Ingenieurwissenschaften und zugeordnete Tätigkeiten
Filtern
Erscheinungsjahr
- 2018 (230) (entfernen)
Dokumenttyp
- Vortrag (99)
- Zeitschriftenartikel (76)
- Beitrag zu einem Tagungsband (38)
- Posterpräsentation (13)
- Buchkapitel (1)
- Dissertation (1)
- Handbuch (1)
- Forschungsbericht (1)
Schlagworte
- Hydrogen (19)
- Niobium carbide (18)
- Friction (17)
- Wear (17)
- Welding (17)
- Additive manufacturing (16)
- Residual stress (12)
- NbC (11)
- Eigenspannungen (10)
- MAG-Schweißen (10)
Organisationseinheit der BAM
- 9 Komponentensicherheit (230) (entfernen)
Eingeladener Vortrag
- nein (99)
Hybrid laser-arc welding of thick-walled ferromagnetic steels with electromagnetic weld pool support
(2018)
The hybrid laser-arc welding (HLAW) process provides many advantages over laser welding and arc welding alone, such as high welding speed, gap bridgeability, and deep penetration. The developments in hybrid laser-arc welding technology using modern high-power lasers allow single-pass welding of thick materials. This technology can be used for the heavy metal industries such as shipbuilding, power plant fabrication, and line-pipe manufacturing. The obvious problem for single-pass welding is the growth of the hydrostatic pressure with increasing thickness of materials leading to drop-out of molten metal. This phenomenon is aggravated at slow welding velocities because of increasing weld seam width followed by a decrease of Laplace pressure compensating the hydrostatic pressure. Therefore, weld pool support is necessary by welding of thick materials with slow welding velocities. The innovative electromagnetic weld pool support system is contactless and has been used successfully for laser beam welding of aluminum alloys and austenitic and ferromagnetic steels. The support system is based on generating Lorentz forces within the weld pool. These are produced by an oscillating magnetic field orientated perpendicular to the welding direction. The electromagnetic weld pool support facilitates a decrease in the welding speed without a sagging and drop-out of the melt thus eliminating the limitations of weldable material thickness.
The hybrid laser arc welding (HLAW) process provides many advantages such as improved gap bridgeability, deep penetration and misalignment of edges, that is why the process is used increasingly in industrial applications e.g. shipbuilding, power plant industry and line-pipe manufacturing. The obvious encountered problem for single pass welding in flat position is the gravity drop-out at low welding velocities. With the usage of an electromagnetic weld pool support system, which is based on generating Lorentz forces within the weld pool, wide seams followed by reduced welding velocities could be achieved in this study leading to the realization of a gap bridgeability up to 1 mm, misalignment of edges up to 2 mm and a single pass weld up to 28 mm thickness with a 20-kW fibre laser. These developments expand the boundaries of the HLAW process for different industrial applications. As a result, less accurate preparation of the edges would be sufficient, which saves time for manufacturing.
The laser hybrid welding process offers many advantages regarding deep penetration, increased welding velocity and with the help of the supplied filler wire an improved bridgeability to gap and misalignment tolerances. High power laser systems with a power of approx. 30 kW are already available on the market. Nevertheless, multi-layer technology with an arc process is still used for welding of plates from a thickness from 20 mm. A potential cause is the process instability with increasing laser power. It is inevitable that gravity drop-out due to the high hydrostatic pressure at increasing wall thickness especially at welding in flat position and with a low welding speed. The surface tension decreases with increasing root width resulting from low welding velocities. To prevent such inadmissible defects of the seam a use of weld pool support is required. Usual weld pool support systems such as ceramic or powder supports require a mechanical detachment which is time-consuming. The electromagnetic weld pool support system described in this work shows an alternative weld pool support which works contactless. It is based on generating Lorentz forces in the weld pool due to oscillating magnetic field and induced eddy currents. This innovative technology offers single pass welds up to 28 mm in flat position and reduced welding velocity with a laser power of just 19 kW. It also leads to improved mechanical-technological properties of the seams because of the slow cooling rate. With usage of an electromagnetic weld pool support the limitation of the hybrid laser arc welding process in the thick sheet metal will be extend.
Three high-strength Nb-,.Ti- and Ti+ V-bearing S690QL steels were welded to investigate and compare the effects of microalloy addition on heat-affected zone (HAZ) toughness. Charpy V notch impact tests from three microalloyed welds under different cooling rates have been performed. Fractographic examination shows that several factors, including large-sized grain, upper bainite or hard second phase, interact to determine brittle fracture and impaired toughness in Nb-bearing weld with high heat input. In contrast to this reduced toughness, Ti-bearing welds exhibits satisfied toughness regardless of at fast or slow cooling. This is attributed to its limited austenite grain and refines favorable intragranular acicular ferrite structure. Moreover, in the case of such refined structure as matrix, TiN particles are found to be irrelevant to the facture process. The crystallographic results also confirm that high-angle boundaries between fine ferrites plates provide effective barriers for crack propagation and contribute to improved toughness.
Common fracture mechanics based fatigue considerations are usually limited to the residual lifetime determination of so-called long cracks. The extension of this concept to the total lifetime, as in the S-N curve approach, requires an adequate description of short crack propagation which cannot be based on the Delta K concept, and it must consider the crack closure phenomenon as well as its gradual build-up at the short crack stage. Further, it has to provide a meaningful definition of initial crack dimensions and a solution for the multiple crack problem at stress levels higher than the fatigue limit as it is specific for some configurations such as weldments. This paper aims at a discussion of all these points and offers possible solutions which are illustrated by examples taken from the German IBESS project on fracture mechanics based determination of the fatigue strength of weldments, the results of which will be discussed in more detail in this Special issue.
The cyclic J-integral (∆J-integral) is a crack tip parameter of elastic-plastic fracture mechanics which can be used as governing parameter for the description of fatigue crack growth (FCG) in metallic structures. In this contribution, it is applied for modelling FCG in weldments. The ∆J-integral is determined by means of analytical approximation formulas as well as numerical methods. An analytical solution, which takes into account effects of the local ligament plasticity, was derived. This solution is based on well established methods such as R6, BS7910 and SINTAP which were modified for cyclic loading. It incorporates methods for the description of short crack closure behaviour as well as the well known analytical (long) crack closure function of Newman. A specific code was written to evaluate the ∆J-integral numerically in the course of finite element based crack growth simulations. The code was first validated for an infinite plate with centre crack by applying elastic and elastic-plastic material behaviour. Next, the ∆J-integral was calculated for cracks in various butt and cruciform welded joints. The results were compared with the results of the derived analytical approximation formula. A good accordance was achieved between the results.
The paper provides an application of the IBESS approach to the investigation of the influence of various parameters of the global and local weld geometry as well as material defects on the fatigue strength of weldments. For this purpose, the global weld parameters, such as the weld toe radius, the flank angle, the excess weld metal, local secondary notches (in the present study as a measure of surface imperfections) and inclusions sizes have been determined as statistical distributions for different joint types and geometries and two steels of different strengths. The results are in line with literature data and reveal the potential of the theoretical approach to predict the correct trends. The combination with an advanced weld quality system has been demonstrated to be possible.
The so-called cyclic R curve, i.e. the crack size dependence of the fatigue crack propagation threshold in the physically short crack regime, is a key parameter for bringing together fatigue strength and fracture mechanics concepts. Its adequate determination is of paramount importance. However, notwithstanding this relevance, no test guideline is available by now and only very few institutions have spent research effort on cyclic R curves so far. The aim of the present paper is to give an overview on the state-of-the-art. Besides an introduction into the basic principles, the discussion will concentrate on the experimental determination on the one hand and questions of its application on the other hand.
Any fracture mechanics based determination of the fatigue strength of weldments requires different input information such as the local weld geometry and material data of the areas the crack is passing through during its propagation. The latter is so far not a trivial task as the fatigue crack is usually initiated at the weld toe at the transition from the weld metal to the heat affected zone and it subsequently propagates through the different microstructures of the latter to eventually grow into the base material and to cause final fracture. This paper describes how the material input information has gained particularly for heat affected zone material by thermo-mechanically simulated material specimens for two steels of quite different static strength. The data comprise the cyclic stress-strain curve, the crack closure effect-corrected crack growth characteristics, long crack fatigue crack propagation thresholds, the dependency of the parameter on the crack length and monotonic fracture resistance. The substantial experimental effort was necessary for the validation exercises of the IBESS approach, however, within the scope of practical application more easily applicable estimating methods are required. For that purpose the paper provides a number of appropriate proposals in line with its check against the reference data from the elaborate analyses.
Analytical flaw assessment
(2018)
The paper provides a review on analytical flaw assessment methods with the focus on fracture under monotonic loading and fatigue crack propagation. The first topic comprises linear elastic as well as elastic-plastic fracture mechanics approaches. It essentially follows their historical development. Topics which are separately discussed are reference/Limit loads, the treatment of secondary stresses, strength mismatch, constraint, unstable crack propagation (monotonic R-curve analyses) and statistical aspects. With respect to fatigue crack propagation the analytical treatment of crack closure and constraint and the Determination of the cyclic elastic-plastic crack driving force is discussed. Finally, cyclic Rcurve analyses are briefly addressed.
Welding residual stresses have an impact on the performance of welded structures, on their fracture resistance, their resistance against fatigue crack propagation and, most important, their fatigue strength and fatigue lifetime. The present paper provides an overview on the issue mainly from the point of view of the application of fracture mechanics to the determination of the fatigue strength as the topic of this Special issue. Besides own experimental and theoretical data a comprehensive discussion is provided in that context which includes the definition and interaction of short- and long-range (or reaction) residual stresses, the effect of cyclic mechanical loading and its treatment in fracture and fatigue analyses.
Foreword
(2018)
The subject of this Special Issue is the fracture mechanics-based determination of the fatigue strength of weldments. Except for one, all papers were written in closer or wider relation to a methodology developed within the framework of the German Project cluster IBESS. Some of them provide background or supplementary information needed in that context but which is also relevant in a wider frame of research activities. The acronym IBESS stands for the topic of this Special Issue (in German: „Integrale Methode zu Bruchmechanischen Ermittlung der Schwingfestigkeit von Schweißverbindungen). Eight partners were involved. The cluster was cooperatively founded by the German Research Foundation (Deutsche Forschungsgemeinschaft) and by the German AiF Network (Arbeitsgemeinschaft industrieller Forschungsvereinigungen) for industrial research.
Ein Defekt ist „eine Imperfektion …, für die in einer quantitativen Analyse gezeigt werden kann, dass sie Versagen verursacht hat, welches ohne die Imperfektion nicht aufgetreten wäre“. Defekte in diesem Sinn können einerseits Werkstoffimperfektionen wie nichtmetallische Einschlüsse, Poren und Porennester, Nichtdurchschweißungen oder Bereiche defekter Mikrostruktur, andererseits unbeabsichtige geometrische Imperfektionen wie Kratzer, Eindrücke, Korrosionsgrübchen, Einbrandkerben, zu große Oberflächenrauheit u.a. sein. Sie können in der Fertigung, im Betrieb oder auch bei der Wartung entstehen. Nicht jede Imperfektion ist ein Defekt im oben genannten Sinn. Entscheidend ist zumeist nicht, dass an ihr ein oder mehrere Risse initiiert werden, sondern dass wenigstens ein Riss wachstumsfähig bleibt und so innerhalb der projektierten Lebensdauer zum Bruch oder anderweitigem Versagen führt. Aufgrund des begrenzten Umfangs bleibt die vorliegen-de Übersicht beschränkt.
Unter der zyklischen R-Kurve versteht man die Abhängigkeit des Schwellenwertes gegen Ermüdungsrissausbreitung von der Risstiefe im Kurzrissbereich. Bei Spannungsverhältnissen R = omin/omax < ca. 0,7 erhöht sich der Schwellenwert AKltl ausgehend von einer intrinsischen, werkstoffspezifischen Untergrenze mit zunehmender Risstiefe, bis er einen risslängenunabhängigen Wert erreicht.
Ursache ist der graduelle Aufbau unterschiedlicher Rissschließeffekte. Die besondere Bedeutung des Kurzrisswachtums allgemein und der zyklischen R-Kurve speziell besteht darin, dass sie ein physikalisches Bindeglied zwischen der konventionellen Schwingfestigkeit (Wöhlerkurve) und der Bruchmechanik repräsentieren. Der Beitrag befasst sich sowohl mit der experimentellen Ermittlung der zyklischen R-Kurve als auch mit ihrer Anwendung auf Rissarrest im Zusammenhang mit Schwingfestigkeitsbetrachtungen.
Die experimentelle Ermittlung der zyklischen R-Kurve erfordert einen experimentellen Aufwand, der deutlich über den der Langrissbruchmechanik hinausgeht. Insbesondere im Anfangsbereich ist eine sehr genaue Messung der Risstiefe erforderlich, was eine Verbesserung etwa der konventionellen Potentialmethode erforderlich macht. Von wesentlicher Bedeutung ist auch, dass der Ausgangsriss vor
Beginn des eigentlichen Versuchs keine Rissschließeffekte gesehen haben darf. Realisiert wird das durch eine vorgeschaltete Phase von sog. „Compression Pre-cracking“, d.h. durch Anschwingen komplett im Druckbereich.
Die Präsentation diskutiert Besonderheiten von Schweißnähten bei der Bestimmung der Zähigkeit bei monotoner Belastung, bei der Ermittlung des zyklischen Rissfortschritts und bei der Ermittlung der Gesamtlebensdauer/Schwingfestigkeit mittels moderner bruchmechanischer Methoden. Besonderes Augenmerk liegt auf der Inhomogenität des Werkstoffs in den einzelnen Nahtbereichen, die sich statistisch (stochastische Verteilung von Gefügeschwachstellen) und systematisch (Effekte von Festigkeits-Mismatch) auswirkt. Als weiterer Faktor kommen Schweißeigenspannungen hinzu, bei denen für die bruchmechanische Analyse eine Fallunterscheidung in primäre und sekundäre Eigenspannungen vorgenommen werden muss. Diskstiert werden die Konsequenzen für die Zähigkeitsermittlung und die Bauteilbewertung.
The Topic of the presentationis a discussion on defects which can cause failure in cyclically loaded metallic components. Although also touching Features such as material defects such as pores or micro-shrinkages, etc. and geometric defects such as surface roughness and secondary notches (which are not considered in the design process) which origin in manufacturing, and others the presentation concentrates on non-metallic inclusions. It is prefaced by an introduction to the life cycle of a fatigue crack from initiation up to fracture. Special emphasis is put on the fact that only cracks which are not arrested during one of their distinct Propagation stages can grow to a critical size.
Niobium carbide is a ceramic material which can be used with excellent results to replace tungsten carbide with cobalt binder. Furthermore, it might be manufactured by classic ceramic technologies and even colloidal processing. To achieve high toughness and strength, it is necessary to have a perfect mix of hard phase and binder, which is mainly achieved by ball milling. Mechanical and physical properties as well as results on different tribological and application-oriented machining tests are presented. The results have been compared with results obtained with NbC grades with Co and Fe3Al binders as well as with pure binderless hot-pressed NbC and SPS sintered Nb2O5.
The wear rates of self-mated alumina couples show that friction as well as wear is largely determined by the above-mentioned hydro-thermal conditions. The presence of water and its amount available in the surrounding system either in liquid or in gaseous form plays a key role for friction and wear behavior and can be beneficial for the tribological profile of steam degradation resistant materials. Hot steam enhances the tribo-chemical formations of oxides and hydroxides on MgO-ZrO2 alumina and antimony impregnated carbon.
Research and development of WC grades is 90 years ahead of niobium carbide-based hard materials, which showed already as light-weight and unexplored material a very high potential for many technical applications, especially for wear protection and machining. NbC evoluted recently from lab scale to pilot scale, especially in areas where established WC-based materials are causing economic, environmental or technical concerns. Benchmark trials of NbC-based hard metals indicated already a favorable performance in machining of steel components.
Metallurgy and Tribology offer different novel tools for meeting fuel economy targets.
Each of metallurgy, coatings, additives and base oils promote itself as exclusively blessed way to assure fuel economy. It is likely, that two, three or all generate the bigger fuel economy benefits and make the team working difficult for the OEM.
Metallurgy and Tribology enables the implementation of new technologies for waste heat recovery, like hot steam.
In consequence, multi-disciplinary co-engineering needs to be established. Finally, this is the most promising way, but people dislike changes.
Embargo and dual use regulations limits the global availability of thin films and also some alternative steels.
The present paper illuminates the metallurgical progress on niobium carbide based hard metal developments, which are characterized by: a.) the substitution of cobalt binder by nickel, b.) the change from SPS to conventional sintering and c.) by switching from lab to pilot scale. The toughness was increased in the frame of these developments without loosening the hardness level. The hardness-toughness profile of NbC grades match those of WC and cermet grades. Apart from the aforementioned parameters, the properties depend from the powder processing and sintering conditions.
The functional profile of nickel and NiMo bonded NbC versus cobalt bondedWC grades bonded by cobalt and nickel are benchmarked under dry sliding wear (T= 22/400°C; v= 0,1-10 m/s), abrasive wear (G65) and under dry turning and dry milling against different work piece alloys (C45E, 42CrMo4, 300WA, GG35, AlSi9Cu4Mg). The different elements explaining the wear resistance of NbC over WC will be illuminated.
The steam technology has attracted attention for recovering energy from waste heat in transportation systems. 40% of the calorific value of the fuel is wasted through the tailpipe. The use of waste heat recovery systems (WHRS) in cars and especially in trucks corresponds to possible energy savings in terms of less fuel consumption in the range of 7 – 18 %. This relates not only to the savings of fuel but also to the non-production of green house gas CO2. Steam expander form tribosystems, which can´t be lubricated with oils, as hot steam hydro-cracks these fluids. Suited tribomaterials as well as their tribo-oxidatively reaction layers must be first steam degradation resistant and for the tribotesting of such candidate material, tribological testing devices for a hot steam environment are needed. Not much is known so far about the tribological properties of any material system running under pressurized hot steam conditions. For these reasons and for being able to evaluate tribological properties in hot steam, BAM has developed and built a new and sealed tribometer for hot steam allowing evaluating tribological properties up to 700°C and 10 bars in gaseous atmospheres like hot steam or ethanol.
Experimental results on the wear of self-mated aluminum oxide and MgO-ZrO2 couples show that friction as well as wear is largely determined by the above mentioned hydro-thermal conditions. In this system the presence of water and its amount available in the system either in liquid or in gaseous form plays a key role for wear behavior and can beneficial. Ethanol and/or water-ethanol mixtures can form beneficial tribofilms, also on specific diamond-like carbon films.
The present paper illuminates the metallurgical progress on niobium carbide based hard metal developments, which are characterized by: a.) the substitution of cobalt binder by nickel, b.) the change from SPS to conventional sintering and c.) by switching from lab to pilot scale. The toughness was increased in the frame of these develop¬ments without loosening the hardness level. Stoichiometric and sub-stoichiometric, submicron NbC powders were used. The hardness-toughness profile of NbC grades match those of WC and cermet grades. Apart from the aforementioned parameters, the properties depend from the powder processing and sintering conditions. The functional profile of NbC and WC grades bonded by cobalt and nickel are benchmarked by 4-point bending strength, elastic moduli and hot hardness until 1000°C, dry sliding wear (T= 22/400°C; v= 0,1-10 m/s), abrasive wear (G65) and cutting performances under emulsion and coolant-free turning and milling against different alloys (C60, 100Cr6, 42CrMo4, X90CrMoV18, 300WA, GG35).
The present work deals with Niobcarbid (NbC). Strategic reflections on tungsten carbide and more and more stringent toxicological restrictions for cobalt associated for both with spiraling stock market prices have attracted recently some attention for Niobium carbide as a substitute for tungsten carbide in machining.
The present work deals with Niobcarbid (NbC). Strategic reflections on tungsten carbide and more and more stringent toxicological restrictions for cobalt associated for both with spiraling stock market prices have attracted recently some attention for Niobium carbide as a substitute for tungsten carbide in machining.
Metallsulfide werden den meisten Bremsbelägen als Reibungsstabilisatoren zugesetzt, obwohl die Auswirkungen auf die Bremsleistung sowie die Art und Weise, wie sie im dritten Körper wirken, wenig verstanden ist. Um zu untersuchen wie synergistische Effekte im Tribofilm das Reibverhalten bestimmen, wurde eine Stift-Scheibe-Anordnung mit Pulverzufuhr genutzt, welche einen künstlichen dritten Körper erzeugt. Die verwendeten Pulvermischungen wurden nach dem Bottom-up-Prinzip entwickelt: Beginnend mit Einstoffsystemen wird über Zweistoffsysteme aus Magnetit und Metallsulfid (Massenanteile: 85 % zu 15 %) zu Dreistoffsystemen aus Magnetit (85 %), Graphit (7,5 %) und Metallsulfid (7,5 %) entwickelt. Zusätzlich wurden ausgewählte ternäre Pulvermischungen mittels Hochenergie-Kugelmühle gemahlen, um Partikelgrößen im Nanometerbereich zu erhalten. Sämtliche Pulvermischungen wurden bei Raumtemperatur und bei 400 °C getestet, um die höheren Beanspruchungen während eines Bremsvorgangs zu simulieren. Des Weiteren wurde in oxidierender und nicht-oxidierender Atmosphäre getestet, um den Einfluss der Oxidbildung zu identifizieren. Die mittleren Reibungszahlen bei 400 °C und in Luft sind durchschnittlich höher als in Stickstoffatmosphäre, was der Bildung von Metalloxiden zugeordnet werden kann und durch thermische Analysen an den Pulvern bestätigt wird. Es zeigt sich, dass die Verwendung von nur einem Metallsulfid in einer Rezeptur für Bremsbeläge nicht ausreichend ist, um die Reibungszahl dieses Tribosystems unter verschiedenen Beanspruchungen zu stabilisieren. Ein stabileres Reibverhalten konnte erreicht werden, indem zwei verschiedene Festschmierstoffe als Reibungsstabilisatoren kombiniert wurden.
Two-dimensional residual stress mapping of multilayer LTT weld joints using the contour method
(2018)
Low transformation temperature (LTT) weld filler materials offer an attractive alternative to cost intensive postweld treatments as they can mitigate detrimental welding residual stresses during the welding process. Compared to conventional weld filler materials, LTT alloys are characterized by a delayed martensite transformation at low temperatures, which can result in compressive residual stresses in the weld. The high strength of these filler materials makes them potentially applicable to high-strength steels as well as for a large amount of requested repair works in steel structures. The focus of the study is on the confirmation of the LTT idea with regard to the residual stress state for multipass weld lines processed by metal active gas welding. It is demonstrated that the contour method is a well-suited technique for measuring the residual stress in the weld joint as it gives an entire two-dimensional map of the residual stress state in the weld line, heat affected zone (HAZ), and base material. The technique was applied at different LTT alloys with varying chemical compositions. Additionally, the results are compared to residual stress maps that were determined by Neutron diffraction using the Strain Analyzer for Large Scale Engineering Applications, an
instrument referred to as SALSA, at the Institut Laue-Langevin in Grenoble. For all investigated specimens, compressive residual stress distributions were determined in the area of the weld joint and the HAZ. They are balanced by tensile residual stresses in the surrounding base material. However, it is shown that the size of theregion exhibiting compressive residual stresses and the absolute values of the compressive residual stresses depend on the chemical composition of the weld filler material.
Investigations on weldability often deal with hot cracking as one of the most prevalent failure mechanisms during weld fabrication. The modified varestraint transvarestraint hot cracking test (MVT) is well known to assess the hot cracking susceptibility of materials. The shortcoming of this approach is that the information is only from the very near surface region which inhibits access to the characteristic of the hot crack network in the bulk. Here, we report about an alternative approach to monitor the entire 3D hot crack network after welding by means of microfocus X-ray computer tomography (µCT). However, to provide sufficient high spatial resolution small samples must be sectioned from the MVT-welded joint. The sampling is accompanied by local relaxation of the residual stress distributions that are induced by welding, which can have an impact on the crack volumes prior to the sampling. The studies were carried out to investigate the hot cracking susceptibility of low transformation temperature filler materials (LTT). As high compression residual stresses up to -600 MPa in the area of the crack networks were determined by means of the contour method, stress relaxation caused by sectioning for µCT sample extraction can affect the detectability of the cracks later on. X-ray diffraction studies revealed surface residual stress relaxations up to about 400 MPa due to cutting. To investigate this effect, the specimens with hot cracks were subjected to a load test with known stress states. The results clearly show that local stress relaxations will have a strong impact on the volume images reconstructed from tomography analysis. This effect must be considered during hot crack assessment on basis of µCT data.
Niobcarbid (NbC) stellt aufgrund vorteilhafter Eigenschaften, wie zum Beispiel eine geringe Diffusionsneigung, in der Zerspannung eine vielversprechende Alternative zu konventionellen Schneidstoffen wie Wolframcarbid (WC) dar. Als Substitution der Hartstoff-Phase WC im Hartmetall wird NbC in der trockenen Drehbearbeitung von eisen-basierten Werkstoffen untersucht. Diesbezüglich wurden zwei NbC-Substrate mit WC hinsichtlich ihres Werkzeugverschleißes quantitativ verglichen. Im Gegensatz zu WC-Werkzeugen wird das Potential von NbC bei zunehmender Schnittgeschwindigkeit vc durch eine steigende Prozessstabilität deutlich.
Die Verwendung von Low Transformation Temperature (LTT) Schweißzusatzwerkstoffen ist eine innovative Möglichkeit, um beim Schweißen von hochfesten Stählen die schweißbedingten Zugeigenspannungen zu reduzieren. Durch die Zugabe von Legierungselementen, wie beispielsweise Nickel oder Mangan haben diese Werkstoffe eine, im Vergleich zu herkömm-lichen Schweißzusatzwerkstoffen deutlich herabgesetzte Martensitstarttemperatur (MS). Dadurch ist es möglich, die schweißbedingten Zugeigenspannungen mit LTT-Schweißzusatz-werkstoffen gezielt zu reduzieren oder sogar Druckeigenspannungen zu erzeugen.
Im Verlauf vorangegangener Arbeiten hat sich herausgestellt, dass einige der untersuchten LTT-Legierungen aufgrund ihres Erstarrungs- bzw. Seigerungsverhaltens eine gegenüber vielen konventionellen Schweiß-zusatzwerkstoffen erhöhte Heißrisssensibilität aufweisen.
Die aktuellen Arbeiten zielen darauf, die Heißrissneigung neuartiger LTT-Schweißzusatzwerkstoffe weiter zu ergründen.
Additive Manufacturing (AM) of metals has become industrially viable for a large variety of applications, including aerospace, automotive and medicine. Powder bed techniques such as Selective Laser Melting (SLM) based on layer-by-layer deposition and laser melt enable numerous degrees of freedom for the geometrical design. Developing during the manufacturing process, residual stresses may limit the application of SLM parts by reducing the load bearing capacity as well as induce unwanted distortion depending on the boundary conditions specified in manufacturing.
The residual stress distribution in the bulk of IN718 elongated prisms produced by SLM was studied non-destructively by means of neutron diffraction. The samples with different scanning strategies, i.e. hatching length, were measured in as-build condition (on a build plate) and after removal from the build plate.
The absolute values of all stress components decreased after removal from the build plate. Together with surface scan utilizing a coordinate-measuring machine (CMM), it is possible to link the stress release to the sample distortion. Obtained results indicated different residual stress states for each of the transversal, longitudinal and normal component depending on the thermal gradient in the respective direction.
The residual stress distribution in IN718 elongated prisms produced by Selective Laser Melting was studied by means of neutron (bulk) and laboratory X-ray (surface) diffraction.
Two deposition hatch lengths were considered. A horizontal plane near the top surface (perpendicular to the building direction) and a vertical plane near the lateral surface (parallel to the building direction) were investigated. Samples both in as-built (AB) condition and removed (RE) from the base plate were characterized.
While surface stress fields seem constant for AB condition, X-ray diffraction shows stress gradients along the hatch direction in the RE condition. The stress profiles correlate with the distortion maps obtained by tactile probe measurements.
Neutron diffraction shows bulk stress gradients for all principal components along the main sample directions. We correlate the observed stress patterns with the hatch length, i.e. with its effect on temperature gradients and heat flow. The bulk stress gradients partially disappear after removal from the baseplate.