Ingenieurwissenschaften und zugeordnete Tätigkeiten
Filtern
Erscheinungsjahr
- 2019 (287) (entfernen)
Dokumenttyp
- Vortrag (287) (entfernen)
Sprache
- Englisch (287) (entfernen)
Referierte Publikation
- nein (287) (entfernen)
Schlagworte
- Additive Manufacturing (29)
- Corrosion (19)
- MIC (9)
- Microstructure (9)
- Welding (9)
- Additive manufacturing (8)
- Diffraction (8)
- Surface functionalization (8)
- Magnetocaloric (7)
- Nanoparticle (7)
Organisationseinheit der BAM
- 6 Materialchemie (74)
- 9 Komponentensicherheit (66)
- 8 Zerstörungsfreie Prüfung (55)
- 5 Werkstofftechnik (51)
- 8.5 Röntgenbildgebung (35)
- 9.3 Schweißtechnische Fertigungsverfahren (33)
- 7 Bauwerkssicherheit (29)
- 6.6 Physik und chemische Analytik der Polymere (23)
- 9.4 Integrität von Schweißverbindungen (23)
- 4 Material und Umwelt (21)
- 1 Analytische Chemie; Referenzmaterialien (18)
- 6.2 Material- und Oberflächentechnologien (18)
- 5.4 Multimateriale Fertigungsprozesse (17)
- 7.6 Korrosion und Korrosionsschutz (17)
- 8.0 Abteilungsleitung und andere (16)
- 3 Gefahrgutumschließungen; Energiespeicher (14)
- 6.3 Strukturanalytik (13)
- 1.2 Biophotonik (12)
- 4.5 Kunst- und Kulturgutanalyse (11)
- 5.1 Mikrostruktur Design und Degradation (11)
- 6.1 Oberflächen- und Dünnschichtanalyse (11)
- 5.6 Glas (10)
- 9.5 Tribologie und Verschleißschutz (10)
- 2 Prozess- und Anlagensicherheit (9)
- 4.1 Biologische Materialschädigung und Referenzorganismen (8)
- 5.2 Metallische Hochtemperaturwerkstoffe (8)
- 5.3 Polymere Verbundwerkstoffe (7)
- 6.7 Materialsynthese und Design (7)
- 7.5 Technische Eigenschaften von Polymerwerkstoffen (6)
- 6.5 Synthese und Streuverfahren nanostrukturierter Materialien (5)
- 3.2 Gefahrguttanks und Unfallmechanik (4)
- 5.5 Materialmodellierung (4)
- 7.1 Baustoffe (4)
- 8.4 Akustische und elektromagnetische Verfahren (4)
- 9.0 Abteilungsleitung und andere (4)
- 1.9 Chemische und optische Sensorik (3)
- 2.4 Prüfung und Bewertung von Explosivstoffen/Pyrotechnik (3)
- 3.0 Abteilungsleitung und andere (3)
- 3.3 Sicherheit von Transportbehältern (3)
- 3.4 Sicherheit von Lagerbehältern (3)
- 6.0 Abteilungsleitung und andere (3)
- 8.6 Faseroptische Sensorik (3)
- 1.1 Anorganische Spurenanalytik (2)
- 2.1 Sicherheit von Energieträgern (2)
- 2.2 Prozesssimulation (2)
- 2.5 Konformitätsbewertung Explosivstoffe/Pyrotechnik (2)
- 4.2 Material-Mikrobiom Wechselwirkungen (2)
- 7.4 Baustofftechnologie (2)
- 9.2 Versuchsanlagen und Prüftechnik (2)
- 1.5 Proteinanalytik (1)
- 3.1 Sicherheit von Gefahrgutverpackungen und Batterien (1)
- 5.0 Abteilungsleitung und andere (1)
- 7.0 Abteilungsleitung und andere (1)
- 7.2 Ingenieurbau (1)
- 8.1 Sensorik, mess- und prüftechnische Verfahren (1)
- 8.2 Zerstörungsfreie Prüfmethoden für das Bauwesen (1)
- S Qualitätsinfrastruktur (1)
- S.2 Digitalisierung der Qualitätsinfrastruktur (1)
Eingeladener Vortrag
- nein (287)
Chemical compositions of the welds have significant effect on weld quality. Current inspection methods for the weld seams employ mostly post factum methods and cannot prevent weld defects.Elemental burn offs may significantly affect solidification leading to embrittlement or cracking. Control of weld chemical compositions insures a controlled solidification and resistance to related weld defects.
Chemical composition of the welding seam and HAZ has significant effect on weld quality.
Current inspection methods for weld seams measure and investigate post factum and cannot prevent weld defects. Element burn-off may significantly affect solidification leading to embrittlement or cracking. Control of weld chemical compositions insures a controlled solidification and resistance to related weld defects. “Industry 4.0” is the current trend of automation and data exchange in manufacturing technologies. With this trend “intelligent” welding machines will be developed. LIBS can provide significantly important online data for such systems.
Broadband dielectric spectroscopy in the frequency range from 10-1 to 109 Hz is employed to revisit the segmental dynamics of the miscible blend system poly(vinyl methyl ether)/polystyrene (PVME/PS) in dependence on the composition firstly in the bulk state. Here especially the case of high polystyrene concentrations is considered. It is important to note that only the molecular dynamics of PVME segments as affected by PS is observed because the dipole moment of polystyrene is negligible. Three relaxation processes are found which are due to fluctuations of differently constrained or confined PVME segments. The degree of the confinement of PVME segments due to PS is discussed in dependence on the composition.
Further a spatial confinement is considered by investigating thin films of the PVME/PS blend where the film thickness was varied from 100 nm down to 5 nm. Two concentrations of PVME/PS (50/50 wt% and 25/75 wt%) are investigated. To measure nanometer thick films a novel electrode system based on nanostructured electrodes was employed. Nanostructured electrodes can be considered as a cut-edge technology in dielectric spectroscopy. The relaxation spectra of the films showed multiple processes which are discussed in dependence on the film thickness.
Polymers at interfaces play a major role in a broad variety of applications ranging from engineering purposes (for instance polymer based nanocomposites) to high tech implications (for instance light emitting diodes). Here the glass transition and glassy dynamics is considered for epoxy-based nanocomposite with Layered Double Hydroxide nanofiller and for thin films of a misicble polymer blend of PVME/PS with thicknesses down to 7 nm. The materials are investigated by spectroscopic techniques (broadband and specific heat spectroscopy), as well as by fast scanning calorimetry and small- and wide-angle X-ray scattering.
Two epoxy-based nanocomposites with different nanofillers (layered double hydroxide and boehmite) were investigated employing temperature modulated DSC, flash DSC and broadband dielectric spectroscopy. Detailed investigation on the molecular mobility of the two systems showed the effect of the fillers on the structure of the bulk epoxy matrix and the interface formed at the polymer/particle interface
It was found for inorganic/polymer nanocomposites that a so-called Rigid Amorphous Phase (RAF) is formed in the interfacial region by adsorption of polymer segments onto the nanoparticles. The segmental dynamics of RAF is expected to be altered, as compared to the pure matrix, which might percolate into the entire system, affecting the overall nanocomposite properties. Here, the structure and molecular mobility of epoxy-based PNCs with different nanofillers (layered double hydroxide and boehmite) was studied by a combination of calorimetric and X-Ray scattering techniques. Temperature modulated DSC (TMDSC) showed that depending on the nanofiller, RAF can reach up to 40 wt % of the system or, on the contrary, the overall mobility of the matrix might increase due to the presence of particles. Such contrasting results, including the high amount of RAF, which was never shown before for epoxy-based PNCs, emphasize the importance of interfaces. Additionally, glass transition and glassy dynamics were investigated by a novel technique, Flash DSC (heating rates up to 10 kK/s) employed for the first time to a thermosetting system and electrospun fibers, which did not result in their degradation. It was used to study both the vitrification kinetics and glassy dynamics of the PNCs, for instance further confirming the presence of RAF and its impact on the overall material properties.
For inorganic/polymer nanocomposites a so-called Rigid Amorphous Phase (RAF) is formed in the interfacial region by adsorption of polymer segments onto the nanoparticles. The segmental dynamics of RAF is expected to be altered, as compared to the pure matrix, which might percolate into the entire system, affecting the overall nanocomposite properties. A combination of two relaxation spectroscopy techniques (Broadband Dielectric Spectroscopy (BDS) and Specific Heat Spectroscopy (SHS) in a form of Temperature Modulated DSC (TMDSC)) as well as Fast Scanning Calorimetry (FSC) was employed to investigate the structure and molecular mobility of nanocomposites based on Epoxy and Layered Doubled Hydroxides with different nanoparticle content.
First, BDS investigations proved the existence of a process, which is present only for nanocomposites, assigned to the dynamics of polymer segments within RAF. Second, the amount of RAF was quantified by analyzing the change of specific heat capacity step of nanocomposites, comparing to the pure material.
Thirdly, the glass transition of nanocomposites was studied with FSC, applying high heating rates (500-10 000 K/s). Considering that all techniques probe essentially the same molecular process, an activation plot was constructed, delivering a complete picture of the molecular mobility and structure of the polymer nanocomposites including RAF.
For inorganic/polymer nanocomposites a so-called Rigid Amorphous Phase (RAF) is formed in the interfacial region by adsorption of polymer segments onto the nanoparticles. The segmental dynamics of RAF is expected to be altered, as compared to the pure matrix, which might percolate to the entire system, affecting the overall nanocomposite properties. A combination of two relaxation spectroscopy techniques (Broadband Dielectric Spectroscopy (BDS) and Temperature Modulated DSC (TMDSC)) as well as Fast Scanning Calorimetry (FSC) was employed to investigate the structure and molecular mobility of nanocomposites based on Epoxy and Layered Doubled Hydroxides with different nanoparticle content. First, BDS investigations proved the existence of a process, which is present only for nanocomposites, assigned to the dynamics of polymer segments within RAF. Second, the amount of RAF was quantified by analyzing the change of specific heat capacity step of nanocomposites, comparing to the pure material. Thirdly, the glass transition of nanocomposites was studied with FSC, applying high heating rates (0.5-10 kK/s). Considering that all techniques probe essentially the same molecular process, an activation plot was constructed, delivering a complete picture of the molecular mobility and structure of the polymer nanocomposites including RAF.
Because of its excellent corrosion resistance, high tensile strength and high ductility, duplex stainless steel 2205 offers many areas of application. Though laser beam welding accompanied by high cooling rates, duplex steels tend to perform higher ferrite contents in weld metal as the base metal, which leads to a reduction of ductility and corrosion resistance of the weld joint. To overcome this problem, a solution, based on buttering the plate edges by laser metal deposition (LMD) with material containing higher Ni concentrations prior to laser welding was suggested.
In this context different process parameters for LMD and different mixtures of duplex and nickel powder, were investigated. In a second step the possibility of welding those edges defect free while achieving balanced austenite-ferrite ratio was verified with metallographic analysis, Electron Backscatter Diffraction (EBSD) and impact testing according to Charpy. The improved corrosion resistance was observed with ASTM G48 standard test method.
Because of its excellent corrosion resistance, a high tensile strength together with a high ductility, duplex stainless steel 2205 offers many areas of application in the chemical and the offshore industry, to name just two. Though welding, especially laser beam welding accompanied by high cooling rates, duplex steels tend to perform higher ferrite contents in weld metal upon cooling down from melting temperature as the base metal. This trend leads to a reduction of the ductility as well as the corrosion resistance of the weld joint. To overcome this problem a solution, based on buffering the plate edges by laser metal deposition with material containing higher Ni concentrations prior to the laser welding was suggested. This method offers more benefits in comparison to conventional usage of higher Ni-alloyed filler wire due to the better control over Ni-distribution in the weld seam, resulting in balanced austenite- ferrite ratio everywhere in the weld metal.
In this context different mixtures of duplex and nickel powder were investigated as well as different process parameters, that enable a smooth surface structure with slightly reduced ferrite contents. In a second step the possibility of welding those edges defect free with standard parameters while achieving balanced austenite- ferrite ratio was verified with metallographic analysis of the microstructure, Electron Backscatter Diffraction (EBSD) and impact testing according to Charpy. The improved corrosion resistance of the welds in comparison to unbuffered ones was observed with the ASTM G48 standard test method.
Explosive spalling is caused by, among others, the thermohydraulic spalling mechanism. During this process, vaporization, dehydration, moisture-transport and condensation processes interact. As a result, a drying and dehydration zone as well as a saturated zone, known as a moisture clog, are observed inside the unilaterally-heated concrete. The presented research is focused on the experimental investigation of the underlying thermohydraulic processes.
To investigate these, a test methodology based on X-ray computed tomography (CT) and nuclear magnetic resonance (NMR) was developed. Thereby, the X-ray CT scans are carried out simultaneously during the application of a defined unilateral-heating regime on a specially-constructed specimen. This miniaturized specimen, equipped with a double-layer casing, reproduces the condition within a planar, unilaterally-heated building component.
A preliminary test methodology and the first experimental results were presented at the 5th International Workshop on Concrete Spalling in Borås, Sweden (2017). The contribution for the upcoming workshop presents an improved version of this test methodology and new results for a high-performance concrete (HPC) mixture exposed to temperatures up to 500 °C. Regarding the CT measurements, a higher time-resolution of 15 min was achieved and a quantification of the moisture changes was implemented. Due to an increase in signal quality of the NMR measurements, a pore-size specific moisture distribution can now be resolved. This allows to conclude about the moisture reconfiguration between small gel pores and larger interhydrate pores. Additionally, the NMR measurement are no longer limited to first 2.5 cm below the heated surface but a one-dimensional moisture distribution can now be estimated over the whole 10 cm long specimen.
The presented results demonstrate that the combination of X-ray CT and NMR measurements enables to image and quantify the thermally-induced moisture transport and reconfiguration from small gel pores up to macro pores. This provides important insights into the thermohydraulic damage mechanism and leads to a better understanding of spalling avoidance strategies, like the addition of polypropylene fibres.
The shape of the parts, created by the technology of direct laser metal deposition (DLMD), is influenced by various parameters, for example, the power and diameter of the laser source spot. The contribution of energy from the laser affects the temperature distribution in the formed layers. The changing temperature in the working area entails a change in the geometry of the layers and affects the stability of the process. In this paper, experiments on the measurement of temperature cycles in the DLMD process with different directions of the filling track are carried out. An infrared camera was used to measure thermal cycles. The calibration of the acquired data (i.e. correspondence table between the intensity of thermal radiation of the material and the absolute temperature) was done with help of two-color pyrometer ex situ and in situ measurements. The experiments are carried out on two materials 316L and Inconel 718. The effect of the maximum temperature on the layer height is shown, and thermal cycles in the formation of layers for different filling strategies are presented.
Laser based Powder Bed Fusion (L-PBF) is an additive manufacturing technique that has been continuously developed in the past years. It offers unparalleled design freedom and the resulting mechanical properties match, in some cases even exceed, those of materials processed by conventional manufacturing techniques. Nonetheless the process is prone to create Residual Stresses (RS) resulting from the sequential melting and solidification of the material. RS can reduce load bearing capacity and generate unwanted distortions thus diminishing the potential of L-PBF. This research activity aimed at characterizing the RS state in Inconel 718 L-PBF specimens using multiple diffraction methods. The microstructure as well as the surface and bulk residual stresses were investigated. The RS analysis was performed using X-ray, synchrotron and neutron diffraction methods to provide information at different depths within the specimen. The measurements were performed at the Bundesanstalt für Materialforschung und –prüfung (BAM), the EDDI beamline at BESSY II synchrotron and E3 line at BER II neutron reactor of the Helmholtz-Zentrum für Materialien und Energie (HZB) Berlin. The results revealed a depth depending RS state. The longitudinal and transverse stress components measured by X-ray and synchrotron at the surface agree well, exhibiting stress values around the yield strength of the material. In addition, synchrotron mapping showed gradients along the width and length of the sample for the longitudinal and transverse stress components. Lower RS values compared to surface RS were measured in the bulk of the material using neutron diffraction. The longitudinal stress component in the bulk was tensile and gradually decreased towards the edge of the specimen. The normal component however did not change significantly along the specimen dimensions and was of compressive nature. The transversal component was almost negligible. The results indicate that a stress re-distribution takes place during the deposition of the consecutive layers, which has to be further investigated.
The control of friction and wear is a major concern in many industrial applications. A promising method for a tailored surface modification is the so-called laser implantation technique. This method combines surface texturing and material optimization in one processing step by a localized dispersing of hard ceramic particles using pulsed laser radiation. Wear resistant, protruding micrometric features (implants) with defined geometry can be created in deterministic pattern where needed on highly stressed surfaces, i.e. on forming or cutting tools. However, in order to maintain the implants over the tool’s lifetime, a suitable selection of hard ceramic particles is a prerequisite. They must provide a defect-free Metal Matrix Composite with a high share of homogeneously distributed particles and especially a high implant hardness.
In this study TiN, TiC and TiB2 hard particles were compared as implant materials for the first time. By a systematic variation of the pulse power and pulse duration, their dispersing behavior and influence on the material properties of AISI D2 tool steel was investigated. Although all powder materials had grain sizes smaller than 10 µm, it was possible to disperse them by pulsed laser radiation and to obtain defect-free protruding implants. The highest share of dispersed particles (~64 %) was observed for TiB2. By scanning electron microscopy and energy dispersive X-ray spectroscopy, it was also shown that a significant share of the pre-placed particles was dissolved by the laser beam and precipitated as nanometer sized particles within the matrix during solidification. These in-situ formed particles have a decisive influence on the material properties. While the TiN and TiC implants have shown maximum hardness values of 750 HV1 and 850 HV1, the TiB2 implants have shown the highest hardness values with more than 1600 HV1. By X-ray diffraction, it was possible to ascribe the lower hardness values of TiC and TiN implants to high amounts of retained austenite in the metal matrix. By implanting TiB2, the formation of retained austenite was successfully suppressed due to the in-situ formation of TiC particles, which was proven by electron backscatter diffraction. In conclusion, all the implant materials are basically suitable for laser implantation on AISI D2 tool steel. However, TiB2 has shown the most promising results.
Renowned institutions in the field of tribology combine their testing and analytical capabilities with experts in materials/process information management technology to provide the respective services in Europe (i-TRIBOMAT). This requires a centralized materials information management system or the standardised capture, consolidation and harmonization of tribological information.
Microstructure ageing of stainless steel AISI 316L manufactured by selective laser melting (SLM)
(2019)
Additive manufacturing (AM) processes, such as SLM, offer a variety of advantages compared to conventional manufacturing. Today AM parts are still comparatively less cost-effective if they are manufactured in large quantities. To make the AM parts more cost-efficient, the AM process has to be improved. It requires a good understanding of microstructure formation, microstructure-property-relations and ageing processes affected by different loads.
In this work the ageing behavior of SLM manufactured AISI 316L stainless steel is evaluated. The microstructure effected by mechanical, thermal and corrosive loads are investigated and compared to as-built microstructure. Tensile tests are used for mechanical ageing. For thermal and corrosive loads the typical application conditions of 316L apply. The methods of microstructure investigation include SEM, TEM, CT and EBSD. The main object of this work is the description of microstructure and ageing processes of AM parts.
Additive manufacturing (AM) offers diverse advantages compared to conventional manufacturing. In this work the microstructure of austenitic steel 316L, manufactured with Selective Laser Melting (SLM), was analyzed and compared to microstructure of 316L hot rolled material. Methods used for analysis are microprobe, optical microscopy and electron backscatter diffraction.