting that the CoCrFeMnNi-HEA has obviously a way higher trapping capability compared to the conventional austenitic 316L, which could be a major advantage in terms of resistance to hydrogen assisted cracking.
Influence of Residual Stresses on Stress Relief Cracking of Thick-Walled Creep-Resistant Steel Welds
(2023)
Controlling the residual stress level during welding of creep-resistant Cr-Mo-V steels is crucial to avoid so called stress relief cracking (SRC) during post weld heat treatment (PWHT) of large-scale components. In the present study, a laboratory scale test specimen (400 mm x 400 mm x 25 mm) was used to simulate thick-walled component welds made of 13CrMoV9-10. The aim was to identify the level and distribution of residual stresses to evaluate the suitability of the specimen for laboratory based SRC testing. High restraint was ensured by the specimen geometry with a narrow welding gap in the center. This gap was filled by submerged arc welding in a multi-layer technique. Two specimens were welded with identical parameters and compared in the as-welded state and after PWHT (705 °C for 10 h). Neutron diffraction was used to determine the residual stresses in the weld metal, the heat-affected zone (HAZ) and the base material at different depths longitudinal, transverse, and normal to the welding direction. The experiments were performed on the instrument E3 of the research reactor BERII of HZB Berlin, Germany. Complementarily, laboratory X-ray diffraction was applied to characterize the surface residual stresses. In the welded state, especially in the weld metal and the adjacent HAZ, the residual stress can reach the yield strength of the untreated material. The highest levels occur in the longitudinal direction. The transverse and normal directions are characterized by residual stress of lower magnitude. As expected, the residual stress is almost completely relieved after PWHT.
Bei dem Vortrag werden die potentiellen mikrobiologischen Einflüsse im Falle der Lagerung von Wasserstofflagerung in unterirdischen geologischen Formationen vorgestellt, die Zusammenarbeit mit internen und auch externen Partnern. Der Fokus liegt dabei auf UGF; anaerobe Umgebungen, Sulfate reduzierenden Bakterien, methanogenen Archaea, weiterleitenden Systeme und die Kombination der Untersuchung abiotisch/biotische
Mikrolegierungselemente, wie Nb und Ti, sind für die signifikante Festigkeitssteigerung von vergüteten, hochfesten Feinkornbaustählen mit einer Nominalstreckgrenze ≥ 690 MPa unerlässlich. Normvorgaben zur chemischen Zusammensetzung geben dabei nur obere Grenzwerte für die Hersteller vor. Weiterhin wirken sich bereits kleine Abweichungen in der Legierungsroute teilweise drastisch auf die mechanischen Eigenschaften aus. Somit wird eine adäquate Vorhersage der Schweißeignung und der Integrität der Schweißverbindung aufgrund der variierenden Mikrogefüge erschwert bis unmöglich. Unerwünschte Nebeneffekte sind die mögliche Erweichung der Wärmeeinflusszone (WEZ) als auch der gegenteilige Effekt der Aufhärtung. Vor diesem Hintergrund werden erstmals systematisch die unterschiedlichen Mikrolegierungsrouten mit variierenden Ti- und Nb-Gehalten an Versuchsschmelzen untersucht. Die Stahlgüte S690QL bildet dabei die Grundlage der chemischen Zusammensetzung sowie der entsprechenden Wärmebehandlung. Zur Untersuchung der jeweiligen Schweißeignung wurden Dreilagen-Schweißungen mittels moderner MAG-Hochleistungsschweißprozesse durchgeführt und kritische Gefügebereiche mit hoher Erweichung/Aufhärtung identifiziert. Mechanisch-technologische Untersuchungen zur Kerbschlagzähigkeit mittels Kerbschlagbiegeversuchen durchgeführt wurden, bestätigen dabei die Ergebnisse der thermodynamischen Simulation bezüglich des Ausscheidungsverhaltens während der Temperatur-Zeit Schweißzyklen. Daraus lässt sich der Einfluss der Wärmeeinwirkung beim Schweißen auf die Gefügeausbildung in der WEZ und der korrespondierenden mechanischen Eigenschaften qualitativ beschreiben.
Hydrogen has great potential into the decarbonization process of the energy and transport sectors, thus helping to mitigate the urgent issue of global warming. It can be sustainably produced through water electrolysis with potentially zero emissions, and efficiently used in fuel cell systems. Despite its environmental advantages, hydrogen is an extremely flammable substance and its interaction with most metallic materials could result in their mechanical properties degradation to an extent that could make them inherently unsafe.
Extensive material testing under realistic operating conditions is required to determine the criteria under which hydrogen-induced damage is to be expected. In-situ slow strain rate tensile (SSRT) test is an option that allow the quantification of the behavior of metals in hydrogenated environments. The standardized procedure for testing in-situ the pressurized gaseous hydrogen
effect on metals consists of the utilization of an autoclave as a containment volume. Testing inside an autoclave is difficult, expensive, and time-consuming, and requires specialized equipment and trained personnel. A relatively recent method to circumvent these issues and provide affordable and reliable test results consists in using hollow specimens as the gas containment volume, thus applying the hydrogen pressure inside rather than outside the
specimen. This experimental setup allows us to minimize the volume of hydrogen and perform the tests safely and effectively. This study focuses on the evaluation of tensile properties of X65 pipeline steel, which was in vervice for natural gas transport, tested in a high-pressure hydrogen environment using hollow specimens. A constant nominal strain rate of 1ꞏ10-6 s-1 is applied. Tests are performed with different manufacturing techniques for the drilling process, which results in difeerent surface conditions. The effect of the roughness on the HE was investigated. For the evaluation the effect on the reduced area at fracture (RA) and the elongation loss were determined. Further fractographic analysis were performed. In this way, this study provides insights on the applicability of novel, reliable, and safer testing method which can be used to assess HE, particularly in relation with hydrogen-induced loss of ductility in metallic material.
Mikrolegierungselemente, wie Nb und Ti, sind für die signifikante Festigkeitssteigerung von vergüteten, hochfesten Feinkornbaustählen mit einer Nominalstreckgrenze ≥ 690 MPa unerlässlich. Normvorgaben zur chemischen Zusammensetzung geben dabei nur obere Grenzwerte für die Hersteller vor. Weiterhin wirken sich bereits kleine Abweichungen in der Legierungsroute teilweise drastisch auf die mechanischen Eigenschaften aus. Mechanisch-technologische Untersuchungen zur Kerbschlagzähigkeit mittels Kerbschlagbiegeversuchen durchgeführt wurden, bestätigen dabei die Ergebnisse der thermodynamischen Simulation bezüglich des Ausscheidungsverhaltens während der Temperatur-Zeit Schweißzyklen. Daraus lässt sich der Einfluss der Wärmeeinwirkung beim Schweißen auf die Gefügeausbildung in der WEZ und der korrespondierenden mechanischen Eigenschaften qualitativ beschreiben.
Mikrolegierungselementen, wie Nb und Ti sind für eine signifikante Festigkeitssteigerung von vergüteten, hochfesten Feinkornbaustählen mit einer Nominalstreckgren-ze ≥ 690 MPa unerlässlich. Normvorgaben zur chemischen Zusammensetzung dieser Stähle geben zur Erzielung der vorgeschriebenen Eigenschaften dabei oft nur Grenzgehalte für die Hersteller vor. Die Wirkung der Mikrolegierungselemente bzw. ihrer Karbide und/oder Nitride ist teilweise komplett konträr, insbesondere bei Auflösung und Wiederausscheidung in der WEZ bei identischem Schweißzusatz. Somit wird eine adäquate Vorhersage der Chargenabhängigkeit hinsichtlich der Schweißeignung und des Tragverhaltens der Schweißverbindung erschwert. Eine unerwünschte Eigenschaft ist dabei die Erweichung der WEZ, wie auch u.U. der gegenteilige Effekt der Aufhärtung.
Microalloying elements, such as Nb and Ti, are essential for significantly increasing the strength of quenched and tempered, high-strength structural steels with a nominal yield strength ≥ 690 MPa and their welded joints. The standard specifications (e.g., EN 10025-6) for the chemical composition are only tolerated limit contents within which the steel manufacturers operate. The standard composition, however, says nothing per se about the properties of the material. Even small deviations in the alloy route can have a drastic effect on the mechanical properties. This makes it difficult or even impossible to adequately predict the weldability and integrity of the welded joint. An undesirable side effect is the possible softening of the heat-affected zone (HAZ), as well as the opposite hardening.Mechanical-technological investigations of the notched impact strength confirm the results of the simulation regarding the development of different microalloy routes in the welded state. From this, the influence of the heat effect of welding on the microstructure formation in the HAZ and the corresponding mechanical properties can be described qualitatively.
Mikrolegierungselemente, wie Nb und Ti, sind für die signifikante Festigkeitssteigerung von vergüteten, hochfesten Feinkornbaustählen mit einer Nominalstreckgrenze ≥ 690 MPa unerlässlich. Normvorgaben zur chemischen Zusam-mensetzung geben dabei nur obere Grenzwerte für die Hersteller vor. Weiterhin wirken sich bereits kleine Abwei-chungen in der Legierungsroute teilweise drastisch auf die mechanischen Eigenschaften aus. Somit wird eine adä-quate Vorhersage der Schweißeignung und der Integrität der Schweißverbindung aufgrund der variierenden Mikro-gefüge erschwert bis unmöglich. Unerwünschte Nebeneffekte sind die mögliche Erweichung der Wärmeeinflusszone (WEZ) als auch der gegenteilige Effekt der Aufhärtung.
Das Schweißen von hochfesten Feinkornbaustählen erfordert aufgrund der Sicherstellung der Gütewerte des Grundwerkstoffes (Zähigkeit, Festigkeit) auch in der Schweißverbindung, die Einhaltung von engen Grenzen bei der Auswahl von Schweißparametern. Die Reproduzierbarkeit von beanspruchungsgerechten hochfesten Schweißverbindungen hängt vom Schweißverfahren und der damit einhergehenden komplexen Gefügeausbildung ab. Hierbei müssen hochfeste Schweißverbindungen mindestens die gleichen Festigkeitsanforderungen erfüllen wie der eingesetzte Grundwerkstoff. In diesem Vortrag werden speziell die Herausforderungen wie der Empfindlichkeit gegenüber der wasserstoffunterstützen Kaltrissbildung beim Schweißen von hochfesten Feinkornbaustählen und dem Mikrolegierungseinfluss auf die divergente Ausbildung der Wärmeeinflusszone thematisiert.
Large scale hydrogen assisted cracking test for thick walled SAW joints for offshore applications
(2023)
Offshore wind turbines continuously increase in size and weight and demand adequate offshore foundations concepts like monopiles, tripods or jackets. These components are typically submerged arc welded (SAW) high-strength thick steel plates like the S420ML. During welding, the occurrence of delayed hydrogen assisted cracking (HAC) must be anticipated. HAC is a critical combination of the local hydrogen concentration within a susceptible microstructure under certain mechanical load, i.e., the occurring (welding) residual stresses. The welding sequence of the thick-walled plates complicate the residual stress distribution due to the necessary repeated thermal cycling, i.e., welding seam / layer deposition to fill the joint. For that purpose, SAW with two-wire-technique was used to weld a specially designed and prototype-like mock-up of a real component with a thickness of 50 mm, filled with 22 passes and a seam length of 1,000 mm. Additional welded stiffeners simu-lated the effect of a high restraint, to stimulate critical HAC conditions. The necessity of a minimum waiting time (MWT) before the NDT can be conducted (to exclude HAC) was critically verified by the application of ultrasonic testing of the welded joint at different time-steps of the NDT of 48 h after welding. The residual stresses were determined by a robot XRD goniometer. Tensile residual stresses up to the yield limit are found both in the weld metal and in the heat-affected zone. Numerical modelling allowed the qualitative estimation of the hydrogen diffusion in the weld. A remarkable HAC occurrence was not identified and proves both, a certain resistance of the weld joint to HAC and the (questionable) duration of the MWT.
Die vorliegende Präsentation fasst die Ergebnisse von drei laufenden bzw. beendeten AiF/IGF-Projekten zusammen, die über die Forschungsvereinigung Stahlanwendung FOSTA e.V. an der BAM bearbeitet wurden zum Thema: Bewertung und Vermeidung von schweißverarbeitungsbedingten Rissen in hochfesten Baustählen.
The following presentation provides an overview on some of the challenges with metallic materials used as structural materials in the energy sector for the transport and storage of hydrogen. The presentation contains explanations about the methodologies utilized to characterize the susceptibility of these materials for hydrogen.
As the world shifts to a decarbonized economy, the demand for hydrogen-based technologies is rapidly increasing. In order to make optimal use of hydrogen as an energy carrier, the infrastructure for hydrogen storage and transport in particular, must meet high technical safety standards. The indispensable basis for such safety assessments are the material properties, which must be evaluated under operating conditions that are as real as possible.
The conventional method for the assessment of the material properties in gaseous hydrogen is conducted by testing materials in high-pressure hydrogen gas in a pressure vessel (autoclave). It is an established method that allows to perform common standardized tests such as tensile, fatigue and crack growth tests under varying hydrogen conditions. However, this method is complex and entails high costs due to extensive safety regulations.
The hollow specimen technique is a more efficient test method, which can be used to assess the mechanical properties of materials under high-pressure hydrogen gas. The procedure is conducted by enclosing high-pressure gas into a hole along the axis of the tensile test specimen. Recently, this method has been successfully performed at pressures up to 1000 bar and over a wide range of temperatures. Due to the low hydrogen volume needed, this method requires minimal safety regulation; therefore, the costs are reduced when compared to the conventional autoclave technique. This method is now in a standardization process, which has been initiated by Japan as a new working package in ISO (TC 164/SC 1/WG 9).
The following contribution presents preliminary results obtained testing common grades of metastable austenitic stainless steel. For this purpose, the mechanical properties and fracture surface of solid and tubular specimens were assessed and compared using slow strain rate tensile (SSRT) test as part of the preliminary work at the Fraunhofer IWM. In a similar way, pipeline steels evaluated under hydrogen atmospheres using the geometry adapted by BAM will be presented. Within the framework of the TransHyDE flagship project, more results with the goal of supporting the standardization of the hollow specimen technique are expected to be obtained.
Der Vortrag gibt einen kurzen Überblick über die Bedeutung der Fügetechnik in Wasserstofftechnologien und über zukünftige Herausforderungen. Fügetechnologien, insbesondere die Schweißtechnik, haben dabei wesentliche Bedeutung für die Umsetzung von technischen Komponenten der Wasserstofftechnologien. Forschungsschwerpunkte ergeben sich insbesondere für die Erzeugung und den Transport des Wasserstoffs.
Die schädigende Wirkung von Wasserstoff auf die mechanischen Eigenschaften von Stählen ist zwar bekannt, aber noch immer nicht ausreichend erforscht. Die schnelle und sichere Markteinführung von Wasserstofftechnologien macht es erforderlich, dieses Thema genauer zu untersuchen. Im Allgemeinen wird dies oft als Wasserstoffversprödung bezeichnet. Daher ist es wünschenswert, eine Prüfmethode zu entwickeln, die auf einfache Weise die Materialeigenschaften unter Wasserstoffatmosphäre ermitteln kann. Derzeit werden mechanische Prüfungen unter Wasserstoffatmosphäre in Autoklaven durchgeführt. Für diese Technik ist eine aufwendige Hardware erforderlich, daher sind die Prüfungen teuer und die Prüfkapazitäten nur in geringem Umfang verfügbar. Die hier vorgestellte Prüfmethode verspricht einen zukunftsweisenden Ansatz zur Reduzierung von Kosten und Bearbeitungszeiten durch die Verwendung von Hohlkörpern, d.h. die Probe selbst stellt den Autoklav dar.
Large scale hydrogen assisted cracking test for thick walled SAW joints for offshore applications
(2023)
Offshore wind turbines continuously increase in size and weight and demand adequate offshore foundations concepts like monopiles, tripods or jackets. These components are typically submerged arc welded (SAW) high-strength thick steel plates like the S420ML. During welding, the occurrence of delayed hydrogen assisted cracking (HAC) must be anticipated. HAC is a critical combination of the local hydrogen concentration within a susceptible microstructure under certain mechanical load, i.e., the occurring (welding) residual stresses. The welding sequence of the thick-walled plates complicate the residual stress distribution due to the necessary repeated thermal cycling, i.e., welding seam / layer deposition to fill the joint. For that purpose, SAW with two-wire-technique was used to weld a specially designed and prototype-like mock-up of a real component with a thickness of 50 mm, filled more than 20 passes and a seam length of 1,000 mm. Additional welded stiffeners simulated the effect of a high restraint, to stimulate critical HAC conditions. The necessity of a minimum waiting time (MWT) before the NDT can be conducted (to exclude HAC) was critically verified by the application of ultrasonic testing of the welded joint at different time-steps of the NDT of 48 h after welding. The residual stresses were determined by a robot XRD goniometer. Tensile residual stresses up to the yield limit are found both in the weld metal and in the heat-affected zone. Numerical modelling allowed the qualitative estimation of the hydrogen diffusion in the weld. A remarkable HAC occurrence was not identified and proves both, a certain resistance of the weld joint to HAC and the (questionable) duration of the MWT.
Die Wasserstoffinfrastruktur ist eine zentraler Bestandteil der erfolgreichen Umsetzung der wasserstoffbasierten Energiewende. Dabei bilden Ferngasleitungen quasi das "Rückgrat" der Transportinfrastruktur großer Gasmengen. Dabei müssen unter Umständen Reparaturen an den Pipelines durchgeführt werden. Dabei ist in der Erdgasinfrastruktur das Schweißen an in Betrieb befindlichen (d.h. von Gas durchflossenen) Pipelines Stand der Technik. Es ist jedoch vollkommen offen, inwieweit diese Technik auf die reine Wasserstoffpipelines übertragbar sind. Hierzu leistet das Projekt H2SuD wichtige Beiträge zur Aufklärung des Einfluss eines Reparaturschweißprozesses auf die Wasserstoffaufnahme und Degradation im Betrieb befindlicher H2 Gasleitungen.
Der Vortrag gibt einen kurzen Überblick über die Bedeutung der Fügetechnik in Wasserstofftechnologien und über zukünftige FuE-Bereiche. Fügetechnologien haben dabei wesentliche Bedeutung für die Umsetzung von technischen Komponenten der Wasserstofftechnologien. Forschungsschwerpunkte ergeben sich insbesondere für die Erzeugung und den Transport des Wasserstoffs.
The new alloying concept of multi-element systems with defined entropy (HEA - High Entropy Alloy or MEA - Medium Entropy Alloy) is gaining increasing importance in materials research. Significantly improved properties or combinations of properties are shown by some HEA/MEA-systems, which have the potential to substitute conventional alloys such steels and are therefore promising for a wide range of applications, e.g., overcome of the trade-off between high strength and ductility. Thus, primarily the production and resulting microstructures of HEA as well as properties have been investigated so far. Furthermore, processing is a main issue to transfer HEA systems from the laboratory to real components, e.g., for highly stressed components. Since welding is the most important joining process for metals, it is crucial to investigate the influence of welding processing on these material properties to guarantee component integrity. Welding leads to residual stresses, which significantly affect the component integrity. Only a very few studies on the effect of welding on residual stresses in HEA and MEA weld joints are available so far. Hence, the focus of this study is the residual stress formation and distribution in a CoCrFeMnNi HEA and ternary CoCrNi MEA using two different welding processes: Tungsten Inert Gas (TIG) welding and soldi-state Friction Stir Welding (FSW). As a pathway for application of HEA in this investigation for the first time residual stress analyses in realistic near-component specimens were performed. The residual stresses were determined by X-ray diffraction (XRD) on the surfaces of top and root weld side. The results were correlated with the local welding microstructures. The results show that both FSW and TIG generate significant tensile residual stresses on the weld surfaces in and transverse to the welding direction. In the case of FSW of the CoCrFeMnNi HEA, the longitudinal residual stresses are in the range of the yield strength of approx. 300 MPa in the weld zone.
With the introduction of a hydrogen-based energy and national economy, safety-relevant components for hydrogen technologies are becoming increasingly important. Characteristic of hydrogen technologies are, for example, harsh environmental conditions such as cryogenic or high-pressure storage, corrosion issues in fuel cells and electrolyzers, turbines, and many more. Additive manufacturing of components is becoming increasingly important and irreplaceable for the production of complex technical systems. Using the case studies of burners for gas turbines and electrodes and membranes for polymer (PEMFC) and solid oxide (SOFC) fuel cells, this article shows the potential of additive manufacturing of components. At the same time, however, the challenge of considering divergent mechanical properties depending on the direction of assembly in a "hydrogen-compatible" manner is also highlighted. Finally, the challenges posed by additive manufacturing and hydrogen for materials testing are highlighted under scenarios that are as realistic as possible.
We could show in GTAW experiments with steel samples that the attenuation of neutron transmission underneath the welding torch due to the Debye-Waller-effect correlates well with sample temperatures obtained by FE numerical simulations. This would allow principally to determine sample temperatures by measuring the neutron beam attenuation.
Future structural components made of the novel high-entropy (HEA) or medium-entropy alloys (MEA) components can be potentially exposed to hydrogen containing environments like high-temperature water in pressurized nuclear reactors or aerospace structures. Further applications are vessels wall materials for cryogenic or high-pressure hydrogen storage. So far, the susceptibility of HEA/MEAs to hydrogen assisted cracking (if any) and the hydrogen diffusion is not investigated in detail yet and can limit or extend possible applications of HEA/MEA as structural materials. In our work, we focused on the hydrogen absorption, diffusion, and distribution in a HEA (Co20Cr20Fe20Mn20Ni20, the original Cantor-alloy) and a MEA (Co33.3Cr33.3Ni33.3). Conventional cathodic hydrogen charging was carried out for the hydrogen ingress in the materials. Thermal desorption analysis (TDA) via carrier gas hot extraction with coupled mass spectrometry revealed complex hydrogen trapping in both alloy types up to 300 °C. The absorbed total hydrogen concentrations were ≥ 70 ppm for the HEA and approximately 40 ppm for the MEA-type. Although both materials have different chemical composition, the TDA spectra were comparable. In addition, it was shown that the consideration of the sample geometry is an important influence on the sample temperature. It decreases the effective applied heating rate, which must be anticipated for each hydrogen peak after deconvolution of the spectra. This increases the activation energy and shifts the peak to lower temperatures. As a result, microstructure effects can be separated from experimental boundary conditions like the concentration gradient due to the charging process and later thermal activation.
Competence Centre H2Safety@BAM – Safeguarding the Quality Infrastructure in the Hydrogen Economy
(2022)
Hydrogen is a central component of the energy transition and the European Green Deal for a climate-neutral Europe. To achieve the goals defined for 2050, the EU and the German government have developed a framework for action and are making long-term investments in research, development, and the rapid implementation of innovative hydrogen technologies.
With the Competence Centre "H2Safety@BAM", BAM is creating the safety-related prerequisites for the successful implementation of hydrogen technologies at national as well as European level.
To this end, BAM conducts research, testing and consulting in a holistic and inter-disciplinary manner under one roof – in the Competence Centre H2Safety@BAM. The activities of the competence centre focus on ensuring the safety of infra-structures, plants, and processes as well as innovative hydrogen transport and storage systems based on digital quality testing and the experimental testing of components and systems. It thus creates the prerequisites for the implementation and adaptation of legal framework conditions as well as for standardization. Closely related to this are investigations into the properties and compatibility of metallic materials and polymers as well as friction systems for the safe operation of components, plants, processes, and systems. This interdisciplinary and holistic approach is complemented by the development of gas analytics and suitable sensors, online measurements of gas properties in process control, test scenarios under real conditions as well as impact assessments of accidents and risk assessments and risk management systems derived from them. With its portfolio of tasks and competences, BAM builds trust in the safety and reliability of technical system solutions for hydrogen.
Für eine signifikante Festigkeitssteigerung von vergüteten, hochfesten Feinkornbaustählen mit einer Normstreckgrenze > 690 MPa, ist die Zugabe von Mikrolegierungselementen, wie Nb und Ti, unerlässlich. Die Normvorgaben zur chemischen Zusammensetzung dieser Stähle (bspw. in DIN EN 10025-6) geben zur Erzielung der vorgeschriebenen Eigenschaften dabei oft nur Grenzgehalte für die Hersteller vor. Die Wirkung der Legierungselemente bzw. ihrer Karbide und/oder Nitride ist teilweise komplett konträr, insbesondere bei Auflösung und Wiederausscheidung in der WEZ bei identischem Schweißzusatz. Somit wird eine adäquate Vorhersage der Chargenabhängigkeit hinsichtlich der Schweißeignung und des Tragverhaltens der Schweißverbindung erschwert. Zuzüglich können moderne Schweißprozesse, wie MSG mit modifiziertem Sprühlichtbogen (mod. SLB) durch ihre hohe Wärmeeinwirkung die Phasenumwandlung in der Wärmeeinflusszone negativ beeinflussen. Eine unerwünschte Eigenschaft ist dabei die Erweichung (engl.: softening) der WEZ, wie auch u.U. der gegenteilige Effekt der Aufhärtung (engl.: hardening). Vor diesem Hintergrund werden im Rahmen eines DFG-Vorhabens systematisch Mikrolegierungsrouten mit variierenden Ti- und Nb-Gehalten des hochfesten und vergüteten Feinkornbaustahls S690QL untersucht. Dazu wird das MAGSchweißen mit mod. SLB verwendet, welches durch hohe Abschmelzleistung gekennzeichnet ist und schmalere Fugenöffnungswinkel (α = 30°) ermöglicht. An diesen Schweißungen wird der Effekt der metallurgischen Zusammensetzung in Kombination mit hoher Wärmeeinwirkung auf dDie Ausbildung einer kritischen WEZ-Gefügezone mit Erweichung und/oder exzessiver Aufhärtung untersucht. Ein besonderes Augenmerk wird auf die Phasenumwandlungen und das Ausscheidungsverhalten im Gefüge der Wärmeeinflusszone gelegt. Neben umfangreichen metallographischen Untersuchungen einzelner WEZ-Bereiche wurden, unter Variation der chemischen Zusammensetzung, thermodynamische Phasenberechnungen mittels ThermoCalc durchgeführt. Hierdurch wird ein Verständnis zur Phasentransformation und Ausscheidungswachstum und -auflösung während des Schweißens in Abhängigkeit von Temperatur und Abkühlbedingungen geschaffen. Das Ziel ist es, mittels erster Untersuchungen den Einfluss der Wärmeeinwirkung auf die Gefügeausbildung in der WEZ zu zeigen. Insbesondere wird hier auf die Auswirkung der unterschiedlichen Mikrolegierungskonzepte (Ti oder Nb) geachtet.
Martensitic 9 %-Cr steels like P91 and P92 can show an increased susceptibility to delayed hydrogen assisted cracking. The focus of this study was the microstructure and heat treatment effect on the mechanical properties of P92 base material and P91 multi-layer weld metal in both as-welded and post weld heat treated (PWHT) condition.
Tensile tests with hydrogen free reference samples and electrochemically hydrogen charged samples were carried out, the mechanical properties were assessed and supported by dedicated fractographic analysis. In addition, hydrogen and microstructure dependent fracture criteria were calculated. All investigated microstructures showed a hydrogen influenced degradation of the mechanical properties compared to the hydrogen free reference samples. In that connection, the as welded martensitic P91 weld metal had the highest degree of degradation in presence of hydrogen. The P91 PWHT weld metal and the P92 base material had comparable properties. From that point of view, a significantly increased risk for hydrogen assisted cold cracking during welding fabrication of P91 weld joints must be considered before any heat treatment is conducted.
Influence of Residual Stresses on Stress Relief Cracking of Thick Walled Creep Resistant Steel Welds
(2022)
Controlling the residual stress level during welding of creep-resistant Cr-Mo-V steels is crucial to avoid so called stress relief cracking (SRC) during post weld heat treatment (PWHT) of large-scale components. In the present study, a laboratory scale test specimen (400 mm x 400 mm x 25 mm) was used to simulate thick-walled component welds made of 13CrMoV9-10. The aim was to identify the level and distribution of residual stresses to evaluate the suitability of the specimen for laboratory based SRC testing. High restraint was ensured by the specimen geometry with a narrow welding gap in the center. This gap was filled by submerged arc welding in a multi-layer technique. Two specimens were welded with identical parameters and compared in the as-welded state and after PWHT (705 °C for 10 h). Neutron diffraction was used to determine the residual stresses in the weld metal, the heat-affected zone (HAZ) and the base material at different depths longitudinal, transverse, and normal to the welding direction. The experiments were performed on the instrument E3 of the research reactor BERII of HZB Berlin, Germany. Complementarily, laboratory X-ray diffraction was applied to characterize the surface residual stresses. In the welded state, especially in the weld metal and the adjacent HAZ, the residual stress can reach the yield strength of the untreated material. The highest levels occur in the longitudinal direction. The transverse and normal directions are characterized by residual stress of lower magnitude. As expected, the residual stress is almost completely relieved after PWHT.
Offshore wind turbines continuously increase in size and weight and demand adequate offshore foundations concepts like monopiles, tripods or jackets. These components are typically submerged arc welded (SAW) high-strength thick steel plates like the S420ML. During welding, the occurrence of delayed hydrogen assisted cracking (HAC) must be anticipated. HAC is a critical combination of the local hydrogen concentration within a susceptible microstructure under certain mechanical load, i.e., the occurring (welding) residual stresses. The welding sequence of the thick-walled plates complicate the residual stress distribution due to the necessary repeated thermal cycling, i.e., welding seam / layer deposition to fill the joint. For that purpose, SAW with two-wire-technique was used to weld a specially designed and prototype-like mock-up of a real component with a thickness of 50 mm, filled with 22 passes and a seam length of 1,000 mm. Additional welded stiffeners simulated the effect of a high restraint, to stimulate critical HAC conditions. The residual stresses were determined by a robot XRD goniometer. A least square regression analysis of the sin²ψ-law by using multiple ψ- and φ-tilts was applied. Tensile residual stresses up to the yield limit are found both in the weld metal and in the heat-affected zone. Numerical modelling allowed the qualitative estimation of the hydrogen diffusion in the weld, enabling the determination of critical conditions for the formation of HAC. In a future step, a structural simulation will allow the assessment of the welding residual stresses and the comparison to the XRD-values.
In vielen Bereichen des industriellen Stahlbaus, wie z. B. bei Mobilkränen und im Offshore-Bereich, werden seit langem hochfeste Feinkornbaustähle mit einer Streckgrenze von über 690 MPa eingesetzt. Um die notwendige Tragfähigkeit zu gewährleisten, erfordert die schweißtechnische Verarbeitung dieser Stähle eine zuverlässige Kenntnis des komplexen Zusammenspiels zwischen dem Schweißprozess, der zugrundeliegenden Wärmeeinbringung und den entsprechenden Abkühlungsbedingungen, der chemischen Zusammensetzung von Grund- und Zusatzwerkstoff und den daraus resultierenden metallurgischen Phänomenen in der Schweißnaht und der WEZ. Mikrolegierungselemente wie Ti und Nb leisten einen unverzichtbaren Beitrag zur Erhöhung der Festigkeit durch Ausscheidungshärtung. Frühere Untersuchungen haben gezeigt, dass ein signifikanter Einfluss der Mikrolegierungselemente auf die Phasenumwandlung hinsichtlich der Aufhärtung und/oder Erweichung der Wärmeeinflusszone angenommen werden kann. Die Normvorgaben für die chemische Zusammensetzung nach DIN EN 10025-6 geben dem Hersteller oft nur Grenzen vor, um die gewünschten mechanischen Eigenschaften zu erreichen. Die Wirkung der Legierungselemente und der entsprechenden Ausscheidungen (Karbide und/oder Nitride) ist manchmal völlig konträr, insbesondere bei Auflösung und Wiederausscheidung in der WEZ bei identischem Zusatzwerkstoff. Dies erschwert eine adäquate Vorhersage der Chargenabhängigkeit im Hinblick auf die Schweißbarkeit und die Belastbarkeit der Schweißnaht. Das Fügen dieser Stähle erfolgt hauptsächlich durch das Metall-Schutzgasschweißen (MSG). Moderne Inverterschweißquellen und mikroelektronische Steuerungstechnik ermöglichten den Einsatz von gesteuerten Lichtbogenvarianten, wie dem modifizierten Sprühlichtbogen. Diese Lichtbogenvariante zeichnet sich durch mehrere Eigenschaften aus, wie z.B. reduzierte Nahtöffnungswinkel und erhöhte Abschmelzleistungen. Wobei sich diese hohe Wärmeeinwirkung negativ auf die Phasenumwandlung in der WEZ auswirken kann. Eine unerwünschte Eigenschaft ist die Erweichung der WEZ, ebenso wie der gegenteilige Effekt der Aufhärtung.
In many industrial steel construction branches, like mobile cranes and the offshore sector, high-strength fine-grained structural steels with a yield strength of over 690 MPa have long been used. To guarantee the necessary load-bearing capacity, the welding processing of these steels requires reliable knowledge of the complex interaction between the welding process, its underlying heat input and corresponding cooling conditions, chemical composition of base and filler materials, and resulting metallurgical phenomena in the weld seam and HAZ. Microalloying elements such as Ti and Nb make an indispensable contribution to increasing the strength by precipitation hardening. Previous investigation has shown that significant influence of the microalloying elements on the phase transformation can be assumed regarding the hardening and/or softening of the heat-affected zone. The standard specs for the chemical composition according to DIN EN 10025-6 often just specify chemical limitations for the manufacturer to achieve the desired mechanical properties. The effect of the alloying elements and the corresponding precipitates (carbides and/or nitrides) is sometimes entirely contrary, especially in case of dissolution and re-precipitation in the heat-affected zone (HAZ) with identical filler metal. This makes an adequate prediction of the batch dependency with regard to weldability and the load-bearing capacity of the welded joint difficult. The joining of these steels is mainly carried out by gas metal arc welding (GMAW). Modern inverter welding sources and micro-electronics control technology enabled the use of controlled arc variants, such as the modified spray arc (Mod. SA). Several characteristics from this arc variant e.g. reduced weld seam opening angles and increased deposition rates. Whereby this high heat exposure can have a negative effect on the phase transformation in the HAZ. An undesirable property is the softening of the HAZ, as well as the opposite effect of hardening.
Joining processes for components in hydrogen technologies: Current need and future importance
(2022)
This presentation gives an overview on the importance of joining processes for component fabrication in hydrogen technologies. For that reason, the current need and future research and developement activites are highlighted for the three technological fields: hydrogen storage, transport and use (in terms of the emerging field of additive manufacturing). Finally, some remarks are given for necessary changes in the standardization.
Um die Absorption von Wasserstoff und dessen Verhalten in den Werkstoffen beim Einsatz unter Druck-H2 sowie die H- abhängigen Materialeigenschaften zu definieren, entwickelt die BAM mit ihrer langjährigen Erfahrung adäquate Prüfkonzepte, die einsatzrelevante Bedingungen und reale Beanspruchungen (Temperatur, Wasserstoff und mech. Beanspruchung) hierarchisch berücksichtigen. Der Vortrag gibt eine Einführung in das Thema von wasserstoffunterstützen Materialschäden durch die Problematik der Einspeisung von Wasserstoff in bestehende Erdgasnetze. Ferner wird auf die Hochdruck-Infrastruktur (sowie H2-Tankstellen) und die Entwicklung von Prüfkonzepten für die Gasinfrastruktur unter Druckwasserstoffbeaufschlagung eingegangen.
Influence of Hydrogen Uptake and Diffusion in Structural Components in the Field of Renewable Energy
(2021)
Great efforts are invested worldwide in the development of efficient electrolysis processes, fuel cells technologies and hydrogen transport and storage infrastructures. This includes the exploitation of existing gas-grid infrastructure for the injection of hydrogen. Considering transport and storage facilities, the utilization of gaseous hydrogen can be divided into two main groups which are differentiating in the pressure regime. Fueling stations are operating in high pressure (>800 bar) and high purity and therefore use austenitic stainless steels in their compression systems. On the other hand, existing gas infrastructure where the natural gas is transported across long distances is usually operating with up to 300 bar. In this case the pipe-systems consist of several steel classes, mainly low alloyed steels in which the surface quality and the gas mixture are strongly varying.
Even though ingress of hydrogen can lead to catastrophic failures in all steels, its exact impact on the mechanical properties, as well as its interaction with the surface, microstructure and lattice and the underlying mechanisms remain unclear. Therefore, research on the impact of gaseous hydrogen in pressure vessels and pipes has clearly an integral part on the path to safe and sustainable use of the different components along the different chains. This becomes even more relevant considering the influence of impurities in the gas, e.g. sulfur and with the introduction of new production technologies, such as additive manufacturing, into the market.
Determination of these interactions and impact that might lead to the degradation of the properties can allow a safe use of steels in present and future hydrogen-based energy applications.
The following contribution gives an overview of the problem and introduction to the conventional and innovative tools used and developed nowadays to analyze it. For this purpose, materials were loaded with hydrogen by electrochemical means and under high pressure and elevated temperatures. The results presented provide an invaluable insight into the impact of hydrogen on the integrity of selected steels used in the two mentioned above applications. This work is part of an ongoing research in which mechanical, chemical, structural, and microstructural analyses tools are combined in-situ and ex-situ.
This study gives an overview on the important field of joining processes for component fabrication in hydrogen technologies. For that reason, the current need and future research and developement activites are highlighted for the different technological field of hydrogen generation, storage, transport and use. In addition, the emerging field of additive manufacturing is included. Finally, some remarks are given for necessary changes in the standardization and its challenges.
Increasing environmental problems with conventional energy technology are stimulating the demand for alternative energy solutions. With air quality reaching catastrophic levels in large cities worldwide, Fuel Cell Electric Vehicles offer the ideal combination of clean power with the amenities of electric drives. Hydrogen use on vehicles, nevertheless, also raises some issues about safe handling. As fuel cells and hydrogen applications, including vehicles, approach technological maturity, developing their business cases becomes crucial in introducing them to the consumer markets.
The Joint European Summer School JESS 2021 addresses these issues by offering high quality graduate level courses on selected topics of vehicle technology, innovation & business development, safe handling of hydrogen, and modelling. This series of summer schools has been ongoing since 2004 and targets an audience of university students (MSc and PhD levels) and post-doctoral researchers. We also welcome more experienced researchers and engineers wishing to expand their general knowledge, for instance, to suit a newly acquired position or collect credits for Continuous Professional Development (CPD). The course content is tailored to the needs of a diverse audience: newcomers to the field, experienced students, and young professionals working at the forefront of fuel cell and hydrogen applications.