Ingenieurwissenschaften und zugeordnete Tätigkeiten
Filtern
Erscheinungsjahr
- 2018 (32) (entfernen)
Dokumenttyp
- Vortrag (16)
- Posterpräsentation (8)
- Zeitschriftenartikel (4)
- Beitrag zu einem Tagungsband (4)
Schlagworte
- KorroPad (21)
- Korrosion (15)
- Nichtrostender Stahl (15)
- Corrosion (12)
- EPR (12)
- Heat treatment (12)
- Corrosion resistance (11)
- Stainless steel (11)
- Lochkorrosion (10)
- Corrosion testing (9)
- Korrosionsbeständigkeit (7)
- Pitting corrosion (7)
- Martensitic stainless steels (6)
- Passivschicht (6)
- Korrosionsschutz (5)
- ThermoCalc (5)
- Korrosionsprüfung (4)
- Wärmebehandlung (4)
- Duplexstahl (3)
- REM (3)
- Schweißen (3)
- Strahlen (3)
- EBSD (2)
- Korrosionsschnelltest (2)
- Martensitischer nichtrostender Stahl (2)
- Nitrogen (2)
- Normung (2)
- Oberflächenbearbeitung (2)
- Qualitätssicherung (2)
- Quenching and partitioning (2)
- Atmospheric corrosion (1)
- Auslagerung (1)
- Bauwesen (1)
- Betonstahl (1)
- CoCrMo (1)
- Duplex stainless steels (1)
- Electrochemical noise (1)
- Electrochemical potentiokinetic reactivation (1)
- Gelartige Elektrolyte (1)
- High ductility (1)
- Interkristalline Korrosion (1)
- Korosionsschutz (1)
- Korrosionsbelastung (1)
- Korundschleifen (1)
- Legierungselemente (1)
- Martensitic stainless steel (1)
- Mechanical testing (1)
- Norm (1)
- Oberfläche (1)
- Oberflächen (1)
- Oberflächenanalytik (1)
- Passivität (1)
- Schleifen (1)
- Schneidwaren (1)
- Sensibilisierung (1)
- Spaltkorrosion (1)
- Stainless steels (1)
- Surface treatment (1)
- TRIP (1)
- Titan (1)
- Transformation induced plasticity (1)
- WIPANO (1)
- Werkstoffauswahl (1)
- Werkstoffklassen (1)
- Werkstoffprüfung (1)
- Zinkdeckschichten (1)
Organisationseinheit der BAM
Eingeladener Vortrag
- nein (16)
The duplex stainless steel 1.4062 (X2CrNiN22-2) is used as alternative material to austenitic stainless steels in the construction industry. The corrosion resistance of welded seams is influenced by the base material, the weld filler material, the welding process and also by the final surface treatment. The scale layer next to the weld seam can be removed by grinding, pickling, electro-polishing or blasting depending on the requested corrosion resistance. Blasted surfaces are often used in the industrial practice due to the faster and cheaper manufacturing process compared to pickled or electro-polished surfaces. Furthermore blasting with corundum-grain is more effective than blasting with glass-beads which also lower the process costs. In recent years, stainless steel surfaces showed an unusually high susceptibility to pitting corrosion after grinding with corundum. For this reason, it is now also questioned critically whether the corrosion resistance is influenced by the applied blasting agent. This question was specifically investigated by comparing grinded, pickled, corundum-grain- and glass-bead-blasted welding seams. Results of the SEM analyses of the blasting agents and the blasted surfaces will be presented and correlated with the results of different corrosion tests (KorroPad-testing and pitting potentials).
Nickel-free, nitrogen alloyed austenitic stainless-steels, with about 19 wt.-% Mn and 0,8 wt. % N, are an interesting alternative to classic CrNi austenitic stainless steels due to their superior mechanical properties (Rm > 900 MPa, A5 > 50 %, Av > 350 J) in the solution annealed condition. The formation of chromium-rich nitrides during suboptimal heat treatment, processing or application leads to an inhomogeneous distribution of alloying elements in the microstructure, which reduces the corrosion resistance. Consequently, an accurate knowledge of the sensitization behavior is indispensable for the use of nickel-free, high-nitrogen austenitic stainless steels. The relationship between artificial aging, phase formation and corrosion resistance was investigated on the alloys X8CrMnN18-19 (1.3815) and X8CrMnMoN18-19-2 (1.4456), both alloyed with 0,8 wt.-% Nitrogen, in the present work. The microstructural evolution was studied by LM and SEM while the corrosion resistance was characterized with the electrochemical potentiodynamic reactivation (EPR) and the KorroPad indicator-test. Both alloys showed increased corrosion susceptibility within critical aging parameters. Finally, a sensitization diagram was described successfully for both alloys showing the positive effect of molybdenum.
The copper alloyed stainless steel 1.4542 (X5CrNiCuNb16-4) is used in different areas due to its good mechanical properties and corrosion resistance. Strength and corrosion resistance can be adjusted by the heat treatment, which is of importance for the application of this alloy. The mechanical properties (strength and hardness) are attributed to the dispersive precipitation of the copper rich ε–Phase. The additional precipitation of chromium carbides can reduce the corrosion resistance. Different ageing states were produced to investigate the precipitation behaviour with various methods. Furthermore, the influence of cold-rolling on the precipitation behaviour was studied in comparison to a solution annealed state without deformation. The microstructure was studied by SEM and the variations of hardness and magnetic proportion were characterised. The electrochemical potentiodynamic reactivation (EPR) was used to determine the corrosion resistance and detect chromium depletion in all heat-treated states. The results show that a work hardening accelerates the precipitation rate, while ageing at 600 °C reduces the corrosion resistance due to chromium depletion.
Electrochemical tests, hardness measurements, and microstructure analysis are performed to study the influence of austenitizing, quenching, and tempering parameters on the corrosion resistance of the martensitic stainless steel grade X50CrMoV15 (1.4116). Different heat treatment states were studied using an adapted EPR-Test to evaluate the chromium distribution and depletion caused by the formation and dissolution of chromium rich carbides. The EPR results were correlated with pitting corrosion behavior, demonstrating the strong effect of heat treatment parameters on the susceptibility of martensitic stainless steels to corrosion phenomena.
Normung der KorroPad-Prüfung zum Nachweis lochkorrosionsanfälliger Oberflächen und Werkstoffzustände
(2018)
Mit der KorroPad-Prüfung kann die Lochkorrosionsbeständigkeit nichtrostender Stähle auf sehr einfache, schnelle und kostengünstige Weise eingeschätzt werden. Das KorroPad ist damit für Hersteller, Verarbeiter und Anwender nichtrostender Stähle eine interessante Alternative zu zeitintensiven Langzeitversuchen und komplexen elektrochemischen Untersuchungsmethoden. Die prinzipiellen Funktionsweise der KorroPad-Prüfung wird im Vortrag beschrieben, um anschließend verschiedene Anwendungen vorzustellen. Exemplarisch werden dazu die Bewertung von Schleif-, Strahl- und Passivierungsprozessen, die der Einfluss von Schwefel und die werkstoffbezogene Nachweisgrenze der KorroPad-Prüfung. Abschließend wird auf ein geplantes Vorhaben zur Normung der KorroPad-Prüfung eingegangen.
Einfluss industrieller Korundschleifprozesse auf die Korrosionsbeständigkeit nichtrostender Stähle
(2018)
Im Vortrag werden Ergebnisse des AiF Forschungsvorhabens "Optimierung industrieller Korundschleifprozesse zur Sicherstellung der Korrosionsbeständigkeit nichtrostender Stähle" vorgestellt, die den Einfluss verschiedener Schleifmittel auf die Korrosionsbeständigkeit geschliffener Oberflächen nichtrostender Stähle belegen. Es konnte ein signifikanter Einfluss durch die Verwendung von Granulatschleifbändern nachgewiesen werden, der die Korrosionsbeständigkeit der Oberflächen reduziert. Grund sind auf der Oberfläche zurückbleibende Materialaufplattungen von Eigenmaterial aus dem Schleifprozess. Es wurden unterschiedliche Korrosionsuntersuchungen durchgeführt und durch Oberflächenanalytik im Rasterelektronenmikroskop untermauert.
Einfluss der Schweißnaht-Nachbehandlung auf die Korrosionsbeständigkeit des Duplex-Stahls 1.4062
(2018)
Die Korrosionsbeständigkeit von Schweißverbindungen aus dem Duplex-Stahl 1.4062 wird, neben dem Grundwerkstoff, dem Schweißzusatzwerkstoff und dem Schweißverfahren, auch sehr stark von der Oberflächennachbehandlung der Schweißnaht beeinflusst. Je nach zukünftigem Anwendungsbereich und geforderter Korrosionsbeständigkeit wird die Schweißnaht geschliffen, gebeizt, elektropoliert oder gestrahlt, um die beim Schweißen entstandenen Anlauffarben zu entfernen. Gestrahlte Oberfläche sind in der industriellen Praxis häufig anzutreffen, da sie deutlich einfacher und kostengünstiger herzustellen sind als gebeizte oder elektropolierte Oberflächen. Die Auswahl des Strahlmittels bestimmt auch die Prozesskosten, wobei das Strahlen mit Korund effektiver als das Strahlen mit Glasperlen ist. Ziel der Untersuchungen war es festzustellen, ob das Strahlen aus Sicht der Korrosionsbeständigkeit äquivalent zu anderen Nachbehandlungsverfahren ist. Diese Fragestellung wird im Vortrag beantwortet indem geschliffene, gebeizte, mit Korund gestrahlte und mit Glasperlen gestrahlte Schweißverbindungen vergleichend untersucht werden. Die Ergebnisse der Untersuchungen von den Strahlmitteln und den gestrahlten Oberflächen werden mit den Ergebnissen der Salzsprühnebelprüfung, den kritischen Lochkorrosionspotentialen und der KorroPad-Prüfung korreliert.
Der Vortrag behandelt zunächst die wesentlichen Grundlagen der elektrolytischen Korrosion, die für das Verständnis der Eigenschaften korrosionsbeständiger (nichtrostender) Stähle notwendig sind. Anschließend wird das Phänomen der Passivität vorgestellt und die Wirkung von Legierungselementen auf Gefüge und Korrosionsbeständigkeit erläutert.
Der Vortrag behandelt zunächst die wichtigsten lokalen Korrosionserscheinungen (Spaltkorrosion, Interkristalline Korrosion, Lochkorrosion und Spannungsrisskorrosion), die bei korrosionsbeständigen (nichtrostenden) Stählen auftretenden können und gibt wichtige Hinweise zu deren Vermeidung. Außerdem werden die verschiedenen Werkstoffklassen (Ferrite, Austenite, Martensite und Duplexstähle) im Bereich der nichtrostenden Stähle vorgestellt und auf die Eigenschaften und Besonderheiten eingegangen.