Ingenieurwissenschaften und zugeordnete Tätigkeiten
Filtern
Erscheinungsjahr
- 2018 (21) (entfernen)
Dokumenttyp
- Zeitschriftenartikel (8)
- Vortrag (6)
- Beitrag zu einem Tagungsband (5)
- Posterpräsentation (2)
Schlagworte
- Residual stress (9)
- Welding (5)
- Additive manufacturing (4)
- Eigenspannungen (4)
- Additive Manufacturing (3)
- High-strength steels (3)
- IN718 (3)
- Residual Stresses (3)
- Residual stresses (3)
- Selective Laser Melting (3)
Organisationseinheit der BAM
- 9 Komponentensicherheit (21)
- 9.4 Integrität von Schweißverbindungen (21)
- 9.2 Versuchsanlagen und Prüftechnik (9)
- 5 Werkstofftechnik (8)
- 5.0 Abteilungsleitung und andere (8)
- 8 Zerstörungsfreie Prüfung (7)
- 8.5 Röntgenbildgebung (7)
- 9.0 Abteilungsleitung und andere (2)
- 5.1 Mikrostruktur Design und Degradation (1)
Eingeladener Vortrag
- nein (6)
Influence of deposition hatch length on residual stress in selective laser melted Inconel 718
(2018)
The present study aims to evaluate the bulk residual stresses in SLM parts by using neutron diffraction measurements performed at E3 line -BER II neutron reactor- of Helmholtz-Zentrum für Materialien und Energie (HZB) Berlin. Together with microstructure characterization and distortion measurements, it is possible to describe the stress state throughout the whole sample. The sample was measured in as-build condition (on a build plate) and after releasing from the build plate. The used material is the nickel based superalloy 718. This alloy is widely used in aerospace and chemical industries due to its superior corrosion and heat resistant properties.
Obtained results indicated different residual stress states for each of the transversal, longitudinal and normal component. The normal and transversal component exhibits a rather compressive behavior while the longitudinal was tensile in the center part of the sample and became compressive towards the tip. As expected, the absolute values of all stress components decreased after releasing the sample from the building plate. A surface scan utilizing a coordinate-measuring machine (CMM) allowed us to present top surface distortion before and after releasing. The top surface showed a distortion around ±80µm after releasing. Microstructure evolution in the scanning-building cross-section is largely dominated by columnar grains. In addition, many small random orientated grains are prominent in the regions of a laser overlap during SLM.
In summary, for the sample of superalloy 718 manufactured by SLM, a small distortion occurred when removing the sample from the build plate whereby the residual stress state decreases. Moreover, the observed columnar grains in the building direction could give a reason for the lowest stress values in that normal direction. However, the most important parameter controlling the residual stresses is the temperature gradient. Hence, future investigations are planned for a different scan strategy to distribute the laser impact in a more homogenous manner.
Compared to conventional welding consumables using low transformation temperature (LTT) filler materials is an innovative method to mitigate tensile residual stresses due to delayed martensite transformation of the weld. For the effective usage of LTT filler materials, a deeper understanding of the complex processes that lead to the final residual stress state during multipass welding is necessary. Transformation kinetics and the strain evolution of multi-pass welds during welding were investigated in situ at the beamline HEMS@PETRAIII, Germany. Compared to conventional welds, the total strain was reduced and compression strain was achieved when using LTT filler materials. For an optimal use of the LTT effect in the root of multi-pass welds, the alloying concept must be adapted taking care of dilution.
The phase transformation under various cooling rates and in different HAZ regions for high-strength armour steel was analysed by dilatometry. To develop a continuous cooling transformation (CCT) diagram, the samples were heated up to a peak temperature of 1250 °C to achieve a coarse-grained microstructure and then cooled down with a cooling time t 8/5 varying from 3 to 240 s. Analysis of dilatation curves revealed the austenite decomposition process, during which transformation temperatures were determined. The results showed martensitic transformations for all welding-relevant cooling times. Furthermore, to analyse different heat-affected subzones of the weld, the peak temperature was varied between 550 and 1250 °C at a constant cooling time t 8/5 of 6 s. The simulated coarse-grained heat-affected zone (CGHAZ) and fine-grained-heat affected zone (FGHAZ) showed only martensitic transformations with transformation temperatures below 400 °C. The steel exhibited an inhomogeneous hardness with hardening in the CGHAZ and FGHAZ and softening in the intercritical and subcritical HAZ. The physically simulated microstructure was validated by a real hybrid laser-arc weld microstructure.
Beim Schweißen höherfester Stähle mit LTT-Zusatzwerkstoffen im Wurzelbereich der Schweißverbindung wird eine Erhöhung der Kaltrisssicherheit durch die Erzeugung von Druckeigenspannungen erreicht.
Es sind mechanische Gütewerte und Eigenspannungen in Abhängigkeit der Randbedingungen, insbesondere der Wärmeführung und des Nahtaufbaus im Wurzelbereich, systematisch zu ermitteln. Durch das Ableiten von Verarbeitungsempfehlungen wird eine sichere und optimale Handhabung der LTT-Zusätze ermöglicht.
Ziel ist die Entwicklung eines Maßnahmenkatalogs für die schweißtechnische Verarbeitung von LTT-Zusatzwerkstoffen zur Kaltrissvermeidung im Wurzelbereich höherfester Schweißverbindungen speziell für den Offshore-Bereich.
Der zunehmende Bedarf an hochfesten Feinkornbaustählen in modernen Schweißkonstruktionen, in einer deutlich wachsenden Anzahl von Branchen wie dem Hoch-, Anlagen- und Kranbau, führte in den letzten Jahren zur Entwicklung zahlreicher Grund- und Zusatzwerkstoffe. Neben der Erreichung anforderungsgerechter mechanischer Eigenschaften wird die wirtschaftliche Verarbeitung dieser Güten durch hohe Sicherheitsanforderungen an die Schweißnaht bestimmt. Hohe Zugeigenspannungen in der Schweißverbindung können die Beanspruchbarkeit und Sicherheit eines geschweißten Bauteils wesentlich reduzieren. Insbesondere bei einer hohen konstruktiven Schrumpfbehinderung können die Beanspruchungen auch schon während der Fertigung ein risskritisches Niveau erreichen.
Mittels geeigneten Wärmeführungen beim Schweißen und der adäquaten Auswahl von Schweißprozess und Zusatzwerkstoffen ist sowohl eine Minimierung der sich lokal in der Naht bildenden Zugeigenspannungen als auch der globalen infolge von Abstützeffekten auftretenden Reaktionsspannungen und -momente erzielbar. Im Rahmen zweier AiF-Forschungsvorhaben IGF.-Nr. 17267 N und 17978 N wurden verschiedene experimentelle Beanspruchungsanalysen durchgeführt, um den Schweißprozess hinsichtlich der resultierenden schweißbedingten Beanspruchungen zu untersuchen. Hierfür war es erforderlich, die Steifigkeitsverhältnisse so wie sie beim Schweißen realer Bauteilstrukturen auftreten, auf Schweißexperimente im Labor zu übertragen.
Dazu wurde bspw. eine an der BAM eigens entwickelte Prüfanlage eingesetzt, mit der die mehraxialen Belastungen analysiert wurden, die mit bis zu 2 MN beim Vorwärmen, Schweißen und Abkühlen auftreten. Die Schweißeigenspannungen wurden mittels Röntgendiffraktometrie bestimmt. Zwar zeigten sich für niedrige Arbeitstemperaturen beim Schweißen ein signifikant reduziertes Gesamtbeanspruchungsniveau nach der Abkühlung der gesamten Schweißnaht. Die langen Abkühlphasen während der mehrlagigen schweißtechnischen Fertigung führen jedoch speziell bei den ersten Schweißraupen zu sehr hohen Reaktionsspannungen. Dabei erwiesen sich schmalere Nahtfugen verbunden mit dem Einsatz modifizierter Schweißprozesse und der Einsatz dehnfähiger Schweißzusätze für das Wurzelschweißen als geeignete Mittel, um eine deutliche Absenkung des Beanspruchungsniveaus beim Schweißen unter Schrumpfbehinderung zu erreichen. Ferner ist damit eine weitere wesentliche Reduzierung der Gesamtbeanspruchung und insbesondere der Zugeigenspannungen in der WEZ möglich. Mithilfe dieser Erkenntnisse ist die Optimierung der schweißbedingten Beanspruchungen unter Nutzung einer adaptierten Wärmeführung zur verbesserten Ausnutzung des Festigkeitspotentials höherfester Feinkornbaustähle erreichbar.
Die Verwendung von LTT-Zusatzwerkstoffen stellt einen alternativen Ansatz zu den sonst üblichen Verfahren der Schweißnahtnachbehandlung zur Schwingfestigkeitserhöhung geschweißter Stahlkonstruktionen dar. Der wesentliche Wirkmechanismus beruht auf der Beeinflussung des Eigenspannungszustands durch die niedrige Martensitstarttemperatur bereits während des Schweißens. Dadurch werden die Druckeigenspannungen aus der behinderten Volumenausdehnung infolge Phasenumwandlung voll wirksam. Weiter weist die Schweißnaht eine hohe Härte auf, die die Schwingrissbildung verzögern kann, allerdings auch zu einer niedrigen Kerbschlagarbeit führt.
Im ersten Teil dieses Beitrages werden grundlegende Untersuchungen zur schweißtechnischen Verarbeitung eines LTT-Zusatzwerkstoffes präsentiert. Dies beinhaltet zunächst die Sicherstellung der Schweißbarkeit sowie die Charakterisierung der Schweißgefüge und deren Härte mit dem Ziel, reproduzierbare Verbindungseigenschaften für die nachfolgende Schwingfestigkeitsprüfung herzustellen.
Der zweite Teil des Beitrages beschäftigt sich mit den dazugehörigen Schwingfestigkeitsuntersuchungen an den Stählen S355J2 und S960Q unter Verwendung konventioneller Zusatzwerkstoffe im Vergleich zum LTT-Zusatz. Das verwendete Schweißdetail ist eine Verbindungsschweißung am Stumpfstoß unter Variation der Schweißnahtausführung (DY-Naht und V-Naht). Weitergehend wird eine bauteilähnliche Probe (die Längssteife) untersucht, bei der der LTT-Zusatzwerkstoff als zusätzliche Schweißlage aufgebracht wurde. Neben der Schwingfestigkeit werden die Schweißnähte hinsichtlich der Eigenspannungen, der Eigenspannungsstabilität im Schwingversuch sowie metallo-grafisch charakterisiert. Die Ergebnisse zeigen, dass LTT-Zusatzwerkstoffe unter Einhaltung wesentlicher Konstruktionsrichtlinien zu einem deutlichen Anstieg der Schwingfestigkeit führen. Dadurch kann das Leichtbaupotential hochfester Stahlgüten genutzt werden.
Submerged arc welded (SAW) components of creep-resistant low-alloyed Cr-Mo-V steels are used for thick-walled heavy petrochemical reactors (wall-thickness up to 475 mm) as well as employed in construction of modern high-efficient fossil fired power plants. These large components are accompanied by significant restraints during welding fabrication, especially at positions of different thicknesses like welding of nozzles. As a result, residual stresses occur, playing a dominant role concerning so-called stress relief cracking (SRC) typically during post weld heat treatment (PWHT). Besides specific metallurgical factors (like secondary hardening due to reprecipitation), high tensile residual stresses are a considerable influence factor on SRC.
For the assessment of SRC susceptibility of certain materials mostly mechanical tests are applied which are isolated from the welding process. Conclusions regarding the influence of mechanical factors are rare so far. The present research follows an approach to reproduce loads, which occur during welding of real thick-walled components scaled to laboratory conditions by using Tests designed on different measures. A large-scale slit specimen giving a high restraint in 3 dimensions by high stiffness was compared to a medium-scale multi-pass welding U-Profile specimen showing a high degree of restraint in longitudinal direction and a small-scale TIG-remelted specimen. The small-scale specimens were additionally subjected to mechanical bending to induce loads that are found during fabrication on the real-scale in heavy components. Results show for all three cases comparable high tensile residual stresses up to yield strength with high gradients in the weld metal and the heat affected zone. Those high tensile stresses can be significant for cracking during further PWHT.
Additive Manufacturing (AM) through the Selective Laser Melting (SLM) route offers ample scope for producing geometrically complex parts compared to the conventional subtractive manufacturing strategies. Nevertheless, the residual stresses which develop during the fabrication can limit application of the SLM components by reducing the load bearing capacity and by inducing unwanted distortion, depending on the boundary conditions specified during manufacturing.
The present study aims at characterizing the residual stress states in the SLM parts using different diffraction methods. The material used is the nickel based superalloy Inconel 718. Microstructure as well as the surface and bulk residual stresses were characterized. For the residual stress analysis, X-ray, synchrotron and neutron diffraction methods were used. The measurements were performed at BAM, at the EDDI beamline of -BESSY II synchrotron- and the E3 line -BER II neutron reactor- of the Helmholtz-Zentrum für Materialien und Energie (HZB) Berlin.
The results reveal significant differences in the residual stress states for the different characterization techniques employed, which indicates a dependence of the residual state on the penetration depth in the sample. For the surface residual stresses, longitudinal and transverse stress components from both X-ray and synchrotron agree well and the obtained values were around the yield strength of the material. Furthermore, synchrotron mapping disclosed gradients along the width and length of the sample for the longitudinal and transverse stress components. On the other hand, lower residual stresses were found in the bulk of the material measured using neutron diffraction. The longitudinal component was tensile and decreased towards the boundary of the sample. In contrast, the normal component was nearly constant and compressive in nature. The transversal component was almost negligible. The results indicate that a stress re-distribution takes place during the deposition of the consecutive layers. Further investigations are planned to study the phenomenon in detail.
Additive Manufacturing (AM) through the Selective Laser Melting (SLM) route offers ample scope for producing geometrically complex parts compared to the conventional subtractive manufacturing strategies. Nevertheless, the residual stresses which develop during the fabrication can limit application of the SLM components by reducing the load bearing capacity and by inducing unwanted distortion, depending on the boundary conditions specified during manufacturing. The present study aims at characterizing the residual stress states in the SLM parts using different diffraction methods. The material used is the nickel based superalloy Inconel 718. Microstructure as well as the surface and bulk residual stresses were characterized.
For the residual stress analysis, X-ray, synchrotron and neutron diffraction methods were used. The measurements were performed at BAM, at the EDDI beamline of -BESSY II synchrotronand the E3 line -BER II neutron reactor- of the Helmholtz-Zentrum für Materialien und Energie (HZB) Berlin. The results reveal significant differences in the residual stress states for the different characterization techniques employed, which indicates the dependence of the residual state on the penetration depth in the sample. For the surface residual stresses, longitudinal and transverse stress components from X-ray and synchrotron agree well and the obtained values were around the yield strength of the material. Furthermore, synchrotron mapping disclosed gradients along the width and length of the sample for the longitudinal and transverse stress components. On the other hand, lower residual stresses were found in the bulk of the material measured using neutron diffraction. The longitudinal component was tensile and decreased towards the boundary of the sample. In contrast, the normal component was nearly constant and compressive in nature. The transversal component was almost negligible. The results indicate that a stress re-distribution takes place during the deposition of the consecutive layers. Further investigations are planned to study the phenomenon in detail.
Additive Manufacturing (AM) through the Selective Laser Melting (SLM) route offers ample scope for producing geometrically complex parts compared to the conventional subtractive manufacturing strategies. Nevertheless, the residual stresses which develop during the fabrication can limit application of the SLM components by reducing the load bearing capacity and by inducing unwanted distortion, depending on the boundary conditions specified during manufacturing. The present study aims at characterizing the residual stress states in the SLM parts using different diffraction methods. The material used is the nickel based superalloy Inconel 718. Microstructure as well as the surface and bulk residual stresses were characterized. For the residual stress analysis, X-ray, synchrotron and neutron diffraction methods were used. The measurements were performed at BAM, at the EDDI beamline of -BESSY II synchrotronand the E3 line -BER II neutron reactor- of the Helmholtz-Zentrum für Materialien und Energie (HZB) Berlin. The results reveal significant differences in the residual stress states for the different characterization techniques employed, which indicates the dependence of the residual state on the penetration depth in the sample. For the surface residual stresses, longitudinal and transverse stress components from X-ray and synchrotron agree well and the obtained values were around the yield strength of the material. Furthermore, synchrotron mapping disclosed gradients along the width and length of the sample for the longitudinal and transverse stress components. On the other hand, lower residual stresses were found in the bulk of the material measured using neutron diffraction. The longitudinal component was tensile and decreased towards the boundary of the sample. In contrast, the normal component was nearly constant and compressive in nature. The transversal component was almost negligible. The results indicate that a stress re-distribution takes place during the deposition of the consecutive layers. Further investigations are planned to study the phenomenon in detail.
Die Verwendung von LTT-Zusatzwerkstoffen stellt einen alternativen Ansatz zu den sonst üblichen Verfahren der Schweißnahtnachbehandlung zur Schwingfestigkeitserhöhung geschweißter Stahlkonstruktionen dar. Der wesentliche Wirkmechanismus beruht auf der Beeinflussung des Eigenspannungszustands durch die niedrige Martensitstarttemperatur bereits während des Schweißens. Dadurch werden die Druckeigenspannungen aus der behinderten Volumenausdehnung infolge Phasenumwandlung voll wirksam. Weiter weist die Schweißnaht eine hohe Härte auf, die die Schwingrissbildung verzögern kann, allerdings auch zu einer niedrigen Kerbschlagarbeit führt.
Im ersten Teil dieses Beitrages werden grundlegende Untersuchungen zur schweißtechnischen Verarbeitung eines LTT-Zusatzwerkstoffes präsentiert. Dies beinhaltet zunächst die Sicherstellung der Schweißbarkeit sowie die Charakterisierung der Schweißgefüge und deren Härte mit dem Ziel, reproduzierbare Verbindungseigenschaften für die nachfolgende Schwingfestigkeitsprüfung herzustellen. Der zweite Teil des Beitrages beschäftigt sich mit den dazugehörigen Schwingfestigkeitsuntersuchungen an den Stählen S355J2 und S960Q unter Verwendung konventioneller Zusatzwerkstoffe im Vergleich zum LTT-Zusatz.
Das verwendete Schweißdetail ist eine Verbindungsschweißung am Stumpfstoß unter Variation der Schweißnahtausführung (DY-Naht und V-Naht). Weitergehend wird eine bauteilähnliche Probe (die Längssteife) untersucht, bei der der LTT-Zusatzwerkstoff als zusätzliche Schweißlage aufgebracht wurde. Neben der Schwingfestigkeit werden die Schweißnähte hinsichtlich der Eigenspannungen, der Eigenspannungsstabilität im Schwingversuch sowie metallografisch charakterisiert. Die Ergebnisse zeigen, dass LTT-Zusatzwerkstoffe unter Einhaltung wesentlicher Konstruktionsrichtlinien zu einem deutlichen Anstieg der Schwingfestigkeit führen. Dadurch kann das Leichtbaupotential hochfester Stahlgüten genutzt werden.
Residual stresses are crucial when assessing the performance of welded components. The present work deals with the possibilities of transferring the real-life boundary conditions of welding, which influence the residual stress, into the laboratory. The possibilities of a test system specifically developed for this purpose with a maximum capacity of 2 MN are shown. Due to the structural design, global process, geometry and material-dependent stresses are induced, which can be simulated and quantified within the system. Additionally, X-ray diffraction can be applied to determine the resulting local residual stress distribution precisely with high spatial resolution. Two examples are presented how the conditions to be found during production are simulated in the laboratory. It is shown how welding residual stresses in high-strength steels are affected by the heat control. It was possible to clarify why elevated working temperatures significantly increase the bending stresses in the welded joint and therefore the tensile residual stresses in the heat affected zone (HAZ). The effect of a heat treatment applied under mechanical stress resulting from welding is demonstrated by the example of a creep resistant steel. Reheat cracking is significantly increased in this case compared to small scale laboratory based tests.
Residual stresses are crucial when assessing the performance of welded components. The present work deals with the possibilities of transferring the real-life boundary conditions of welding, which influence the residual stress, into the laboratory. The possibilities of a test system specifically developed for this purpose with a maximum load capacity of 2 MN are shown. Due to the structural design, global process, geometry and material-dependent stresses are induced, which can be simulated and quantified within the system. Additionally, X-ray diffraction can be applied to determine the resulting local residual stress distribution precisely with high spatial resolution. Examples are presented how the conditions to be found during production are simulated in the laboratory. It is shown how welding residual stresses in high-strength steels are affected by the heat control. It was possible to clarify why elevated working temperatures significantly increase the tensile residual stresses in the heat affected zone (HAZ). The effect of a heat treatment applied under mechanical stress resulting from welding is demonstrated by the example of a creep resistant steel. Reheat cracking is significantly increased in this case compared to small scale laboratory based tests.
The influence of the support structure on residual stress and distortion in SLM Inconel 718 parts
(2018)
The effect of support structure and of removal from the base plate on the residual stress state in selective laser melted IN718 parts was studied by means of synchrotron X-ray diffraction. The residual stresses in subsurface region of two elongated prisms in as-built condition and after removal from the base plate were determined. One sample was directly built on a base plate and another one on a support structure. Also, the distortion on the top surface due to stress release was measured by contact profilometry. High tensile residual stress values were found, with pronounced stress gradient along the hatching direction. In the sample on support, stress redistribution took place after removal from the base plate, as opposed to simple stress relaxation for the sample without support. The sample on support structure showed larger distortion compared to sample without support. We conclude that the use of a support decreases stress values but stress-relieving heat treatments are still needed.
Influence of support configurations on the characteristics of selective laser-melted Inconel 718
(2018)
Samples fabricated using two different support configurations by following identical scan strategies during selective laser melting of superalloy Inconel 718 were characterized in this study. Characterization methods included optical microscopy, electron back-scattered diffraction and x-ray diffraction residual stress measurement. For the scan strategy considered, microstructure and residual stress development in the samples were influenced by the support structures. However, crystallographic texture intensity and the texture components formed within the core part of the samples were almost independent of the support. The formation of finer grains closer to the support as well as within the columnar grain boundaries resulted in randomization and texture intensity reduction by nearly half for the sample built on a lattice support. Heat transfer rates dictated by the support configurations in addition to the scan strategy influenced the microstructure and residual stress development in selective laser-melted Inconel 718 samples.
Submerged arc welded (SAW) components of creep-resistant low-alloyed Cr-Mo-V steels are used for thick-walled heavy petrochemical reactors (wall-thickness up to 475 mm) as well as employed in construction of modern high-efficient fossil fired power plants. These large components are accompanied by significant restraints during welding fabrication, especially at positions of different thicknesses like welding of nozzles. As a result, residual stresses occur, playing a domi-nant role concerning so-called stress relief cracking (SRC) typically during post weld heat treat-ment (PWHT). Besides specific metallurgical factors (like secondary hardening due to re-precipitation), high tensile residual stresses are a considerable influence factor on SRC. For the assessment of SRC susceptibility of certain materials mostly mechanical tests are applied which are isolated from the welding process. Conclusions regarding the influence of mechanical factors are rare so far. The present research follows an approach to reproduce loads, which occur during welding of real thick-walled components scaled to laboratory conditions by using tests designed on different measures. A large-scale slit specimen giving a high restraint in 3 dimensions by high stiffness was compared to a medium-scale multi-pass welding U-profile specimen showing a high degree of restraint in longitudinal direction and a small-scale TIG-re-melted specimen. The small-scale specimens were additionally subjected to mechanical bending to induce loads that are found during fabrication on the real-scale in heavy components. Results show for all three cases compa-rable high tensile residual stresses up to yield strength with high gradients in the weld metal and the heat affected zone. Those high tensile stresses can be significant for cracking during further PWHT.
The performance and safety of welded high-strength low-alloyed steel (HSLA) components are substantially affected by the stresses occurring during and after welding fabrication, especially if welding shrinkage and distortion are severely restrained. The surrounding structure of the whole component affects loads in the far-field superimposing with welding stresses in the near-field of the weld. In this study a unique testing facility was used to restrain shrinkage and bending while analyse multiaxial far-field loads (max. 2 MN) during assembly of thick-walled component. A novel approach for the assessment of the in-situ-measured far-field data in combination with the actual weld geometry was elaborated. For the first time, analyses of the global bending moments of restrained welds based on the neutral axis of the actual weld load bearing section were achieved. Hence, far-field measurements offered the possibility to determine critical near-field stresses of the weld crosssections for the entire joining process. This work presents the approach for far-to-near field in-situ determination of stresses in detail for the 2-MN-testing system based on an extensive experimental work on HSLA steel welds, which demonstrates sources and consequences of these high local welding stresses. Thus, it was clarified, why the first weld beads are crucial regarding welding stresses and cold cracking, which is well known, but has never been measured so far. Accompanying analyses using X-ray diffraction (XRD) after welding show effects on local residual stress distributions. These analyses indicated viable prospects for stress reduction during assembly of thick-walled HSLA steel components.
In an increasing number of modern steel applications, high-strength structural steel grades are demanded to meet specifications regarding a high load-bearing capacity and a low operating weight. Lightweight design rules enhance the safety requirements, especially for welded joints. Besides a higher cracking risk for high-strength steel welds, the formation of tensile residual stresses might lead to fracture due to overloading or premature failure if not adequately considered. In this study, a stress-strain analysis was conducted at component-related structures from S960QL using digital image correlation while preheating, welding and cooling adjacent to the weld seam. X-ray diffraction analysis of the local residual stresses in the weld seam showed a good comparability with global analyses using either a DIC system or a special testing facility, which allowed in situ measurements of welding loads. By analysing two different seam geometries, it could be shown that lower multi-axial stresses arise if a narrower weld groove is used. Comparative analyses revealed a direct correlation of the local residual stresses in the weld with transverse shrinkage restraint, whereas the residual stress level in the HAZ is significantly affected by the bending restraint of the weld construction and the occurring bending stresses, respectively.
Today, an expanding application of high-strength steels in modern welded constructions can be observed. The economical use of these steel grades largely depends on the strength and reliability of the weldments. Therefore, the special microstructure and mechanical properties of these grades have to be taken into account by keener working ranges regarding the welding parameters.
However, performance and safety of welded components are strongly affected by the stresses occurring during and after welding fabrication locally in the weld seam and globally in the whole component, especially if the shrinkage and distortion due to welding are restrained. Some extensive studies describe the optimization of the welding stresses and the metallurgical effects regarding an adapted welding heat control. Lower working temperatures revealed to be particularly effective to reduce the local and global welding-induced residual stresses of the complete weld significantly. However, decreased interpass temperatures cause concurrently higher stresses during welding fabrication. This work shows strategies to reduce these in-process stresses.
With help of multi-axial welding stress analyses in component-related weld tests, using a special 2-MN-testing facility, differences in stress build-up are described in detail for root welds, filler layers and subsequent cooling to ambient temperature.
The residual stress distribution in IN718 elongated prisms produced by Selective Laser Melting was studied by means of neutron (bulk) and laboratory X-ray (surface) diffraction.
Two deposition hatch lengths were considered. A horizontal plane near the top surface (perpendicular to the building direction) and a vertical plane near the lateral surface (parallel to the building direction) were investigated. Samples both in as-built (AB) condition and removed (RE) from the base plate were characterized.
While surface stress fields seem constant for AB condition, X-ray diffraction shows stress gradients along the hatch direction in the RE condition. The stress profiles correlate with the distortion maps obtained by tactile probe measurements.
Neutron diffraction shows bulk stress gradients for all principal components along the main sample directions. We correlate the observed stress patterns with the hatch length, i.e. with its effect on temperature gradients and heat flow. The bulk stress gradients partially disappear after removal from the baseplate.
Additive Manufacturing (AM) of metals has become industrially viable for a large variety of applications, including aerospace, automotive and medicine. Powder bed techniques such as Selective Laser Melting (SLM) based on layer-by-layer deposition and laser melt enable numerous degrees of freedom for the geometrical design. Developing during the manufacturing process, residual stresses may limit the application of SLM parts by reducing the load bearing capacity as well as induce unwanted distortion depending on the boundary conditions specified in manufacturing.
The residual stress distribution in the bulk of IN718 elongated prisms produced by SLM was studied non-destructively by means of neutron diffraction. The samples with different scanning strategies, i.e. hatching length, were measured in as-build condition (on a build plate) and after removal from the build plate.
The absolute values of all stress components decreased after removal from the build plate. Together with surface scan utilizing a coordinate-measuring machine (CMM), it is possible to link the stress release to the sample distortion. Obtained results indicated different residual stress states for each of the transversal, longitudinal and normal component depending on the thermal gradient in the respective direction.