Self-mated magnesia stabilized zirconia (Mg-PSZ) ceramic sliding couples have been investigated at 100 N load (P0max= 1324 MPa) in oscillating sliding conditions in different humidity conditions in air and in hot steam. Temperatures have been varied up to 400 °C and pressures up to 6 bars. The results show that the wear behavior of MgO-ZrO2 under high Hertzian contact pressures is strongly dependent on temperature and is similar for both dry oscillating and oscillating in hot steam. However, although the evolution in wear rates on temperature is similar and the wear rates of MgO-ZrO2 plunged above 300 °C in hot steam and air by nearly three orders of magnitude, SEM micrographs revealed in hot steam at 400 °C smooth wear tracks. In contrast, hot steam enhanced the tribochemistry of self-mated alumina couples and reduced wear rates. Hot steam decreased the coefficients of friction of MgO-ZrO2 with increasing temperature, but not the wear rates.
Research and development of WC grades is 90 years ahead of niobium carbide-based hard materials, which showed already as light-weight and unexplored material a very high potential for many technical applications, especially for wear protection and machining. NbC evoluted recently from lab scale to pilot scale, especially in areas where established WC-based materials are causing economic, environmental or technical concerns. Benchmark trials of NbC-based hard metals indicated already a favorable performance in machining of steel components.
In the present work it was shown that the tribologcal profiles of special model oxides under dry unidirectional sliding have shown, that sub-oxides have a contribution to the tribological behavior of carbides and cermets, when they are tribo-oxidatively formed, because their tribological profiles as monolithic materials are homologous in part or totally, or compete with hardmetals or cermets, depending from the operating conditions regarded.
The present paper illuminates the metallurgical progress on niobium carbide based hard metal developments, which are characterized by: a.) the substitution of cobalt binder by nickel, b.) the change from SPS to conventional sintering and c.) by switching from lab to pilot scale. The toughness was increased in the frame of these develop¬ments without loosening the hardness level. Stoichiometric and sub-stoichiometric, submicron NbC powders were used. The hardness-toughness profile of NbC grades match those of WC and cermet grades. Apart from the aforementioned parameters, the properties depend from the powder processing and sintering conditions. The functional profile of NbC and WC grades bonded by cobalt and nickel are benchmarked by 4-point bending strength, elastic moduli and hot hardness until 1000°C, dry sliding wear (T= 22/400°C; v= 0,1-10 m/s), abrasive wear (G65) and cutting performances under emulsion and coolant-free turning and milling against different alloys (C60, 100Cr6, 42CrMo4, X90CrMoV18, 300WA, GG35).
The present work deals with Niobcarbid (NbC). Strategic reflections on tungsten carbide and more and more stringent toxicological restrictions for cobalt associated for both with spiraling stock market prices have attracted recently some attention for Niobium carbide as a substitute for tungsten carbide in machining.
The tribological behavior of neat and filled PEEK and PEKK composites were compared in air and vacuum conditions. Very low friction and wear coefficient were obtained at low sliding speed while severe wear occurred at high speed. Experimental results are discussed by analysing the transfer film and wear debris.
The focus of this study is to evaluate the influence of hydrogen on the friction and wear behavior of a wide range of polymer materials. Thereby, the tribological performance of filled und unfilled polymers from different suppliers were compared at room temperature in air and hydrogen gas (H2) as well as in liquid hydrogen at -235°C (LH2).
The tribological characteristics of pure and graphite filled polymers were investigated in gaseous hydrogen at ambient temperatures and in LH2 at -253°C. It could be shown that the tribological properties of PI and PEEK materials is related to the formation of a transfer film. The influence of both hydrogen and cryogenic temperatures will be discussed in the presentation.
Safety and reliability are the major challenges to face for the development and acceptance of hydrogen technology. It is therefore crucial to study deeply material compatibility, in particular polymer materials that are directly in contact with hydrogen. This paper presents an experimental study on the fretting wear behavior of two types of cross-linked hydrogenated acrylonitrile butadiene rubbers against 316L steel ball in hydrogen environment. Furthermore, aging experiments were conducted for 7 days under static conditions in 100 MPa hydrogen. the influences of hydrogen pressure as well as the aging exposure on the fretting behavior are discussed by means of surface analyses along with the material properties.
This lecture deals with the sliding behaviour of polymer materials in hydrogen environment. After a short introduction of the hydrogen activities at BAM, the tribological performances of polymer materials in gaseous hydrogen are presented and compared with air and vacuum environment. The second part focusses on the influence of the counterface materials in hydrogen. Finally, the last section is dedicated to experiments liquid hydrogen.
This lecture deals with the sliding behaviour of polymer composites in vacuum environment. At first, the effect of the polymer matrix and solid lubricants such as graphite and MoS2 are presented. The second part focusses on the influence of the residual pressure with experimental results obtained in high and ultrahigh vacuum.
The focus of this study is to evaluate of hydrogen on the friction and wear behavior of a wide range of polymer materials. Thereby, the tribological performance of filled and unfilled polymers from different suppliers were compared at room temperature in air and hydrogen gas (H2) as well as in liquid hydrogen at -253°C (LH2).
This lecture deals with the friction and wear of polymeric materials at cryogenic temperatures. The first part is dedicated to the low temperature properties of polymers and cryogenic environment as well as an introduction to cryotribology and friction models. The second part presents some experimental results, focusing on the effect of polymer composition, cryogenic media and stick-slip behaviour.
The tribological characteristics of pure and graphite filled polymers were investigated in gaseous hydrogen at ambient temperatures and in LH2 at -253°C. It could be shown that the tribological properties of PI and PEEK materials is related to the formation of a transfer film. The influence of both hydrogen and cryogenic temperatures will be discussed in the presentation.