Ingenieurwissenschaften und zugeordnete Tätigkeiten
Filtern
Erscheinungsjahr
Dokumenttyp
- Posterpräsentation (669) (entfernen)
Sprache
- Englisch (669) (entfernen)
Schlagworte
- Additive manufacturing (30)
- Corrosion (30)
- Mechanochemistry (23)
- Nanoparticles (19)
- Additive Manufacturing (18)
- Glass (18)
- Crystallization (16)
- Fluorescence (15)
- In situ (14)
- Computed tomography (13)
Organisationseinheit der BAM
- 6 Materialchemie (198)
- 5 Werkstofftechnik (85)
- 8 Zerstörungsfreie Prüfung (80)
- 6.3 Strukturanalytik (62)
- 6.6 Physik und chemische Analytik der Polymere (54)
- 8.5 Röntgenbildgebung (53)
- 6.1 Oberflächen- und Dünnschichtanalyse (48)
- 9 Komponentensicherheit (46)
- 1 Analytische Chemie; Referenzmaterialien (44)
- 4 Material und Umwelt (34)
Eingeladener Vortrag
- nein (1)
Ferritic-martensitic high temperature alloys are widely used as boiler tube and heat exchanger materials in combustion based power plants. All technologies have in common that the applied materials are exposed to different temperatures, process pressures and reactive atmospheres which lead to a change of the material properties and a further degradation of the material.
To date corrosion analytics mainly proceeds via the use of various microscopic techniques and the analysis of the corrosion products after the reaction is completed. Comprehensive efforts have been made to study high temperature corrosion by the use of environmental SEM’s or in-situ TEM technologies. The here presented work will show a different approach to study high temperature gas corrosion in a multiple gas atmosphere by energy dispersive X-ray diffraction (EDXRD). For this technique high energetic white X-ray radiation (10-100 keV) was used as radiation source instead of conventional monochromatic radiation. It enables us to study crystallization procedures on short and medium time scales (1 min < t < 24 h) and the collection of Bragg-Signals of the phases of interest as a function of process time. Their occurrence can directly be correlated with thermodynamic and kinetic parameters. A special designed corrosion reactor was used to combine high temperature gas corrosion experiments with the collection of diffraction patter. The crystallization and reaction paths for oxide and sulfide formation was followed in-situ on Fe-Cr and Fe-Cr-Mn model alloys in a hot SO2 containing (T=650 °C) atmosphere.
Influence of deposition hatch length on residual stress in selective laser melted Inconel 718
(2018)
The present study aims to evaluate the bulk residual stresses in SLM parts by using neutron diffraction measurements performed at E3 line -BER II neutron reactor- of Helmholtz-Zentrum für Materialien und Energie (HZB) Berlin. Together with microstructure characterization and distortion measurements, it is possible to describe the stress state throughout the whole sample. The sample was measured in as-build condition (on a build plate) and after releasing from the build plate. The used material is the nickel based superalloy 718. This alloy is widely used in aerospace and chemical industries due to its superior corrosion and heat resistant properties.
Obtained results indicated different residual stress states for each of the transversal, longitudinal and normal component. The normal and transversal component exhibits a rather compressive behavior while the longitudinal was tensile in the center part of the sample and became compressive towards the tip. As expected, the absolute values of all stress components decreased after releasing the sample from the building plate. A surface scan utilizing a coordinate-measuring machine (CMM) allowed us to present top surface distortion before and after releasing. The top surface showed a distortion around ±80µm after releasing. Microstructure evolution in the scanning-building cross-section is largely dominated by columnar grains. In addition, many small random orientated grains are prominent in the regions of a laser overlap during SLM.
In summary, for the sample of superalloy 718 manufactured by SLM, a small distortion occurred when removing the sample from the build plate whereby the residual stress state decreases. Moreover, the observed columnar grains in the building direction could give a reason for the lowest stress values in that normal direction. However, the most important parameter controlling the residual stresses is the temperature gradient. Hence, future investigations are planned for a different scan strategy to distribute the laser impact in a more homogenous manner.
Ellipsometry is well known as a highly sensitive and reproducible surface analysis technique. However, in a context of metrological applications, the most important property of a measurement process is accuracy, relying on statistical precision, (reproducibility) and trueness (in an absolute sense versus a given standard). The latter is much more difficult to achieve. In this presentation, we discuss the possibility of establishing ellipsometry in a diverse metrological landscape by means of defining standard procedures and best practice methodologies for the measurement and for calibration purposes. The most important task of this approach is to determine the model-inherent uncertainty, originating from parameter coupling. We achieve this by means of sensitivity analysis of the parameters resulting from the fit process. We discuss the definition of reference materials by which accuracy can be made available for ellipsometry, passed along between ellipsometry laboratories and for other measurement techniques. The determination of uncertainty is presented in this work for a number of examples involving difficult analysis models employed for samples from different production environments. We present a standardization initiative with the goal to disseminate this work into an international standard alongside an inter-laboratory study comparing the results for complex samples gained by laboratories with different instrumentation. We also present the results gained within EURAMET projects focused on the metrology of materials with strong non-idealities used in photovoltaics and other energy technology.
As the well-known damage mechanisms slow crack growth (SCG) and environmental stress cracking (ESC) are the major causes for possible failure of polyolefin-based materials, especially for PE-HD, they are highly relevant and need to be considered thoroughly. Furthermore, due to slight but perceptible differences in damaging effect, a differentiation between SCG and ESC is expedient. SCG appears in “inert” or “neutral” media without a decisive influence of the surrounding medium whereas ESC occurs in “active” media, which influence the failure behavior and time to failure crucially.
To characterize the inherent resistance of the material against those damage mechanisms, the well-established Full-Notch Creep Test (FNCT) is used. In this study, the FNCT – usually applied according to ISO 16770 [3] using a few universal model liquid media and mainly for pipe materials – is extended by investigations with appropriate parameters of selected relevant PE-HD container materials also in real media, such as the topical fuels diesel and biodiesel. The investigations were performed using a novel FNCT-device with 12 individual sub-stations, each equipped with individual electronic stress and temperature control and continuous online monitoring of the specimen elongation.
Especially, mechanical stress and temperature were varied systematically during FNCT and time to failure values, time-dependent elongation data as well as detailed fracture surface analysis by laser scanning microscopy (LSM) were combined for the first time (Fig. 1). Particularly, the fracture surface analysis provides a sound basis to characterize failure behavior, mainly regarding the balance between brittle crack propagation and ductile deformation. Therefore, fracture surface analysis is an essential tool for a decent assessment of SCG and ESC by FNCT measurements.
The copper alloyed stainless steel 1.4542 (X5CrNiCuNb16-4) is used in different areas due to its good mechanical properties and corrosion resistance. Strength and corrosion resistance can be adjusted by the heat treatment, which is of importance for the application of this alloy. The mechanical properties (strength and hardness) are attributed to the dispersive precipitation of the copper rich ε–Phase. The additional precipitation of chromi-um carbides can reduce the corrosion resistance. Different ageing states were produced to investigate the precipitation behaviour with various methods. Furthermore, the influence of cold-rolling on the precipitation behaviour was studied in comparison to a solution annealed state without deformation. The microstructure was studied by SEM and the variations of hardness and magnetic proportion were characterised. The electrochemical potentiodynamic reactivation (EPR) was used to determine the corrosion resistance and detect chromium depletion in all heat-treated states. The results show that a work hard-ening accelerates the precipitation rate, while ageing at 600 °C reduces the corrosion resistance due to chromium depletion.
Hyperbranched polyamine ester (HPAE)/ kaolinite nanocomposites were papered via an ex situ (solution-based) method. The kaolinite has been modified by dodecylamine (DCA). SAXS measurements revealed that the Ka interlayer space increased from 0.71 to 3.6 nm-1. A partly exfoliated structure of the HPA/Ka-DCA nanocomposites was proved by SAXS and TEM. By a combination of BDS and SHS, the relaxation properties of the nanocomposites were investigated in dependence on frequency and temperature. The activation energies of γ-relaxation for the nanocomposites were lower than the values found for the pure HPAE. The segmental dynamics (α- relaxation) was found to be screened out by the conductivity contribution. While it is retrieved by SHS employing AC-chip calorimetry. A systematic change of the dynamic glass transition estimated by AC-chip calorimetry was observed, which is in agreement with a behavior expected for a confined sample. The confinement effect of the Ka-DCA nanofillers reduces the glass transition temperature Tg and enhances, meanwhile, the electrical conductivity of the polymer. By comparing the temperature dependence of the dynamic glass transition measured with SHS and that of the dc conductivity measured by dielectric spectroscopy, a decoupling in their temperature dependencies was found.
With increasing concentration of the nanofiller, which results in a stronger glass-formation behavior, this decoupling becomes weaker.
Hybrid materials have attracted growing interest during the last decade, particularly due to their extraordinary properties. Cycloalyphatic-epoxy oligosiloxane (CEO) resin was shown to be a good candidate as a barrier material for the encapsulation purposes. Incorporation of inorganic nanoparticles such as Boehmite (BA) into polymers was observed to modify their specific characteristics, in particular, thermal, thermo-oxidative and barrier ones. In this work, novel BA-embedded organic inorganic hybrid nanocomposite material was engineered by combining the advantageous properties of hybrid polymers and nanoparticle enhancement effect. Impacts of particles on the photocuring kinetics, degree of crosslinking and the resultant changes in the thermal properties of the cured films were investigated. CEO synthesis via condensation reaction was confirmed by 1H and 29Si NMR. The particle distribution within the films was verified by SEM including transmission mode coupled with EDX elemental analysis. Photocuring kinetics and thermal properties of the films were studied by in situ FTIR spectroscopy and DSC with TGA, respectively.
The layer-by-layer Additive Manufacturing (AM) by means of Selective Laser Melting (SLM) offers many prospects regarding the design of a part used in aeroplane components and gas turbines. However, structural deviations from the nominal morphology are unavoidable. The cooling of the finished part leads to shrinkage and a high surface roughness is induced by attached powder particles affecting the part volume too.
The integrity and load-bearing capacity of a SLM produced lattice structure (see Fig.1) has been investigated by means of in-situ X-ray computed tomography during compression. The lattice structure was compressed by 10 % in height with an applied maximum force of 5 kN. Additionally, a single strut has been investigated ex-situ as a component of the lattice structure. With the higher resolution achieved on the single strut, the pore distribution (size and location) as well as the surface roughness were assessed. One of the main results coming from the in-situ analysis was that the nodes were identified as the weakest points in the lattice structure.
Collective Orientational Order and Phase Behavior of a Discotic Liquid Crystal under Confinement
(2018)
Discotic liquid crystals (DLCs) are a promising class of soft matter for electronic applications. This is due to their ability to self-organize into columns in a hexagonal columnar mesophase, driven by the overlapping of the π orbitals of their aromatic cores. This leads to a high charge-carrier mobility along the column axis. Previous studies on DLCs showed that their properties, such as phase transition temperatures and enthalpies, are susceptible to nanoconfinement. In this study, 2,3,6,7,10,11 hexakis[hexyloxy] triphenylene (HAT6) was confined into parallel aligned cylindrical nanopores of anodic aluminum oxide (AAO) membranes by melt infiltration. Furthermore, the pore surfaces of a series of membranes were chemically modified, resulting in a more hydrophobic pore surface than the unmodified ones. Collective orientational order and phase behavior of HAT6 confined into modified and unmodified nanopores of AAO were investigated by broadband dielectric spectroscopy and differential scanning calorimetry respectively.
In recent years, substantial efforts have been devoted to investigating nanoscopic confinement of polymers, and its effect on glassy dynamics. Broadband Dielectric Spectroscopy (BDS) was used to study the dynamics of ultra-thin films of PVME/PS 50/50 wt% blend, employing a novel nano-structured capacitor sample arrangement. The investigated system shows a complex dynamic behavior. First, an α-relaxation, related to a bulk-like layer was found. Second, an α’-relaxation was observed, characteristic for dynamically asymmetric blends, where the out of equilibrium dynamics is attributed to weakly-cooperative PVME segments relaxing within a frozen environment of PS segments. Thirdly, for thinnest films, an Arrhenius-like process was dominant in the dielectric spectra, indicating localized fluctuations of the segments. Relaxation rates of this process resembled that of the degenerated α-relaxation of the adsorbed layer, found for pure PVME, thus it was assigned accordingly. For thinnest films, this process undergoes a further confinement, due to the topological constraints, introduced by PS. Such multiple confinement effect has not been reported for ultra-thin films of polymer blends, before this study.
The polymer matrix region near a filler surface, termed as the interface, witnessed increasing interest, due to its possible influence on the macroscopic properties of the nanocomposite. The interphase is expecting to have different segmental dynamic, as compared to the pure matrix, which can percolate into the entire system. Here, the segmental dynamics of epoxy/Boehmite nanocomposite was studied by Broadband Dielectric Spectroscopy. It was found that an artificial relaxation process is present in the nanocomposite, on the contrary to the pure epoxy system. It was assigned to constrained fluctuations of polymer chains in the interfacial region, due to the nanofiller. However, the overall dynamic Tg of the system decreased with increasing filler concentration, indicating higher segmental mobility. This was in accordance with Temperature Modulated DSC investigations of specific heat capacity of the system, which was found to increase with increasing filler concentration, up to 10 wt%, indicating increasing mobility of the polymer matrix segments. Surprisingly, for the highest filler content, the heat capacity decreases, implying a formation of an immobilized rigid amorphous phase in the interfacial region.
In well-annealed thin polymer films, with non-repulsive polymer/substrate interactions, an irreversibly adsorbed layer is expected to form. These adsorbed layers have shown great potential for technological applications. However, their growth kinetics and molecular dynamics are still not fully understood. This is partially due to the hard accessibility of these layers in thin films. Here, the irreversibly adsorbed layers of homopolymer thin films are revealed by solvent-leaching experiments. First, the growth kinetics of these layers is investigated as a function of annealing times and original film thickness. The thickness, topography and quality of the adsorbed layer is controlled with Atomic Force Microscopy (AFM). Secondly, the molecular mobility of the adsorbed layer is investigated with Broadband Dielectric Spectroscopy (BDS). A recently developed nanostructured capacitor is employed to measure the adsorbed layers with a free surface layer. The results are quantitatively compared and discussed with respect to recently published work.
Optimization of laser treatment parameters of Inconel 686 overlay weld on carbon steel 13Mo4-5
(2017)
The work presents the effects of the change of the laser cladding parameters on microstructure, chemical composition and mechanical properties of Inconel 686 overlays (coatings). To obtain the best quality of these coatings the various parameters of laser cladding such as the power density of the laser beam, the laser beam velocity and overlapping ratio of the weld tracks were applied. The substrates were boilers plate made of the 13Mo4-5 steel. Ni - base alloys characterize by the excellent high-temperature corrosion resistance, good strength and good ability to work in aggressive environments. Applied overlays had a proper combination of the metal substrate in particular small amount of Fe. This could be achieved by the reduction of the substrate melting and its dissolution into the overlays. The microstructure, chemical composition of the obtained overlays were investigated by means of a light microscope, a scanning electron microscope (SEM) equipped with the EDS detector. The overlays had cellular-dendritic structure. The variations of the chemical composition (especially Mo, Ni and W ) in the interdendritic and dendritic regions were observed. The interdendritic regions were enriched during solidifications in Mo and W and had lower content of Ni.
Compact nuclear magnetic resonance (NMR) instruments make NMR spectroscopy and relaxometry accessible in industrial and harsh environments for reaction characterization and process control. Robust field integration of NMR systems have to face explosion protection or integration into process control systems with short set-up times. This paves the way for industrial automation in real process environments.
The design of failsafe, temperature and pressure resistant flow through cells along with their NMR-specific requirements is an essential cornerstone to enter industrial production plants and fulfill explosion safety requirements. Additionally, if fast reactions are monitored, suitable mixing devices need to be placed in close vicinity to the measuring volume to mix the reactants properly.
NMR-specific requirements aim at full quantitative pre-magnetization and acquisition with maximum sensitivity while reducing sample transfer times and dwell-times. All parameters are individually dependent on the applied NMR instrument.
Luckily, an increasing number of applications are reported together with an increasing variety of commercial equipment. However, these contributions have to be reviewed thoroughly.
The performance of sample flow cells commonly used in online analytics and especially for low-field NMR spectroscopy was experimentally and theoretically investigated by 1H-NMR experiments and numerical simulations. Especially, the applicability of 3D printed zirconium dioxide for innovative flow cell designs was of interest. Here, we demonstrate and discuss an automated test method to determine the critical parameters of flow through cells for quantitative online NMR spectroscopy. The setup is based on randomized setpoints of flow rates in order to reduce temperature related effects. Five flow cells and tubing were assessed and compared for high-field as well as low-field NMR spectrometers.
An understanding on crystallization behavior and kinetics in glasses is one of the important topics in the glass science and technology. Tsukada et al.1) found an extremely unique and curious phenomenon in the crystallization of multiferroic (ferroelectric and ferroelastic properties) ’-Gd2(MoO4)3 crystals in Gd2O3-MoO3-B2O3 glasses. That is, crystals formed in the crystallization break into small pieces with a triangle prism or pyramidal shape having a length of 50-150 um spontaneously during the crystallization in the inside of an electric furnace, not during the cooling in air after the crystallization. They proposed to call this phenomenon “self-powdering phenomenon”. To the best of our knowledge, such a self-powdering phenomenon has not been observed in the crystallization of any other glasses. To investigate this phenomenon is very important for the glass science and for the preparation of bulk crystallized glasses with ferroelastic crystals. In this work, the preparation of crystallized glasses keeping the original shape is challenged, and the mechanism of self-powdering phenomenon is proposed. Glasses with the compositions of 21Gd2O3-63MoO3-(16-x)B2O3-xTeO2 (mol%) (x=0, 2, 4, 8) such as 21Gd2O3-63MoO3-16B2O3 (GM16B) and 21Gd2O3-63MoO3-8B2O3-8TeO2 (GM8T8B) were prepared using a conventional melt quenching technique. The quenched glasses were heat-treated at some temperatures, and the crystalline phase present in the crystallized samples was identified by X-ray diffraction (XRD) analyses, and the morphology and birefringence of crystals formed were observed using a polarized optical microscope (POM). The densities of GM16B and GM8T8B glasses are 4.76 g/cm3 and 4.91 g/cam3, respectively, and these values are higher than the density of ’-Gd2(MoO4)3 crystal, 4.555 g/cm3. These differences in the density might induce the large stresses in the inside of crystals during the crystal growth. The crystallized glasses of GM16B with ’-Gd2(MoO4)3 crystals do not keep the original glass shape, showing self-powdering phenomenon (breaking into small pieces). However, the crystallized glasses of GM8T8B keep the original glass shape without indicating any self-powdering. It is proposed that the stress at the interface between the glassy phase and ’-Gd2(MoO4)3 crystalline phase might be reduced in GM8T8B glasses containing TeO2 with weak Te-O bonds.
Additive manufacturing (AM) offers an effective solution to the medical sector. It enables the production, on demand, of customised implants which match the patient’s anatomy, with grafts that promote bone growth, as well as surgical guides that help the surgeons. The objective of this project is to provide a comprehensive basis to enable the safe use of medical AM products with traceable and reliable dimensionalmeasurements. This will guarantee the reliability of medical AM products to notified bodies and facilitate acceptance of AM in the medical sector for a better quality of life.
We present an in situ PXRD investigation of the mechanochemical cocrystal formation of pyrazinamide with pimelic acid in two milling jar materials. DFT calculations of the two synthesized polymorphs suggest that the relative stability is based on a conformation change of pyrazinamide in the cocrystal.
Up to now, the mechanisms of surface nucleation and surface-induced texture formation are far from being understood. Corresponding phenomena are discussed hypothetically or even controversial, and related studies are restricted to very few glasses. As a main drawback, the vast majority of previous work on oriented growth of surface crystals do not consider the possible effects of glass surface treatments (like polishing defects, adhered particles and cracks, …) or ambient annealing conditions (vacuum or atmospheric pressure) which both can influence crystal nucleation and growth. Moreover, very few observations of crystal orientation related to surface crystallization were focused on separately growing crystals. In conclusion, up to now, no systematic studies on initially oriented crystal growth or nucleation from defined active nucleation sites have been pursued.
Therefore, the main objective of the proposed project is to gain a basic understanding of the mechanisms of surface-induced microstructure formation in glass ceramics. We shall answer the question whether preferred orientation of surface crystals is the result of oriented nucleation or caused by other orientation selection mechanisms acting during early crystal growth. In both cases, crystal orientation may be caused by the orientation of the glass surface itself or the anisotropy and orientation of active surface nucleation defects.
New techniques of experimental characterization of surface-crystallized glasses shall be applied to find answers to the questions posed above. Based on a controlled preparation and annealing of the glass sample surfaces, that includes the defined creation of active nucleation defects, and followed by the microstructural characterization especially during the very early growth stages of separated surface crystals, the orientation relations between defect and initiated surface crystal will be analyzed. In order to gain new insights, a couple of entirely new microstructure diagnostics techniques, including chemically contrasted XRM, laser-based sample preparation for XRM, and 3D electron backscatter diffraction shall be developed or applied.
This way, using X-ray microscopy as a pivotal technique for the non-destructive 3D characterization of relatively large samples at superior spatial resolution (but also complemented by other microstructure diagnostics techniques, e.g. TEM elemental mappings at cross-sectioned samples) unprecedented insights into the microstructure evolution upon surface crystallization of model glasses will be gained.
The work presents the microstructure, chemical composition and mechanical properties of Inconel 686 coatings after high - temperature corrosion in environment of aggressive gases. To produce the Ni - base weld overlays the QS Nd:YAG laser beam was used. The substrates were 13Mo4-5 boilers plate steel. Ni - base alloys characterize the excellent high temperature corrosion resistance, good strength and good ability to work in aggressive environments. Applied overlays had a proper combination of the metal substrate in particular small amount of Fe. This could be achieved by the reduction of the melting of the substrate and its dissolution into the overlays. The microstructure, chemical composition of the obtained overlays were investigated by means of a light microscope, a scanning electron microscope (SEM) equipped with the EDS detector. The overlays had cellular-dendritic structure. The variations of the chemical composition (especially Mo, Ni and W ) in the interdendritic and dendritic regions were observed. The interdendritic regions were enriched during solidifications in Mo and W and had lower content of Ni.
The microstructure of weld overlay Ni - base alloy deposited on carbon steel by laser QS-Nd:YAG
(2017)
Ni- base alloys are used as a one of the most important coating material and can be applied in a different environments and elements of devices having various applications. To protect the surface of the material from aggressive gases at high temperature, there are use different kinds of the Ni- base alloys. One of such alloy is Ni-Cr-Mo-W called commercial Inconel 686. This alloy based on NiCr22Mo9Nb (Inconel 625), in which content of molybdenum increased and niobium was replaced with the addition of tungsten, in order to counteract the strong segregation in the microstructure, which results in homogeneity of the chemical composition of the structure. Inconel 686 is also characterized by greater resistance to high temperature corrosion and heat resistance than Inconel 625. The Inconel 686 alloy was deposited on 13CrMo4-5 steel by laser QS - Nd:YAG. In the poster the microstructure (SEM) and chemical composition (EDS) of obtained weld overlays were investigated.