Ingenieurwissenschaften und zugeordnete Tätigkeiten
Filtern
Erscheinungsjahr
Dokumenttyp
- Vortrag (41)
- Zeitschriftenartikel (32)
- Posterpräsentation (13)
- Beitrag zu einem Tagungsband (8)
- Dissertation (3)
- Beitrag zu einem Sammelband (1)
Schlagworte
- Residual stress (98) (entfernen)
Organisationseinheit der BAM
- 8 Zerstörungsfreie Prüfung (51)
- 8.5 Röntgenbildgebung (51)
- 9 Komponentensicherheit (42)
- 9.4 Integrität von Schweißverbindungen (39)
- 5 Werkstofftechnik (16)
- 9.2 Versuchsanlagen und Prüftechnik (11)
- 5.2 Metallische Hochtemperaturwerkstoffe (8)
- 5.1 Mikrostruktur Design und Degradation (7)
- 9.3 Schweißtechnische Fertigungsverfahren (6)
- 3 Gefahrgutumschließungen; Energiespeicher (5)
- 5.0 Abteilungsleitung und andere (5)
- 3.0 Abteilungsleitung und andere (4)
- 5.5 Materialmodellierung (3)
- 8.0 Abteilungsleitung und andere (3)
- 9.0 Abteilungsleitung und andere (2)
- 9.6 Additive Fertigung metallischer Komponenten (2)
- 3.5 Sicherheit von Gasspeichern (1)
- 7 Bauwerkssicherheit (1)
- 7.1 Baustoffe (1)
- 8.4 Akustische und elektromagnetische Verfahren (1)
Paper des Monats
- ja (1)
Eingeladener Vortrag
- nein (41)
Modifying the level of mostly detrimental welding residual stresses already during the welding process would be highly attractive as time- and cost-consuming post processing may be prevented. The nature of stress buildup during welding-associated cooling is highly affected by phase transformations. Up to now, it is not clear in which way this is applicable to real component welding exhibiting high shrinkage restraint and complex heat input. In this study, two different low transformation temperature (LTT) alloys have been investigated concerning the stress development in restrained multi-run butt welding in order to evaluate the potential of stress reduction. Pulsed gas metal arc welding (P-GMAW) welding was executed on a testing facility designed to simulate real lifelike restraint conditions of component weldments. The effect of reducedMS-temperatures and the heat control on the globally acting stresses was monitored by in-situ measurement of the reaction forces during welding fabrication. Additional local residual stress measurements allowed analyzing global as well as local loading of the welded construction. Although phase transformation has a significant influence on unloading the joint during each weld pass, the reaction stress upon cooling to room temperature seems to be determined mainly by the heat input. On the surface, low longitudinal residual stresses were observed in case of LTT whereas transverse residual stresses are less affected.
Observation of martensite formation by combined use of synchrotron diffraction and dilatometry
(2016)
Welding residual stress engineering by means of an adjusted martensite phase transformation would be highly attractive as detrimental tensile residual stresses may be prevented already during welding without time and cost intensive post processing. The present study shows a synchrotron diffraction analysis of a martensitic steel subjected to thermo-mechanical load cycles. Experiments were conducted regarding the microstructural strain response during the austenite to martensite transformation. The strains are a function of the temperature and the specific loads applied during cooling. The relation between the transformation plasticity of the material, the amount of martensite formed and the arising strains can thus be assessed. The lattice plane specific strains were compared to experimental findings from (macro) dilatation tests. It is shown that the microscopic material behavior differs remarkably from the one observed on the macroscopic scale, what leads to characteristic residual stresses in the material.
Characterization of residual stress state by neutron diffraction and residual magnetic field mapping
(2016)
Based on the residual stress characterization of tungsten inert gas welded S235JRC+C plates by means of neutron diffraction, the evaluation of residual stress with high spatial resolution GMR (giant magneto resistance) sensors is discussed. The experiments performed indicate a correlation of residual stress changes and local residual magnetic stray fields.
Selective Laser Melting (SLM) technique allows to produce parts with complex geometry. Due to the rapid solidification and heat gradient during production, SLM results in presence of residual stress. The present study shows the influence of manufacturing parameters on surface residual stress of Ti-6Al-4V SLM parts. High tensile stresses in the front surface are found. Heat Treatment conditions relax residual stresses almost to zero. High scanning speed during manufacturing results in higher tensile stresses in the surface.
Additive Manufacturing (AM) by Selective Laser Melting (SLM) offers ample scope for producing geometrically complex parts as compared to the traditional subtractive manufacturing strategies. However, the residual stresses developed during the processing can reduce the load bearing capacity as well as induce unwanted distortion, limiting the application of SLM parts.
IN718 manufactured by SLM process can show high tensile residual stresses in the surface as high as the yield strength of the wrought alloy. On the other hand, residual stresses in the bulk Show considerably lower stress values, even in compression, indicating a stress re-distribution during deposition of the SLM layers.
Magnetic testing methods are frequently applied in non-destructive evaluation of ferromagnetic materials. In the past decade, metal magnetic memory (MMM) technique according to ISO 24497 is gaining considerable interest in the magnetic NDT community. In contrast to traditional Magnetic Flux Leakage (MFL) testing, the inspection objects are not intentionally magnetized by an external magnetic field. Due to physical coupling between mechanical stress and magnetization in ferromagnetic materials, it is assumed that the distribution of the “natural” MFL (self-magnetic-leakage field, SMLF) indicate zones of different remanent magnetization, which in turn, correspond to the internal stress of specimen or in the most general sense to material degradation.
Usually, MMM measurements are performed by relatively bulky magnetic inspection sensors providing a spatial resolution in millimetre range. High precision GMR (Giant Magneto Resistance) measurements in the micrometer regime along with image based representation and evaluation can provide a higher degree of information. We present a concise summary of a broader research project aimed at studying the correlation of magnetic structure and microstructure of steels. Particularly, we compare residual stress measurements in S235JR steel by means of neutron diffraction with high resolution magnetic field measurements. In addition, we discuss the influence of deformation-induced magnetization in plastically deformed specimens with and without notches due to various quasi-static and cyclic load levels. Furthermore, comparative measurements with common non-destructive testing methods are presented.
Despite of a quantitative evaluation of material degradation, the in the field inspection by MMM remains problematic due to substantial influences on such as external magnetization, anisotropy of internal magnetization and material degradation, as well as geometry and surface effects of the inspection objects on SMFL signals. The prospects and restrictions of the MMM technique are discussed in this contribution.
The goal of reducing CO2 emissions in the automobile industry has led to the development of increasingly efficient lightweight material solutions that yield enhanced performance. In light of this goal, this current work involves the optimization of the pre-conditioning of novel, high toughness steel bearings without thermo-chemical treatment, with the aim of transferring the running-in phase into the final step of the mechanical finishing process. A case-hardened gear steel and two novel non-case-hardened steels were evaluated.
X-ray stress analysis on crystalline materials is based on the determination of elastic lattice strains. The strains described by the shift of peak positions are converted to stresses by the means of theory of elasticity. The development of the sin2ψ-method of X-ray stress analysis introduced an enormous progress in X-ray stress analysis during the last decades. This report outlines some important elements of X-ray physics and fundamentals of theory of elasticity. The Standard measuring procedure are described and special experimental differences to the common powder diffractometry are outlined.