Ingenieurwissenschaften und zugeordnete Tätigkeiten
Filtern
Dokumenttyp
- Vortrag (282)
- Zeitschriftenartikel (119)
- Beitrag zu einem Tagungsband (50)
- Posterpräsentation (20)
- Forschungsbericht (5)
- Dissertation (4)
- Sonstiges (3)
- Monografie (2)
- Buchkapitel (2)
Sprache
- Englisch (308)
- Deutsch (176)
- Spanisch (2)
- Mehrsprachig (1)
Schlagworte
- Eigenspannungen (52)
- Welding (51)
- Additive Fertigung (50)
- Additive manufacturing (43)
- Additive Manufacturing (39)
- Residual stress (39)
- Wasserstoff (35)
- Hochfester Stahl (34)
- MAG-Schweißen (34)
- Ultraschallunterstütztes Fräsen (31)
- Residual stresses (29)
- Schweißen (29)
- Hydrogen (22)
- TIG welding (21)
- LIBS (20)
- Legierungsmodifikation (19)
- Residual Stress (19)
- Ultrasonic-assisted milling (19)
- High-strength steels (18)
- Wärmeführung (18)
- In situ measurement (17)
- Cyclic R-curve (15)
- Kaltrisssicherheit (15)
- Surface integrity (15)
- Alloy 36 (14)
- Oberflächenintegrität (14)
- AGIL (13)
- Duplex stainless steel (13)
- Fatigue (13)
- High-strength steel (13)
- Microstructure (13)
- Neutron diffraction (13)
- Fracture mechanics (12)
- Hochfester Feinkornbaustahl (12)
- Alloy modification (11)
- Creep-resistant steel (11)
- Reparatur (11)
- Stress relief cracking (11)
- Diffraction (10)
- Windenergie (10)
- 316L (9)
- Fatigue crack propagation threshold (9)
- Hochfeste Feinkornbaustähle (9)
- Restraint (9)
- X-ray diffraction (9)
- Implant-Test (8)
- Kaltriss (8)
- L-PBF (8)
- Post weld heat treatment (8)
- Werkzeugverschleiß (8)
- Fatigue crack growth (7)
- Fatigue strength (7)
- Heat control (7)
- Heat treatment (7)
- Hydrogen assisted cracking (7)
- Kaltrisse (7)
- Laser powder bed fusion (7)
- Mechanical properties (7)
- Residual Stresses (7)
- Schwingfestigkeit (7)
- Steel (7)
- Submerged arc welding (7)
- AM (6)
- AlSi10Mg (6)
- Carrier gas hot extraction (6)
- Chemical composition (6)
- Component assessment (6)
- Forschung (6)
- Fracture Mechanics (6)
- Fügetechnik (6)
- ISO 3690 (6)
- LTT (6)
- Laser Powder Bed Fusion (6)
- Pipeline (6)
- Process parameters (6)
- Turbine disk (6)
- UP-Schweißen (6)
- Austenitic stainless steels (5)
- Bruchmechanik (5)
- Crack closure (5)
- Digital image correlation (5)
- Erstarrungsriss (5)
- Fatigue crack propagation (5)
- Gefügedegradation (5)
- Heißriss (5)
- Hochfest (5)
- Hydrogen-assisted cracking (5)
- Kitagawa-Takahashi diagram (5)
- LIBS TIG welding (5)
- Large-scale test (5)
- Neutron imaging (5)
- Prüfverfahren (5)
- Repair-welding (5)
- Reparaturschweißen (5)
- Spannungsrelaxationsriss (5)
- Stainless Steel (5)
- Studie (5)
- WAAM (5)
- WRC 1992 diagram (5)
- Weldments (5)
- Wärmenachbehandlung (5)
- X-ray and Neutron Diffraction (5)
- Bauteilprüfung (4)
- Cold cracking (4)
- Cold cracking safety (4)
- Constraint (4)
- Defects (4)
- Diffusion (4)
- Evaporation (4)
- GMA welding (4)
- Heißrisse (4)
- High strength steel (4)
- High-strength structural steels (4)
- Hochentropielegierung (4)
- Intrinsischer Schwellenwert gegen Ermüdungsrissausbreitung (4)
- Kaltrissprüfung (4)
- MVT (4)
- Neutron Diffraction (4)
- Pipelines (4)
- Plasma-transferred arc welding (4)
- Research (4)
- Restlebensdauer (4)
- Schadenstolerante Bauteilauslegung (4)
- Solidification cracking (4)
- Synchrotron (4)
- Tool wear (4)
- Varestraint-Test (4)
- Wind energy (4)
- Zerspankräfte (4)
- Zyklische R-Kurve (4)
- AISI 316L (3)
- Burst (3)
- Component test (3)
- Computed tomography (3)
- Crack propagation (3)
- Cyclic R-Curve (3)
- DVS (3)
- Diffusible hydrogen (3)
- Dilatometry (3)
- Dissimilar metal weld (3)
- Duplex Stainless Steel (3)
- Eigenspannung (3)
- Endurance limit (3)
- Experimental procedure (3)
- FEM (3)
- Fatigue life (3)
- Fatigue limit (3)
- Feinkornbaustahl (3)
- Fortschrittsbericht (3)
- High-entropy alloy (3)
- High-strength Steels (3)
- Hot cracking (3)
- Hydrogen diffusion (3)
- IN718 (3)
- Implant test (3)
- Measurement (3)
- Mediumentropielegierung (3)
- Neutron radiography (3)
- Ni alloy (3)
- Offshore (3)
- Overspeed (3)
- Phase transformation (3)
- Plasma-Pulver-Auftragschweißen (3)
- Repair (3)
- Residual stress analysis (3)
- Rissarrest (3)
- Selective Laser Melting (3)
- Selective laser melting (3)
- Spannungsrelaxationsrisse (3)
- Structural integrity (3)
- TEKKEN (3)
- TEKKEN-Test (3)
- Thermisches Ausfugen (3)
- Thermography (3)
- WIG-Schweißen (3)
- Wasserstofftechnologien (3)
- 13CrMoV9-10 (2)
- AISI D2 (2)
- ASTM E647 (2)
- Analytisches Modell (2)
- Auftragschweißen (2)
- Austenite-to-martensite transformation (2)
- Bauteilauslegung (2)
- Bauteilbewertung (2)
- Bragg-edge imaging (2)
- Calibration free (2)
- Co-Cr-alloy (2)
- Crack closure effect (2)
- Crack-closure (2)
- Cracking (2)
- Creep resistant steel (2)
- Cutting tool (2)
- Cyclic J-integral (2)
- Cyclic R-curve analysis (2)
- DED-arc (2)
- Damage tolerance (2)
- Data evaluation methods (2)
- Debye-Waller-Faktor (2)
- Debye–Waller factor (2)
- Dissimilar metal weld (DMW) joint (2)
- Effective crack propagation data (2)
- Einspanngrad (2)
- Environmental conditions (2)
- Ermüdung (2)
- Ermüdungsrisswachstum (2)
- Experimental design (2)
- Experimental determination (2)
- Fail-safe (2)
- Failure Assessment Diagram (2)
- Fatigue Crack Propagation (2)
- Fatigue Strength (2)
- Fatigue properties (2)
- Fractography (2)
- Fracture (2)
- Fracture resistance (2)
- GMA Welding (2)
- GMAW (2)
- Gas metal arc welding (2)
- Gas tungsten arc welding (GTAW) (2)
- HSLA steel (2)
- Heat-affected zone (2)
- High Cycle Fatigue (2)
- High Entropy Alloy (2)
- High entropy alloy (2)
- Hydrogen embrittlement (2)
- Härteprüfung nach Vickers (2)
- Höherfeste Feinkornbaustähle (2)
- Höherfester Feinkornbaustahl (2)
- Höherfester Stahl (2)
- ISO 12108 (2)
- In situ (2)
- L-PBF 316L (2)
- LPBF (2)
- LTT Weld Filler Materials (2)
- LTT weld filler materials (2)
- Laser implantation (2)
- Low transformation temperature (LTT) steel (2)
- MAG welding (2)
- Machining (2)
- Martensite (2)
- Material defects (2)
- Mechanical Engineering (2)
- Mechanics of Materials (2)
- Metallschutzgasschweißen (2)
- Metallurgie (2)
- Metals and Alloys (2)
- Micro-shrinkages (2)
- Microstructure and texture (2)
- Microstructure characterization (2)
- Modification of structural morphology (2)
- Multi-principal element alloys (2)
- Nachwärmung (2)
- Neutron (2)
- Niobium carbide (2)
- Non-metallic inclusions (2)
- Numerische Simulation (2)
- PWHT (2)
- Plasma-Transferred-Arc (2)
- Pores (2)
- Reheat cracking (2)
- Repair Welding (2)
- Repair welding (2)
- Ressidual stress (2)
- Review (2)
- Rissschließeffekte (2)
- S-N curve (2)
- SLM (2)
- Schweißverbindungen (2)
- Schweißzusatzmodifikation (2)
- Schwellenwert gegen Ermüdungsrissausbreitung (2)
- Schwer spanbar (2)
- Short crack (2)
- Short cracks (2)
- Small-scale specimens (2)
- Stahl (2)
- Steel 316L (2)
- Structural Integrity (2)
- Struktur Integrität (2)
- Surface texturing (2)
- Tensile properties (2)
- Texture (2)
- TiB2 (2)
- Turbinenscheibe (2)
- Ultrasonic assisted milling (2)
- Varestraint (2)
- Varestraint test (2)
- Varestraint testing (2)
- Vickers hardness (2)
- Wasserstoffdegradation (2)
- Welded Joints (2)
- Welded joints (2)
- Welding residual stresses (2)
- Wire Arc Additive Manufacturing (2)
- X-ray Diffraction (2)
- Zerspanung (2)
- μCT-analysis (2)
- 2101 duplex stainless steel (1)
- 3D Scanning (1)
- ADXRD (1)
- AM 316L stainless steel (1)
- AXRD (1)
- Acero 316L (1)
- Acero alta resistencia (1)
- Additiv (1)
- Additiver Fertigung (1)
- Ageing (1)
- Aging (1)
- AlSi10Mg alloy (1)
- Alternative test procedure (1)
- Aluminium Alloy (1)
- Aluminum alloys (1)
- Anlagenbau (1)
- Application properties (1)
- As-built LPBF IN718 alloy (1)
- Aufheizrate (1)
- Austenit (1)
- Austenitic (1)
- Austenitic Stainless Steel (1)
- Austenitic stainless steel (1)
- Austenitischer Rostfreier Stahl (1)
- BMDK (1)
- Backlight (1)
- Bainitischer Schmiedestahl (1)
- Bauteilversuch (1)
- Bayesian technique (1)
- Beanspruchungsanalyse (1)
- Bedarf (1)
- Bedeutung (1)
- Betriebsfestigkeit (1)
- Beugung (1)
- Biaxial test (1)
- Bragg-edge (1)
- Bragg-edge neutron 2D imaging (BENI) (1)
- Brazil nut Mesocarp (1)
- Bruch (1)
- Bruchmechanische Kennwerte (1)
- Bruchmechanische Konzepte (1)
- CCT diagrams (1)
- Carrier gas hot extraction (CGHE) (1)
- Chapetti’s and IBESS model (1)
- Characterisation (1)
- Chemische Zusammensetzungen (1)
- Co-Cr-Legierung (1)
- Cobalt-chromium alloy (1)
- Codes and standards (1)
- Cold Spray (1)
- Cold cracking and welding (1)
- Component Assessment (1)
- Component-like test (1)
- Computed Tomography (1)
- Constraint faktor (1)
- Contact fatigue (1)
- Cooling rate (1)
- Coordinate measurement machine (1)
- Corrosion pits (1)
- Co–Cr-alloy (1)
- CrMoV-Stahl (1)
- Crack Tip Opening Displacement (CTOD) (1)
- Crack arrest (1)
- Crack closure mechanisms (1)
- Crack propagation resistance (1)
- Crack-tip constraint (1)
- Crown-abutment connection (1)
- Crystal Plasticity Modelling (1)
- Crystal plasticity (1)
- Crystallographic texture (1)
- Crystallographic texture control (1)
- Curvas FCGR (1)
- Cutting forces (1)
- Cyclic loading (1)
- Cyclic stress-strain curve (1)
- Damage Tolerance (1)
- Damage tolerance assessment (1)
- Damage tolerant component design (1)
- Debys-Waller-Factor (1)
- Defekte Eigenspannung (1)
- Dehydrogenation heat treatment (1)
- Dental materials (1)
- Determinación Kth intrínseco (1)
- Dickblech (1)
- Diffraction-elastic constants (1)
- Digital Image Correlation (DIC) (1)
- Digitalisierung (1)
- Dislocation density (1)
- Distortion (1)
- Distortion upon baseplate removal (1)
- Ditigtal image correlation (1)
- Druckanschwingen (1)
- Duplex stainless steels (1)
- Dynamic load (1)
- EA4T railway axle steel (1)
- EA4T steel (1)
- EDS (1)
- EN AW-2618A (1)
- Effect of scanning strategies (1)
- Eigensapnnungen (1)
- Eigenspannungsmessung (1)
- Einflussfaktoren (1)
- Einflussfaktoren auf Rissfortschrittsdaten (1)
- Einschlüsse (1)
- Eisenaluminid (1)
- Elastic follow-up (1)
- Elastic-plastic fracture mechanics (1)
- Electrochemical permeation (1)
- Electron backscatter diffraction (EBSD) (1)
- Electron backscattered diffraction (1)
- Electron microscopy (1)
- Energetic reference parameter (1)
- Entwicklung (1)
- Environment (1)
- Environmental effect (1)
- Environmental effects (1)
- Ermüdungslebensdauer (1)
- Ermüdungsriss (1)
- Ermüdungsrissfortschritt (1)
- Ersatzgeometrie (1)
- Erstarrungsrisse (1)
- FAT class (1)
- FAT class approach (1)
- FSW (1)
- Fabricación Aditiva (1)
- Fail-safe design (1)
- Fatigue Crack Growth (1)
- Fatigue Limit (1)
- Fatigue S-N curve (1)
- Fatigue assessment (1)
- Fatigue crack initiation (1)
- Fatigue crack propagation stages (1)
- Fatigue crack propagation stagesdefects (1)
- Fatigue lifetime prediction (1)
- Fatigue loading (1)
- Fatigue propagation threshold (1)
- Fatigue strength and life (1)
- Fatigue threshold (1)
- Feinkornbaustähle (1)
- Ferngasleitung (1)
- Ferrit (1)
- Ferrite (1)
- Filler metal modification (1)
- Finite Element Analysis (1)
- Finite element (FE) (1)
- Finite element analysis (1)
- Fit4AM (1)
- Flaw assessment procedures (1)
- Flaw interaction (1)
- Forschungsprojekt (1)
- Fracture assessment (1)
- GMAwelding (1)
- Gas analytic (1)
- Generative Fertigung (1)
- Global stability criterion (1)
- Graphite modules (1)
- HAZ (1)
- HCF (1)
- HSLA (1)
- Hastelloy X (1)
- Heat Treatment (1)
- Heat affected zone (1)
- Heating rate (1)
- High strength fine grained structural steels (1)
- High strength steels (1)
- High-entropy alloys (1)
- High-pressure (1)
- High-strength (1)
- High-strength filler metals (1)
- High-strength steel filler metal (1)
- High-strength structural steel (1)
- Hochdruck (1)
- Hochfeste Stähle (1)
- Hot Cracking (1)
- Hot Cracks (1)
- Hot crack (1)
- Hot tensile test (1)
- Hydrogen concentration (1)
- Hydrogen degradation (1)
- Hydrogen measurement (1)
- Hydrogen trapping (1)
- I-Träger (1)
- IBESS (1)
- IBESS Approach (1)
- IBESS model for short cracks (1)
- IBESS-Prozedur (1)
- IN718 PBF-LB/M (1)
- IN725 (1)
- Impact damage (1)
- Imperfektion (1)
- Implant-supported prostheses (1)
- Implant-test (1)
- Implants (1)
- In situ LIBS (1)
- In situ measurement, (1)
- In-service (1)
- In-situ Process Monitoring (1)
- In-situ diffraction (1)
- In-situ thermography (1)
- In718 (1)
- Inclusion cluster (1)
- Inclusion size (1)
- Inclusions (1)
- Infractstructure (1)
- Intrinsic fatigue crack propagation threshold (1)
- Intrinsic fatigue propagation threshold (1)
- Iron aluminides (1)
- J-Integral (1)
- Joining (1)
- Joining process (1)
- Kaltriss und Schweißen (1)
- Kaltrissbildung (1)
- Kitagawa-Takahashi (K-T) diagram (1)
- Kritische Last (1)
- Kurzrissbruchmechanik (1)
- Kurzrisswachstum (1)
- Kurzzeitfestigkeit (1)
- L-PBF IN718 material (1)
- LCF (1)
- LCF region (1)
- LTT filler material (1)
- LTT filler metal (1)
- LTT-Legierung (1)
- LTT-Zusatzwerkstoff (1)
- Laboratory X-ray diffraction (1)
- Large scale test (1)
- Laser beam melting (LBM) (1)
- Laser-based additive manufacturing (1)
- Life prediction (1)
- Lifetime (1)
- Ligamentplastifizierung (1)
- Local Weld Geometry (1)
- Localized laser dispersing (1)
- Low Cycle Fatigue (1)
- Low Transformation Temperature (1)
- Low transformation temperature (1)
- Low transformation temperature filler materials (1)
- L‐PBF (1)
- MAG (1)
- MAG-Welding (1)
- MANUFACT (1)
- MSG-Schweißen (1)
- Manufact (1)
- Margin design (1)
- Materialprüfung (1)
- Materialschaedigung (1)
- Materialschädigung (1)
- Mechanical anisotropy (1)
- Mechanical behavior (1)
- Mechanische Eigenschaften (1)
- Mecánica de Fractura (1)
- Medium entropy alloy (1)
- Messung (1)
- Metal additive manufacturing (MAM) (1)
- Metal vapor (1)
- Metallic components (1)
- Metals (1)
- Microalloyed steels (1)
- Microcracking (1)
- Microfocus X-ray computer tomography (μCT) (1)
- Micromechnical properties (1)
- Microstructure characterisation (1)
- Mikrostruktur (1)
- Mikrostrukturentwicklung (1)
- Minimum Waiting Time (1)
- Minimum waiting time (1)
- Mis-match (1)
- Mischverbindung (1)
- Misfit (1)
- Mismatch (1)
- Mock-up (1)
- Modified Varestraint-/Transvarestraint test (1)
- Modifizierter Sprühlichtbogen (1)
- Monotonic and cyclic crack driving force (1)
- Multi-pass welding (1)
- Multielement-Legierung (1)
- Multiple crack initiation (1)
- Multiple crack propagation (1)
- Multiple cracking (1)
- Multiple cracks (1)
- NDT (1)
- Nahtgeometrie (1)
- Near-surface X-ray diffraction (1)
- Near-threshold regime (1)
- Neutron Imaging (1)
- Neutron and X-ray diffraction (1)
- Neutron tomography (1)
- Neutronbeugungsverfahren (1)
- Neutronenbeugung (1)
- Neutronendiffraktion (1)
- Neutronenradiographie (1)
- Neutronentomographie (1)
- Nickel-based superalloys (1)
- Nickel-iron-alloy (1)
- Node-release (1)
- Non-destructive Materials (1)
- Non-destructive testing (1)
- Non-sharp defects (1)
- Normung (1)
- Nuclear reactor systems (1)
- Oberflächenschädigung (1)
- Offshore steel grade (1)
- Offshore steels (1)
- Offshore wind turbine (1)
- Online Process Monitoring (1)
- Oxide-induced crack closure (1)
- PBF-LB/M (1)
- PBF/LB (1)
- Peak stress method (1)
- Peak stress method (PSM) (1)
- Permeation (1)
- Perspektiven (1)
- Phase field modeling (1)
- Phasenumwandlung (1)
- Photogrammetry (1)
- Plasma transferred arc welding (1)
- Pore formation (1)
- Poren (1)
- Post Weld Heat Treatment (PWHT) (1)
- Post processing heat treatment (1)
- Post-weld heat treatment (1)
- Powder Bed Fusion of Metals with Laser Beams (1)
- Preciptiates (1)
- Predicción vida a fatiga (1)
- Principal stress (1)
- Probabilistic Assessment (1)
- Probabilistic assessment (1)
- Probengeometrie (1)
- Probetas miniatura (1)
- Process Monitoring (1)
- Process Simulation (1)
- Process development (1)
- Projekt AGIL - Alterung additiv gefertigter metallischer Materialien und Komponenten (1)
- Projektbegleitender Ausschuss (1)
- Prostheses (1)
- Prozesse (1)
- Prüfung (1)
- Pulverbettbasiertes Laserstrahlschmelzen (1)
- R-curve analysis (1)
- Radiography (1)
- Rauheit (1)
- Recomendaciones procedimiento de ensayo (1)
- Reference standards (1)
- Refraction (1)
- Representative Specimens (1)
- Representative material properties (1)
- Repräsentative Werkstoffeigenschaften (1)
- Research and Development (1)
- Residual lifetime (1)
- Residual stress in AM (1)
- Residual stress state (1)
- Restlebensdauerprognose (1)
- Retained Austenite (1)
- Riss (1)
- Rissausbreitung (1)
- Rissausbreitungsstadien (1)
- Rissbildung (1)
- Rissfortschrittsdaten (1)
- Rissschließfunktion (1)
- Rissschließphenomen (1)
- Rissspitzenbelastung (1)
- Risswachstum (1)
- Risswiderstand (1)
- Roughness (1)
- Röntgenradiographie (1)
- S-N diagram (1)
- S-N probabilistic field (1)
- S-Phase (1)
- Safety (1)
- Sample random results (1)
- Scan strategies (1)
- Scan strategy influence (1)
- Scattering (1)
- Schadenstolerante Bauteilauslegung, (1)
- Schadenstolerante Bauteilauslegung, Restlebensdauer, intrinsischer Schwellenwert gegen Ermüdungsrissausbreitung (1)
- Schallemissionsanalyse (1)
- Schallemmission (1)
- Schlichtfräsen (1)
- Schutzgasschweißen (1)
- Schweißeigenspannungen (1)
- Schweißeignung (1)
- Schweißprozessparameter (1)
- Schweißverbindung (1)
- Scratches (1)
- Secondary stresses (1)
- Selective laser melting (SLM) (1)
- Short Crack Propagation (1)
- Short crack Propagation (1)
- Short crack propagation (1)
- Shrinkages (1)
- Sicherheit (1)
- Slow Strain Rate Testing (1)
- Small scale testing (1)
- Snergiedispersive Röntgendiffraktion (1)
- Software (1)
- Solidification (1)
- Solidification Cracking (1)
- Spannung (1)
- Stainless steels (1)
- Staircase method (1)
- Standardisation (1)
- Standardization (1)
- Static load (1)
- Statistics (1)
- Stiffness (1)
- Stochastic sample functions (1)
- Strain-free lattice references (1)
- Strain-free lattice spacing (1)
- Strength mismatch (1)
- Stress Relief Cracking (SRC) (1)
- Stress balance (1)
- Stress balance condition (1)
- Stretch-Zone (1)
- Supermartensit (1)
- Supermartensitic steel (1)
- Supermatensitischer Stahl (1)
- Support configurations (1)
- Surface preparation (1)
- Surface roughness (1)
- Synchrotron X-ray diffraction (1)
- Synchrotron diffraction (1)
- Synchrotron radiation (1)
- Synchrotronbeugung (1)
- TEKKEN test (1)
- TEM (1)
- TIG (1)
- Temperature (1)
- Tensile testing (1)
- Testing parameters (1)
- Thermal conductivity device (1)
- Thermal desorption analysis (1)
- Thick-walled (1)
- Thoughness (1)
- Threshold regime (1)
- TiC (1)
- TiN (1)
- Tomography (1)
- Toughening mechanisms (1)
- Toughness (1)
- Traglastverhalten (1)
- Transient stresses (1)
- Trägergasheißextraktion (1)
- UP Schweißen (1)
- Ultraschallunterstützter Fräsprozess (1)
- Varestraint Test (1)
- Verschleißschutz (1)
- Versetzungsstrukturen (1)
- WAAM Ti-6Al-4V (1)
- WIG (1)
- WIG Schweißen (1)
- WRC 92 (1)
- Waiting time (1)
- Warmfeste Stähle (1)
- Warmfester Stahl (1)
- Wasserstoffbindungsverhalten (1)
- Wasserstoffdiffusion (1)
- Wasserstoffgradient (1)
- Wasserstoffkonzentration (1)
- Wasserstoffunterstützte Kaltrissbildung (1)
- Weld geometry (1)
- Weld metal cracking (1)
- Weld toe geometry (1)
- Welded joint (1)
- Werkstoff (1)
- Werkstoffe (1)
- Werstoff- und geometrische Imperfektion (1)
- Wind Energy (1)
- Wärmbehandlung (1)
- Wärmebehandlung (1)
- X-ray and neutron diffraction (1)
- X-ray refraction (1)
- XRF (1)
- Zugversuch (1)
- carrier gas hot extraction (1)
- cold cracking safety (1)
- contour method (1)
- digitalisation (1)
- duplex stainless steel (1)
- fatigue crack growth (1)
- high-strength steel (1)
- hochfester Stahl (1)
- miniature specimens; FCGR curves; intrinsic threshold (1)
- neutron diffraction (1)
- residual stress analysis (1)
- µCT-analysis (1)
- μCT (1)
Organisationseinheit der BAM
- 9.4 Integrität von Schweißverbindungen (487) (entfernen)
Paper des Monats
- ja (5)
Carrier gas hot extraction (CGHE) is a commonly applied technique for determination of hydrogen in welded joints using a thermal conductivity device (TCD) for quantitative measurement. The CGHE is based on the accelerated hydrogen effusion due to thermal activation at elevated temperatures. The ISO 3690 standard suggests different specimen geometries as well as necessary minimum extraction time vs. temperature. They have the biggest influence on precise hydrogen determination. The present study summarizes the results and experience of numerous test runs with different specimen temperatures, geometries and factors that additionally influence hydrogen determination. They are namely: specimen surface (polished/as-welded), limited TCD sensitivity vs. specimen volume, temperature measurement vs. effects of PID-furnace controller as well as errors due to insufficient data assessment. Summarized, the temperature is the driving force of the CGHE. Two different methods are suggested to increase the heating rate up the reach the desired extraction temperature without changing the experimental equipment. Suggestions are made to improve the reliability of hydrogen determination depended on the hydrogen signal stability during extraction accompanied by evaluation of the recorded data. Generally, independent temperature measurement with calibration specimens is useful for further data analysis, especially if this data is used for calculation of trapping kinetics by thermal desorption analysis (TDA).
Das DVS-Vorhaben 01.3211 „Herstellung beanspruchungsgerechter Oberflächen durch Kombination innovativer additiver und abtragender Fertigungsschritte an hochbelasteten Komponenten“ ist ein Kooperationsprojekt der Bundesanstalt für Materialforschung und -prüfung (BAM) und dem Institut für Schweißtechnik und Trennende Fertigungsverfahren (ISAF) der Technischen Universität Clausthal. Das Übergeordnete Projektziel ist das Erlangen von Erkenntnissen für eine sichere und wirtschaftliche, kombinierte additive und abtragende Fertigung aus kostenintensiven Werkstoffen hochbelasteter Komponenten insbesondere für KMU. Dabei stehe die beiden Werkstoffe CoCr26Ni9Mo5W (2.4681) und FeNi36 (1.3912) im Fokus. Mittels Modifikation der Schweißzusätze sind homogen und isotrop ausgeprägte Werkstoffeigenschaften und eine Erhöhung der Prozessstabilität und Fertigungsfreiheitsgrade bei der additiven Fertigung erzielbar. Darüber hinaus wird der Einfluss nachfolgender abtragender Bearbeitungsschritte des ultraschallunterstützen und des konventionellen Fräsprozesses untersucht. Im Laufe der Sitzung des projektbegleitenden Ausschusses (PbA) wurde der aktuelle Bearbeitungsstand sowie der Zeitplan vorgestellt. Darüber hinaus wurde mit dem PbA über die bereits erzielten Ergebnisse diskutiert. Abschließend wurde ein kurzer Ausblick über die zeitnah beginnenden Arbeiten beider Forschungseinrichtungen sowie ein Überblick über die vorhabenbezogenen Aufwendungen der Wirtschaft und des Ergebnistransfers in die Wirtschaft gegeben.
As opposed to reviewing results on experimental determination of residual stress by diffraction, this paper discusses the open issues when dealing with residual stress determination in additive manufactured parts, in particular those manufactured with laser powder bed fusion techniques. Three points are addressed in detail: (a) the proper determination of the strain-free reference d0, (b) the problem of the determination of the principal axes, and (c) the use of the correct diffraction elastic constants. It is shown that all methods to determine the strain-free reference d0 suffer from caveats, and care must be taken in evaluating the most suitable for the problem being tackled. In addition, it is shown that, in some systems, the principal axes do correspond to the geometrical axes of the specimen, but this needs to be systematically checked, especially in the case of uni- or bidirectional hatching strategies. Finally, the need to experimentally determine the proper diffraction elastic constants is underlined, especially in the case of strongly textured specimens, which again depends on the deposition strategy.
Sample functions, i.e., stochastic process realizations, are used to define cumulative damage phenomena which end into an observable terminal state or failure. The complexity inherent to such phenomena justifies the use of phenomenological models associated with the evolution of a physical magnitude feasible to be monitored during the test. Sample functions representing the damage evolution may be identified, once normalized to the interval [0,1], with cumulative distribution functions (cdfs), generally, of the generalized extreme value (GEV) family. Though usually only a fraction of the whole damage evolution, according to the specific problem handled, is available from the test record, the phenomenological models proposed allow the whole damage process to be recovered. In this way, down- and upwards extrapolations of the whole damage process beyond the scope of the experimental program are provided as a fundamental tool for failure prediction in the practical design. The proposed methodology is detailed and its utility and generality confirmed by its successive application to representative well-known problems in fatigue and fracture characterization. The excellent fittings, the physical interpretation of the model parameters and the good expectations to achieve a complete probabilistic analysis of these phenomena justify the interest of the proposed phenomenological approach with possible applications to other cumulative damage processes.
The sustainable and resource-efficient production of wind energy plants requires the use of modern high-strength fine-grain structural steels. This applies to both foundation and erection structures. During the assembly of steel structures, unacceptable defects can occasionally be found in the weld area. In most cases, the economical solution would be local thermal gouging of the affected areas and re-welding. Due to the high shrinkage restraint of the joint groove in the overall structure, the superposition of design and welding-induced residual stress can lead to crack formation and ultimately to component failure, particularly in interaction with the degradation of the microstructure and mechanical properties high-strength steels during the repair process.
In this context, component-related investigations (FOSTA-P1311/IGF-Nr. 20162 N) focusing on welding residual stress evolution during local thermal gouging and rewelding of S500MLO and S960QL are carried out using in-situ digital image correlation (DIC) and ex-situ X-ray diffraction methods (XRD). Therefore, self-restrained specimens were systematically gouged and rewelded with defined welding heat control (heat input, working temperature) and parameters. By means of structural mechanics calculations, geometries of self-restrained specimens were identified, that represent defined rigidity conditions of repair welds of real components. It could be shown that with increasing restraint intensity significantly higher residual stresses occur in the weld metal and heat affected zone. Furthermore, it revealed that the transverse stresses along the weld seam decrease at the weld seam ends leading to different stress state during gouging and welding. XRD analysis of the local residual stresses after cooling to RT longitudinal and transverse to the weld direction showed a good comparability with global DIC analyses.
The sustainable and resource-efficient production of wind energy plants requires the use of modern high-strength fine-grain structural steels. This applies to both foundation and erection structures. During the assembly of steel structures, unacceptable defects can occasionally be found in the weld area. In most cases, the economical solution would be local thermal gouging of the affected areas and re-welding. Due to the high shrinkage restraint of the joint groove in the overall structure, the superposition of global and local welding-induced stresses may lead to crack formation and component failure, particularly in interaction with the degradation of the microstructure and mechanical properties of high-strength steels during the repair process [1]. Corresponding standards hardly provide any information on adequate repair concepts, and there is no uniform scientific data on which to base such concepts.
In this study, several relevant findings are discussed based on examples of structural engineering focusing on mechanical-technological properties and residual stresses, e.g. [1]. Further experimental and numerical work as conducted by [2] and weld tests under defined restraint conditions in special weld test-setups [3] show that an optimization of the welding-induced stresses of high-strength structural steels is achievable by means of an adapted heat control. The present research involves systematic investigations of influences of shrinkage restraint, the number of repair cycles and heat control during repair welding of a recently available high-strength offshore steel S500MLO (EN 10225-1). A quantification of the shrinkage restraint of repair weld joints is achievable by means of restraint intensity concept [4], analogous to previous studies [5]. Using structural mechanics calculations, geometries of self-restrained specimens are identified representing different defined rigidity conditions of repair welds considering actual high-strength steel components. Welding experiments with DIC analyses (digital image correlation) of the occurring strains during welding and XRD analyses (X-ray diffraction) of the resulting residual stresses after welding and cooling show increasing transient loads and significantly elevated residual stress profiles in the weld area with increasing restraint intensity. Especially in the heat affected zone, tensile residual stresses of up to 80 % of the nominal yield strength occur when welding under increased restraint conditions. In relation to the presented existing results, this indicates that a safe repair welding is primarily achievable by means of appropriate repair concepts and heat control taking into account the high welding stresses and special microstructures of high-strength steels. Finally, the aim of this research is to derive recommendations for repair concepts appropriate to the stresses and materials involved providing a basis for standards and guidelines, especially for SMEs, in order to avoid damage and, in most cases, expensive reworking and to improve the full utilization of the potential of high-strength steels.
Laser powder bed fusion (LPBF) is an additive manufacturing process for materials which inherently tends to yield various degrees of metastable hierarchical microstructures, defects and high residual stresses in the as-built condition depending on the process parameters. The understanding of the evolution of these typical features during heat treatment and subsequent thermal and mechanical ageing is crucial for the wider acceptance for safety critical structures. A multi-disciplinary research project at BAM studying the development of the microstructure, defects, residual stresses typical of LPBF 316L and their evolution during thermal and mechanical ageing has led to insights into the stability of these inherent features. This presentation aims to give a broad overview of the project with a few specific cases of investigation. Firstly, the formation of residual stresses, the nature of the initial microstructure, the tensile properties and a modelling approach to understand the anisotropy will be presented. This will be followed by examples of studies of their evolution during heat treatment, long term thermal exposure, and room temperature and high temperature mechanical testing compared to a baseline of conventional wrought variant of the same alloy.
An overview of the BAM funed Focus Area Materials Project "AGIL" will be presented. AGIL focussed on the stdiy of the ageing characteristics of additively manufactured austenitic stainless steel with a "powder to mechanical failure" Approach. Recent Highlights are presented and a perspective for future studies.
Alloy Modification and ultrasonic assisted milling of wear resistant alloys with defined surfaces
(2023)
The targets for reducing CO2 emissions are closely linked to the development of highly efficient and economical steel components in plant, process and power plant technology, which require wear protection coatings tailored to the application and steel material for high combined corrosive, tribological, thermal and mechanical stresses. There is a growing demand in industry for defined functional surfaces of high quality for these coatings. Milling is a standard process for finish machining. The desired properties of wear resistant alloys imply significant challenges for the milling process due to high tool wear and surface defects. Besides the hardness of the coating materials, especially due to the precipitations, inhomogeneous, anisotropic weld structures of the claddings lead to further deteriorations of milling processes due to unstable milling conditions and process forces.
A joint project of BAM and ISAF of TU Clausthal (Fosta P1550/IGF 21959 N) investigates the optimization of these challenging machining conditions by means of alloy modifications of the welding powder for plasma transferred arc cladding, without reducing the wear protection potential and using ultrasonic assisted milling process.
In this paper, the influence of the microstructure and precipitation morphology adjusted by means of alloy modification on machining for a NiCrMoSiFeB alloy (trade name: Colmonoy 56 PTA) is investigated. Through metallurgical investigations and in-situ measurement of cutting forces and temperatures at the cutting edge during the milling process as well as the subsequent investigation of tool wear and surface integrity, a detailed analysis and correlation between microstructural properties and machinability is feasible. The findings allow recommendations for standards and processing guidelines, enabling safe and economical production of highly stressed steel components with non-critical, cost-reduced materials.
Alloy Modification and ultrasonic assisted milling of wear resistant alloys with defined surfaces
(2023)
The targets for reducing CO2 emissions are closely linked to the development of highly efficient and economical steel components in plant, process and power plant technology, which require wear protection coatings tailored to the application and steel material for high combined corrosive, tribological, thermal and mechanical stresses. There is a growing demand in industry for defined functional surfaces of high quality for these coatings. Milling is a standard process for finish machining. The desired properties of wear resistant alloys imply significant challenges for the milling process due to high tool wear and surface defects. Besides the hardness of the coating materials, especially due to the precipitations, inhomogeneous, anisotropic weld structures of the claddings lead to further deteriorations of milling processes due to unstable milling conditions and process forces.
A joint project of BAM and ISAF of TU Clausthal (Fosta P1550/IGF 21959 N) investigates the optimization of these challenging machining conditions by means of alloy modifications of the welding powder for plasma transferred arc cladding, without reducing the wear protection potential and using ultrasonic assisted milling process.
In this paper, the influence of the microstructure and precipitation morphology adjusted by means of alloy modification on machining for a NiCrMoSiFeB alloy (trade name: Colmonoy 56 PTA) is investigated. Through metallurgical investigations and in-situ measurement of cutting forces and temperatures at the cutting edge during the milling process as well as the subsequent investigation of tool wear and surface integrity, a detailed analysis and correlation between microstructural properties and machinability is feasible. The findings allow recommendations for standards and processing guidelines, enabling safe and economical production of highly stressed steel components with non-critical, cost-reduced materials.
Alloy modification and ultrasonic assisted milling of wear resistant alloys with defined surfaces
(2023)
The targets for reducing CO2 emissions are closely linked to the development of highly efficient and economical steel components in plant, process and power plant technology, which require wear protection coatings tailored to the application and steel material for high combined corrosive, tribological, thermal and mechanical stresses. In addition to increasing demands to replace conventional cobalt alloys with nickel alloys as a result of price and supply risks, there is a growing demand in industry for defined functional surfaces of high quality for these coatings. Milling is a standard process for finish machining. The desired properties of wear resistant alloys imply significant challenges for the milling process due to high tool wear and surface defects. Besides the hardness of the coating materials, especially due to the precipitations, inhomogeneous, anisotropic weld structures of the claddings lead to further deteriorations of milling processes due to unstable milling conditions and process forces.
A joint project of BAM and ISAF of TU Clausthal (Fosta P1550/IGF 21959 N) investigates the optimization of these challenging machining conditions by means of alloy modifications of the welding powder for plasma transferred arc cladding, without reducing the wear protection potential and using ultrasonic assisted milling process.
In this paper, the influence of the microstructure and precipitation morphology adjusted by means of alloy modification on machining is investigated. The alloy used is a NiCrMoSiFeB alloy (trade name: Colmonoy 56 PTA). Through metallurgical investigations and in-situ measurement of cutting forces and temperatures at the cutting edge during the milling process as well as the subsequent investigation of tool wear and surface integrity, a detailed analysis and correlation between microstructural properties and machinability is feasible. The findings allow recommendations for standards and processing guidelines, enabling safe and economical production of highly stressed steel components with non-critical, cost-reduced materials.
Alloy 36 (1.3912), also known as “Invar”, is an alloy with 36% nickel. The alloy has a remarkably low thermal expansion coefficient in certain temperature ranges. Therefore, it is used in applications in which dimensional stability is critical, such as moulding tools for composite materials in aerospace and automotive applications. Moreover, increasingly complex structures and the optimisation of resource efficiency also require additive manufacturing steps for the production or repair of components. Additively manufactured components have a heterogeneous microstructure and anisotropic mechanical properties. In part I of this investigation, the initial alloy 36 is modified with the elements Ti, Zr and Hf up to a maximum of 0.33 wt.-%. The influence of the modification elements on the microstructure as well as on the hardness of the AM components is examined. Part II focusses on the effect of the alloy modifications on machinability as well as on the surface integrity of plasma-transferred-arc-welded (PTA) and finish milled invar components. The results show that PTA welding cause numerous finely distributed precipitates with high silicon content.
Alloy 36 is an iron-based alloy with 36% nickel. It is used in applications in which dimensional stability is critical, such as molding tools for composite materials in aerospace and automotive applications. Moreover, increasingly complex structures and the optimisation of resource efficiency also require additive manufacturing steps for the production or repair of components. Additively manufactured components have a heterogeneous microstructure and anisotropic mechanical properties. In addition, the manufactured components require subsequent machining surface finishing due to the high requirements. Nickel iron alloys are difficult to machine. Additionally, inhomogeneous microstructure may lead to unstable cutting forces and conditions. Alloy modifications are made to the alloy 36. For this purpose, titanium, zirconium and niobium are added up to 1 % by mass each. Plasma-Transferred-Arc is used for the welding tests. The hardness profile is determined on the transverse section. The initial structure as well as the modifications have an austenitic structure. The microstructure of the modifications of Alloy 36 with 1% Ti and 1% Zr is not refined, instead the grain size increases.
Alloy 36 (1.3912), also known as “Invar”, is an alloy with 36% nickel. It was developed in 1897 by Guillaume and stands out for its very low thermal expansion coefficient. It is classified as a difficult-to-cut material and is commonly used for the production of fiber-reinforced composites in the field of mold construction. Additive manufacturing (AM) offers many economic advantages regarding the repair, modification and manufacture of entire components. Subsequent machining of the AM components is necessary to account for complex structures, final contours or defined surfaces. This is usually done using a tool with a geometrically defined cutting edge, i.e., milling processes. Surface integrity is determined by metallurgical (e.g., microstructure of the subsurface), topological (e.g., surface defects, roughness) and mechanical (e.g., residual stresses) factors, which is crucial in terms of component safety and performance. Modern, hybrid cutting processes, such as ultrasonic-assisted milling (US), provide potentially improvement of the cutting situation of these components.
In part I of this investigation, the initial alloy 36 is modified with the elements Ti, Zr and Nb up to a maximum of 1 wt.-%. The influence of the modification elements on the microstructure as well as on the hardness of the AM components is examined. Part II focusses on the effect of the alloy modifications on machinability as well as on the surface integrity of plasma-transferred-arc-welded (PTA) and finish milled invar components.
The results show a significant positive influence of ultrasonic assistance on the resulting cutting force of both materials. The modification with 1% Ti shows a positive influence on the surface integrity, as the roughness of the conventional machining processes is lower compared to the initial alloy, which has to be confirmed in further experiments.
Alloy 36 (1.3912), also known as “Invar”, is an alloy with 36% nickel. It was developed in 1897 by Guillaume and stands out for its very low thermal expansion coefficient. It is classified as a difficult-to-cut material and is commonly used for the production of fiber-reinforced composites in the field of mold construction. Additive manufacturing (AM) offers many economic advantages regarding the repair, modification and manufacture of entire components. Subsequent machining of the AM components is necessary to account for complex structures, final contours or defined surfaces. In part I of this investigation, the initial alloy 36 is modified with the elements Ti, Zr and Hf up to a maximum of 0.33 wt.-%. The influence of the modification elements on the microstructure as well as on the hardness of the AM components is examined. Part II focusses on the effect of the alloy modifications on machinability as well as on the surface integrity of plasma-transferred-arc-welded (PTA) and finish milled invar components. Machining tests were carried out, to investigate the influence of ultrasonic assistance and the effects of modification elements Ti, Zr and Hf on the occurring cutting forces, temperatures and resulting surface integrity of the AM components made of alloy 36 and their modifications. The results show a significant positive influence of ultrasonic assistance on the resulting cutting force as well as on the roughness of all materials investigated.
Alloy 36 (1.3912) is an alloy with 36% nickel and 64% iron and is generally classified as a difficult-to-cut material. Increasingly complex structures and the optimization of resource efficiency are making additive manufacturing (AM) more and more attractive for the manufacture or repair of components. Subsequent machining of AM components is unavoidable for its final contour. By using modern, hybrid machining processes, e.g., ultrasonic-assisted milling (US), it is possible to improve the cutting situation regarding the resulting surface integrity as well as the cutting force. Part I deals with the influence of the alloying elements Ti, Zr, and Hf on the microstructure and the hardness of the initial alloy 36. Part II focusses on the effect of the alloy modifications and the ultrasonic assistance on machinability as well as on the surface integrity after finish-milling. The results show a highly significant influence of the ultrasonic assistance. The cutting force during the US is reduced by over 50% and the roughness of approx. 50% compared to conventional milling (CM) for all materials investigated. Moreover, the US causes a defect-free surface and induces near-surface compressive residual stresses. CM leads to a near-surface stress state of approx. 0 MPa.
Alloy 36 (1.3912), also known as “Invar,” is an alloy with 36% nickel. The alloy has a remarkably low thermal expansion coefficient in certain temperature ranges. This peculiarity is called the invar effect, which was discovered in 1896 by the Swiss physicist Charles Édouard Guillaume. Therefore, it is used in applications in which dimensional stability is critical, such as molding tools for composite materials in aerospace, automotive applications, or liquified natural gas (LNG) cargo tanks. Moreover, increasingly complex structures and the optimization of resource efficiency also require additive manufacturing steps for the production or repair of components. Additively manufactured components have a heterogeneous microstructure and anisotropic mechanical properties. In addition, the manufactured components require subsequent machining surface finishing, like finish milling, to achieve their final contour. Nickel iron alloys are difficult to machine. Additionally, inhomogeneous microstructure may lead to unstable cutting forces and conditions. In part I of this investigation, the initial alloy 36 is modified with the elements Ti, Zr, and Hf up to a maximum of 0.33 wt.-%. The influence of the modification elements on the microstructure as well as on the hardness of the AM components is examined. Furthermore, one modification is applied to metal arc welding process and investigated. Part II focuses on the effect of the alloy modifications on machinability as well as on the surface integrity of plasma-transferred-arc-welded (PTA) and finish milled invar components.
Additive Manufacturing (AM) of metals has become industrially viable for a large variety of applications, including aerospace, automotive and medicine. Powder bed techniques such as Selective Laser Melting (SLM) based on layer-by-layer deposition and laser melt enable numerous degrees of freedom for the geometrical design. Developing during the manufacturing process, residual stresses may limit the application of SLM parts by reducing the load bearing capacity as well as induce unwanted distortion depending on the boundary conditions specified in manufacturing.
The residual stress distribution in the bulk of IN718 elongated prisms produced by SLM was studied non-destructively by means of neutron diffraction. The samples with different scanning strategies, i.e. hatching length, were measured in as-build condition (on a build plate) and after removal from the build plate.
The absolute values of all stress components decreased after removal from the build plate. Together with surface scan utilizing a coordinate-measuring machine (CMM), it is possible to link the stress release to the sample distortion. Obtained results indicated different residual stress states for each of the transversal, longitudinal and normal component depending on the thermal gradient in the respective direction.
Having been introduced almost two decades ago, Additive Manufacturing (AM) of metals has become industrially viable for a large variety of applications, including aerospace, automotive and medicine. Powder bed techniques such as Selective Laser Melting (SLM) based on layer-by-layer deposition and laser melt enable numerous degrees of freedom for the geometrical design. Developing during the manufacturing process, residual stresses may limit the application of SLM parts by reducing the load bearing capacity as well as induce unwanted distortion depending on the boundary conditions specified in manufacturing.
The residual stress distribution in IN718 elongated prisms produced by SLM was studied non-destructively by means of neutron (bulk) and laboratory X-ray (surface) diffraction. The samples with different scanning strategies, i.e. hatching length, were measured in as-build condition (on a build plate) and after removal from the build plate.
The absolute values of all stress components decreased after removal from the build plate. Together with surface scan utilizing a coordinate-measuring machine (CMM), it is possible to link the stress release to the sample distortion. Obtained results indicated different residual stress states for each of the transversal, longitudinal and normal component depending on the thermal gradient in the respective direction.
Having been introduced almost two decades ago, Additive Manufacturing (AM) of metals has become industrially viable for a large variety of applications, including aerospace, automotive and medicine. Powder bed techniques such as Selective Laser Melting (SLM) based on layer-by-layer deposition and laser melt enable numerous degrees of freedom for the geometrical design. Developing during the manufacturing process, residual stresses may limit the application of SLM parts by reducing the load bearing capacity as well as induce unwanted distortion depending on the boundary conditions specified in manufacturing.
The residual stress distribution in IN718 elongated prisms produced by SLM was studied non-destructively by means of neutron (bulk) and laboratory X-ray (surface) diffraction. The samples with different scanning strategies, i.e. hatching length, were measured in as-build condition (on a build plate) and after removal from the build plate.
The absolute values of all stress components decreased after removal from the build plate. Together with surface scan utilizing a coordinate-measuring machine (CMM), it is possible to link the stress release to the sample distortion. Obtained results indicated different residual stress states for each of the transversal, longitudinal and normal component depending on the thermal gradient in the respective direction.
Die Kombination aus hoher Korrosionsbeständigkeit und guten mechanischen Eigenschaften von Duplexstählen (DSS) ist auf ihre chemische Zusammensetzung und das ausgewogene Phasenverhältnis von Ferrit (α) und Austenit (γ) zurückzuführen.
Viele industrielle Anwendungen erfordern eine stoffschlüssige Verbindung von DSS. Das Wolfram-Inertgas-Schweißen (WIG) ist relativ einfach zu handhaben, benötigt nur wenig Platz und ermöglicht ein automatisiertes Schweißen, mit sehr hoher Reproduzierbarkeit und ist daher hervorragend zum Schweißen von DSS.
Während der Erstarrung dieser Dualphasenstähle kann es zu kritischen Phasenverhältnissen von α und γ kommen, was zu Erstarrungsrissen, Korrosionsanfälligkeit, geringerer Duktilität und kritischen Festigkeitswerten führt. Um die gewünschten Werkstoffeigenschaften zu erhalten, muss daher die α/γ-Verteilung zuverlässig vorhergesagt werden. Dies geschieht in der Regel mit Hilfe des WRC1992-Diagramms. Die Vorhersagegenauigkeit des Ferritgehalts in diesem Diagramm ist jedoch meist nicht genau genug und muss daher optimiert werden. Daher ist es notwendig, selbst kleinste Veränderungen in der chemischen Zusammensetzung des Schweißguts idealerweise während des Schweißens zu überwachen. Dies wird in diesen Experimenten mit Hilfe der laser-induzierten Plasmaspektroskopie (LIBS) durchgeführt. Ein großer Vorteil dieser Technik ist die hochgenaue zeit- und ortsaufgelöste Messung der chemischen Zusammensetzung während des Schweißens. In vorherigen Arbeiten wurde bereits die chemische Zusammensetzung im Schweißgut und der WEZ quantifiziert. In der präsentierten Untersuchung wird der Einfluss einzelner Elemente, wie Nb und Cu, auf das resultierende Schweißmikrogefüge untersucht.
Solidification cracking of metals is a well-researched topic in the field of welding science. A material’s susceptibility to solidification cracking can be tested using numerous different specialized test procedures, one of which is the Modified Varestraint-/Transvarestraint test (MVT). It was developed at BAM in 1982 and is internationally standardised. Over the decades, this test has been extensively used to characterise the solidification cracking resistance of many different materials.
The present study was conducted to further investigate the influences of the standardised MVT testing parameters, as well as the characteristics of evaluation methods on the results. Several different high alloyed martensitic LTT (low transformation temperature) filler materials, CrNi and CrMn type, were used. In previous pilot studies, these alloys have shown a rather distinctive solidification cracking behaviour (Fig. 1). During testing, energy input per unit length and bending speed were varied (especially the latter is usually kept at standard values), in addition to the most commonly altered factor - total deformation.
First, the effects of different process parameter sets on the solidification cracking response were measured using the standard approach - microscopic analysis of the specimen surface. It was found that not all parameter changes had the expected outcome. For the Cr8Ni6 and Cr11Mn5 filler materials, influences of energy input per unit length and welding speed were in direct opposition.
In order to investigate those apparent contradictions, µCT scans of MVT specimens were made. The results consistently show sub surface cracking, to significant, yet varying extents. Different primary solidification types were found using WDX-analysis, an aspect that is believed to be the main difference between the CrNi- and CrMn-type materials and their cracking characteristics.
Results show that when it comes to testing of modern high-performance alloys, one set of standard MVT testing parameters might not be equally suitable for all materials. Also, to properly accommodate different solidification types, sub-surface cracking has to be taken into account.
Die Verwendung von Low Transformation Temperature (LTT) Schweißzusatzwerkstoffen ist eine innovative Möglichkeit, um beim Schweißen von hochfesten Stählen die schweißbedingten Zugeigenspannungen zu reduzieren. Durch die Zugabe von Legierungselementen, wie beispielsweise Nickel oder Mangan haben diese Werkstoffe eine, im Vergleich zu herkömm-lichen Schweißzusatzwerkstoffen deutlich herabgesetzte Martensitstarttemperatur (MS). Dadurch ist es möglich, die schweißbedingten Zugeigenspannungen mit LTT-Schweißzusatz-werkstoffen gezielt zu reduzieren oder sogar Druckeigenspannungen zu erzeugen.
Im Verlauf vorangegangener Arbeiten hat sich herausgestellt, dass einige der untersuchten LTT-Legierungen aufgrund ihres Erstarrungs- bzw. Seigerungsverhaltens eine gegenüber vielen konventionellen Schweiß-zusatzwerkstoffen erhöhte Heißrisssensibilität aufweisen.
Die aktuellen Arbeiten zielen darauf, die Heißrissneigung neuartiger LTT-Schweißzusatzwerkstoffe weiter zu ergründen.
Das DVS-Vorhaben 01.3211 „Herstellung beanspruchungsgerechter Oberflächen durch Kombination innovativer additiver und abtragender Fertigungsschritte an hochbelasteten Komponenten“ ist ein Kooperationsprojekt der Bundesanstalt für Materialforschung und -prüfung (BAM) und dem Institut für Schweißtechnik und Trennende Fertigungsverfahren (ISAF) der Technischen Universität Clausthal. Das Übergeordnete Projektziel ist das Erlangen von Erkenntnissen für eine sichere und wirtschaftliche, kombinierte additive und abtragende Fertigung aus kostenintensiven Werkstoffen hochbelasteter Komponenten insbesondere für KMU. Dabei stehe die beiden Werkstoffe CoCr26Ni9Mo5W (2.4681) und FeNi36 (1.3912) im Fokus. Mittels Modifikation der Schweißzusätze sind homogen und isotrop ausgeprägte Werkstoffeigenschaften und eine Erhöhung der Prozessstabilität und Fertigungsfreiheitsgrade bei der additiven Fertigung erzielbar. Darüber hinaus wird der Einfluss nachfolgender abtragender Bearbeitungsschritte des ultraschallunterstützen und des konventionellen Fräsprozesses untersucht. Die ersten Ergebnisse der Mikrostruktur sowie der Härte der via PTA gefertigten Probenkörper des CoCr-Werkstoffes und den ersten Modifizierungen werden vorgestellt. Darüber hinaus wird ein Ausblick auf die folgenden Arbeiten gegeben.
Analytical flaw assessment
(2018)
The paper provides a review on analytical flaw assessment methods with the focus on fracture under monotonic loading and fatigue crack propagation. The first topic comprises linear elastic as well as elastic-plastic fracture mechanics approaches. It essentially follows their historical development. Topics which are separately discussed are reference/Limit loads, the treatment of secondary stresses, strength mismatch, constraint, unstable crack propagation (monotonic R-curve analyses) and statistical aspects. With respect to fatigue crack propagation the analytical treatment of crack closure and constraint and the Determination of the cyclic elastic-plastic crack driving force is discussed. Finally, cyclic Rcurve analyses are briefly addressed.
Bruchmechanik-basierende Methoden können für die Ermüdungsbewertung von mechanischen Bauteilen angewendet werden, die Defekte oder Risse enthalten und zyklischen Belastungen ausgesetzt sind. Die Kenntnis des Risswachstumsverhaltens für kurze und lange Risse ermöglicht die Bestimmung sowohl endlicher als auch unendlicher Lebensdauer. Ein erstes Problem ergibt sich jedoch aus der empirischen Bestimmung von Ermüdungswerkstoffkennwerten, die je nach Prüfbedingungen, z. B. Prüfmethode, Frequenz und Spannungsverhältnis R, variieren. Dies ist auf die Rissschließeffekte und weitere Umgebungsphänomene zurückzuführen, die das Rissfortschrittsverhalten beeinflussen. Ein zweites Problem ist das Fehlen von Standardversuchsverfahren zur Bestimmung des Schwellenwerts gegen Ermüdungsrissausbreitung ΔKth in Abhängigkeit von der Rissausbreitung. Dies ist problematisch, da ΔKth mit der Zunahme der Rissschließeffekte im Kurzrissbereich zunimmt und seine ungenaue experimentelle Bestimmung zu großen Abweichungen bei der Bewertung und, was noch kritischer ist, zu nicht konservativen Vorhersagen führt. Mit dem Ziel, zuverlässigere und sicherere Bewertungsverfahren bereitzustellen, wird in dieser Arbeit eine Methode vorgeschlagen, die auf effektiven Risswachstumsdaten basiert, die bei hohen Spannungsverhältnissen (R ≈ 0,8) ermittelt wurden. Zur Beschreibung der Entwicklung der Rissschließeffekte wird ein Kurzrissmodell auf der Grundlage von zyklischen R-Kurven und CPLR-Daten verwendet. Die analytischen Vorhersagen werden mit experimentellen Daten verglichen, die zur Validierung des Verfahrens durchgeführt wurden, und die daraus entstandenen Unterschiede werden diskutiert.
Übersetzt mit DeepL.com (kostenlose Version)
Various industrial applications require the joining of DSS components. Tungsten Inert Gas (TIG) welding is particularly well-suited for this purpose due to the ability to achieve highly reproducible automated welds. However, during solidification of the weld pool, critical phase ratios of ferrite (α) and austenite (γ) may occur, leading to solidification cracking, increased corrosion susceptibility, lower ductility and critical strength values. Hence, in order to achieve the desired material characteristics, it is crucial to accurately predict the α/γ phase ratio within the weld. Conventionally, the WRC-1992 diagram is employed for this purpose. In our study, we used Laser-Induced Breakdown Spectroscopy (LIBS) to track alterations in the chemical composition of the weld metal on the surface throughout the welding process. One significant benefit of this method is its capability to provide precise and real-time measurements of chemical compositions during welding, both temporally and spatially. In previous investigations, we could develop routines to quantify the measurement of chemical compositions within the weld metal and the Heat-Affected Zone (HAZ). The conducted research focuses on examining the alterations in chemical concentrations of specific alloying elements, namely Cu and Mn as γ-forming elements, and Nb and Cr as α-forming elements, during welding. These changes are measured in real-time using Laser-Induced Breakdown Spectroscopy (LIBS). To achieve this, both the ferrite number, determined through magnetic-inductive techniques, and the weld microstructure are analyzed. Through image-analytical methods, a correlation is established between the microstructure and the LIBS data obtained.
Im Rahmen eines Kooperationsprojekts mit der Schottel GmbH wurde eine bauteilnahe Probengeometrie entwickelt, mit der sich unter Verwendung einer einachsigen Prüfmaschine das Spannungstiefenprofil in dem unter überlagerter Biege- und Zugspannung beanspruchtem Querschnitt im Schweißnahtübergang des Bauteils reproduzieren ließ.
Proben dieser Geometrie wurden vom Kooperationspartner im geschweißten bzw. geschweißten und spannungsarmgeglühten Zustand bereitgestellt. An der BAM wurden je Wärmebehandlungszustand mittels Senkerodieren zwei verschiedene künstliche Defektgeometrien im Schweißnahtübergang eingebracht.
Anhand der Proben wurden experimentell für alle vier Probenzustände Wöhlerlinien für ein Spannungsverhältnis von R = 0,1 ermittelt.
Zusätzlich wurde das u.a. an der BAM entwickelte IBESS-Verfahren angewandt, um die Wöhlerlinien analytisch zu bestimmen. Hierbei wurde eine sehr gute Übereinstimmung von Berechnung und Experiment erreicht, wobei die Berechnung zu einer leicht konservativen Lebensdauervorhersage führte.
The two-part paper series provides an overview on the state-of-the-art in the application of engineering fracture mechanics to weldments limited to butt and fillet welds with crack initiation at weld toes. In the present second part, one focus is on welding residual stresses, their characteristics and stability under cyclic loading and their effect on structural integrity. Subsequently, features will be addressed which are essential for applying fracture mechanics to overall fatigue life and fatigue strength considerations of weldments. These comprise fatigue life relevant initial crack sizes and multiple crack initiation and Propagation due to various stress peaks along the weld toe. A concept is briefly introduced which covers all these aspects.
Welded joints show large variation of the weld toe geometry along the weld seam, which is one important reason for the comparably large scatter in fatigue life. Therefore, it is crucial to take the local geometry at the weld toe into account, to reduce the conservatism in fatigue assessment of welded joints. This study is based on the IBESS procedure for the calculation of the fatigue strength, whereby the evaluation of local geometrical parameters is carried out by means of 3D surface scans. The approach is validated against 26 fatigue test series. The fatigue life is in general overpredicted, whereas good agreement is achieved for high stress ratio (R = 0.5). A sensitivity analysis conducted with IBESS shows that weld toe radii ρ < 2 mm and flank angle α < 30° have a significant influence on the calculated fatigue strength. In contrast to this, no strong correlation between ρ and the fatigue strength was determined experimentally in this study.
Am Beispiel eines abgesetzten zylindrischen Bauteils (Achsschenkel) werden Probleme der analytischen bruchmechanischen Bauteilbewertung diskutiert. Als Basis-philosophie wird ein Fail Safe-Kriterium (kontrolliertes Versagen) angesetzt. Die Forderung ist, dass sich der Achsschenkel, bevor er bricht, in einem Ausmaß plastisch verformen kann, bei dem der Fahrer bemerkt, dass mit seinem Fahrzeug etwas nicht in Ordnung ist. Um das zu gewährleisten, muss der Werkstoff einen bestimmten Riss-widerstand aufweisen. Dazu werden im hier vorgestellten ersten Teil des Projektes mittels FEM Rissspitzenbeanspruchungen in Abhängigkeit von der Auslenkung des Zylinders und angenommener Rissgrößen ermittelt. Diese finden als Zielgrößen in der weiteren Analyse Anwendung. Da eine einfach umzusetzende Lösung angestrebt wird, werden zusätzlich analytische Rechnungen an Ersatzgeometrien (halbunendliche Platte und Vollzylinder), aber mit den realen Spannungen am Bauteil durchgeführt. Es zeigt sich, dass die Ergebnisse wegen des Steifigkeitsunterschieds zwischen Bauteil und Ersatzgeometrie unvertretbar konservativ sind. Alternativ wird ein hybrides Konzept vorgestellt, für das die Modellparameter mittels FEM bestimmt werden. Es liefert sehr genaue Ergebnisse. Im Rahmen der analytischen Rechenvorschrift können die Lösungen auf andere Werkstoffe übertragen werden, ohne dass zusätzliche FEM-Analysen notwendig sind.
Am Beispiel eines abgesetzten zylindrischen Bauteils (Achsschenkel) werden Probleme der analytischen bruchmechanischen Bauteilbewertung diskutiert. Als Basis-philosophie wird ein Fail Safe-Kriterium (kontrolliertes Versagen) angesetzt. Die Forderung ist, dass sich der Achsschenkel, bevor er bricht, in einem Ausmaß plastisch verformen kann, bei dem der Fahrer bemerkt, dass mit seinem Fahrzeug etwas nicht in Ordnung ist. Um das zu gewährleisten, muss der Werkstoff einen bestimmten Riss-widerstand aufweisen. Dazu werden im hier vorgestellten ersten Teil des Projektes mittels FEM Rissspitzenbeanspruchungen in Abhängigkeit von der Auslenkung des Zylinders und angenommener Rissgrößen ermittelt. Diese finden als Zielgrößen in der weiteren Analyse Anwendung. Da eine einfach umzusetzende Lösung angestrebt wird, werden zusätzlich analytische Rechnungen an Ersatzgeometrien (halbunendliche Platte und Vollzylinder), aber mit den realen Spannungen am Bauteil durchgeführt. Es zeigt sich, dass die Ergebnisse wegen des Steifigkeitsunterschieds zwischen Bauteil und Ersatzgeometrie unvertretbar konservativ sind. Alternativ wird ein hybrides Konzept vorgestellt, für das die Modellparameter mittels FEM bestimmt werden. Es liefert sehr genaue Ergebnisse. Im Rahmen der analytischen Rechenvorschrift können die Lösungen auf andere Werkstoffe übertragen werden, ohne dass zusätzliche FEM-Analysen notwendig sind.
The weldability of stainless steels is largely controlled by the chemical composition, and alloys with ferritic or ferritic-austenitic solidification show the highest resistance to hot cracking. As the resulting phase balance also
affects the final properties, it may be beneficial to both foresee and measure the weld metal ferrite content. The WRC ’92 constitution diagram is currently the most accurate prediction tool available, but it does not take the cooling rate into consideration and the precision may be less accurate for stainless steels with high ferrite numbers (FN). This study aims to validate the reliability of the WRC ’92 diagram for weld metals with FN > 50. The chemical composition was altered through gas tungsten arc welding (GTAW) of UNS S32205 with ER347 filler wire that had been PVD-coated with either niobium (Nb), copper (Cu), nickel (Ni), manganese (Mn), carbon (C), or silicon (Si). The actual ferrite content was assessed using image analysis, FERITSCOPE® and X-ray diffraction (XRD). While the WRC ’92 diagram predictions were deemed accurate to acceptable for Ni, Si, and Mn, notable deviations were observed for Nb, Cu, and C. The FeriteScope exhibited a consistent trend with image analysis, though the values were higher, and scatter was wider, and the conversion factor is open for discussion. The lowest accuracy and largest spread were obtained using non-contact XRD, rendering it unsuitable for ferrite measurements of welds.
Offshore-Windenergieanlagen erfordern Gründungskonzepte aus unterpulver-(UP-)geschweißten Dickblechen (bspw. der Güte S420ML). Während der Schweißfertigung kann eine zeitverzögerte wasserstoffunterstützte Kaltrissbildung auftreten, deren Bewertung aufgrund der Bauteilgröße von Offshore-Strukturen sehr komplex ist. Deswegen wurde eine bauteilähnliche Geometrie (Mock-Up) entwickelt, um reale Steifigkeitsverhältnisse auf den Labormaßstab zu übertragen. Zusätzliche Versteifungen simulieren die Wirkung einer Einspannung bzw. Schrumpfbehinderung der Schweißnaht. Über die Verwendung von Schweißpulvern mit definierter Feuchte wurden zudem ein Extremszenario der Wasserstoffaufnahme simuliert. Entsprechend der vorgegebenen Mindestwartezeit für die ZfP von bis zu 48 h wurde die Schweißnaht zerstörungsfrei mit Phased-Array-Ultraschall-Prüfung (PAUT) geprüft und die Eigenspannungen über Röntgendiffraktometrie (XRD) bestimmt. Zusätzlich wurde die Wasserstoffverteilung in der Schweißverbindung numerisch simuliert. Außer zulässigen Defekten (wie Poren), wurde keine verzögerte Kaltrissbildung in den Mock-Ups festgestellt, was auf hohe Rissbeständigkeit hindeutet.
Eine nachhaltige und ressourceneffiziente Fertigung und Errichtung von Windenergieanlagen, sowohl auf See als auch an Land, erfordert zunehmend den Einsatz moderner hochfester Feinkornbaustähle. Werden nach dem Schweißen dieser hochfesten Konstruktionen unzulässige Defekte detektiert, sind nach geltenden Verarbeitungsrichtlinien die defekten Bereiche durch lokales Ausfugen und anschließendes Schweißen zu reparieren. Fehlende Informationen zu adäquaten Reparaturkonzepten in den Regelwerken bedingen oftmals eine unzureichende Berücksichtigung dabei auftretender zusätzlicher Beanspruchungen durch die erhöhte Schrumpfbehinderung der Ausfugenuten. Zusätzlich haben die ausführenden Betriebe vielfach kaum Kenntnis über die Degradation angrenzender Gefüge durch thermische Ausfugeprozesse und erneutes Schweißen, die in diesem Zusammenhang besonders bei den hochfesten Stählen als kritisch anzusehen sind. Das aktuelle Forschungsvorhaben der BAM (FOSTA P1311/IGF-Nr.20162N) fokussiert hierfür systematisch bauteilrelevante Untersuchungen zu den schweißbedingten Beanspruchungen und Gefügeveränderungen bei der Reparatur von hochfesten Schweißverbindungen. Wesentlich sind hierbei der Einfluss der Schrumpfbehinderung, der Wärmeführung beim Schweißen und Ausfugen sowie der Reparaturzyklenanzahl und die metallurgischen Aspekte bei den hochfesten Güten S500MLO für zukünftige Offshore-Anwendungen und S960QL für aktuelle Mobilkrananwendungen. Aufbauend auf einigen Studien zur schweißbedingten Beanspruchung hochfester Stähle zeigt der vorliegende Beitrag die Identifikation geeigneter Probengeometrien und Schweißdetails mittels numerischer und experimenteller Analysen. Dadurch wird die Übertragbarkeit der vorgestellten Schweißexperimente und Ergebnisse hinsichtlich der resultierenden Schweißeigenspannungen auf reale Reparaturfälle im Bereich des hochfesten Stahlbaus sichergestellt. Es zeigt sich in Übereinstimmung mit früheren Ergebnissen eine signifikante Erhöhung der Beanspruchungen an den variierten schlitzförmigen Prüfnähten. Das Eigenspannungsniveau sowohl im Schweißgut als auch in der WEZ korreliert mit dem Einspanngrad. Mit dem Ziel beanspruchungs- und werkstoffgerechte Reparaturkonzepte zu erarbeiten, sind zum einen geringere Wärmeinbringungen, besonders durch niedrige Zwischenlagentemperaturen und Einspannbedingungen anzustreben, um hohe Beanspruchungen und kritische Gefügedegradationen im Reparaturbereich zu vermeiden. Dies wird durch systematische Untersuchungen zum Ausfugen und Schweißen sowie letztlich dem Transfer von Verarbeitungsempfehlungen für die Anwender und Richtlinien erreicht.
Eine nachhaltige und ressourceneffiziente Fertigung und Errichtung von Windenergieanlagen, sowohl auf See als auch an Land, erfordert zunehmend den Einsatz moderner hochfester Feinkornbaustähle. Werden nach dem Schweißen dieser hochfesten Konstruktionen unzulässige Defekte detektiert, sind nach geltenden Verarbeitungsrichtlinien die defekten Bereiche durch lokales Ausfugen und anschließendes Schweißen zu reparieren. Fehlende Informationen zu adäquaten Reparaturkonzepten in den Regelwerken bedingen oftmals eine unzureichende Berücksichtigung dabei auftretender zusätzlicher Beanspruchungen durch die erhöhte Schrumpfbehinderung der Ausfugenuten. Zusätzlich haben die ausführenden Betriebe vielfach kaum Kenntnis über die Degradation angrenzender Gefüge durch thermische Ausfugeprozesse und erneutes Schweißen, die in diesem Zusammenhang besonders bei den hochfesten Stählen als kritisch anzusehen sind. Das aktuelle Forschungsvorhaben der BAM (FOSTA P1311/IGF-Nr.20162N) fokussiert hierfür systematisch bauteilrelevante Untersuchungen zu den schweißbedingten Beanspruchungen und Gefügeveränderungen bei der Reparatur von hochfesten Schweißverbindungen. Wesentlich sind hierbei der Einfluss der Schrumpfbehinderung, der Wärmeführung beim Schweißen und Ausfugen sowie der Reparaturzyklenanzahl und die metallurgischen Aspekte bei den hochfesten Güten S500MLO für zukünftige Offshore-Anwendungen und S960QL für aktuelle Mobilkrananwendungen. Aufbauend auf einigen Studien zur schweißbedingten Beanspruchung hochfester Stähle zeigt der vorliegende Beitrag die Identifikation geeigneter Probengeometrien und Schweißdetails mittels numerischer und experimenteller Analysen. Dadurch wird die Übertragbarkeit der vorgestellten Schweißexperimente und Ergebnisse hinsichtlich der resultierenden Schweißeigenspannungen auf reale Reparaturfälle im Bereich des hochfesten Stahlbaus sichergestellt. Es zeigt sich in Übereinstimmung mit früheren Ergebnissen eine signifikante Erhöhung der Beanspruchungen an den variierten schlitzförmigen Prüfnähten. Das Eigenspannungsniveau sowohl im Schweißgut als auch in der WEZ korreliert mit dem Einspanngrad. Mit dem Ziel beanspruchungs- und werkstoffgerechte Reparaturkonzepte zu erarbeiten, sind zum einen geringere Wärmeinbringungen, besonders durch niedrige Zwischenlagentemperaturen und Einspannbedingungen anzustreben, um hohe Beanspruchungen und kritische Gefügedegradationen im Reparaturbereich zu vermeiden. Dies wird durch systematische Untersuchungen zum Ausfugen und Schweißen sowie letztlich dem Transfer von Verarbeitungsempfehlungen für die Anwender und Richtlinien erreicht.
Bei der Montage von Stahlkonstruktionen kommt es trotz anforderungsgerechter schweißtechnischer Fertigung vereinzelt zur Detektion von unzulässigen Unregelmäßigkeiten im Schweißbereich. Die Verarbeitungsregelwerke empfehlen das lokale thermische Ausfugen betroffener Bereiche und erneutes Schweißen, geben aber aufgrund fehlender wissenschaftlich fundierter Untersuchungen kaum Informationen zu adäquaten Reparaturkonzepten. Dies betrifft insbesondere die Berücksichtigung und Optimierung resultierender schweißbedingter Beanspruchungen durch hohe Schrumpfbehinderungen der Ausfugenuten sowie der Gefügedegradation angrenzender Bereiche durch das Ausfugen und erneute Schweißen. Gerade bei hochfesten Stahlgüten ergeben sich dadurch häufig reduzierte mechanische Eigenschaften und zusätzliche schweißbedingte Beanspruchungen sowie erneut auftretende Nahtdefekte.
Deshalb wurden für das Forschungsvorhaben systematische bauteilrelevante Untersuchungen der schweißbedingten Beanspruchungen und Gefügeveränderungen reparierter Schweißnähte in Abhängigkeit von der Schrumpfbehinderung und Wärmeführung beim Schweißen und Ausfugen sowie von der Reparaturzyklenanzahl durchgeführt. Die Untersuchungsergebnisse zeigen auf, welche Faktoren sich für eine Beanspruchungsreduzierung auch bei hohen Einspannbedingungen eignen und wie eine Degradation des Gefüges und der Eigenschaften der Schweißnaht sowie wiederholte Schweißnahtdefekte in der Reparaturnaht vermieden werden können. Insbesondere können mittels adaptiver Wärmeführung geringere schweißbedingte Beanspruchungen in den Reparaturschweißnähten bewirkt werden. Bauteilversuche sichern zudem die Übertragbarkeit der Schweißexperimente in die Praxis ab.
Aufgrund der Erkenntnisse konnten Empfehlungen für beanspruchungs- und werkstoffgerechte Reparaturkonzepte abgeleitet und ausgesprochen werden. Die Analysen wurden an den hochfesten Stahlgüten S500MLO für den Offshore-Bereich und S960QL für den Mobilkranbau realisiert. Damit wird insbesondere der wirtschaftlichen Fertigung hocheffizienter Konstruktionen für Windenergieanlagen und hochfester Strukturen, die für deren Errichtung notwendig sind, Rechnung getragen.
So bieten die Forschungsergebnisse eine wesentliche Grundlage für die Weiterentwicklung entsprechender Normen und Regelwerke. Damit können letztlich Schäden und zumeist teure Nacharbeiten verhindert und eine verbesserte Ausnutzung des hohen Festigkeitspotentials hochfester Stähle erreicht werden. Gerade auch KMU können mit Blick auf die Kosten für Fertigung, Schweißarbeit und Material von den Erkenntnissen beim Einsatz hochfester Stähle, die für eine effiziente Realisierung der Energiewende in Deutschland notwendig sind, profitieren.
Das DVS-Vorhaben 01.3211 „Herstellung beanspruchungsgerechter Oberflächen durch Kombination innovativer additiver und abtragender Fertigungsschritte an hochbelasteten Komponenten“ ist ein Kooperationsprojekt der Bundesanstalt für Materialforschung und -prüfung (BAM) und dem Institut für Schweißtechnik und Trennende Fertigungsverfahren (ISAF) der Technischen Universität Clausthal. Das Übergeordnete Projektziel ist das Erlangen von Erkenntnissen für eine sichere und wirtschaftliche, kombinierte additive und abtragende Fertigung aus kostenintensiven Werkstoffen hochbelasteter Komponenten insbesondere für KMU. Dabei stehe die beiden Werkstoffe CoCr26Ni9Mo5W (2.4681) und FeNi36 (1.3912) im Fokus. Mittels Modifikation der Schweißzusätze sind homogen und isotrop ausgeprägte Werkstoffeigenschaften und eine Erhöhung der Prozessstabilität und Fertigungsfreiheitsgrade bei der additiven Fertigung erzielbar. Darüber hinaus wird der Einfluss nachfolgender abtragender Bearbeitungsschritte des ultraschallunterstützen und des konventionellen Fräsprozesses untersucht. Es wird eine kurze Übersicht über die bisher erzielten Ergebnisse gegeben. Thematisiert wird sowohl die Mikrostruktur und Härte als auch Ergebnisse der Zerspanbarkeit hinsichtlich der resultierenden Zerspankraft, der Temperatur sowie der erzielten Rauheit unterschiedlicher Modifikationen der FeNi36- und der CoCr-Legierung.
Dieses Dokument fasst den Projekfortschritt des BAM-Projektes "Entwicklung von Wärmenachbehandlungsstrategien zur Vermeidung von Spannungsrelaxationsrissen" im Rahmen des Fachausschusses 1 "Schweißmetallurgie" des DVS e.V. für das Projektjahr 2021 zusammen und stellt die wichtigsten Ergebnisse in Kurzform vor.
Das DVS-Vorhaben 01.3211 „Herstellung beanspruchungsgerechter Oberflächen durch Kombination innovativer additiver und abtragender Fertigungsschritte an hochbelasteten Komponenten“ ist ein Kooperationsprojekt der Bundesanstalt für Materialforschung und -prüfung (BAM) und dem Institut für Schweißtechnik und Trennende Fertigungsverfahren (ISAF) der Technischen Universität Clausthal. Das Übergeordnete Projektziel ist das Erlangen von Erkenntnissen für eine sichere und wirtschaftliche, kombinierte additive und abtragende Fertigung aus kostenintensiven Werkstoffen hochbelasteter Komponenten insbesondere für KMU. Dabei stehe die beiden Werkstoffe CoCr26Ni9Mo5W (2.4681) und FeNi36 (1.3912) im Fokus. Mittels Modifikation der Schweißzusätze sind homogen und isotrop ausgeprägte Werkstoffeigenschaften und eine Erhöhung der Prozessstabilität und Fertigungsfreiheitsgrade bei der additiven Fertigung erzielbar. Darüber hinaus wird der Einfluss nachfolgender abtragender Bearbeitungsschritte des ultraschallunterstützen und des konventionellen Fräsprozesses untersucht. Die mit dem Forschungsvorhaben verbundenen Nutzen für KMU sind die Stärkung der Innovationsfähigkeit und der Wirtschaftlichkeit sowie die Erhöhung der Wettbewerbsfähigkeit. In AP-2 wurden die Legierungsmodifikationen des CoCr-Ausgangswerkstoffes sowie des FeNi36-Ausgangswerkstoffes abgeschlossen. In AP-4 wurden Zerspanversuche an den Modifikationen des FeNi36-Ausgangswerkstoffes sowie des CoCr-Ausgangswerkstoffes gefahren. Ferner wurden die zur Übertragung auf den MSG-Prozess ausgewählten Modifikationen beider Ausgangswerkstoffe vorgestellt.
Das DVS-Vorhaben 01.3211 „Herstellung beanspruchungsgerechter Oberflächen durch Kombination innovativer additiver und abtragender Fertigungsschritte an hochbelasteten Komponenten“ ist ein Kooperationsprojekt der Bundesanstalt für Materialforschung und -prüfung (BAM) und dem Institut für Schweißtechnik und Trennende Fertigungsverfahren (ISAF) der Technischen Universität Clausthal. Das Übergeordnete Projektziel ist das Erlangen von Erkenntnissen für eine sichere und wirtschaftliche, kombinierte additive und abtragende Fertigung aus kostenintensiven Werkstoffen hochbelasteter Komponenten insbesondere für KMU. Dabei stehe die beiden Werkstoffe CoCr26Ni9Mo5W (2.4681) und FeNi36 (1.3912) im Fokus. Mittels Modifikation der Schweißzusätze sind homogen und isotrop ausgeprägte Werkstoffeigenschaften und eine Erhöhung der Prozessstabilität und Fertigungsfreiheitsgrade bei der additiven Fertigung erzielbar. Darüber hinaus wird der Einfluss nachfolgender abtragender Bearbeitungsschritte des ultraschallunterstützen und des konventionellen Fräsprozesses untersucht. Die mit dem Forschungsvorhaben verbundenen Nutzen für KMU sind die Stärkung der Innovationsfähigkeit und der Wirtschaftlichkeit sowie die Erhöhung der Wettbewerbsfähigkeit. In AP-2 wurden die Legierungsmodifikationen des CoCr-Ausgangswerkstoff abgeschlossen und weitere Legierungsmodifikationen des FeNi36-Ausgangswerkstoffes erstellt. In AP-4 wurden erste Zerspanversuche an den Modifikationen des FeNi36-Ausgangswerkstoffes gefahren. Ferner wurden erste Eigenspannungsanalysen an schlichtgefrästen Proben durchgeführt.
Das DVS-Vorhaben 01.3211 „Herstellung beanspruchungsgerechter Oberflächen durch Kombination innovativer additiver und abtragender Fertigungsschritte an hochbelasteten Komponenten“ ist ein Kooperationsprojekt der Bundesanstalt für Materialforschung und -prüfung (BAM) und dem Institut für Schweißtechnik und Trennende Fertigungsverfahren (ISAF) der Technischen Universität Clausthal. Das Übergeordnete Projektziel ist das Erlangen von Erkenntnissen für eine sichere und wirtschaftliche, kombinierte additive und abtragende Fertigung aus kostenintensiven Werkstoffen hochbelasteter Komponenten insbesondere für KMU. Dabei stehe die beiden Werkstoffe CoCr26Ni9Mo5W (2.4681) und FeNi36 (1.3912) im Fokus. Mittels Modifikation der Schweißzusätze sind homogen und isotrop ausgeprägte Werkstoffeigenschaften und eine Erhöhung der Prozessstabilität und Fertigungsfreiheitsgrade bei der additiven Fertigung erzielbar. Darüber hinaus wird der Einfluss nachfolgender abtragender Bearbeitungsschritte des ultraschallunterstützen und des konventionellen Fräsprozesses untersucht. Die mit dem Forschungsvorhaben verbundenen Nutzen für KMU sind die Stärkung der Innovationsfähigkeit und der Wirtschaftlichkeit sowie die Erhöhung der Wettbewerbsfähigkeit. In AP-1 wurden Zerspanversuche am FeNi- und CoCr-Ausgangswerkstoff durchgeführt. Ziel der Versuche war in erster Linie die Identifikation geeigneter Fräswerkzeuge und -parameter. In AP-2 wurden die Legierungsmodifikationen des CoCr-Ausgangswerkstoffes durchgeführt und die Mikrostruktur sowie die Härte analysiert. In AP-4 wurden erste Zerspanversuche in Abhängigkeit der Legierungsmodifikation der CoCr-Legierung durchgeführt.
Das DVS-Vorhaben 01.3211 „Herstellung beanspruchungsgerechter Oberflächen durch Kombination innovativer additiver und abtragender Fertigungsschritte an hochbelasteten Komponenten“ ist ein Kooperationsprojekt der Bundesanstalt für Materialforschung und -prüfung (BAM) und dem Institut für Schweißtechnik und Trennende Fertigungsverfahren (ISAF) der Technischen Universität Clausthal. Das Übergeordnete Projektziel ist das Erlangen von Erkenntnissen für eine sichere und wirtschaftliche, kombinierte additive und abtragende Fertigung aus kostenintensiven Werkstoffen hochbelasteter Komponenten insbesondere für KMU. Dabei stehen die beiden Werkstoffe CoCr26Ni9Mo5W (2.4681) und FeNi36 (1.3912) im Fokus. Mittels Modifikation der Schweißzusätze sind homogen und isotrop ausgeprägte Werkstoffeigenschaften und eine Erhöhung der Prozessstabilität und Fertigungsfreiheitsgrade bei der additiven Fertigung erzielbar. Darüber hinaus wird der Einfluss nachfolgender abtragender Bearbeitungsschritte des ultraschallunterstützen und des konventionellen Fräsprozesses untersucht. Die mit dem Forschungsvorhaben verbundenen Nutzen für KMU sind die Stärkung der Innovationsfähigkeit und der Wirtschaftlichkeit sowie die Erhöhung der Wettbewerbsfähigkeit. In AP-1 wurden erste Zerspanversuche am CoCr-Ausgangswerkstoff durchgeführt. Ziel der Versuche war in erster Linie die Identifikation geeigneter Fräswerkzeuge und -parameter. In AP-2 wurden erste Legierungsmodifikationen des CoCr-Ausgangswerkstoffes durchgeführt und die Mikrostruktur sowie die Härte analysiert.
Das DVS-Vorhaben 01.3211 „Herstellung beanspruchungsgerechter Oberflächen durch Kombination innovativer additiver und abtragender Fertigungsschritte an hochbelasteten Komponenten“ ist ein Kooperationsprojekt der Bundesanstalt für Materialforschung und -prüfung (BAM) und dem Institut für Schweißtechnik und Trennende Fertigungsverfahren (ISAF) der Technischen Universität Clausthal. Das Übergeordnete Projektziel ist das Erlangen von Erkenntnissen für eine sichere und wirtschaftliche, kombinierte additive und abtragende Fertigung aus kostenintensiven Werkstoffen hochbelasteter Komponenten insbesondere für KMU. Dabei stehe die beiden Werkstoffe CoCr26Ni9Mo5W (2.4681) und FeNi36 (1.3912) im Fokus. Mittels Modifikation der Schweißzusätze sind homogen und isotrop ausgeprägte Werkstoffeigenschaften und eine Erhöhung der Prozessstabilität und Fertigungsfreiheitsgrade bei der additiven Fertigung erzielbar. Darüber hinaus wird der Einfluss nachfolgender abtragender Bearbeitungsschritte des ultraschallunterstützen und des konventionellen Fräsprozesses untersucht. Die mit dem Forschungsvorhaben verbundenen Nutzen für KMU sind die Stärkung der Innovationsfähigkeit und der Wirtschaftlichkeit sowie die Erhöhung der Wettbewerbsfähigkeit. In AP-3 wurden die Mikrostruktur der MSG-Schweißung der CoCr-Referenzlegierung untersucht. In AP-4 wurden Zerspanversuche an der MSG-Schweißung der CoCr-Referenzlegierung durchgeführt.
In vielen Anwendungen werden aufgrund zunehmender Anforderungen an den Widerstand gegenüber hohen, kombinierten mechanischen, tribologischen, thermischen und korrosiven Beanspruchungen Hochleistungsle¬gierungen eingesetzt. Den vielfach komplexen Bauteilstrukturen, herausfordernden Fertigungseigenschaften und der Erhöhung der Ressourceneffizienz lässt sich heute mit der additiven Fertigung (AM) begegnen, dem oftmals noch unzureichende Kenntnisse über die resultierende Homogenität und Anisotropie der speziellen Gefüge und den damit verbundenen Eigenschaften entgegensteht. Viele Anwendungen benötigen zudem definierte Oberflächen mit hohen Anforderungen an die Oberflächenintegrität, dem durch komplementären Einsatz von additiven und abtragenden Fertigungsschritten Rechnung getragen wird. Hochleistungslegierungen auf der Basis von Nickel oder Kobalt sind infolge der niedrigen Wärmeleitfähigkeit verbunden mit hoher Festigkeit und Zähigkeit äußerst herausfordernd mit Blick auf eine wirtschaftliche Zerspanung mit geometrisch bestimmter Schneide. Ein Vorhaben (IGF-Nr. 20.979 N/DVS-Nr. 1.3211) der BAM und TU Clausthal/ISAF befasst sich mit der Lösung dieser Problemstellung durch gezielte Beeinflussung des Gefüges mittels Modifikation der Schweißzusatzwerkstoffe und den Einsatz des ultraschallunterstützten Fräsens (US), bei gleichzeitiger Sicherstellung der geforderten Eigenschaften der untersuchten Werkstoffe. Im vorliegenden Beitrag werden für die beiden untersuchten FeNi und CoCr-Legierungen wesentliche Zusammenhänge zwischen ver¬schiedenen Legierungsmodifikationen, der entstehenden Gefüge¬morphologie und den Zerspanungseigenschaften von mittels PTA additiv gefertigter Proben dargestellt. Hierbei ließen sich Ti, Zr und Hf pulvermetallurgisch zu den jeweiligen Ausgangsschweißzusätzen hinzulegieren.
Bei der Montage von Stahlkonstruktionen kommt es trotz anforderungsgerechter schweißtechnischer Fertigung vereinzelt zur Detektion von unzulässigen Unregelmäßigkeiten im Schweißbereich. Die Verarbeitungsregelwerke empfehlen das lokale thermische Ausfugen betroffener Bereiche und erneutes Schweißen, geben aber aufgrund fehlender wissenschaftlich fundierter Untersuchungen kaum Informationen zu adäquaten Reparaturkonzepten. Dies betrifft insbesondere die Berücksichtigung und Optimierung resultierender schweißbedingter Beanspruchungen durch hohe Schrumpfbehinderungen der Ausfugenuten sowie der Gefügedegradation angrenzender Bereiche durch das Ausfugen und erneute Schweißen. Gerade bei hochfesten Stahlgüten ergeben sich dadurch häufig reduzierte mechanische Eigenschaften und zusätzliche schweißbedingte Beanspruchungen sowie erneut auftretende Nahtdefekte.
Deshalb sind für das Forschungsvorhaben systematische bauteilrelevante Untersuchungen der schweißbedingten Beanspruchungen und Gefügeveränderungen reparierter Schweißnähte in Abhängigkeit von der Schrumpfbehinderung und Wärmeführung beim Schweißen und Ausfugen sowie von der Reparaturzyklenanzahl geplant, mit dem Ziel Empfehlungen für beanspruchungs- und werkstoffgerechte Reparaturkonzepte abzuleiten. Hierfür sind gerade Analysen an hochfesten Stahlgüten S500 für den Offshore-Bereich und S960QL für den Mobilkranbau interessant, die zur Errichtung und Fertigung hocheffizienter Konstruktionen wie Windenergieanlagen notwendig sind. Die Erkenntnisse bieten eine Grundlage für entsprechende Normen und Regelwerke. Damit können letztlich Schäden und zumeist teure Nacharbeiten verhindert und eine verbesserte Ausnutzung des hohen Festigkeitspotentials hochfester Stähle erreicht werden. Gerade auch KMU können mit Blick auf die Kosten für Fertigung, Schweißarbeit und Material von den Erkenntnissen beim Einsatz hochfester Stähle, die für eine effiziente Realisierung der Energiewende in Deutschland notwendig sind, profitieren.
Die neue Generation von bainitischen Schmiedestählen bietet auf der einen Seite ein erhebliches Festigkeitspotenzial, das es im Sinne des Leichtbaus auch für zyklisch belastete Sicherheitsbauteile zu heben gilt. Auf der anderen Seite geht mit dieser Festigkeitssteigerung im Vergleich zu Vergütungsstählen ein Verlust an Duktilität und Zähigkeit einher. Am Beispiel des Demonstratorbauteils Achsschenkel ging das Forschungsvorhaben der Frage nach, wie ein Freigabeprozess zu gestalten ist, damit das Festigkeitspotenzial der neuen Stähle zuverlässig ausgenutzt werden kann. Als Ergebnis wird eine Vorgehensweise dargestellt, die den Eigenschaften der neuen Generation von Schmiedestählen Rechnung trägt, um den sicheren Betrieb der Komponenten zu gewährleisten.
Höherfester Feinkornbaustahl mit Streckgrenzen von 960 MPa findet in vielen Industriebranchen zunehmend Einsatz. Allerdings werden mit zunehmender Festigkeit deutlich höhere Anforderungen an deren schweißtechnische Verarbeitung gestellt. Die Sensibilität gegenüber einer Degradation der mechanischen Eigenschaften kann durch den beim Schweißen aufgenommenen diffusiblen Wasserstoff zunehmen. Eine mögliche wasserstoffunterstützte Kaltrissbildung ist die Folge. In dem Vortrag werden vergleichende Untersuchungen von konventionellem Übergangslichtbogen und modifiziertem Sprühlichtbogen mittels Implant-Test vorgestellt. Der Einsatz beider Lichtbögen führt zu ähnlichen kritischen Implantspannungen. Jedoch kommt es beim modifiziertem Sprühlichtbogen zu einer zeitverzögerten Rissbildung. Zudem unterscheidet sich die Bruchtopographie der beiden Fälle.