Ingenieurwissenschaften und zugeordnete Tätigkeiten
Filtern
Erscheinungsjahr
- 2019 (287) (entfernen)
Dokumenttyp
- Vortrag (287) (entfernen)
Sprache
- Englisch (287) (entfernen)
Referierte Publikation
- nein (287) (entfernen)
Schlagworte
- Additive Manufacturing (29)
- Corrosion (19)
- MIC (9)
- Microstructure (9)
- Welding (9)
- Additive manufacturing (8)
- Diffraction (8)
- Surface functionalization (8)
- Magnetocaloric (7)
- Nanoparticle (7)
Organisationseinheit der BAM
- 6 Materialchemie (74)
- 9 Komponentensicherheit (66)
- 8 Zerstörungsfreie Prüfung (55)
- 5 Werkstofftechnik (51)
- 8.5 Röntgenbildgebung (35)
- 9.3 Schweißtechnische Fertigungsverfahren (33)
- 7 Bauwerkssicherheit (29)
- 6.6 Physik und chemische Analytik der Polymere (23)
- 9.4 Integrität von Schweißverbindungen (23)
- 4 Material und Umwelt (21)
- 1 Analytische Chemie; Referenzmaterialien (18)
- 6.2 Material- und Oberflächentechnologien (18)
- 5.4 Multimateriale Fertigungsprozesse (17)
- 7.6 Korrosion und Korrosionsschutz (17)
- 8.0 Abteilungsleitung und andere (16)
- 3 Gefahrgutumschließungen; Energiespeicher (14)
- 6.3 Strukturanalytik (13)
- 1.2 Biophotonik (12)
- 4.5 Kunst- und Kulturgutanalyse (11)
- 5.1 Mikrostruktur Design und Degradation (11)
- 6.1 Oberflächen- und Dünnschichtanalyse (11)
- 5.6 Glas (10)
- 9.5 Tribologie und Verschleißschutz (10)
- 2 Prozess- und Anlagensicherheit (9)
- 4.1 Biologische Materialschädigung und Referenzorganismen (8)
- 5.2 Metallische Hochtemperaturwerkstoffe (8)
- 5.3 Polymere Verbundwerkstoffe (7)
- 6.7 Materialsynthese und Design (7)
- 7.5 Technische Eigenschaften von Polymerwerkstoffen (6)
- 6.5 Synthese und Streuverfahren nanostrukturierter Materialien (5)
- 3.2 Gefahrguttanks und Unfallmechanik (4)
- 5.5 Materialmodellierung (4)
- 7.1 Baustoffe (4)
- 8.4 Akustische und elektromagnetische Verfahren (4)
- 9.0 Abteilungsleitung und andere (4)
- 1.9 Chemische und optische Sensorik (3)
- 2.4 Prüfung und Bewertung von Explosivstoffen/Pyrotechnik (3)
- 3.0 Abteilungsleitung und andere (3)
- 3.3 Sicherheit von Transportbehältern (3)
- 3.4 Sicherheit von Lagerbehältern (3)
- 6.0 Abteilungsleitung und andere (3)
- 8.6 Faseroptische Sensorik (3)
- 1.1 Anorganische Spurenanalytik (2)
- 2.1 Sicherheit von Energieträgern (2)
- 2.2 Prozesssimulation (2)
- 2.5 Konformitätsbewertung Explosivstoffe/Pyrotechnik (2)
- 4.2 Material-Mikrobiom Wechselwirkungen (2)
- 7.4 Baustofftechnologie (2)
- 9.2 Versuchsanlagen und Prüftechnik (2)
- 1.5 Proteinanalytik (1)
- 3.1 Sicherheit von Gefahrgutverpackungen und Batterien (1)
- 5.0 Abteilungsleitung und andere (1)
- 7.0 Abteilungsleitung und andere (1)
- 7.2 Ingenieurbau (1)
- 8.1 Sensorik, mess- und prüftechnische Verfahren (1)
- 8.2 Zerstörungsfreie Prüfmethoden für das Bauwesen (1)
- S Qualitätsinfrastruktur (1)
- S.2 Digitalisierung der Qualitätsinfrastruktur (1)
Eingeladener Vortrag
- nein (287)
The life time of mechanical components in high temperature applications is basically determined by their workings. Corrosion determines the loss of material corresponding to the loss of the effective load-bearing section and consequently increasing stress levels. To improve the material selection for such applications a numerical life prediction corrosion model for different alloys and environments is needed. Based on the ferritic alloys FeCr and FeCrCo a first quantitative model is to be developed. For this purpose, the alloys are aged at 600 °C, 650 °C and 700 °C in synthetic air under normal pressure for between 10 and 240 hours. The first objective is to establish a quantitative relationship between the oxidation rate as a function of composition and microstructure of the alloys. The influence of the inner interface as an essential parameter for transport by diffusion on the oxidation kinetics is discussed in this paper.
Microbiologically induced corrosion due to bacterial biofilms causes several problems in industrial systems, technical applications and in medicine. Prior to the formation of a biofilm on a substrate, planktonic cells attach on the surface. Hence, the properties of the surface play a key role in biofilm formation and are of great importance for the development of strategies to prevent bacterial attachment and biofilm formation.
This project aims at clarifying to which extent surface micro-/nanostructuring and chemical functionalization affects bacterial attachment and whether a synergistic combination of the two can be used to control bacterial adhesion. To answer these questions, model surfaces with regular patterns of 5-10 micrometers in size have been prepared, which provide distinct zones differing in terms of their chemistry or nano-roughness. This was achieved by micro contact printing of self-assembled monolayers with different functional groups and deposition of patterned ZnO nanorod arrays for studying the effect of surface chemistry and morphology, respectively. Typical contrasts studied were combinations of positively/negatively charged, hydrophobic/hydrophilic or flat/rough.
The attachment behavior of bacteria on tailored surfaces were studied in a flow chamber as a function of time. The strain Pseudomonas fluorescens SBW25 was chosen as a model organism. DNA-intercalating dyes such as Syto9 have a high affinity to adsorb on ZnO nanorods. To overcome this limitation a genetic modification was performed by introducing a gene which expresses a green fluorescent protein in P. fluorescens SBW25 enabling the quantitative evaluation of the flow chamber studies by means of fluorescence microscopy. Further analysis of the attachment behavior was performed by means of scanning electron microscopy.
The presentation will summarize the results of our systematic study on the role of individual parameters on bacterial attachment and highlight synergistic combinations, showing an inhibition or enhancing effect. As the investigations with model substrates enable a precise control of the surface parameters, this approach can be applied to different microorganisms and material systems to achieve a correlative description of bacterial adhesion on solid surfaces.
Modern wind turbine rotor blades consist of sandwich shell segments made from glass fiber reinforced polymers. During manufacturing, defects can arise which could lead to failure of the whole component under dynamic mechanical and thermal loads. Hence during operation defects can arise which, if detected, can be repaired locally and in-situ by applying repair patches instead of taking the whole rotor blade down and repair it remotely. This method is much more time and cost effective, since the shut-down time of the energy converter is limited to a minimum. These repair patches can, however, also lead to new defects if not applied optimally. Therefore, it is necessary to control the quality of the repair patches to ensure the best possible restoration of structural integrity of the component. As a rotor blade is an object with a large aspect ratio, X-ray laminography is predestined to provide 3D information of the objective volume. To enhance the amount of information gained from laminographic reconstruction, we use in this study a photon counting and energy discriminating X-ray detector and apply a material decomposition algorithm to the data. By inherently separating the incident spectra within the detection process into two distinct energy bins, the basis material decomposition can provide material resolved images. Choosing glass and epoxy resin as basis materials and numerically solving the inverse dual-energy equation system, the reconstructed laminographic datasets contain highly valuable information about the distribution of the basis materials within the structure. Furthermore, cross- artifacts arising from the limited angle of the projection data can be reduced by this method which allows to investigate structures that were hidden underneath the artefacts.
The study presented here focusses on a systematic analysis of oxidation mechanisms of the well-known Cr20Mn20Fe20Co20Ni20 alloy and one of its ternary sub-system Cr33.3Co33.3Ni33.3 which were reported in the literature to exhibit attractive mechanical properties. Both alloys are single phase fcc prior to oxidation and were simultaneously exposed to different oxygen containing atmospheres at 700° C and 800° C for durations up to 288 h. Cr20Mn20Fe20Co20Ni20 showed poor oxidation resistance at high temperatures due to its high amount of manganese leading to the formation of non-protective Mn-oxide scales. In contrast, a relatively homogeneous and protective chromia layer was found to form on CrCoNi at 700° C and 800° C after each exposure time. Mass change-, SEM- and XRD analysis of the oxide layers were performed in the present study and provide a better understanding of the oxidation mechanisms as well as the impact of the alloy composition on oxidation behavior.
Over the past years economic and environmental considerations have led to a markedly increased demand for efficiency and flexibility in petrochemical plants. The operational temperatures and pressures required today can only be achieved by using new creep-resistant grades of steel. The modified 13CrMoV9-10 vanadium steel shows a good resistance against creep and compressed hydrogen and has been in use for the construction of petrochemical reactors since the mid-1990s. Nevertheless, processing of this type of steel requires extreme care during the welding procedure. This is due to its low toughness and high strength in the welded state when not post weld heat treated combined with increased susceptibility to cracking during stress relaxation. Previous research into crack formation in creep-resistant steels has largely focused on thermal and metallurgical factors; however, little knowledge has been gathered regarding the influence of the welding procedure on crack formation during post weld heat treatment considering real-life manufacturing conditions. The influence of heat control on the mechanical properties has been investigated by simulating the welding and subsequent post weld heat treatment operations during the construction of petrochemical reactors using a special 3-D testing facility on the laboratory scale.
This work is subdivided in two parts. In part I of this study the stresses resulting from preheating, welding, dehydrogenation heat treatment and the final post weld heat treatment were analyzed during experiments under varied heat control. In all experiments stress relief cracks formed during post weld heat treatment could be observed. The total crack lengths correlated with the welding induced stresses.
Part II of this work is dedicated to the characterization of the cracks and the microstructure. The application of a special acoustic emission analysis indicated that the cracks formed in a temperature range between 300 °C and 500 °C during the post weld heat treatment. In comparison to small scale specimens welded without additional shrinkage restraint, the toughness of the restrained welds was significantly decreased. SEM and TEM analyses of all samples revealed accelerated aging due to early precipitation of special carbides during post weld heat treatment under component relevant restraint.
Degradation of polyurethanes in various environments – Effects on molecular mass and crosslinking
(2019)
The increasing application of polyurethanes (PU) in safety relevant sectors (fire protection, insulation, medicine technique) requires detailed knowledge of the stability and reliability of these materials. Different climate factors are supposed to induce diverse and overlapping degradation reactions. The knowledge of these degradation mechanisms is necessary for an estimation of the period of application depending on usage of the material. An essential property of a polymeric system is represented by the molecular weight. Since a change of the molecular weight is a measure for the chemical stability of a polymer, size-exclusion chromatography (SEC) was used to monitor changes of the molecular weight of thermoplastic polyether- and polyester urethane (TPU) exposed to thermal, hydrolytic and photo-oxidative (UV) degradation conditions for several days. Thermal treatments were performed at elevated temperatures (100 - 200 °C) under oxidative (air) as well as non-oxidative (nitrogen) conditions to evaluate the specific influence of oxygen on the degradation. At higher temperatures (≥ 175 °C) a fast decrease of the molecular masses of both PU accompanied by a high degree of crosslinking was found. At lower temperatures (≤ 150 °C) the polymers remained widely unaffected by thermal degradation within the investigated degradation interval of up to two weeks, which was already known from FTIR spectroscopy[1]. In contrast to that, UV treatment at 25 °C at less than 10 % rel. humidity (RH) resulted in a fast crosslinking, whereas the molecular masses of both PU decreased slower than during the thermal treatments. The depth of penetration of the UV radiation was determined using 3D printed PU samples with different thicknesses. Hydrolysis based degradation effects were less significant. Only slight molecular mass changes were detected at temperatures ≤ 80 °C within a time span of 14 days, while no crosslinking could be measured. Considering the degradation results at the investigated exposure parameters, it could be shown that ester-based PU in general exhibits a significant higher stability compared to ether-based materials.
Polymers at interfaces play a major role in a broad variety of applications ranging from engineering purposes (for instance polymer based nanocomposites) to high tech implications (for instance light emitting diodes).
Here, thin films with thicknesses down to few nanometers are prepared on different substrates as model systems for polymer composites. The thin films are investigated by a combination of surface analytical and volume sensitive methods. As surface analytical methods atomic force microscopy (AFM), X-ray photoelectron spectroscopy (XPS), and contact angle measurements (CAM) are employed. As volume sensitive broadband dielectric spectroscopy (BDS), specific heat spectroscopy (SHS), and ellipsometry are used. Especially attention is paid to understand the glass transition behavior of thin films because the glass transition is the key phenomenon determines the application of polymers also in thin films.
To understand the glass transition behavior of thin films, which is controversially discussed in literature, a three layer model is discussed. Firstly, a mobile surface layer is assumed at polymer air interface of the film due to missing of segment/segment interactions. Secondly, in the middle of the film a bulk-like layer should be expected. Thirdly, for polymers having non-repulsive interactions with the substrate an irreversibly adsorbed layer is expected to be formed. Due the adsorption the molecular mobility of the segments in this layer is slowed down. What is measured for the glass transition of thin films is a complicated average of all of these effects. The different layers are hardly to address separately. Therefore, in the presentation especially model systems are selected and investigated to verify the layer model.