Self-mated magnesia stabilized zirconia (Mg-PSZ) ceramic sliding couples have been investigated at 100 N load (P0max= 1324 MPa) in oscillating sliding conditions in different humidity conditions in air and in hot steam. Temperatures have been varied up to 400 °C and pressures up to 6 bars. The results show that the wear behavior of MgO-ZrO2 under high Hertzian contact pressures is strongly dependent on temperature and is similar for both dry oscillating and oscillating in hot steam. However, although the evolution in wear rates on temperature is similar and the wear rates of MgO-ZrO2 plunged above 300 °C in hot steam and air by nearly three orders of magnitude, SEM micrographs revealed in hot steam at 400 °C smooth wear tracks. In contrast, hot steam enhanced the tribochemistry of self-mated alumina couples and reduced wear rates. Hot steam decreased the coefficients of friction of MgO-ZrO2 with increasing temperature, but not the wear rates.
Hydraulic oils are well established formulations developed around the pump test. Requirements for energy efficiency and also environmentally acceptable properties increased the demand for development. In the same time, system pressure and the used of servo-hydraulic vanes increased bringing specific formulations and materials to their limit.
The vane pump is a key component in hydraulic systems and many other tribosystems in hydraulic circuits operate under different tribological operating conditions. The concept for ranking of hydraulic oils consists in using existing SRV-based ASTM test methods for evaluation of friction, wear and extreme pressure properties: D6425, friction and wear of oils (homologue to DIN 51834-2), D7421, extreme pressure properties of oils and D7755, wear volumes of ball and disks (homologue to DIN 51834-3. The tribological properties are assessed under the regime of mixed/boundary lubrication The SRV-based concept of tribological profile generates the wear volumes on two triboelements (specimen) and the extreme pressure properties as well as the evolution of friction in the wear and extreme pressure load step test. Thus, the benchmark and validation of hydraulic oils bear on a wider range of tribological properties. Round robin test results using the aforementioned testing concept will be shown. Another outcome is tribological set limits for inclusion in hydrau¬lic oil speci¬fications.
Several phases, like Nb₄C₃, Nb₆C₅ and other short and long range ordered phases occur in the region of homogeneity of NbCₓ (0,75≤ x ≤1.0) in the binary phase diagram. Properties, like micro-hardness, hot hardness, sliding wear resistance, elastic modulus and toughness can be tailored by the C/Nb ratio, the addition of secondary carbides and the type of binder. Supporting results from different grades with varying C/Nb ratio or binder types were illuminated. Thus, the NbC system offers to producers a wider process window, than WC. The impact of These tailored properties on sliding wear and cutting performance was illuminated by tribological and machining results. Niobium is today largely available. NbC can be synthesized by carbothermal conversion of Nb₂O₅ or be metallurgically grown and leached out, provides comparably low friction in many relevant tribo-contacts and displays low wear. NbC and Nb₂O₅ have so far no REACH classification related to human toxicology and are not listed as substances of very high concern contrary to WO₃ and Co₃O₄.
Substituting tungsten carbide (WC) as cutting tools and for wear protection by niobium carbide (NbC)
(2016)
As a refractory carbide, niobium carbide (NbC) is today still a forgotten carbide with hidden properties, such as wear resistance, thus qualifying NbC for the group of tribological materials with enhanced wear resistance. Several phases, like Nb₄C₃, Nb₆C₅ and other short and long range ordered phases occur In the region of homogeneity of NbCx (0,75≤ x ≤1.0) in the binary phase diagram, which enable the tailoring of properties and offers a much wider process window than known from WC. The type binder (Co, Ni, NiMo) and its concentration as well as the sintering process (SPS, liquid phase sintering) determine the box “hardness-toughness”, which will be illuminated based on more than 100 grades.
The impact of these tailored properties on sliding wear (T= 22/400°C; v= 0,1-10 m/s) and cutting performance will be illuminated by tribological and machining results. Cutting test results under emulsion and coolant-free operation of cobalt and Fe3Al bonded, straight NbC versus WC based inserts against different alloys (C60, 100Cr6, 42CrMo4, X90CrMoV18, 300WA, GG35) will be highlighted.
In the present work it was shown that the tribologcal profiles of special model oxides under dry unidirectional sliding have shown, that sub-oxides have a contribution to the tribological behavior of carbides and cermets, when they are tribo-oxidatively formed, because their tribological profiles as monolithic materials are homologous in part or totally, or compete with hardmetals or cermets, depending from the operating conditions regarded.
Niobium is today largely available. The initial NbC grade was substoichiometric, SPS sintered and cobalt bonded. The NiMo-bonded stoichiometric NbC1.0 grades enable the substitution of cobalt by nickel, SPS by conventional sintering and NbC0.88 by NbC1.0 in view of functional properties. Nickel bonded NbC grades have improved toughnesses versus cobalt NbC grades, but lose hardness. NiMo and NiMo2C bonded NbC1.0 grades compensated the loss in hardness while keeping the toughness.
Niobium is today largely available. The initial NbC grade was substoichiometric, SPS sintered and cobalt bonded (NbC0.88-12Co SPS). The NiMo-bonded stoichiometric NbC1.0 grades enable the subtituion of cobalt by nickel, SPS by conventional sintering and NbC0.88 by NbC1.0 in view of functional properties. Nickel bonded NbC grades have improved toughnesses versus cobalt bonded NbC grades, but lose hardness. NiMo and NiMo2C bonded NbC1.0 grades compensated the loss in hardness while keeping the toughness.
Results of rolling contact fatigue (RCF) tests by balls-on-rod (BOR) method and two-roller methods have been compared to those by the balls-on-flat (BOF) method by using three different silicon nitride grades. The results suggest that the two-roller method could differentiate the bearing grade materials in terms of wear behavior.
Research and development of WC grades is 90 years ahead of niobium carbide-based hard materials, which showed already as light-weight and unexplored material a very high potential for many technical applications, especially for wear protection and machining. NbC evoluted recently from lab scale to pilot scale, especially in areas where established WC-based materials are causing economic, environmental or technical concerns. Benchmark trials of NbC-based hard metals indicated already a favorable performance in machining of steel components.
The differences between the binary phase diagrams W-C and Nb-C illuminate several parameters for tailoring the properties of NbC. In the region of homogeneity of NbCx, with Nb4C3 and Nb6C5 other Niobium carbide phases occur. Properties, like micro-hardness, hot hardness, sliding wear, elastic modules and toughness can be tailored by the C/Nb Ratio, secondary carbides and the type of binder. Supporting results from different grades with varying C/Nb ratio or binder types will be illuminated. Thus, the NbC system offers to producers a wider parameter window, than WC.
The present paper illuminates the metallurgical progress on niobium carbide based hard metal developments, which are characterized by: a.) the substitution of cobalt binder by nickel, b.) the change from SPS to conventional sintering and c.) by switching from lab to pilot scale. The toughness was increased in the frame of these develop¬ments without loosening the hardness level. Stoichiometric and sub-stoichiometric, submicron NbC powders were used. The hardness-toughness profile of NbC grades match those of WC and cermet grades. Apart from the aforementioned parameters, the properties depend from the powder processing and sintering conditions. The functional profile of NbC and WC grades bonded by cobalt and nickel are benchmarked by 4-point bending strength, elastic moduli and hot hardness until 1000°C, dry sliding wear (T= 22/400°C; v= 0,1-10 m/s), abrasive wear (G65) and cutting performances under emulsion and coolant-free turning and milling against different alloys (C60, 100Cr6, 42CrMo4, X90CrMoV18, 300WA, GG35).