Ingenieurwissenschaften und zugeordnete Tätigkeiten
Filtern
Erscheinungsjahr
- 2019 (133) (entfernen)
Dokumenttyp
- Vortrag (82)
- Posterpräsentation (27)
- Beitrag zu einem Tagungsband (14)
- Zeitschriftenartikel (6)
- Dissertation (4)
Sprache
- Englisch (93)
- Deutsch (38)
- Mehrsprachig (2)
Referierte Publikation
- nein (133) (entfernen)
Schlagworte
- Additive Manufacturing (31)
- Additive manufacturing (18)
- Additive Fertigung (17)
- Computed tomography (12)
- Thermografie (11)
- Computed Tomography (10)
- Magnetocaloric (8)
- Material Science (8)
- Neutron Diffraction (7)
- Residual stress (7)
Organisationseinheit der BAM
- 8 Zerstörungsfreie Prüfung (133) (entfernen)
Eingeladener Vortrag
- nein (82)
Additive Manufacturing (AM) in terms of laser powder-bed fusion (L-PBF) offers new prospects regarding the design of parts and enables therefore the production of lattice structures. These lattice structures shall be implemented in various industrial applications (e.g. gas turbines) for reasons of material savings or cooling
channels. However, internal defects, residual stress, and structural deviations from the nominal geometry are unavoidable.
In this work, the structural integrity of lattice structures manufactured by means of L-PBF was non-destructively investigated on a multiscale approach.
A workflow for quantitative 3D powder analysis in terms of particle size, particle shape, particle porosity, inter-particle distance and packing density was established.
Synchrotron computed tomography (CT) was used to correlate the packing
density with the particle size and particle shape. It was also observed that at least about 50% of the powder porosity was released during production of the struts.
Struts are the component of lattice structures and were investigated by means of laboratory CT. The focus was on the influence of the build angle on part porosity and surface quality. The surface topography analysis was advanced by the quantitative characterisation of re-entrant surface features. This characterisation was compared with conventional surface parameters showing their complementary
information, but also the need for AM specific surface parameters.
The mechanical behaviour of the lattice structure was investigated with in-situ CT under compression and successive digital volume correlation (DVC). The Deformation was found to be knot-dominated, and therefore the lattice folds unit cell layer wise.
The residual stress was determined experimentally for the first time in such lattice structures. Neutron diffraction was used for the non-destructive 3D stress investigation. The principal stress directions and values were determined in dependence of the number of measured directions. While a significant uni-axial stress state was found in the strut, a more hydrostatic stress state was found in the knot. In both cases, strut and knot, seven directions were at least needed to
find reliable principal stress directions.
Composite-Druckgefäße für den Gefahrguttransport sowie für Wasserstoff- und Erdgasfahrzeuge bestehen aus einem lasttragenden Composite und einer gasdichten, metallischen oder polymeren Barriereschicht (Liner). Zur Untersuchung des Alterungsverhaltens solcher Composite-Druckgefäße wurde in der BAM das interdisziplinäre Themenfeldprojekt COD-AGE durchgeführt. Ziel des Projektes war die Entwicklung von Methoden und Modellen zur Beschreibung und Bestimmung des Alterungsverhaltens von Carbonfaser-Compositen am Beispiel von Druckgefäßen, um eine bessere Vorhersage der Alterung und der sicheren Gebrauchsdauer zu ermöglichen. Ein Schwerpunkt in diesem Projekt war die Bereitstellung geeigneter ZfP-Methoden. Dabei ging es sowohl um versuchsbegleitende Prüfungen, als auch um die mögliche Entwicklung von Prüfeinrichtungen für den späteren praktischen Gebrauch.
In dem Vortrag werden Prüfergebnisse der alterungsbegleitenden Wirbelstromprüfung an Composite-Druckgefäßen vorgestellt.
In Alterungsversuchen wurden Druckgefäße aus einem ca. 4 mm dicken Aluminiumliner und ca. 8 mm dicker CFK-Ummantelung untersucht. Typisches Einsatzgebiet solcher Druckgefäße sind Atemschutzgeräte der Feuerwehr. Die Druckgefäße wurden sowohl mit konventioneller Wirbelstromtechnik von außen und von innen als auch mit hochfrequenter Wirbelstromtechnik von außen geprüft. Es konnten sowohl Beschädigungen des metallischen Liners, als auch Strukturen des CFK-Geflechts nachgewiesen werden. Eine besondere mechanische Herausforderung bestand in der Prüfung der Innenseite der Liner, da hier eine zylindrische Fläche mit einem Innendurchmesser von 150 mm durch einen Zugang von nur 15 mm Durchmesser geprüft werden muss.
Composite-Druckgefäße für den Gefahrguttransport sowie für Wasserstoff- und Erdgasfahrzeuge bestehen aus einem lasttragenden Composite und einer gasdichten, metallischen oder polymeren Barriereschicht (Liner). Zur Untersuchung des Alterungsverhaltens solcher Composite-Druckgefäße wurde in der BAM das interdisziplinäre Themenfeldprojekt COD-AGE durchgeführt. Ziel des Projektes war die Entwicklung von Methoden und Modellen zur Beschreibung und Bestimmung des Alterungsverhaltens von Carbonfaser-Compositen am Beispiel von Druckgefäßen, um eine bessere Vorhersage der Alterung und der sicheren Gebrauchsdauer zu ermöglichen. Ein Schwerpunkt in diesem Projekt war die Bereitstellung geeigneter ZfP-Methoden. Dabei ging es sowohl um versuchsbegleitende Prüfungen, als auch um die mögliche Entwicklung von Prüfeinrichtungen für den späteren praktischen Gebrauch.
In dem Vortrag werden Prüfergebnisse der alterungsbegleitenden Wirbelstromprüfung an Composite-Druckgefäßen vorgestellt.
In Alterungsversuchen wurden Druckgefäße aus einem ca. 4 mm dicken Aluminiumliner und ca. 8 mm dicker CFK-Ummantelung untersucht. Typisches Einsatzgebiet solcher Druckgefäße sind Atemschutzgeräte der Feuerwehr. Die Druckgefäße wurden sowohl mit konventioneller Wirbelstromtechnik von außen und von innen als auch mit hochfrequenter Wirbelstromtechnik von außen geprüft. Es konnten sowohl Beschädigungen des metallischen Liners, als auch Strukturen des CFK-Geflechts nachgewiesen werden. Eine besondere mechanische Herausforderung bestand in der Prüfung der Innenseite der Liner, da hier eine zylindrische Fläche mit einem Innendurchmesser von 150 mm durch einen Zugang von nur 15 mm Durchmesser geprüft werden muss.
µCT is used to validate the capability of online monitoring for in-situ detection of defects during the L-PBF build process, which is a focus of the TF project ProMoAM.
Our first experiments show that online monitoring using thermography and optical tomography cameras are able to detect defects in the built part. But further research is needed to understand root cause of the correlation.
The Influence of the Temperature Gradient on the Distribution of Residual Stresses in AM AISI 316L
(2019)
Steep temperature gradients and solidification shrinkage are the main contributors to the formation of residual stresses in additively manufactured metallic parts produced by laser beam melting. The aim of this work was to determine the influence of the temperature gradient.
Diffraction results show a similar pattern for both specimens, indicating the shrinkage to be more dominant for the distribution of residual stresses than the temperature gradient. Thermography results imply that a higher energy input result in higher compressive residual stresses in the bulk.
The introduction of the 5G technology and automotive radar applications moving into higher frequency ranges trigger further miniaturization of LTCC technology (low temperature co-fired ceramics). To assess dimensional tolerances of inner metal structures of an industrially produced LTCC multilayer, computer tomography (CT) scans were evaluated by machine learning segmentation.
The tested multilayer consists of several layers of a glass ceramic substrate with low resistance silver-based vertical interconnect access (VIA). The VIAs are punched into the LTCC green tape and then filled with silver-based pastes before stacking and sintering. These geometries must abide by strict tolerance requirements to ensure the high frequency properties.
This poster presents a method to extract shape and size specific data from these VIAs. For this purpose, 4 measurements, each containing 3 to 4 samples, were segmented using the trainable WEKA segmentation, a non-commercial machine learning tool. The dimensional stability of the VIA can be evaluated regarding the edge-displacement as well as the cross-sectional area. Deviation from the ideal tubular shape is best measured by aspect ratio of each individual layer. The herein described method allows for a fast and semi-automatic analysis of considerable amount of structural data. This data can then be quantified by shape descriptors to illustrate 3-dimensional information in a concise manner. Inter alia, a 45 % periodical change of cross-sectional area is demonstrated.
This talk presents a new application for high-spatial resolution eddy current testing (ET) with magneto resistive (MR) sensor arrays. With rising popularity and availability of additive manufacturing (AM), companies mainly in the aerospace sector, set high requirements on quality control of AM parts, especially produced with selective laser melting (SLM). Since it was shown that those parts are prawn to flaws like pores or cracks, every part needs to be tested. Therefore, NDT Methods, like ET, could help to characterize SLM parts. Research on ET has shown, that offline ET with high spatial resolution MR sensor arrays is possible and that flaws as small as 50 µm could be detected while significantly reducing testing time. In this talk a first approach on automated online ET method for testing SLM parts is proposed. An approach with hundreds of MR sensor is made to maintain spatial resolution and short testing times. Classic signal conditioning methods are used to reduce cost and complexity while maintaining high testing bandwidths. The proposed idea enables further research on automated generation of testing reports, process control or automated flaw curing.
For metal-based additive manufacturing, sensors and measuring systems for monitoring of the energy source, the build volume, the melt pool and the component geometry are already commercially available. Further methods of optics, spectroscopy and non-destructive testing are described in the literature as suitable for in-situ application, but there are only a few reports on practical implementations.
Therefore, a new BAM project aims to develop process monitoring methods for the in-situ evaluation of the quality of additively manufactured metal components. In addition to passive and active thermography, this includes optical tomography, optical emission and absorption spectroscopy, eddy current testing, laminography, X-ray backscattering and photoacoustic methods. These methods are used in additive manufacturing systems for selective laser melting, laser metal deposition and wire arc additive manufacturing. To handle the sometimes huge amounts of data, algorithms for efficient preprocessing are developed and characteristics of the in-situ data are extracted and correlated to defects and inhomogeneities, which are determined using reference methods such as computer tomography and metallography. This process monitoring and fusion of data of different measurement techniques should result in a significant reduction of costly and time-consuming, destructive or non-destructive tests after the production of the component and at the same time reduce the production of scrap.
Here, first results of simultaneous measurements of optical emission spectroscopy and thermography during the laser metal deposition process using 316L as building material are presented. Temperature values are extracted from spectroscopic data by fitting of blackbody emission spectra to the experimental data and compared with results from a thermographic camera. Measurements with and without powder flow reveal significant differences between welding at a pristine metal surface and previously melted positions on the build plate, illustrating the significant influence of the partial oxidation of the surface during the first welding process on subsequent welding. The measurement equipment can either be mounted stationary or following the laser path. While first results were obtained in the stationary mode, future applications for online monitoring of the build of whole parts in the mobile mode are planned.
This research was funded by BAM within the focus area Material.
19th and 20th centuries glass paint layers consist of a colour body and a colourless lead silicate flux, in which borax or boric acid was added as further component to improve the paint ability and to reduce the firing temperature for multiple layers of paint. Model glasses were used in laboratory tests to investigate the stability of glass paints with additions of boron oxide. To determine boron in paint layers, a LIBS-system with pulsed NdYAG-laser was used.
The applicability of 1D-quadrupole-model on the depth estimation of overload-induced delaminations is tested in this contribution. While classical 1D-methods like Pulsed Phase Transformation and Thermographic Signal Reconstruction determine the depth of a defect by one parameter, a two-layer quadrupole model provides two parameters: depth and thermal resistance. In addition, the convectional losses at the surfaces may be considered. The defect investigated is a large-scale delamination in glass fibre reinforced polymer generated by tension overload.
Die zeitaufgelöste THz-Spektroskopie (THz-TDS) operiert mit elektromagnetischen Impulsen, die ein Amplitudenspektrum im unteren THz-Bereich aufweisen. Die THz-TDS ist in der Lage, dielektrische Volumina zerstörungs- und kontaktfreie zu durchstrahlen. Um eine 3D-THz Bildung zu ermöglichen, wurde für die THz-TDS ein rechnergestütztes Mess- und Rekonstruktionsverfahren (THz-TDSAFT) entwickelt, mit dem es gelingt, unter Verwendung der im Zeitbereich registrierten THz-TDS-Daten das Volumeninnere in Form eines dreidimensionalen Tomogramms zu rekonstruieren. Die THz-TD-SAFT basiert auf die für die Ultraschalltechnik entwickelte Synthetische Apertur Fokussierung (SAFT) bzw. des heuristisch begründeten Algorithmus des Synthetischen Apertur Radars (SAR). Anhand von Beispielen wird die Möglichkeiten der THz-TD-SAFT demonstriert und nachgewiesen, dass mit dem Rekonstruktionsansatz die künstlich eingebauten Fehlstellen bezüglich der Position und Größe geometrisch richtig im Tomogramm abgebildet werden können.
Im Rahmen des Themenfeld Projektes „Process Monitoring of AM“ (ProMoAM) evaluiert die BAM gegenwärtig die Anwendbarkeit verschiedenster ZfP-Verfahren, darunter die Thermografie, zur Prozessüberwachung in der additiven Fertigung von Metallen in Hinblick auf die Qualitätssicherung.
In diesem Beitrag werden SWIR-Thermografiemessungen während des Bauprozesses mittels Laser Pulver Auftragsschweißen (LPA) vorgestellt. Eine Herausforderung im Rahmen dieser Messungen liegt in der Positionierung der Kamera, welche entweder fixiert am Schweißarm, also mitbewegt, oder fixiert in der Baukammer, also stationär, erfolgen kann, wobei beide Varianten mit individuellen Vor- und Nachteilen verbunden sind. Eine stationäre Befestigung der Kamera ermöglicht zwar eine einfachere Zuordnung der Messdaten zu der jeweiligen Position im Bauteil, führt jedoch bei komplexeren Geometrien zwangsläufig zu Problemen durch Abschattungen und zu defokussierten Bereichen. Zur Auswertung von Thermogrammen, welche durch eine mit dem Schweißarm mitbewegte Kamera aufgenommen wurden, sind hingegen für jedes Bild akkurate Positionsdaten der Kamera nötig um die Messdaten einer Position im Bauteil zuzuordnen. Da die Positionsdaten des Schweißarmes im allgemeinen Fall durch die Anlagensoftware nicht zur Verfügung gestellt werden, muss diese Information durch zusätzliche Messungen aufgezeichnet werden. Hierzu verwenden wir einen an der Kamera befestigten Beschleunigungssensor. Dieser ermöglicht einen zeitlichen Abgleich mit dem vorprogrammierten Verfahrweg des Schweißarmes, welcher im Allgemeinen noch Unsicherheiten bezüglich genauer Geschwindigkeiten und Beschleunigungen offenlässt. Weiterhin untersuchen wir den Einfluss des empfindlichen Spektralbereiches der IR-Kamera durch den Vergleich von Messungen mit verschiedenen schmalbandigen Bandpassfiltern (25 nm FWHM) in einem Bereich von 1150 nm bis 1550 nm.
In this paper we report on the characterization by X-ray computed tomography of calcium phosphate (CaP) and polycaprolactone (PCL) coatings on Ti-6Al-4V alloy scaffolds used as a material for medical implants. The cylindrical scaffold has greater porosity of the inner part than the external part, thus, mimicking trabecular and cortical bone, respectively. The prismatic scaffolds have uniform porosity. Surface of the scaffolds was modified with calcium phosphate (CaP) and polycaprolactone (PCL) by dip-coating to improve biocompatibility and mechanical properties. Computed tomography performed with X-ray and synchrotron radiation revealed the defects of structure and morphology of CaP and PCL coatings showing small platelet-like and spider-web-like structures, respectively.
Most knowledge about the structure, function, and evolution of early compound eyes is based on investigations in trilobites. However, these studies dealt mainly with the cuticular lenses and little was known about internal anatomy. Only recently some data on crystalline cones and retinula cells were reported for a Cambrian trilobite species. Here, we describe internal eye structures of two other trilobite genera. The Ordovician Asaphus sp. reveals preserved crystalline cones situated underneath the cuticular lenses. The same is true for the Devonian species Archegonus (Waribole) warsteinensis, which in addition shows the fine structure of the rhabdom in the retinula cells. These results suggest that an apposition eye with a crystalline cone is ancestral for Trilobita. The overall similarity of trilobite eyes to those of myriapods, crustaceans, and hexapods corroborates views of a phylogenetic position of trilobites in the stem lineage of Mandibulata.
Die Additive Fertigung (AM) wird eingesetzt, um komplexe Bauteile für die Luftfahrt-, Medizin- und Automobilindustrie kostengünstig und zeitsparend herzustellen. Der Einsatz von AM in der Industrie erfordert eine strenge Qualitätskontrolle der hergestellten Teile, um die geforderten Normen erfüllen zu können. Aus diesem Grund spielen die Prozessüberwachung und die Anwendung von Methoden der zerstörungsfreien Prüfung eine große Rolle, was im Fokus unserer aktuellen Forschung steht. In dieser Arbeit benutzen wir Röntgenrückstreuung, welche lediglich einen einseitigen Zugang zum Objekt benötigt, um innenliegende, künstlich hergestellte Defekte in additiv gefertigten Stufenkeilen aus Polyamid 12 (PA 12, Laser Sintering) sowie Acrylnitril-Butadien-Styrol (ABS, Fused Layer Modeling) zu untersuchen. Dafür wurde ein von der Firma AS&E (Boston, USA) konstruierter Prototyp verwendet, der ursprünglich für den Sicherheitsbereich entwickelt wurde. Die Messung der Rückstreuung basiert auf der Flying-Spot Technik mit einem stark kollimierten Nadelstrahl, erzeugt von einem rotierenden Kollimator, wobei großflächige Detektoren die rückgestreute Strahlung sammeln. Da die Anforderungen an die räumliche Auflösung sowie die Kontrastempfindlichkeit in der zerstörungsfreien Prüfung (ZfP) über denen im Sicherheitsbereich liegen, ist eine Optimierung des Prototyps notwendig, um eine Bildqualität zu erreichen, wie sie in der ZfP gefordert ist. Darüber hinaus wurden klassische Durchstrahlungsprüfungen durchgeführt, um die Fähigkeit des Rückstreusystems bei der Defekterkennung in den untersuchten Objekten einschließlich innenliegender Defekte vergleichen und bewerten zu können. Die nachweisbaren Poren und Lufteinschlüsse sind in den Durchstrahlungsaufnahmen, besonders bei den PA 12 Proben, kleiner als in den mittels Rückstreuung erzeugten Bildern. Daher ist eine weitere Optimierung des AS&E- Prototypen notwendig und zusätzliche Untersuchungen sind erforderlich, um die ZfP-Anforderungen zu erfüllen und die Anwendungsgrenzen dieses Geräts zu ermitteln. Jedoch zeigen Vergleichsmessungen mit gedruckten Leichtmetallen (Al), dass die Rückstreutechnik eine vielversprechende Methode zur in-situ Qualitätssicherung mehrerer cm großer Bauteile mit inneren Defekten ab ca. 400 μm Größe ist.
The present work is intended to make a contribution to the monitoring of civil engineering structures. The detection of damage to structures is based on the evaluation of spatially and temporally distributed hybrid measurements. The acquired data can be evaluated purely geometrically or physically. It is preferable to do the latter, since the cause of damage can be determined by means of geometrical-physical laws in order to be able to intervene in time and ensure the further use of the structures. For this reason, the continuum mechanical field equations in conjunction with the finite element method and hybrid measurements are combined into a single evaluation method by the adjustment calculation. This results in two challenges.
The first task deals with the relationship between the finite element method and the method of least squares. The finite element method solves certain problem classes, which are described by a system of elliptical partial differential equations. Whereas the method of least squares solves another class of problems, which is formulated as an overdetermined system of equations. The striking similarity between both methods is known since many decades. However, it remains unresolved why this resemblance exists. The contribution is to clarify this by examining the variational calculus, especially with regard to its methodological procedure. Although the well-known Gauss-Markov model within the method of least squares and the finite element method solve inherently different problem classes, it is shown that both methods can be derived by following the same methodological steps of the variational calculus. From a methodical viewpoint, this implies that both methods are not only similar, but actually the same. In addition, it is pointed out where a possible cross-connection to other methods exists.
The second task introduces a Measurement- and Model-based Structural Analysis (MeMoS) by integrating the finite element method into the adjustment calculation. It is shown in numerical examinations how this integrated analysis can be used for parameter identification of simple as well as arbitrarily shaped structural components. Based on this, it is examined with which observation types, with which precision and at which location of the structure these measurements must be carried out in order to determine the material parameters as precisely as possible. This serves to determine an optimal and economic measurement set-up. With this integrated analysis, a substitute model of a geometrically complex structure can also be determined. The issue of the detection and localisation of damage within a structure is studied by means of this structural analysis. The Measurement and Model-based Structural Analysis is validated using two different test setups, an aluminum model bridge and a bending beam.
Für die Prozessüberwachung in der additiven Fertigung (AM) werden Sensoren und Messsysteme zur Kontrolle der Energiequelle, des Bauraums, des Schmelzbades und der Bauteilgeometrie zumindest im metallbasierten AM schon kommerziell angeboten. Weitere Verfahren der Optik, Spektroskopie und zerstörungsfreien Prüfung werden in der Literatur als geeignet für die in-situ Anwendung bezeichnet, es finden sich aber nur wenige Berichte über konkrete praktische Umsetzungen.
Ein neues Projekt der BAM im Themenfeld Material hat daher das Ziel, Verfahren des Prozessmonitorings zur in-situ Bewertung der Qualität additiv gefertigter Metallbauteile in AM-Prozessen mit Laser- bzw. Lichtbogenquellen zu entwickeln. Dies beinhaltet neben passiver und aktiver Thermografie die optische Tomografie, die optische Emissionsspektroskopie, die Wirbelstromprüfung, die Laminografie, die Röntgenrückstreuung und photoakustische Verfahren. Diese Verfahren werden in verschiedenen AM-Systemen zum selektiven Laserschmelzen, zum Laser-Pulver-Auftragsschweißen und zum Lichtbogenschweißen mit Drahtzuführung zum Einsatz gebracht. Für die zum Teil sehr großen Datenmengen werden Algorithmen für ein effizientes Preprocessing entwickelt und Merkmale der Messdaten in Korrelation zu Fehlern und Inhomogenitäten extrahiert, welche mit Referenzverfahren wie Computertomografie und Ultraschall-Tauchtechnik ermittelt werden. Die Ergebnisse der Einzelverfahren werden fusioniert und mit den Fertigungsparametern korreliert. Diese Prozessüberwachung soll eine deutliche Reduzierung aufwändiger und zeitintensiver, zerstörender oder zerstörungsfreier Prüfungen nach der Fertigung des Bauteiles und zugleich eine Verringerung von Ausschussproduktion bewirken.
Im Beitrag wird zunächst das Projekt als Ganzes vorgestellt und dann der Fokus auf die Thermografie mit Detektoren in verschiedenen Wellenlängenbereichen gelegt. Anforderungen an die Messtechnik für verschiedene AM-Systeme werden diskutiert und experimentelle Ergebnisse im Vergleich zur optischen Tomografie und weiterer Verfahren präsentiert.
In diesem Vortrag wird am Beispiel magnetischer Werkstoffe zur Energiewandlung gezeigt, wie röntgentomographische Untersuchungen zur Strukturaufklärung in Kompositen und Massivproben beitragen können. Die Bauteile werden zerstörungsfrei geprüft, um Risse, Poren und andere Defekte und ihren Einfluss auf die funktionellen Eigenschaften dreidimensional und rechtzeitig im Lebenszyklus des Werkstoffs zu charakterisieren. Kombiniert man Mikrotomographie mit anderen Methoden der magnetischen Werkstoffcharakterisierung, lassen sich einzigartige Aussagen über den Aufbau und die funktionellen Eigenschaften treffen.
Using magnetic materials for energy conversion as an example, this lecture shows how X-ray tomography investigations can contribute to structure elucidation in composites and solid samples. The components are tested non-destructively in order to characterize cracks, pores and other defects and their influence on the functional properties three-dimensionally and in good time in the life cycle of the material. If you combine microtomography with other methods of magnetic material characterization, you can make unique statements about the structure and the functional properties.
Using magnetic materials for energy conversion as an example, this lecture shows how X-ray tomography investigations can contribute to structure elucidation in composites and solid samples. The components are tested non-destructively in order to characterize cracks, pores and other defects and their influence on the functional properties three-dimensionally and in good time in the life cycle of the material. If you combine microtomography with other methods of magnetic material characterization, you can make unique statements about the structure and the functional properties.
To date, there are only very few technologies available for the conversion of low temperature waste heat to electricity. In this talk, we first describe the principle of thermomagnetic generators. Then we focus on the impact of topology of the magnetic circuit within thermomagnetic generators. We demonstrate that the key operational parameters strongly depend on the genus, i.e. the number of holes within the magnetic circuit.
To date, there are only very few technologies available for the conversion of low temperature waste heat to electricity. In this talk, we first describe the principle of thermomagnetic generators. Then we focus on the impact of topology of the magnetic circuit within thermomagnetic generators. We demonstrate that the key operational parameters strongly depend on the genus, i.e. the number of holes within the magnetic circuit.
To date, there are very few technologies available for the conversion of low-temperature waste heat into electricity. Thermomagnetic generators are one approach proposed more than a century ago. Such devices are based on a cyclic change of magnetization with temperature. For thermomagnetic materials, we used a commercial magnetocaloric alloy with a transition temperature of 300 K.
To date, there are only very few technologies available for the conversion of low temperature waste heat to electricity. In this talk, we first describe the principle of thermomagnetic generators. Then we focus on the impact of topology of the magnetic circuit within thermomagnetic generators. We demonstrate that the key operational parameters strongly depend on the genus, i.e. the number of holes within the magnetic circuit.
To date, there are very few technologies available for the conversion of low-temperature waste heat into electricity. Thermomagnetic generators are one approach proposed more than a century ago. Such devices are based on a cyclic change of magnetization with temperature. For thermomagnetic materials, we used a commercial magnetocaloric alloy with a transition temperature of 300 K.
To date, there are only very few technologies available for the conversion of low temperature waste heat to electricity. In this talk, we first describe the principle of thermomagnetic generators. Then we focus on the impact of topology of the magnetic circuit within thermomagnetic generators. We demonstrate that the key operational parameters strongly depend on the genus, i.e. the number of holes within the magnetic circuit.
In diesem Vortrag wird am Beispiel magnetischer Werkstoffe zur Energiewandlung gezeigt, wie röntgentomographische Untersuchungen zur Strukturaufklärung in Kompositen und Massivproben beitragen können. Die Bauteile werden zerstörungsfrei geprüft, um Risse, Poren und andere Defekte und ihren Einfluss auf die funktionellen Eigenschaften dreidimensional und rechtzeitig im Lebenszyklus des Werkstoffs zu charakterisieren. Kombiniert man Mikrotomographie mit anderen Methoden der magnetischen Werkstoffcharakterisierung, lassen sich einzigartige Aussagen über den Aufbau und die funktionellen Eigenschaften treffen.
In diesem Vortrag wird am Beispiel magnetischer Werkstoffe zur Energiewandlung gezeigt, wie röntgentomographische Untersuchungen zur Strukturaufklärung in Kompositen und Massivproben beitragen können. Die Bauteile werden zerstörungsfrei geprüft, um Risse, Poren und andere Defekte und ihren Einfluss auf die funktionellen Eigenschaften dreidimensional und rechtzeitig im Lebenszyklus des Werkstoffs zu charakterisieren. Kombiniert man Mikrotomographie mit anderen Methoden der magnetischen Werkstoffcharakterisierung, lassen sich einzigartige Aussagen über den Aufbau und die funktionellen Eigenschaften treffen.
Explosive spalling is caused by, among others, the thermohydraulic spalling mechanism. During this process, vaporization, dehydration, moisture-transport and condensation processes interact. As a result, a drying and dehydration zone as well as a saturated zone, known as a moisture clog, are observed inside the unilaterally-heated concrete. The presented research is focused on the experimental investigation of the underlying thermohydraulic processes.
To investigate these, a test methodology based on X-ray computed tomography (CT) and nuclear magnetic resonance (NMR) was developed. Thereby, the X-ray CT scans are carried out simultaneously during the application of a defined unilateral-heating regime on a specially-constructed specimen. This miniaturized specimen, equipped with a double-layer casing, reproduces the condition within a planar, unilaterally-heated building component.
A preliminary test methodology and the first experimental results were presented at the 5th International Workshop on Concrete Spalling in Borås, Sweden (2017). The contribution for the upcoming workshop presents an improved version of this test methodology and new results for a high-performance concrete (HPC) mixture exposed to temperatures up to 500 °C. Regarding the CT measurements, a higher time-resolution of 15 min was achieved and a quantification of the moisture changes was implemented. Due to an increase in signal quality of the NMR measurements, a pore-size specific moisture distribution can now be resolved. This allows to conclude about the moisture reconfiguration between small gel pores and larger interhydrate pores. Additionally, the NMR measurement are no longer limited to first 2.5 cm below the heated surface but a one-dimensional moisture distribution can now be estimated over the whole 10 cm long specimen.
The presented results demonstrate that the combination of X-ray CT and NMR measurements enables to image and quantify the thermally-induced moisture transport and reconfiguration from small gel pores up to macro pores. This provides important insights into the thermohydraulic damage mechanism and leads to a better understanding of spalling avoidance strategies, like the addition of polypropylene fibres.
3D images such as those produces by X-ray tomography can provide a wealth of information on the internal structure of materials, but quantification of specific geometrical or topological characteristics linked to some bulk physical property is far from being straightforward. This study focuses on methods to quantify the differences in physical properties as a function of direction, i.e. their anisotropy, and how it can be linked to measures of anisotropy of the internal structure of the material. The auto-correlation function gives a similarity measure in the volume as a function of distance and direction. This is a cross-correlation of the image with itself fast to compute and relatively insensitive to noise. It is why we focus on this method to compare with the physical property of our DPF material. Diesel Particulate Filter (DPF) materials are porous ceramics that; a) can be used at very high temperatures; b) have very good thermal shock resistance; c) are inert; d) can be manufactured with tailored porosity. Their usual way of production consists of the extrusion of a slurry into the desired filter shape, with successive ceramming at high temperature. This process causes anisotropy at both microscopic and macroscopic levels.
Using non-optimum combination of manufacturing parameters in selective laser melting (SLM) may lead to reduction of quality of component: defects generation, distortion of geometry and even cracking. Usually, the optimization of parameters is performed by changing volumetric energy density (Ev) and selecting parameters giving low porosity values. However, not only low porosity but also stable microstructure and low residual stresses will help to achieve advanced mechanical behavior of the component.
In present work, we investigated cuboid-shaped Ti-6Al-4V samples produced with different manufacturing parameters. The parameters leading to the same Ev were considered as well as parameters which are not included in Ev. Residual stresses in subsurface region were investigated by synchrotron X-ray diffraction, which allows to penetrate around 100 µm from the surface therefore overcome the problem of high roughness of SLM components without additional sample preparation. Only tensile stresses were found along the building direction, that can play critical role especially during cyclic loading. The pore shape and spatial distribution obtained by computed tomography varied for samples produced with the same Ev. However, by using some process parameters it was possible to decrease residual stresses and obtain uniform α+β Ti microstructure and relatively low porosity. Additionally, it was found that not included in Ev (e.g., base plate position, focus distance) should be considered as additional manufacturing parameters during SLM process.
Das vorgestellte Projekt beschäftigt sich mit den optischen, thermophysikalischen und mechanischen Materialeigenschaften von additiv gefertigten Kunststoffteilen und deren Alterung. Dazu wurden mittels Fused Layer Modeling (FLM) Probekörper aus ABS hergestellt, die anschließend für drei Monate einer künstlichen Bewitterung unterzogen wurden. Die dabei erzeugte definierte Alterung wurde nach drei Zeitabschnitten jeweils mit zerstörungsfreien Methoden charakterisiert. Dabei wurde neben den spektroskopischen Standardmethoden auch die aktive Thermografie eingesetzt. Die Ergebnisse zeigen, dass sich mittels der Thermografie sowohl chemische Veränderungen als auch mechanische Schädigungen (Fehlstellen) darstellen lassen. Die Bewitterung beeinflusst die Teiltransparenz der Proben zumindest im sichtbaren Spektralbereich, was bei der Charakterisierung der Fehlstellen, die mittels optisch angeregter aktiver Thermografie detektiert wurden, berücksichtigt werden muss.
Explosive spalling is caused by, among others, the thermohydraulic spalling mechanism. During this process, vaporization, dehydration, moisture-transport and condensation processes interact. As a result, a drying and dehydration zone as well as a saturated zone, known as a moisture clog, are observed inside the unilaterally-heated concrete. The presented research is focused on the experimental investigation of the underlying thermohydraulic processes.
To investigate these, a test methodology based on X-ray computed tomography (CT) and nuclear magnetic resonance (NMR) was developed. Thereby, the X-ray CT scans are carried out simultaneously during the application of a defined unilateral-heating regime on a specially-constructed specimen. This miniaturized specimen, equipped with a double-layer casing, reproduces the condition within a planar, unilaterally-heated building component.
A preliminary test methodology and the first experimental results were presented at the 5th International Workshop on Concrete Spalling in Borås, Sweden (2017). The contribution for the upcoming workshop presents an improved version of this test methodology and new results for a high-performance concrete (HPC) mixture exposed to temperatures up to 500 °C. Regarding the CT measurements, a higher time-resolution of 15 min was achieved and a quantification of the moisture changes was implemented. Due to an increase in signal quality of the NMR measurements, a pore-size specific moisture distribution can now be resolved. This allows to conclude about the moisture reconfiguration between small gel pores and larger interhydrate pores. Additionally, the NMR measurement are no longer limited to first 2.5 cm below the heated surface but a one-dimensional moisture distribution can now be estimated over the whole 10 cm long specimen.
The presented results demonstrate that the combination of X-ray CT and NMR measurements enables to image and quantify the thermally-induced moisture transport and reconfiguration from small gel pores up to macro pores. This provides important insights into the thermohydraulic damage mechanism and leads to a better understanding of spalling avoidance strategies, like the addition of polypropylene fibres.
By allowing economic on demand manufacturing of highly customized and complex workpieces, metal based additive manufacturing (AM) has the prospect to revolutionize many industrial areas. Since AM is prone to the formation of defects during the building process, a fundamental requirement for AM to become applicable in most fields is the ability to guarantee the adherence to strict quality and safety standards. A possible solution for this problem lies in the deployment of various in-situ monitoring techniques. For most of these techniques, the application to AM is still very poorly understood. Therefore, the BAM in its mission to provide safety in technology has initiated the project “Process Monitoring of AM” (ProMoAM). In this project, a wide range of in-situ process monitoring techniques, including active and passive thermography, optical tomography, optical emission and absorption spectroscopy, eddy current testing, laminography, X-ray backscattering and photoacoustic methods, are applied to laser metal deposition (LMD), laser powder bed fusion and wire arc AM. Since it is still unclear which measured quantities are relevant for the detection of defects, these measurements are performed very thoroughly. In successive steps, the data acquired by all these methods is fused and compared to the results of reference methods such as computer tomography and ultrasonic immersion testing. The goal is to find reliable methods to detect the formation of defects during the building process. The detailed acquired data sets may also be used for comparison with simulations.
Here, we show first results of high speed (> 300 Hz) thermographic measurements of the LMD process in the SWIR range using 316L as building material. For these experiments, the camera was mounted fixed to the welding arm of the LMD machine to keep the molten pool in focus, regardless of the shape of the specimen. As the thermograms do not contain any information about the current spatial position during the building process, we use an acceleration sensor to track the movement and synchronize the measured data with the predefined welding path. This allows us to reconstruct the geometry of the workpieces and assign the thermographic data to spatial positions. Furthermore, we investigate the influence of the acquisition wavelength on the thermographic data by comparing measurements acquired with different narrow bandpass filters (50 nm FWHM) in a spectral range from 1150 nm to 1550 nm.
This research was funded by BAM within the Focus Area Materials.
The present work is intended to make a contribution to the monitoring of civil engineering structures. The detection of damage to structures is based on the evaluation of spatially and temporally distributed hybrid measurements. The acquired data can be evaluated purely geometrically or physically. It is preferable to do the latter, since the cause of damage can be determined by means of geometrical-physical laws in order to be able to intervene in time and ensure the further use of the structures. For this reason, the continuum mechanical field equations in conjunction with the finite element method and hybrid measurements are combined into a single evaluation method by the adjustment calculation. This results in two challenges.
The first task deals with the relationship between the finite element method and the method of least squares. The finite element method solves certain problem classes, which are described by a system of elliptical partial differential equations. Whereas the method of least squares solves another class of problems, which is formulated as an overdetermined system of equations. The striking similarity between both methods is known since many decades. However, it remains unresolved why this resemblance exists. The contribution is to clarify this by examining the variational calculus, especially with regard to its methodological procedure. Although the well-known Gauss-Markov model within the method of least squares and the finite element method solve inherently different problem classes, it is shown that both methods can be derived by following the same methodological steps of the variational calculus. From a methodical viewpoint, this implies that both methods are not only similar, but actually the same. In addition, it is pointed out where a possible cross-connection to other methods exists.
The second task introduces a Measurement- and Model-based Structural Analysis (MeMoS) by integrating the finite element method into the adjustment calculation. It is shown in numerical examinations how this integrated analysis can be used for parameter identification of simple as well as arbitrarily shaped structural components. Based on this, it is examined with which observation types, with which precision and at which location of the structure these measurements must be carried out in order to determine the material parameters as precisely as possible. This serves to determine an optimal and economic measurement set-up. With this integrated analysis, a substitute model of a geometrically complex structure can also be determined. The issue of the detection and localisation of damage within a structure is studied by means of this structural analysis. The Measurement and Model-based Structural Analysis is validated using two different test setups, an aluminum model bridge and a bending beam.
By means of a small-scale truss bridge, the ability of the Measurement- and Model-based Structural Analysis to detect and localize damage was examined. Although there was no noteworthy difficulty in detecting damage, it turned out that damage localization responds sensitively to systematic influences, i.e. non-modelled properties of the mechanical model. Therefore, another experiment is being conducted to re-examine the Measurement- and Model-based Structural Analysis. For this purpose, the bending test is carried out as it has been already theoretically respectively numerically discussed. In this attempt, the systematic influences such as residual stress are kept as low as possible.
For a better understanding of the damage of glued wood tensile tests on miniature specimens made of glued spruce wood with acoustic emission and in-situ synchrotron-based X-ray computer microtomography has been monitored. As adhesive, urea-formaldehyde resin was used. For comparison purposes, tensile tests were carried out on solid wood and bonded miniature tensile shear samples with acoustic emission. The acoustic emission signals of all experiments were with classified pattern recognition. This resulted in two classes of signals for each two frequency peaks. In one class was the low-frequency, in the other the higher frequency peak of higher intensity, but this essentially independent from the structure (solid wood or plywood) and the size scale of the test specimens. The influence of the adhesive layers was determined on plywood test specimens in laboratory scale and on miniature test specimens with an adhesive layer and selected fiber orientations examined. This gave evidence that the sound emission signals from the failure of the adhesive layer presumably of the class with low frequency signals peak in the range of services can be assigned.
The present study deals with the experimental characterization of short crack propagation in SLM (selective-laser-melting) manufactured stainless steel. More specifically, the determination of cyclic R-curves is discussed. This describes the dependency of the crack propagation threshold on crack growth during the short crack propagation stage. For metals, the threshold, starting at a material-intrinsic value, increases until it reaches a value independent of the crack length due to crack closure phenomena which build up at that stage. The cyclic R-curve, when used in the frame of a cyclic R curve analysis, characterizes the resistance of a material to fatigue crack growth and the ability to arrest a physically short crack. Thus, it is the link between classical fatigue and fracture mechanics. In the high-cycle-fatigue range, the short crack propagation stage dominates the overall lifetime, i.e., the number of cycles until failure. Below the fatigue limit crack arrest of hitherto propagable micro-cracks will occur. The effort for the experimental characterization of the short fatigue crack propagation behavior and the cyclic R-curve is very high compared to experiments on long crack propagation. A very exact measurement of crack extension is required, since small increments need to be depicted. Pre-cracking must leave a closure free initial crack, since closure must be build up only by the cyclic R-curve. The closure-free status is achieved by compression pre-cracking. The aim of the present study is an insight into the influence of an AM process on the short crack propagation threshold. Cyclic R-curves are experimentally determined at different load-ratios for 316L austenitic steel specimens produced by SLM and conventional manufacturing. Residual stresses are measured in the crack plane and their influence on the cyclic R-curve is discussed.
Residual stresses count among the most limiting factors in the application of additively manufactured materials in safety relevant components subject to cyclic loading. The source of such stresses is inherent in the manufacturing Laser Beam Melted (LBM) process due to rapid cooling and solidification and their distribution in the specimen or component is not homogeneous, but it is usually characterized by high gradients. Moreover, the magnitude of the residual stress field depends very much on the orientation, being higher in the build direction.
Many works in the literature advise to carry out a post-LBM treatment to relieve residual stresses, even though particular attention should be paid in choosing the parameters for the thermal treatment in order to avoid microstructural/phase transformations, which would affect greatly the mechanical properties of the material.
Particularly in the case of the austenitic stainless steel 316L, it has been shown that annealing at high temperatures (above 900°C), besides relieving the residual stresses, may cause recrystallization, grain growth and even phase transformation. In contrast, if a too low annealing temperature is chosen in order to preserve the microstructure, the residual stresses cannot be completely relieved.
This work aims to address the effect of residual stresses on short and long crack propagation for SEN(B) specimens made of 316L fabricated by LBM, in which notches have been machined by electro-discharge machining (EDM) on the mid-plane, perpendicular to the build direction. The specimens underwent different annealing treatments in inert atmosphere, in which the maximum temperature has been varied up to 900°C. The amount of residual stresses and their distribution has been measured by X-ray and neutron diffraction and the specimens have been subject to cyclic loading in a resonant testing machine. The tests show a massive influence of the residual stresses in the build direction on the resistance to fatigue crack propagation of additively manufactured 316L. Finally, a comparison with conventionally manufactured 316L is presented.
Laser powder bed fusion (L-PBF) is one of the most promising additive manufacturing (AM) technologies for the production of complex metallic real part components. Due to the multitude of factors influencing process conditions and part quality and due to the layer-wise characteristic of the process, monitoring of process signatures seems to be mandatory in case of the production of safety critical components. Here, the iterative process nature enables unique access for in-situ monitoring during part manufacture. In this talk, the successful test of the synchronous use of a high-frequency infrared camera and a camera for long time exposure, working in the visible spectrum (VIS) and equipped with a near infrared filter (NIR), will be introduced as a machine manufacturer independent thermal detection monitoring set-up. Thereby, the synchronous use of an infrared camera and a VIS NIR camera combines the advantages of high framerate and high spatial resolution. The manufacture of a 316L stainless steel specimen, containing purposely seeded defects and volumes with forced changes of energy inputs, was monitored during the build. The measured thermal responses are analysed and compared with a defect mapping obtained by micro X-ray computed tomography (CT).
The first results regarding methods for data analysis, derived correlations between measured signals and detected defects as well as sources of possible data misinterpretation are presented in this talk.
Diese Arbeit beschäftigt sich mit den Eigenschaften der photonenzählenden und spektralauflösenden Detektortechnik und möglichen Anwendungsgebieten in der zerstörungsfreien Prüfung. Dabei wurden konventionelle und photonenzählende Detektortechniken hinsichtlich der Bildqualität und Anwendbarkeit bei unterschiedlichen Prüfaufgaben verglichen und untersucht, inwiefern sich die Energieschwellwertsetzung auf die erreichbare Bildqualität und eine Materialdiskriminierbarkeit bei verschiedenen radiographischen Verfahren auswirkt.
Anhand von Anwendungsbeispielen wurden diese Eigenschaften und deren Auswirkung auf das Messergebnis analysiert. Neben der Radiographie wurden auch dreidimensionale Verfahren wie CT und Laminographie berücksichtigt.
Als eine der wichtigsten Eigenschaften der photonenzählenden Detektortechnik wurden zunächst die Energieauflösung des photonenzählenden Detektors und die Homogenität der Energieantwort über größere Detektorbereiche bestimmt. Dabei stellte sich heraus, dass die Energieauflösung eines abgegrenzten Detektorbereichs ca. 32 % bei 60 keV beträgt und die Streuung in der Energieantwort der einzelnen Detektorbereiche ca. 12 % ausmacht, woraus sich eine Gesamtunsicherheit in der spektralen Detektorantwort von ca. 44 % ergibt. Die geringe Energieauflösung und das stark heterogene Verhalten der Detektorbereiche ergeben sich vor allem aus der Detektorelektronik, welche nur eine globale Energieschwellwertsetzung zulässt.
Trotz dieser Einschränkungen konnte demonstriert werden, dass auch konventionelle radiographische Verfahren, wie Radiographie oder CT, vom Einsatz der photonenzählenden Technik profitieren. So ist es mit dieser Technik möglich, bei sehr geringen Dosisleistungen (z.B. aufgrund der Durchstrahlung großer Wandstärken von dichten Materialien) noch sehr gute Bildqualitäten zu erreichen. Die hohe Dynamik und Kontrastempfindlichkeit dieser Technik begünstigen die Inspektion von Leichtbauwerkstoffen wie Faserverbunde, was anhand von Vergleichen mit herkömmlicher Detektortechnik und anderen ZfP-Verfahren gezeigt werden konnte. Daneben konnte durch den Einsatz der Energieschwellwertsetzung der Einfluss von nicht bildzeichnender Streustrahlung im Röntgenbild um bis zu 20 % reduziert werden. Die Auswirkungen von Aufhärtungseffekten in der CT konnten sogar um bis zu Faktor 1 000 (in der mittleren quadratischen Abweichung), im Vergleich zu herkömmlicher Detektortechnik, reduziert werden.
Der Einsatz von photonenzählender Detektortechnik mit Röntgenblitzröhren ist hingegen nicht sinnvoll, da aufgrund der hohen Photonendichte pro Puls und einer endlichen Totzeit des Detektors in der Größenordnung der Pulsbreite eines Blitzes nur ein geringes Signal detektiert werden kann.
Im Hinblick auf eine Materialdiskriminierbarkeit konnte demonstriert werden, dass im Fall einer Radiographie anhand der Energieschwellwertsetzung im Detektor eine materialstärkenunabhängige Diskriminierung zwischen zwei Materialien (hier: Al und Fe) erzielt werden kann. Unter Einsatz mehrerer Energiefenster und eines Verfahrens der explorativen und multivariaten Datenanalyse konnte eine materialaufgelöste CT eines Multi-Material-Phantoms erreicht werden, wobei die Schwächungskoeffizienten der enthaltenen Materialien im relevanten Energieberiech teilweise sehr dicht beieinander lagen.
Neben Radiographie und CT wurde auch die Möglichkeit einer materialaufgelösten Laminographie am Beispiel eines glasfaserverstärkten Rotorblatts untersucht. Anhand der Energieschwellwertsetzung war nicht nur eine eindeutige Trennung der Glasfasern von der Epoxidharzmatrix möglich, sondern auch eine signifikante Reduzierung der durch die Laminographie entstandenen Artefakte. Der damit verbundene Gewinn an Information führt zu einer verbesserten Aussagefähigkeit des Untersuchungsergebnisses, was letztendlich eine gesteigerte Betriebssicherheit zur Folge hat.
Diffraction-based experimental determination of Residual Stress in AM parts: A critical discussion
(2019)
Additive manufacturing (AM) technologies have experienced an exceedingly rapid growth, not always paralleled by the knowledge about the materials properties and performance. In particular, residual stress (RS) has been soon recognized as an issue in AM parts, so that parts are always post-heat-treated. Moreover, much effort has been spent on simulating RS, especially using finite element methods.
The experimental determination of RS has thereby become increasingly important, and even simple data constitute (to date) a piece of knowledge to fill the above-mentioned gap. In particular, diffraction methods, which are basically non-destructive, offer enormous possibilities to gain knowledge on real components, since neutrons and synchrotron radiation can penetrate even heavy metals up to several millimeters (or even centimeters). Indeed, some success has been obtained, and the knowledge about the origins of the RS fields, as well as their variation as a consequence of heat or mechanical treatments, has been greatly expanded.
In this talk, a few success stories will be outlined. It will be shown how the determination of RS in metallic parts (with focus on those produced by laser powder bed fusion) has even allowed showing that process parameters that were considered unimportant play a major role in the onset of stress.
However, while RS is starting to be considered in the part design, deposition strategy (e.g. build plate temperature), and even in the definition of the relevant metric to assess the quality of a part, much is still to be investigated about the hypotheses underlying its experimental determination. Therefore, some aspects to be aware of, or even to date unclear will also be discussed, such as the determination of the reference unstrained samples and of the principal axes of stress. All these aspects will draw the path towards a comprehensive understanding of the process-structure-performance relationships in AM materials and parts.
Functional materials for energy conversion are important technology drivers needed for the implementation of low carbon energy. Therefore, researchers commonly focus on improving the intrinsic properties of a functional material. However, for applications, the extrinsic properties are at least as important as the intrinsic ones. Consequently, it is important to investigate and understand the external and internal structure of semi-finished products and especially defect dependent properties. The extrinsic properties may change during application and the life cycle of the material as well as through processing and molding steps.
Our studies show how X-ray tomographic (XCT) investigations can contribute to structure investigations in composites and massive samples using the example of magnetic materials for energy conversion. The components are tested non-destructively in 3D in order to localize and characterize cracks, pores, inclusions as well as other defects and their influence on the functional properties and also “in-time” during the life cycle of the material. Exsitu and in-situ experiments performed with non-destructive XCT are predestinated to follow damaging mechanisms of materials under certain load conditions, atmospheres or liquids, e.g. went through several working cycles of a functional material. By combining microtomography with other methods of magnetic and classical material characterization, unique statements about the structure and the functional properties can be made.
From the applications point of view, sometimes complex, three-dimensional geometries are needed to fully exploit the functional properties of the materials, e.g. to ensure a high surface area for heat exchange. Since many functional materials are brittle and difficult to form, shaping is often a big challenge. In principle, additive manufacturing processes offer the possibility to produce complex, porous components from poorly formable alloys.
If all stages of additive manufacturing are accompanied by X-ray tomographic imaging, the process of finding the optimal parameters for material processing can be significantly accelerated.
Based on the quality control of the initial powder material used and also investigations of the shape and arrangement of defects within the molten structure and their relationship with the melting path scanning strategy, Xray tomography has proven to be an ideal tool for additive manufacturing, even for functional materials. Overall, tomographic methods are important tools for the development of functional materials to application maturity.
Synchrotron based absorption edge tomography for the analysis of 3D printed polymer embedded MOF
(2019)
Absorption edge tomography, also known as differential tomography at absorption edges, is a method which exploits the sudden change of the attenuation coefficient, when the photon energy crosses the absorption edge of an element. Synchrotron radiation is the best source for absorption edge tomography, because of its small bandwidth, high intensity and easily adjustable photon energy. The synchrotron beamline BAMline at the synchrotron radiation facility BESSY II in Berlin, which is operated by the Bundesanstalt für Materialforschung und -prüfung (BAM), provides a monochromatized beam in a photon energy range from 5 keV up to 80 keV with a bandwidth of 2%, when the double multilayer monochromator is used. Together with the microtomography setup, this enables differential tomography with submicron resolution at the K edge of the elements from chromium up to the lanthanides, and up to uranium, when the L edges are used as well.
In this work, metal organic frameworks (MOFs) embedded in polymer are characterized using differential tomography. MOFs are microporous structures of metal ions, coordinated by organic linker molecules, that can be used in a broad field of applications, especially in gas storage and catalysis. In this work, polymer embedded MOFs were extruded into filaments, which were subsequently used for 3d-printing to profit from the specific properties of the MOFs in polymeric materials combined with the arbitrary shapes provided by 3d-printing. For the extrusion, different polymer classes like ABS, polyester- and polyetherurethanes, as well as different MOFs (ZIF-8, ZIF-67, HKUST-1) were used to create MOF containing filaments with a nominal diameter of 3.0 mm. Differential tomography at the edges of the Zn, Co, and Cu was then used to find the distribution of the corresponding MOF in the filament and to analyze the shape of the inclusions.