Ingenieurwissenschaften und zugeordnete Tätigkeiten
Filtern
Erscheinungsjahr
Dokumenttyp
- Posterpräsentation (673) (entfernen)
Sprache
- Englisch (673) (entfernen)
Schlagworte
- Additive manufacturing (31)
- Corrosion (30)
- Mechanochemistry (23)
- Nanoparticles (20)
- Additive Manufacturing (18)
- Glass (18)
- Crystallization (16)
- Fluorescence (15)
- In situ (14)
- Computed tomography (13)
Organisationseinheit der BAM
- 6 Materialchemie (199)
- 5 Werkstofftechnik (87)
- 8 Zerstörungsfreie Prüfung (80)
- 6.3 Strukturanalytik (62)
- 6.6 Physik und chemische Analytik der Polymere (54)
- 8.5 Röntgenbildgebung (53)
- 6.1 Oberflächen- und Dünnschichtanalyse (49)
- 9 Komponentensicherheit (46)
- 1 Analytische Chemie; Referenzmaterialien (45)
- 4 Material und Umwelt (34)
- 1.2 Biophotonik (25)
- 5.1 Mikrostruktur Design und Degradation (25)
- 6.0 Abteilungsleitung und andere (25)
- 7 Bauwerkssicherheit (25)
- 5.4 Multimateriale Fertigungsprozesse (21)
- 4.1 Biologische Materialschädigung und Referenzorganismen (19)
- 5.2 Metallische Hochtemperaturwerkstoffe (19)
- 6.2 Material- und Oberflächentechnologien (18)
- 9.4 Integrität von Schweißverbindungen (18)
- 5.6 Glas (15)
- 9.3 Schweißtechnische Fertigungsverfahren (15)
- 6.5 Synthese und Streuverfahren nanostrukturierter Materialien (14)
- 8.0 Abteilungsleitung und andere (12)
- 3 Gefahrgutumschließungen; Energiespeicher (10)
- 4.2 Material-Mikrobiom Wechselwirkungen (9)
- 6.7 Materialsynthese und Design (8)
- 7.1 Baustoffe (8)
- 7.6 Korrosion und Korrosionsschutz (8)
- 8.3 Thermografische Verfahren (8)
- 9.6 Additive Fertigung metallischer Komponenten (8)
- 1.9 Chemische und optische Sensorik (7)
- 5.3 Polymere Verbundwerkstoffe (7)
- 7.5 Technische Eigenschaften von Polymerwerkstoffen (7)
- 1.4 Prozessanalytik (6)
- 9.0 Abteilungsleitung und andere (6)
- 3.1 Sicherheit von Gefahrgutverpackungen und Batterien (5)
- 1.6 Anorganische Referenzmaterialien (4)
- 2 Prozess- und Anlagensicherheit (4)
- 4.5 Kunst- und Kulturgutanalyse (4)
- 8.1 Sensorik, mess- und prüftechnische Verfahren (4)
- 8.4 Akustische und elektromagnetische Verfahren (4)
- 9.2 Versuchsanlagen und Prüftechnik (4)
- 9.5 Tribologie und Verschleißschutz (4)
- 1.5 Proteinanalytik (3)
- 4.0 Abteilungsleitung und andere (3)
- 5.5 Materialmodellierung (3)
- VP Vizepräsident (3)
- VP.1 eScience (3)
- 1.1 Anorganische Spurenanalytik (2)
- 2.0 Abteilungsleitung und andere (2)
- 3.2 Gefahrguttanks und Unfallmechanik (2)
- 3.4 Sicherheit von Lagerbehältern (2)
- 8.2 Zerstörungsfreie Prüfmethoden für das Bauwesen (2)
- 8.6 Faseroptische Sensorik (2)
- 1.0 Abteilungsleitung und andere (1)
- 1.8 Umweltanalytik (1)
- 2.1 Sicherheit von Energieträgern (1)
- 2.2 Prozesssimulation (1)
- 3.3 Sicherheit von Transportbehältern (1)
- 3.6 Elektrochemische Energiematerialien (1)
- 5.0 Abteilungsleitung und andere (1)
- 6.4 Materialinformatik (1)
- 7.2 Ingenieurbau (1)
- 7.4 Baustofftechnologie (1)
- MP Mitglied des Präsidiums (1)
- MP.0 Mitglied des Präsidiums und andere (1)
- P Präsident (1)
- PST Präsidiale Stabsstelle (1)
Eingeladener Vortrag
- nein (1)
In the present study, internal damage to an AlSi12CuMgNi alloy reinforced with planar random Al2O3 short fibres was investigated after compression testing. Due to the alloy composition, this composite contains a second reinforcement phase in the form of eutectic Si, which builds interpenetrated networks in the volume and increases the creep resistance and load-bearing capacity of the material. Materials with their fibre plane parallel and transversal to the load direction were characterized in order to investigate the dependence of load partition and damage on fibre plane orientation. In-situ compression testing during neutron diffraction measurements showed that internal damage is strongly influenced by the load partition between matrix and reinforcement. Moreover, micro-computed tomography was performed in the same material after ex-situ compression for damage analysis. In the case of a fibre plane perpendicular to the applied load, breakage and interconnected cracks appeared in a significantly higher volume fraction than with a fibre plane parallel to load.
Two polyethylene types with ultra high (UHMWPE) and high molecular weight (HMWPE), which are used as neutron radiation shielding materials in storage casks for radioactive waste, were subjected to gamma irradiation doses up to 600 kGy and subsequent thermal ageing at 125 °C for up to one year. One material was a medical grade UHMWPE and the other a HMWPE containing an antioxidant. Degradation effects in the materials were characterized using colorimetry, UV-Vis spectroscopy, MIR and FTIR measurements, DSC and, in the case of HMWPE, insoluble content determination. Both materials exhibited a yellowing upon irradiation. The discoloration of UHMWPE disappeared again after thermal ageing, which is why it was attributed to annealable color centers in the form of free radicals entrapped in the crystalline regions of the polymer that recombine during thermal ageing. Furthermore, oxidation species were observed with MIR and FTIR spectroscopy. For HMWPE, the yellowing occurred during both irradiation and thermal ageing and was correlated to antioxidant decomposition. Additionally, black spots were observed after thermal ageing of HMWPE that were attributed to reaction products of antioxidant derivatives and catalyst residues. While only little evidence of oxidation species was found in the light material parts, oxidation is expected to concentrate in the black spots as the catalyst residue promotes hydroperoxide decomposition and thus radical formation that initiate polymer oxidation
A test campaign was launched to determine the mechanical properties of the HL-LHC 11 T Nb₃Sn magnet components in order to accurately model the mechanical properties in Finite Element simulations that predict the stress and strain distribution in these magnets. Static and dynamic test methods have been applied for determining elastic materials behavior, and highly accurate Young’s moduli are obtained with the dynamic methods resonance and impulse excitation. These non-destructive methods also enable temperature dependent modulus measurements during in situ heat cycles.
Polymers are favorable materials for gas separation membranes. In general, gas transport experiments are performed with films in the range of 100 µm thickness. However, in large-scale processes very thin selective polymer layers in the range of 100 nm to 1 µm are used. Moreover, it was shown that thin films behave different compared to thick films with respect to gas transport properties and physical aging as well. Thus, for fundamental research it is important to realize gas transport experiments with thin films. The Quartz Crystal Microbalance (QCM) is a very sensitive method to detect mass changes in the range of nanograms. Therefore, this method enables sorption experiments with thin films or layers attached to the QCM crystal (100 nm up to 1 µm). Here, we present the experimental set-up for using the QCM technique for characterizing the gas sorption behavior of thin polymer films in a temperature controlled pressurized environment (up to 50 bar) - also quartz crystals and crystal holders were optimized. The study aims for the characterization of long-term behavior and physical aging of high-performance polymers for gas separation membranes - such as polyimides and polymers of intrinsic microporosity (PIMs) and respective nanocomposites. Especially the differences of the behavior of thin films compared to films with thicknesses up to 100 µm as well as nanofiller induced-effects are adressed.
Low-alloyed CrMoV steels, such as T24, are widely used for welded components in fossil power stations due to their excellent creep-strength. Spectacular failure cases in the recent years exhibited severe cracking in T24 welds. The results showed that hydrogen-assisted cracking (HAC) occurring up to 200 degree Celsius cannot be excluded. Hence, a basic understanding is necessary on how hydrogen affects the material properties of welded microstructures. In this regard, each weld microstructure (HAZ and weld metal) has influence on the HAC susceptibility and respective hydrogen diffusion. Thus, the present contribution summarizes different results obtained from experiments with grades T24 (CrMoV alloy) and T22 (CrMo) and thermally simulated HAZ. Tensile tests were conducted with hydrogen charged specimens and compared to hydrogen-assisted stress corrosion cracking results obtained from slow strain rate tests (SSRT) up to 200 degree Celsius. Electrochemical permeation and degassing experiments were performed to identify a particular weld microstructure influence on hydrogen diffusion and trapping (especially in the HAZ). The results showed that T24 base material has improved resistance to hydrogen-assisted degradation/cracking. In contrast, the as-welded HAZ had remarkably increased susceptibility (tesnile tests at hydrogen concentration of 1 to 2 ppm). SSRT experiments confirmed this at elevated temperatures for both the T24 and the T22. Hence, the evaluation of a particular degradation of the mechanical properties should be performed independently for each weld microstructure. In addition, the HAZ showed decreased diffusion coefficients (at room temperature) of approximately one magnitude compared to the base materials. Trapped hydrogen was determined in the T24 at temperatures up to 120 degree Celsius compared to 75 degree Celsius in the T22. This has to be considered in case of changing operational temperatures, e.g. in the case of start-up and shutdown processes of boiler components.
Since geothermal wells are a feasible energy source to replace fossil fuel supply, many technologies have been developed to take advantage of geothermal energy. Nevertheless, service conditions in geothermal facilities are due to the chemical composition of hydrothermal fluids and temperatures, in many cases, extreme in terms of corrosion.
Therefore, materials selection based on preliminary material qualification is essential to guarantee a secure and reliable operation of the facilities. The corrosion behavior of different high-alloyed metals including Duplex and austenitic stainless steels as well as a nickel alloy have been evaluated in artificial geothermal fluids simulating the conditions in some locations with geothermal potential in Germany as well as two sites in Indonesia. The suitability of carbon steel 25CrMo4, stainless steels X2CrNiMo17-12-2, X2CrNiMo-22-5, X2CrNiMoCuWN25-7-4 and super austenitic steel X1CrNiMoCu32-28-7 in these geothermal fluids obtained by electrochemical measurements and exposure tests is limited. The nickel alloy NiCr23Mo16Al shows an excellent corrosion resistance against pitting corrosion. Excluding its high cost, it is a very good alternative to be used in the construction of geothermal facilities having highly saline brines. Stainless and Duplex steels exhibit a limited corrosion resistance concerning pitting and crevice corrosion. Beside of the higher alloyed materials, also the lowalloyed steel 25CrMo4 could be employed as a constructional material for the geothermal power plant in stagnant highly acidic non Saline environments, as long as the wall thickness of the material vs. corrosion rate is taken into account.
The formation of biofilms on different materials provokes high costs in industrial processes, as well as in medical applications. Therefore, the interest in development of new materials with improved surfaces to reduce bacterial colonization rises. In order to evaluate the quality and safety of these new materials, it is highly important to ensure world-wide comparable tests that are relying on statistical evidence. The only way to reach this statistical safety is through a high-throughput Screening under standardized test conditions.
We developed a flow through system for cultivation of biofilm-forming bacteria under controlled conditions with a total capacity for testing up to 32 samples in parallel. Quantification of the surface colonization was done by staining the bacterial cells with a fluorescence marker, followed by epifluorescence microscopy. More than 100 images of each sample were automatically taken and the surface coverage was estimated with the free open source software gmic (http://gmic.eu), followed by a precise statistical evaluation. Overview images of all gathered pictures of the whole material coupon were generated to illuminate the colonization characteristics of the selected bacteria on certain materials.
With this method, differences in bacterial colonization on different materials can be quantified in a statistically validated manner. The innovative and solid test procedure will support the design of improved materials for medical and industrial applications such as implants, ship hulls, pipelines, heat exchangers, aquaculture equipments, photovoltaic-panels and fundaments of wind power plants.
The Full-Notch Creep Test (FNCT) is widely used to characterize the slow crack growth (SCG) behavior of polyolefin materials in “inert” media as well as effects of environmental stress cracking (ESC) in which the medium has decisive influence on damage mechanism and time to failure tf*. Usually the FNCT is applied as a standardized testing method (ISO 16770) using a few universal liquid media, such as solutions of Arkopal N 100 (detergent).
Selected relevant PE-HD materials are investigated also in real media and influences of temperature and geometry of specimen and notch are explicitly addressed. The investigations comprise also the ESC behavior of PE-HD in media that are sorbed to a significant extent – such as Diesel and Biodiesel – based on comparison with samples previously saturated with those media.
Due to their chemical structure, a rigid disk-like aromatic core and flexible alkyl chains attached to the core, discotic liquid crystals (DLCs) can organize and stack themselves into columns in a hexagonal columnar mesophase, a mesophase in between the plastic crystalline and isotropicphase. The overlap of the π orbitals of the aromatic core in the hexagonal columnar mesophase leads to a high charge-carrier mobilitie along the column axis – these columns can be considered as “moleculer nanowires” making liquid crystals a promising class of materials for electronic applications. Previous studies on DLCs showed that the phase behavior of DLCs is susceptible to nano confinement. Here in this study, the thermotropic collective orientational order of 2,3,6,7,10,11 hexakis[hexyloxy] triphenylene (HAT6), a triphenylene based DLC, and the effects of nano confinment on of its phase behavior were investigated by broadband dielectric spectroscopy (BDS) and differential scanning calorimetry (DSC). HAT6 was embedded into nanoporous anodic aluminum oxide membranes by melt infiltration in the isotropic phase under argon atmosphere. The filled membranes have the thickness of 80 µm and the diameter of 15mm and parallel aligned tubular nanopores having the pore diameters of 25, 40, 80 and 180 nm. The filling degree for each sample was checked by thermogravimetric analysis (TGA) in order to ensure complete filling. The bulk HAT6 forms, a hexagonal columnar phase between the isotropic phase above 371 K, and the plastic crystalline phase below 340 K. Unlike the bulk, the confined HAT6 forms two peaks in the heat flow during the plastic crystalline-to-hexagonal columnar phase transition, which might be the evidence of two different phase structures close to the wall and in the pore center. Moreover, the isotropic-to-columnar transition of the confined HAT6 shifts with decreasing pore diameter to lower temperatures.
Advanced methods for 3D green density characterization like computed tomography and 3D FE sinter modeling can be utilized for increasing the reliability of sintered components. The experimental in situ observation of sintering, however, is currently restricted to silhouette methods, i.e. heating microscopy. For complex shaped samples, in situ shape screening during shrinkage would allow much better validation of 3D sinter simulation models. Further, by revealing temporary sinter warpage, 3D high-temperature shape screening would allow to locate potential defects of complex sintered components. Against this background, BAM developed a testing device for in situ 3D high-temperature shape screening for ceramic and glass-ceramic tapes up to 1000°C. Current work is focused on dropping this restriction in sample shape and temperature. The poster illustrates the current state of this work and possible applications of the method e.g. in detecting sinter warpage of metallized glass-ceramic LTCC tapes.