Ingenieurwissenschaften und zugeordnete Tätigkeiten
Filtern
Erscheinungsjahr
- 2019 (287) (entfernen)
Dokumenttyp
- Vortrag (287) (entfernen)
Sprache
- Englisch (287) (entfernen)
Referierte Publikation
- nein (287) (entfernen)
Schlagworte
- Additive Manufacturing (29)
- Corrosion (19)
- MIC (9)
- Microstructure (9)
- Welding (9)
- Additive manufacturing (8)
- Diffraction (8)
- Surface functionalization (8)
- Magnetocaloric (7)
- Nanoparticle (7)
Organisationseinheit der BAM
- 6 Materialchemie (74)
- 9 Komponentensicherheit (66)
- 8 Zerstörungsfreie Prüfung (55)
- 5 Werkstofftechnik (51)
- 8.5 Röntgenbildgebung (35)
- 9.3 Schweißtechnische Fertigungsverfahren (33)
- 7 Bauwerkssicherheit (29)
- 6.6 Physik und chemische Analytik der Polymere (23)
- 9.4 Integrität von Schweißverbindungen (23)
- 4 Material und Umwelt (21)
Eingeladener Vortrag
- nein (287)
Explosion and decomposition limits of flammable and chemically unstable gases were determined experimentally in a dosed autoclave with varying ignition energy up to 1000 J. The ignition source was a lightning arc caused by an exploding wire igniter as described in EN 1839 B .. In case of methane only the upper explosion limit was influenced significantly by the ignition energy, whereas the lower explosion limit was constant. In case of R32 however. it was the lower explosion limit that was influenced significantly by the ignition energy and not the upper explosion limit. A particularly strong dependency from the ignition energy was found for the decomposition limits of the chemically unstable gases in nitrogen.
The present work deals with the development of a strategy for the prevention of end crater defects in high-power laser welding of thick-walled circumferential welds. A series of experiments were performed to understand the influence of the welding parameters on the formation of end crater defects such as pores, cracks, excessive root-side drop-through and shrinkage cavities in the overlap area. An abrupt switch-off of the laser power while closing the circumferential weld leads to a formation of a hole which passes through the whole welded material thickness. A laser power ramp causes solidification cracks which are initiated on the transition from full-penetration mode to partial penetration. Strategies with a reduction of the welding speed shows a creation of inadmissible root sagging. Defocusing the laser beam led to promising results in terms of avoiding end crater defects. Cracks and pores in the overlap area could be effectively avoided by using defocusing techniques. A strategy for avoiding of end crater imperfections was tested on flat specimens of steel grade S355J2 with a wall thickness of 10 mm and then transferred on the 9.5 mm thick pipe sections made of high-strength steel X100Q.
The presentation provides a discussion and damage tolerant assessment of metallic AM components. In the focus are problems of the determination of representative material data, the effect of material defects and residual stresses. Starting with the actual state-of-the-art in the field, options and possibilities of a damage tolerant design for AM are discussed.
Single-pass Hybrid Laser Arc Welding of Thick Materials Using Electromagnetic Weld Pool Support
(2019)
Hybrid laser-arc welding process allows single-pass welding of thick materials, provides good quality formation of joints with minimal thermal deformations and a high productivity in comparison with arc-based welding processes. Nevertheless, thick-walled steels with a thickness of 20 mm or more are still multi-pass welded using arc welding processes, due to increased process instability by increasing laser power. One limitation factor is the inadmissible formation of gravity drop-outs at the root. To prevent this, an innovative concept of electromagnetic weld pool support is used in this study. With help of such system a stable welding process can be established for 25 mm thick steel plates and beyond. Sound welds could be obtained which are tolerant to gaps and misalignment of the welded parts. The adaptation of this system to laser and hybrid laser-arc welding process can dramatically increase the potential field of application of these technologies for real industrial implementation.
In contrast to microplastics, little is known about nanoplastics (1 to 100 nm). In order to make the dectecability of nanoplasics more reliable, we started to develop nanoplastic reference materials. This project also aims to anser the question of how the single chain conformation of bio(polymers) changes in contact with nanoplastics. Small-angle X-ray and neutron scattering methods are suitable methods for studing this topic. Recently the soft and hard interactions between polystyrene nanoplasics and human serum albumin corona was investigated with small-angle neutron scattering. Here we concentrate on small-angle X-ray scattering as our favorite method to study how (bio)polymers change their conformation in contact with nanoplastics. The scattering of bovine serum albumin in its native state can be detected easily. The scattering pattern of this biopolymer changes dramatically when its globular stucture changes to a coil structure. Modeling of chain conformations and the calculation of the scattering pattern is relatively easy to perform. Numerous model calculations will be provided to predict the changes of conformation of single bio(polymer) chains when in conatact with nanoplastics. These predictions will be compared with recent experimenal results from in situ measurments of bio(polymers) in contact with nanoplastics. The impact of temperature, polymer concentration and salt on the single-chain conformation changes will be discussed.
Within polycrystalline porous ceramics used in automotive applications as diesel particulate filters, it is evidenced that during cooling from firing temperature micro cracks are gradually formed. The cracks are formed as a consequence of strong thermal anisotropy of grains. Typically these micro cracks are granting better thermal shock resistance, with respect to dense materials, but reduce stiffness. The reduction can be quantified by measuring the drop in elastic properties of bulk material which, depending on the level of porosity, can decrease even by 50% with respect to its value at high temperature. It is further observed that upon subsequent heating these cracks are closing and partially or totally healing at very high temperatures. Such peculiar behavior results in partial or complete recovery of the elastic properties of bulk material upon completing one thermal cycle. Despite its evident practical application, still there is no constitutive description of this phenomenon, capable of predicting the evolution of Young's modulus as a function of temperature history. For reliable numerical simulation of this phenomenon, it is required to model fracture. To model inter-crystalline fracture, an effective strategy is to use cohesive elements, since crack patterns are a priori known. Major limitation of this approach is that the cohesive elements already implemented within commercial codes cannot take into account crack healing upon subsequent heating. In this study new cohesive element is developed and numerically implemented within ABAQUS commercial finite element code, capable to model crack opening, closing and healing. Further on, a computer code is generated to build numerical model of porous ceramic specimens that takes into account experimentally measured crystallographic orientation and porosity, and models the microstructure by using Voronoi polygons. The developed numerical tools serve as a framework for more realistic simulations, required to study the hysteresis in elastic properties within porous ceramics provoked by thermal cyclic. In a subsequent phase, an inverse analysis procedure is developed, in which macroscopic properties are used to calibrate parameters entering into micro crack model. The approach is centered on a minimization of a discrepancy function designed to quantify the difference between experimentally measured quantities and their computed counterpart. The model is calibrated on the basis of experimental data regarding the drop of bulk Young's modulus with decrease of temperature. Developed procedure is tested with porous cordierite sample, and obtained results are quit promising despite the current limitation of using only two-dimensional model.
Lamb waves are widely used for non-destructive evaluation of material parameters as well as for detection of defects. Another application of Lamb waves is quality control of adhesive joints.
Researchers are currently investigating shear horizontal and zero-group velocity modes for characterisation of the adhesive bonding strength. In a new approach, Lamb wave mode repulsion is used to obtain the coupling strength between different layers to characterise the adhesive bonding strength. The modes of the individual layers become coupled in the multilayered systems forming particular regions, the so-called mode repulsion regions. This study investigates these modes and their interaction in two-layered plate-like structures with varying coupling strength both numerically, with the Scaled Boundary FEM, and experimentally.
Elastomeric O-ring seals are used in a wide range of applications due to their excellent elasticity. However, like all polymers, elastomers degrade under the influence of e.g. time, temperature, oxygen, radiation and mechanical stress. Especially in applications where a replacement of seals after a certain time is hard or almost impossible, it is important to know the seal lifetime. Therefore, an extensive ageing programme with elastomers made of EPDM, HNBR and other materials was started with the aim of determining suitable methods for accelerated ageing and lifetime prediction.
In order to determine the lifetime of polymeric parts, the time-temperature superposition principle is commonly used to shift property changes obtained by accelerated ageing at higher temperatures to lower temperatures. If the shift factors yield a straight line in an Arrhenius diagram, a corresponding activation energy can be determined. However, we have found that the shift factors and thus the predicted lifetime depends on the test method that yielded the shifted data. For example, the shift factor between 125 °C and 150 °C ageing temperature was roughly the same (5/5/4.5 respectively) for hardness, density and maximum of loss factor tan measured on HNBR, but different for elongation at break (8) and compression set (2.2, excluding DLO-affected data). A possible explanation might be that while the different oxidation reactions proceed with a fixed activation energy, they have differing impact on the measured properties. For example, hardness is lowered by chain scission reactions, and increases by crosslinking reactions during ageing. As usually both chain scission and crosslinking reactions occur during ageing, the measured hardness increase reflects only the net effect of both reaction types. On the other hand, compression set is influenced additively by both reaction types: chain scission leads to an increase of the remaining deformation, as broken chains lose their recovery potential, and crosslinking reactions during ageing fix the compressed geometry, which also leads to less recovery. Thus, compression set reflects the total number of changes in the network and shows degradation effects much faster, which results in lower shift factors and lower activation energy. This phenomenon was observed for EPDM as well.
In order to verify our hypotheses and to gain further insights, temperature-dependent oxygen consumption measurements are currently being performed and results will be presented at the conference. The shift factors and activation energy determined by oxygen consumption measurements are expected to be close to the values for compression set.
Ceramic springs offer versatile possibilities for load bearing or sensor applications in challenging environments. Although it may appear unexpected, a wide range of spring constants can be implemented by material selection and especially by the design of the spring. Based on a rectangular cross-section of the windings, it is possible to design a spring geometry that generates the desired spring constant simply by choosing appropriate diameter, height, widths, and number of windings. In a recent research project the calculation of helical compression springs made of rectangular steel (German standard DIN 2090) was applied for the design of ceramic springs. A manufacturing technology has been worked out to fabricate such springs from hollow cylinders of several highly dense technical ceramics by milling. Ceramic springs with precise rectangular section, without edge damage, and mean surface roughness smaller than 0.2 µm were produced after parameter optimization. Tolerances of less than 10 µm were achieved regarding spring diameter, height, and width of cross section. It is shown that the calculations outlined in the standard are valid for a variety of ceramic materials as well. Demonstrator springs with a wide range of spring constants have been fabricated, including zirconia springs with 0.02 N/mm, alumina springs with 1 N/mm and Si3N4 springs with 5 N/mm. A reproducibility study of six zirconia springs with a constant of 0.3 N/mm showed a relative difference in spring constants of less than +/- 1 %. This combination of a valid calculation approach for spring geometry and a reliable manufacturing technology allows for purposeful development and fabrication of ceramic springs with precise mechanical properties and superior chemical stability.
Laser-induced periodic surface structures: from nanoscaled light localization to applications
(2019)
In this contribution the current state in the field of Laser-Induced Periodic Surface Structures (LIPSS) is reviewed. This includes the mechanisms of formation and current applications, particularly the colorization of technical surfaces, the control of surface wetting properties, the tailoring of surface colonization by bacterial biofilms, and the improvement of the tribological performance of nanostructured metal surfaces.
Peptide-polymer bioconjugates combine oligopeptides with synthetic polymer blocks and can be used for various applications in material sciences. In recent years, bioconjugates were applied as compatibilizers and coatings. Biocombinatorial approaches, such as phage display, have been shown to yield strong binding peptides, which exhibit excellent coating properties as peptide-PEO conjugates. Phage display represents a widely exploited strategy to select peptides or proteins that exhibit highly specific affinity to various substrates. Following a phage display experiment, DNA sequencing of binding phage clones is required in order to get the sequence information of the binding peptides. Traditionally, random clone picking followed by Sanger sequencing was applied. However, this method may not necessarily identify the strongest binding clones. Next-generation sequencing made sequencing of whole phage libraries possible, which highly improved the selection of strong binders. Here, we show that the biocombinatorial method of phage display combined with next generation DNA sequencing of whole phage libraries represents a powerful tool for an application in material chemistry. Phage display is used to find specific target binding peptides for polypropylene surfaces (PP). PP binders are of particular interest because thus far gluing or printing on PP is challenging due to its low surface energy. Scripts for sequence data analysis were developed and promising sequences were synthesized as peptide-PEO conjugates. Fluorescence based adsorption experiments on PP surfaces led to the identification of strong binding sequences and a better understanding of the peptide-surface interactions.
Packages for the transport of radioactive material shall withstand severe accidents. Therefore, the IAEA Regulations define different test scenarios to cover severe hypothetical accident conditions. One of these tests defined in detail is the thermal test, mainly consisting of a 30 minute fully engulfing 800 °C pool fire or an equally severe fire test. The heat fluxes into the package are of significant importance and depend substantially on the fire characteristics and the surface temperature of the package.
In order to investigate the heat fluxes over a wide range of surface temperatures during a propane gas fire test and to get information about local fire impact a fire reference package, representing the outer geometry of a specific type of transport cask for radioactive waste, was designed. A closed steel sheet cylinder with a wall thickness of 10 mm was chosen as fire reference package. The cylinder was filled with refractory insulation material and instrumented with thermocouples distributed all over the cylinder. The local steel sheet temperatures measured allow the determination of local as well as global heat fluxes as a function of time and surface temperature.
With this fire reference package three open-air propane gas fire tests were performed at BAM’s open air fire test stand. The flame exposure time period was changed for the different fire tests. Furthermore, the wind conditions changed between and during the tests. Test stand parameters like wind shield location and propane gas volume flow were chosen constant for the three tests. The test results were used to determine the changes of heat flux into the fire reference package in relation to the package surface temperature. This data also allows the calculation of local characteristics of the propane gas fire as there are the flame temperature, the fire convection coefficient and the radiation exchange coefficient in a first approach. The recently conducted tests provide an initial picture of local fire characteristics of the propane gas fire test facility. The test shows that the propane gas fire covers the IAEA-fire over a wide range of surface temperatures with the chosen test stand parameters.
Against the background of sustainable resource management and efficiency, wood-based materials are currently experiencing a revival and, among others, plywood, Laminated Veneer Lumber and glued laminated timber are becoming increasingly more important in the building sector. Even though these materials are so-called engineered products, the element wood is naturally grown with intrinsic variability in mechanical properties and requires professional handling on-site. Otherwise, load-bearing structures made of wood materials may entail certain risks. Critical situations can, in principle, be avoided by implementing a structural health monitoring system into components or structures made from wood material. The aim is to indicate accumulation of mechanical damage and to eliminate or at least significantly reduce the risk of unexpected failure. Toward this purpose, the failure behavior of several layered wood materials under quasi-static tension was investigated in laboratory-scale experiments by means of acoustic emission (AE) measurement. Based on spectral analysis and pattern recognition, two classes of AE signals are identified for each investigated lay-up that are characterized by either low or high frequency contents in the respective power spectra. AE activity and intensity of both signal classes are analyzed, striving for predictors appropriate for AE monitoring concepts.
BAM provides leading expertise in preparation, characterisation and application of fluorescent reference standards and biomedical relevant nanomaterials, as well as in traceable, absolute, and quantitative fluorometric measurements of transparent and scattering systems in the ultraviolet, visible, and near infrared spectral region. BAM will prepare solid low-RI particles in WP1, will develop reference methods to determine the fluorescence intensity and RI of reference materials in WP2, and will measure the fluorescence intensity of EVs in biological test samples of WP3.
Porous materials play an important role in several fields of technology, especially for energy applications like photovoltaics, electrolysis or batteries. The activity of porous films is affected by properties like porosity, film thickness, chemical composition of the material as well as the crystallinity of the framework. The complex morphology of such porous films constitutes a challenge even for modern analytical techniques and requires new approaches employing the combination/complementation of data of different analytical methods. In this contribution we characterize thin mesoporous iridium-titanium mixed oxide film properties by Electron Probe Microanalysis (EPMA) with energy dispersive X-ray spectroscopy (EDS) at an SEM.
Solidification cracking of metals is a well-researched topic in the field of welding science. A material’s susceptibility to solidification cracking can be tested using numerous different specialized test procedures, one of which is the Modified Varestraint-/Transvarestraint test (MVT). It was developed at BAM in 1982 and is internationally standardised. Over the decades, this test has been extensively used to characterise the solidification cracking resistance of many different materials.
The present study was conducted to further investigate the influences of the standardised MVT testing parameters, as well as the characteristics of evaluation methods on the results. Several different high alloyed martensitic LTT (low transformation temperature) filler materials, CrNi and CrMn type, were used. In previous pilot studies, these alloys have shown a rather distinctive solidification cracking behaviour.
First, the effects of different process parameter sets on the solidification cracking response were measured using the standard approach. Subsequently, μCT scans were performed on the specimens. The results consistently show sub surface cracking, to significant, yet varying extents. Different Primary solidification types were found using WDX-analysis, an aspect that is regarded to be the main difference between the CrNi- and CrMn-type materials and their cracking characteristics.
Results show that when it comes to testing of modern high-performance alloys, one set of standard MVT testing parameters might not be equally suitable for all materials. Also, to properly accommodate different solidification types, sub-surface cracking has to be taken into account.
In this study, the influence of the welding speed, the arc power and the laser focal position on the solidification crack formation for partial penetration laser hybrid welded thick-walled plates were investigated. Experimentally, a direct correlation between the welding speed and the crack number was observed. That is by reducing the welding velocity the crack number was decreased. The focal position shows also a significant influence on the crack number. Since by focusing the laser on the specimen surface, the crack number has been significantly diminished.
The wire feed speed showed a very slight influence on the crack formation. That is due to the large distance between the critical region for cracking and the arc region.
The numerical model shows a high-stress concentration in the weld root for both components (vertical and transversal).
Numerically, the reduced welding speed showed a strong impact on stress, as the model demonstrated a lower stress amount by decreasing the welding speed. The solidification cracking in the weld root is a result of interaction between metallurgical and geometrical and thermomechanical factors.
In this study, the influence of the welding speed and the arc power on the solidification crack formation for partial penetration laser hybrid welded Thick-Walled plates were investigated. Experimentally, a linear correlation between the welding velocity and the crack number was observed. That is by reducing the welding velocity the crack number was reduced.
The reduced welding velocity showed a strong impact on stress, as the model demonstrated a very lower stress amount in comparison to the reference case. The reduction of the welding speed could be a helpful technique to reduce the hot cracking. The wire feed speed showed a very slight influence on the crack formation. That can be returned to the large distance between the critical region for cracking and the arc region.