Ingenieurwissenschaften und zugeordnete Tätigkeiten
Filtern
Dokumenttyp
- Vortrag (41) (entfernen)
Referierte Publikation
- nein (41)
Schlagworte
- Residual stress (41) (entfernen)
Organisationseinheit der BAM
- 8 Zerstörungsfreie Prüfung (23)
- 8.5 Röntgenbildgebung (23)
- 9 Komponentensicherheit (19)
- 9.4 Integrität von Schweißverbindungen (19)
- 9.2 Versuchsanlagen und Prüftechnik (4)
- 5 Werkstofftechnik (3)
- 5.2 Metallische Hochtemperaturwerkstoffe (3)
- 3 Gefahrgutumschließungen; Energiespeicher (2)
- 3.0 Abteilungsleitung und andere (2)
- 8.0 Abteilungsleitung und andere (2)
Eingeladener Vortrag
- nein (41)
While additive manufacturing (AM) is blossoming in nearly every industrial field, and the most different process are being used to produce components and materials, little attention is paid on the safety concerns around AM materials and processes.
Leveraging on our leading expertise in non-destructive testing (NDT) and materials characterization, we approach AM at BAM under two important viewpoints: first the on-line monitoring of the process and of the product, second the evolution of the (unstable) microstructure of AM materials under external loads.
These two subjects are the core of the two new-born internal projects ProMoAM and AGIL, respectively.
A detailed view of the goals and the organization of these two projects will be given, together with the expected output, and some preliminary results.
Having been introduced almost two decades ago, Additive Manufacturing (AM) of metals has become industrially viable for a large variety of applications, including aerospace, automotive and medicine. Powder bed techniques such as Selective Laser Melting (SLM) based on layer-by-layer deposition and laser melt enable numerous degrees of freedom for the geometrical design. Developing during the manufacturing process, residual stresses may limit the application of SLM parts by reducing the load bearing capacity as well as induce unwanted distortion depending on the boundary conditions specified in manufacturing.
The residual stress distribution in IN718 elongated prisms produced by SLM was studied non-destructively by means of neutron (bulk) and laboratory X-ray (surface) diffraction. The samples with different scanning strategies, i.e. hatching length, were measured in as-built condition (on a build plate) and after removal from the build plate.
While surface stress fields seem constant for AB condition, X-ray diffraction shows stress gradients along the hatch direction in the RE condition. The stress profiles correlate with the distortion maps obtained by tactile probe measurements.
Neutron diffraction shows bulk stress gradients for all principal components along the main sample directions. We correlate the observed stress patterns with the hatch length, i.e. with its effect on temperature gradients and heat flow. The bulk stress gradients partially disappear after removal from the baseplate.
Together with surface scan utilizing a coordinate-measuring machine (CMM), it is possible to link the stress release to the sample distortion.
We finally propose an explanation of those stress profiles based on the deposition strategy.
The residual stress distribution of IN718 parts produced by Selective Laser Melting (SLM) technique was studied by means of neutron diffraction.
Two deposition hatching lengths were considered in the fabrication. Both lateral (building direction) and top (finishing) near-surface regions were characterized. Measurements on samples in as-built condition and after release from the plate proved the presence of stress gradients both in-plane and along the building direction.
As-built samples presented in top region a longitudinal stress relief for large hatching, whereas small one showed tensile stresses around (200MPa) in the middle, evolving towards compression at the tip of the sample (down to -300MPa). Towards the lateral edge, longitudinal stresses shifted also to compression. The transverse stresses for large hatching were relief in the middle, whereas for small hatching shifted to compression at the edge. As for the normal component, this was more homogenous: stress-relief was proved for large hatching and, in contrast, was in compression (-200MPa) for small hatching. In the building direction (lateral region from base plate to top) of the sample with large hatching all stress components showed tensile values near the base plate (particularly high for normal component around 300MPa), decreasing towards compression to the top, where they were almost released.
After release, in the top region, the longitudinal stress component for small hatching showed high compressive stresses in the central part (down to -250MPa). In contrast, for large hatching a stress relief was found. In the transversal direction, this behavior was inverted: a small hatching released stresses more effectively, while a large hatching presented high tensile stresses (around 200MPa). As for the normal component (i.e., building direction), the sample with small hatching was found in compression, while that with large hatching was stress-released or slightly in tension (around 100MPa). In the lateral surface region, all components showed similar behavior: a small hatching promoted high compressive stresses along the building direction, whereas a large hatching showed small tensile values at the bottom, which balance towards the top region. There is an overall shift of stresses in 3 directions towards tension when compared with as-built condition for top region. In contrast, the lateral region is stress-relief or shifted towards compression after cutting from baseplate.
In conclusion, hatching length parameter strongly influenced the 3D distribution of residual stress in SLM produced parts.
Independent from the interpass temperature residual stresses in longitudinal direction were lower than in transverse direction. This applies for the surface as well as for the bulk of the welds.
Residual stresses in the bulk were in general lower compared to stresses found on the surface.
Compressive residual stresses as a result of the martensite formation were formed in the bulk weld metal, only.
Independent from the LTT filler used high interpass temperatures were beneficial to reduce the stresses mainly in longitudinal direction.
Lower interpass temperatures tend to narrow the tensile zone in the weld metal but they also prevent the formation of compressive residual stresses.
Independent from the interpasstemperature residual stresses in longitudinal direction were lower than in transverse direction. This applies for the surface as well as for the bulk of the welds.
-Residual stresses in the bulk were in general lower compared to stresses found on the surface.
•Compressive residual stresses as a result of the martensite formation were formed in the bulk weld metal, only.
•Independent from the LTT filler used high interpasstemperatures were beneficial to reduce the stresses mainly in longitudinal direction.
•Lower interpasstemperatures tend to narrow the tensile zone in the weld metal but they also prevent the formation of compressive residual stresses.
Additive manufacturing (AM) technologies are experiencing an exceedingly rapid growth, driven by their potential through layer wise deposition for transformational improvements of engineering design, leading to efficiency and performance improvements. Laser Powder Bed Fusion (LPBF) is an Additive Manufacturing (AM) method which permits the fabrication of complex structures that cannot otherwise be produced via conventional subtractive manufacturing methods. Nevertheless, the rapid cooling rates associated with this process results in the formation of significant and complex residual stress (RS) fields. A large body of both experimental and simulation research has been dedicated in recent years to the control and mitigation of RS in AM. In order to validate simulations with the end goal of being able to model the residual stress state in AM components and to devise strategies for their reduction during manufacturing, experimental methods need to be able to accurately determine 3D residual stresses fields in complex geometries. Several destructive and non-destructive methods can be used to analyze the RS state, the choice of which depends on the geometry and the information required. Diffraction-based methods using penetrating neutron and synchrotron X-rays at large scale facilities offer the possibility to non-destructively spatially resolve both surface and bulk residual stresses in complex components and track their changes following applied thermal or mechanical loads. This presentation will overview the success stories of using large scale facilities by the BAM for the characterization of residual stresses in additively manufactured metallic alloys. In particular, the study of the influence of process parameters on the residual stress state and the relaxation of these stresses through heat treatment will be presented. However there remains challenges to overcome particularly of the hypotheses underlying the experimental determination of residual stresses, which will be discussed.
Metal Additive manufacturing (AM) technologies such as Laser Powder Bed Fusion (LPBF) enable the fabrication of complex structures, giving rise to potential improvements in component and manufacturing efficiency. However, the processes are typically characterized by the generation of high magnitude residual stress (RS) which can have detrimental consequences for subsequent applications. Therefore, the characterization of these RS fields and the understanding of their formation and mitigation through optimized processing is crucial for the wider uptake of the technology. Due to the potential complex nature and high value of components manufactured by LPBF, it is important to have suitable characterisation methods which can determine the spatial variations of RS in a non-destructive manner. Neutron diffraction is considered to be the best suited for these requirements. However, the microstructures developed in the complex thermal cycles experience in the production can pose challenges to the ND method for RS analysis. The BAM has conducted significant research over the past years to overcome these obstacles, enabling higher confidence in the RS determined in LPBF materials by neutron diffraction. This contribution will overview some of these advancements made recently at European neutron sources including on Stress-Spec at FRM2/MLZ.
Residual stresses in Laser Beam Melting (LBM) – Critical Review and outlook of activities at BAM
(2019)
Additive manufacturing (AM) technologies have experienced an exceedingly rapid growth, which is coupled with the knowledge about the resulting material properties and performance. In particular, residual stress (RS) was soon recognized as an important issue in AM parts, such that parts are usually subjected to a post build-heat-treated. Significant effort has been spent on simulations of RS in AM, especially using finite element methods. As a consequence, the experimental determination of RS has thereby become increasingly important as a validation tool for simulations, as well as a method for assessing the influence of process parameters. In particular, diffraction methods, which are fundamentally non-destructive, offer enormous possibilities to gain knowledge on the residual stress state in real components, since synchrotron radiation and neutrons can penetrate even heavy metals up to several millimeters or centimeters, respectively. Indeed, significant progress has been achieved, in the understanding of the origins of the RS fields as a function of process parameters, as well as their stability under thermal and/or mechanical exposure.
In this paper, a few success stories will be outlined. It will be shown how the determination of RS in metallic parts (with the focus on those produced by laser powder bed fusion) has even revealed that process parameters that were previously considered unimportant (e.g. the position and orientation on the base plate) play a major role in the onset of residual stress accumulation.
However, while RS characterization is starting to be considered in the component design, deposition strategy (e.g. build plate temperature), and even in the definition of the relevant metric to assess the quality of a part, much is still to be investigates about the hypotheses underlying its experimental determination. Therefore, some aspects to be aware of, or even those which to date are unclear, will also be discussed. These include the determination of the stress-free reference and of the principal axes of stress. All of these aspects will lead towards a comprehensive understanding of the process-structure-performance relationships in AM materials and parts.
An overview of the BAM funed Focus Area Materials Project "AGIL" will be presented. AGIL focussed on the stdiy of the ageing characteristics of additively manufactured austenitic stainless steel with a "powder to mechanical failure" Approach. Recent Highlights are presented and a perspective for future studies.
Residual stresses Analysis in Additively Manufactured alloys using neutron diffraction (L-PBF)
(2023)
An overview of recent progress at BAM of residual stress analysis in additively manufactured, in particular Laser Powder Bed Fusion of metallics materials, using neutron diffraction will be presented. This will cover important topics of the stress-free reference, the diffraction elastic moduli and principal stress determination.
At the Bundesanstalt für Materialforschung und –prüfung (BAM), within a recent research project, the aging process of composite pressure vessels is investigated in order to be able to give more accurate lifetime predictions in future. All investigations are primarily based on type III pressure vessels consisting of an aluminium tank which is fully wrapped with carbon fibre reinforced plastics. Research is focused on residual stresses which are induced into the pressure vessel during manufacturing process in order to increase high cycle fatigue. However, with increasing lifetime residual stress conditions of type III pressure vessels change. For measuring and monitoring inner stress conditions, the application of a non-destructive measurement method is aspired.
Within this paper, the potential of an experimental modal analysis is tested to determine aging and degradation effects of pressure vessels. Based on this method, information about changes of the residual stresses can be obtained via an analysis of the modal parameters. Realizing this, first a finite element model is used to prove and evaluate potential capability and validity for the application of an experimental modal analysis. Based on this, a test bench is set up and successively optimized in its accuracy and efficiency. The sensitivity of the applied measurement technique is experimentally evaluated via measuring multiple prestress modified pressure vessels. Furthermore, a selection of prestress modified pressure vessels is monitored via the presented method. Finally, experimentally obtained results are interpreted and evaluated with the help of numerically gained finding.
Due to high specific stiffness, fibre reinforced plastics are the dominant material group for the design of mobile pressure vessels. At the Federal Institute of Materials Research and Testing (BAM) aging process of composite pressure vessels is studied to be able to give more accurate lifetime predictions in future. Investigations are based on type III breathing air cylinders consisting of an aluminium tank which is fully wrapped with carbon fibre reinforced plastics. Goal is to detect changes of residual stresses over life time which directly affect fatigue strength. Within this paper an approach is presented to monitor residual stresses via an experimental modal analysis (EMA). First, the influence of changed stress conditions on modal parameters is analysed via a numerical study. Secondly, a test bench for an EMA is set up. To be able to analyse cylinders of different prestress condition, several specimens are prestress modified via high-temperature and high-pressure treatment. During modification processes, specimens are monitored via optical fibres to control prestress modifications. Through experimental measurements of the modified specimens via EMA changes in prestressing can be detected. Finally, validity and accuracy of the EMA is evaluated critically by comparing all numerically and experimentally obtained data.
Residual stresses are crucial when assessing the performance of welded components. The present work deals with the possibilities of transferring the real-life boundary conditions of welding, which influence the residual stress, into the laboratory. The possibilities of a test system with a load capacity of 2 MN specifically developed for online monitoring of stress formation and cracking are shown. Due to the structural design, global process, geometry and material-dependent stresses are induced, which can be quantified in-situ during welding and post weld heat treatment. Examples are presented how the conditions to be found during production are simulated in the laboratory. It is shown how welding residual stresses in high-strength steels are affected by the heat control. Elevated working temperatures significantly increase the tensile residual stresses in the heat affected zone (HAZ). The effect of mechanical stresses resulting from welding on stress relief cracking is demonstrated by the example of a creep resistant steel. Reheat cracks were monitored online during post weld heat treatment.
Carbon arc-air gouging is a common technology when repairing defects in welded structures. Often this technique is applied in repeated cycles even on the same location of the joint. Due to the multiple heat input by gouging and subsequent re-welding, the residual stresses are strongly influenced. This can become crucial when microstructure and mechanical properties are adversely affected by multiple weld reparations. Knowledge about the relation of gouging and residual stresses is scarce but important when high strength steels, which are sensitive to residual stresses, are processed. The present study shows the effect of repair welding on a high strength steel structural element. The weld and the heat affected zone were subjected to multiple thermal cycles by gouging and subsequent repair welding. The residual stresses were determined by X-ray diffraction at different positions along the joint. The results showed that the residual stress level has increased by the repair cycles. This is most pronounced for the heat affected zone. Adapted welding procedures may prevent detrimental residual stress distributions.
Residual stresses and distortions in welded I-girders for steel construction are relevant when evaluating the stability of steel beams and column members. The application of high strength steels allows smaller wall thicknesses compared to conventional steels. Therefore, the risk of buckling has to be considered carefully. Due to the lack of knowledge concerning the residual stresses present after welding in high strength steel components conservative assumptions of their level and distribution is typically applied. In this study I-girders made of steels showing strengths of 355 MPa and 690 MPa were welded with varying heat input. Due to the dimension of the I-girders and the complex geometry the accessibility for residual stress measurement using X-ray diffraction was limited. Therefore, saw cutting accompanied by strain gauge measurement has been used to produce smaller sections appropriate to apply X-ray diffraction. The stress relaxation measured by strain gauges has been added to residual stresses determined by X-ray diffraction to obtain the original stress level and distribution before sectioning. The combination of both techniques can produce robust residual stress values. From practical point of view afford for strain gauge application can be limited to a number of measuring positions solely to record the global amount of stress relaxation. X-ray diffraction can be applied after sectioning to determine the residual stresses with sufficient spatial resolution.
Observation of martensite formation by combined use of synchrotron diffraction and dilatometry
(2016)
Welding residual stress engineering by means of an adjusted martensite phase transformation would be highly attractive as detrimental tensile residual stresses may be prevented already during welding without time and cost intensive post processing. The present study shows a synchrotron diffraction analysis of a martensitic steel subjected to thermo-mechanical load cycles. Experiments were conducted regarding the microstructural strain response during the austenite to martensite transformation. The strains are a function of the temperature and the specific loads applied during cooling. The relation between the transformation plasticity of the material, the amount of martensite formed and the arising strains can thus be assessed. The lattice plane specific strains were compared to experimental findings from (macro) dilatation tests. It is shown that the microscopic material behavior differs remarkably from the one observed on the macroscopic scale, what leads to characteristic residual stresses in the material.
Welding residual stress engineering by means of an adjusted martensite phase transformation would be highly attractive as detrimental tensile residual stresses may be prevented already during welding without time and cost intensive post processing. The present study shows a synchrotron diffraction analysis of a martensitic steel subjected to thermo-mechanical load cycles. Experiments were conducted regarding the microstructural strain response during the austenite to martensite transformation. The strains are a function of the temperature and the specific loads applied during cooling. The relation between the transformation plasticity of the material, the amount of martensite formed and the arising strains can thus be assessed. The lattice plane specific strains were compared to experimental findings from (macro) dilatation tests. It is shown that the microscopic material behavior differs remarkably from the one observed on the macroscopic scale, what leads to characteristic residual stresses in the material.
Submerged arc welded (SAW) components of creep-resistant low-alloyed Cr-Mo-V steels are used for thick-walled heavy petrochemical reactors (wall-thickness up to 475 mm) as well as employed in construction of modern high-efficient fossil fired power plants. These large components are accompanied by significant restraints during welding fabrication, especially at positions of different thicknesses like welding of nozzles. As a result, residual stresses occur, playing a dominant role concerning so-called stress relief cracking (SRC) typically during post weld heat treatment (PWHT). Besides specific metallurgical factors (like secondary hardening due to reprecipitation), high tensile residual stresses are a considerable influence factor on SRC.
For the assessment of SRC susceptibility of certain materials mostly mechanical tests are applied which are isolated from the welding process. Conclusions regarding the influence of mechanical factors are rare so far. The present research follows an approach to reproduce loads, which occur during welding of real thick-walled components scaled to laboratory conditions by using Tests designed on different measures. A large-scale slit specimen giving a high restraint in 3 dimensions by high stiffness was compared to a medium-scale multi-pass welding U-Profile specimen showing a high degree of restraint in longitudinal direction and a small-scale TIG-remelted specimen. The small-scale specimens were additionally subjected to mechanical bending to induce loads that are found during fabrication on the real-scale in heavy components. Results show for all three cases comparable high tensile residual stresses up to yield strength with high gradients in the weld metal and the heat affected zone. Those high tensile stresses can be significant for cracking during further PWHT.