P92 is one of the important steels for super heater tubes used in combustion plants. However, in fossil fuel fired environments the formation of oxides and sulfides are challenging the material. To understand early corrosion mechanisms, which are important for process prediction, high temperature in-situ ageing experiments of Fe-Cr-Mn alloys in SO2 and SO2+H2O atmosphere were performed, applying energy dispersive X-ray diffraction (EDXRD) analysis.
Ferritic-martensitic high temperature alloys are widely used as boiler tube and heat exchanger materials in combustion based power plants. All technologies have in common that the applied materials are exposed to different temperatures, process pressures and reactive atmospheres which lead to a change of the material properties and a further degradation of the material.
To date corrosion analytics mainly proceeds via the use of various microscopic techniques and the analysis of the corrosion products after the reaction is completed. Comprehensive efforts have been made to study high temperature corrosion by the use of environmental SEM’s or in-situ TEM technologies. The here presented work will show a different approach to study high temperature gas corrosion in a multiple gas atmosphere by energy dispersive X-ray diffraction (EDXRD). For this technique high energetic white X-ray radiation (10-100 keV) was used as radiation source instead of conventional monochromatic radiation. It enables us to study crystallization procedures on short and medium time scales (1 min < t < 24 h) and the collection of Bragg-Signals of the phases of interest as a function of process time. Their occurrence can directly be correlated with thermodynamic and kinetic parameters. A special designed corrosion reactor was used to combine high temperature gas corrosion experiments with the collection of diffraction patter. The crystallization and reaction paths for oxide and sulfide formation was followed in-situ on Fe-Cr and Fe-Cr-Mn model alloys in a hot SO2 containing (T=650 °C) atmosphere.
The ageing of Fe-Cr model alloys in 0.5 % SO2 and 99.5 % Ar atmosphere was investigated to aim in a fundamental and systematic analysis of the combined oxidation and sulfidation mechanism. The crystallization and reaction paths for oxide and sulfide formation were followed in-situ by energy dispersive X-ray diffraction (EDXRD) in an early stage of corrosion (30 s – 24 h). For this technique, high energetic white synchrotron X-ray radiation (10-100 keV) was used as radiation source. Diffraction pattern were collected continuously in an early stage of corrosion up to 24 h during the complete ageing experiment.
The crystalline phases, growing on top of the coupons, were identified directly via their specific dhkl values. The evolution of the extracted integral intensities of specific reflections of the corrosion products as a function of time access direct information about the kinetics of the nucleation and growth. The results presented here show for iron with 2 wt% Cr wuestite formation first. Wuestite vanishes after 10 min of reaction only and magnetite and hematite appear. Magnetite formation proceeds simultaneously with sulfide formation. Sulfides growth proceeds after an incubation time, which differs for low alloyed (2 wt% Cr) and high alloyed (9 wt% Cr) material.
The ageing of Fe-Cr model alloys in 0.5 % SO2 and 99.5 % Ar atmosphere was investigated to aim in a fundamental and systematic analysis of the combined oxidation and sulfidation mechanism. The crystallization and reaction paths for oxide and sulfide formation were followed in-situ by energy dispersive X-ray diffraction (EDXRD) in an early stage of corrosion (30 s – 24 h). For this technique, high energetic white synchrotron X-ray radiation (10-100 keV) was used as radiation source. Diffraction pattern were collected continuously in an early stage of corrosion up to 24 h during the complete ageing experiment.
The crystalline phases, growing on top of the coupons, were identified directly via their specific dhkl values. The evolution of the extracted integral intensities of specific reflections of the corrosion products as a function of time access direct information about the kinetics of the nucleation and growth. The results presented here show for iron with 2 wt% Cr wuestite formation first. Wuestite vanishes after 10 min of reaction only and magnetite and hematite appear. Magnetite formation proceeds simultaneously with sulfide formation. Sulfides growth proceeds after an incubation time, which differs for low alloyed (2 wt% Cr) and high alloyed (9 wt% Cr) material.
Finally it can be summarized that this book fulfills its intention of providing theoretical background and examples for practical applications of coatings used for corrosion protection.
It can be recommended to those being interested in coatings, serving as an overview on aspects which needs to be considered when working with such systems.
Multielectrodes are arrays of single electrodes arranged in a particular geometry. In our work, all the single electrodes are identical stainless steel X5CrNi18-10 (1.4301) wire electrodes. Using a multielectrode analyser all single electrodes are connected via zero resistance ammeters, simulating a galvanically coupled single electrode surface. The advantage of the multielectrode analyser (MMA) is that the currents flowing between single electrodes can be measured. Thus, real-time maps can be generated indicating where anodic and cathodic areas lie on the surface of the multielectrode and how they behave.
The combination of the multielectrode analyser with the scanning electrochemical microscopy (SECM) enables the identification of corrosion sites and the detailed electrochemical analysis.
The interface of a metal substrate and a biofilm can differ significantly from the surrounding environment. Metal reducing bacteria (MRB), for instance, are capable of utilizing various metallic compounds as electron acceptors. Besides chromium, uranium and manganese as well as many organic compounds, Fe(III) is converted to the soluble form Fe(II) during the bacterial metabolism. This could lead to a weakening of the protective passivation layer on stainless steel and thereby facilitate microbiologically influenced corrosion (MIC). Even tough the processes of electron transfer are not yet entirely explained, the contribution of flavins and other humic substances as electron shuttles is widely discussed in the literature. Moreover, the adsorption of organic thin films on steel surfaces can lead to surface preconditioning and thus to changes in adhesion behavior of bacteria.
The aim of this work is to understand the chemical and electrochemical interaction mechanisms of MRB with steel surfaces by combining electrochemistry and surface-analytical techniques. The investigations primarily focus on the effect of pre-adsorbed thin organic films and self-assembled monolayers (SAMs) on the electron transfer processes between bacteria and steel surfaces. Electrochemical Quartz Crystal Microbalance (eQCM) studies have been performed to investigate the adsorption/desorption kinetics of organic films as well as the formation of biofilms on FeCr electrodes. Furthermore, the evolution of the biofilms on steel surfaces has been analyzed by means of electrochemical impedance spectroscopy (EIS) to support the QCM studies with information on structural changes during different stages of biofilm growth. Electron transfer and corrosion processes have been analyzed by means of square wave voltammetry (SWV) and linear sweep voltammetry (LSV), respectively. The results of electrochemical studies are complemented with microscopic and spectroscopic characterisation of organic adsorbates and analysis of changes in the passive film chemistry and surface morphology.
This presentation will summarize our results on the chemical and electrochemical interaction mechanisms of MRB on steel surfaces leading to passive film degradation. The role of flavins in accelerating corrosion processes will be elucidated in detail to provide useful insights from a fundamental aspect for the understanding of the initial stages of microbiologically influenced corrosion in the presence of MRB.
Metal reducing bacteria (MRB) are capable of utilizing different metals, such as iron, chromium, manganese or uranium as well as many organic compounds, as electron acceptors for their metabolism. Via direct and indirect electron transfer processes MRB are able to convert insoluble passive film species like Fe(III)-oxides to soluble Fe(II)-oxides and hydroxides. This weakening of the passive film not only leads to an acceleration of the general corrosion processes, but also increases the susceptibility of stainless steels to pitting corrosion. Electron transfer mechanisms are not yet fully understood and the role of bacteria in corrosion processes is controversially discussed in the literature. Moreover, recent research indicates that the secretion of electron shuttles like riboflavins by MRB also contributes to the extracellular electron transfer.
This project aims at clarifying the chemical and electrochemical interaction mechanisms of MRB with stainless steel surfaces. To investigate the changes in the oxide chemistry on the stainless steel surface in the presence of biomolecules and MRB a new flow cell has been designed and constructed which enables the collection of XANES (X-ray Absorption Near Edge Structure) spectra in fluorescence mode at the Fe K-edge and electrochemical analysis. Availability of oxygen and the pre-exposure of the MRB to Fe(III) during cultivation have been investigated as parameters with significant effect on the corrosion rates. XANES analysis is supplemented by ex-situ X-Ray Photoelectron Spectroscopy (XPS) and Fourier Transform Infrared Reflection Absorption Spectroscopy (FT-IRRAS) to complete the surface characterisation in terms of the oxide chemistry and the composition of organic residues. Complementary electrochemical quartz crystal microbalance (e-QCM) measurements have been performed to quantify the kinetics of bacterial attachment and biofilm formation. Together with the frequency shift, the evolution of the dissipation signal has been analyzed to investigate the changes in viscosity and structure of the biofilm from initial stages up to maturation. Scanning Electron Microscopy (SEM) and Atomic Force Microscopy (AFM) has been used to study the structure and viscoelastic properties of the biofilms after e-QCM experiments.
The presentation will summarize our results on the effects of individual surface and environment related parameters on the chemical/electrochemical interaction mechanisms of MRB leading to passive film degradation on stainless steel surfaces and provide useful insights from a fundamental aspect for the development of novel mitigation strategies for microbiologically influenced corrosion.
Electrochemically active bacteria such as iron oxidizing bacteria (IOB) or iron reducing bacteria (IRB) accelerate the corrosion of stainless steel via the oxidation and reduction of iron oxides in the passive layer. The exposure to medium containing IOB and IRB leads to pitting corrosion with deep pits on stainless steel surfaces. Improving corrosion control via a better understanding of localized corrosion processes is highly relevant especially for reasons of safety or environmental protection since advancing pitting corrosion can easily lead to unpredictable material failure. Classic electrochemical methods however, provide insufficient information about the spatial heterogeneity of a corroding sample and fall short in detecting localized corrosion.
The aim of this work is to develop methods for the analysis of localized corrosion, on stainless steel surfaces induced by IRB and IOB biofilms. It is quite challenging to address the complexity of the variations in the passive layer composition and microstructure as well as the biofilm’s complexity with its local differential aeration cells and electrochemical parameters both at the same time. Thus in this study, agarose artificial biofilms mimicking the physical properties of a natural biofilm have been used as model systems to be able to differentiate between individual effects. This artificial biofilm is applied on a multi-electrode stainless steel sample to identify local anodic sites during exposure experiments. For more detailed analysis of active sites, a scanning electrochemical microscopy (SECM) has been applied. Using the SECM as an amperometric sensor, we have investigated concentration gradients of iron ions or oxygen within the biofilm and its immediate vicinity on actively corroding electrodes.
The presented analytical approach delivers promising results in clarifying how localized corrosion of stainless steels develops chronologically and spatially in the presence of IRBs and IOBs. Our results on model systems do also provide the basis for the investigation of natural biofilms in the future.
Geothermal brine is considered to be an aggressive
environment as it contains various dissolved salts.
Even though carbon steel is commonly used as a
construction material due to its machinability and
economical reason, it is susceptible to uniform and
localized corrosion in a high temperature and high
pressure system. Therefore, a coating system is
introduced to protect the carbon steel against
corrosion in such environment.
1. Carbon steel is susceptible to uniform corrosion in presence of oxygen, with corrosion rate of immersion at 150 °C of 0.39 mm/a.
2. Exposure test of carbon steel at 150°C and 10 bar (pressurized by Ar) results in pitting corrosion with depth of 19 µm and width 4 µm on average.
3. OCP measurement shows that the stability of measurement is reached after 40 hours of immersion in the solution.
4. EIS measurement is useful to observe the effect of temperature, immersion time, and coating composition on the corrosion processes of coated metals for use in geothermal application.
Geothermal brine is considered to be an aggressive environment as it contains various dissolved salts. Even though carbon steel is commonly used as a construction material due to its machinability and economical reason, it is susceptible to uniform and localized corrosion in a high temperature and high pressure system. Therefore, a coating system is introduced to protect the carbon steel against corrosion in such environment.
-It is necessary to find the optimum composition of SiO2 addition in the organic coatings to enhance the material performance, i.e. coatings adhesion, thickness optimization, thermal resistance.
Current project aims at the addition of Polyaniline (PANi) as the active agent to improve the corrosion resistance of materials against a high saline medium at elevated temperatures.
Methanogenic Archaea
(2017)
Different environmental samples reveal that methanogenic Archaea are part of a multi-species biofilm on corroding metallic structures. Studies on microbial influenced corrosion (MIC) focus mainly on sulphate reducing Bacteria (SRB), leading to the assumption that they are exclusively responsible for metal corrosion. In fact, methanogenic Archaea are known to be involved in metal corrosion as well (e.g. Methanococcus maripaludis DSM 2067). In some cases SRB and methanogenic Archaea have comparable high corrosion rates. However, the underlying mechanisms causing corrosion are still unknown.
The goal of this study is to develop suitable methods for analyzing two environmental isolates (M. maripaludis DSM 2067, M. maripaludis KA1) and two human-related isolates (Methanobrevibacter oralis and Methanobrevibacter smithii) for their ability to deteriorate/transform metals, which are relevant for technical and clinical applications. Moreover, the studies will provide essential information on the interaction mechanisms of human-related Archaea, which are frequently found in peri-implantitis, with dental material such as implants, crowns and bridges leading to their degradation and transformation.
Different environmental samples reveal that methanogenic Archaea are part of a
multi-species biofilm on corroding metallic structures (Fig. 1). Studies on microbial
influenced corrosion (MIC) focus mainly on sulphate reducing Bacteria (SRB),
leading to the assumption that they are exclusively responsible for metal corrosion.
In fact, methanogenic Archaea are known to be involved in metal corrosion as well
(e.g.Methanococcus maripaludis DSM 2067). In some cases SRB and methanogenic
Archaea have comparable high corrosion rates. However, the underlying
mechanisms causing corrosion are still unknown. The goal of this study is to
analyse two environmental isolates (M. maripaludis DSM 2067, M. maripaludis
KA1) and two human-related isolates (Methanobrevibacter oralis and
Methanobrevibacter smithii) for their ability to deteriorate/transform metals,
which are relevant for technical and clinical applications. Moreover, the studies will
provide essential information on the interaction mechanisms of human-related
Archaea, which are frequently found in peri-implantitis, with dental material such
as implants, crowns and bridges leading to their degradation/transformation.
Different environmental samples reveal that methanogenic Archaea are part of a multi-species biofilm on corroding metallic structures (Fig. 1). Studies on microbial influenced corrosion (MIC) focus mainly on sulphate reducing Bacteria (SRB), leading to the assumption that they are exclusively responsible for metal corrosion. In fact, methanogenic Archaea are known to be involved in metal corrosion as well (e.g. Methanococcus maripaludis DSM 2067). In some cases SRB and methanogenic Archaea have comparable high corrosion rates. However, the underlying mechanisms causing corrosion are still unknown. The goal of this study is to analyse two environmental isolates (M. maripaludis DSM 2067, M. maripaludis KA1) and two human-related isolates (Methanobrevibacter oralis and Methanobrevibacter smithii) for their ability to deteriorate/transform metals, which are relevant for technical and clinical applications. Moreover, the studies will provide essential information on the interaction mechanisms of human-related Archaea, which are frequently found in peri-implantitis, with dental material such as implants, crowns and bridges leading to their degradation/ transformation.
Influence of corundum grinding processes on the corrosion behaviour of austenitic stainless steels
(2017)
The scientific poster shows by means of corrosion testing in combination with surface analytical methods to which degree corundum grinding influences the corrosion behaviour of stainless steel surfaces. The austenitic stainless steel AISI 304 from a consistent heat was used for all investigations to guarantee the same chemical composition and thus no additional influences caused by the material itself. A wide range of different grinding parameters such as pressure, cooling medium and grain size of the abrasive was varied. Thus, comparison of the corrosion behaviour of different surface states and the evaluation of an optimum grinding process using corundum abrasives were possible. The results will contribute to present discussions and give novel impulses for companies in the metalworking industry.
Potential of martensitic stainless steel X5CrNiCuNb 16-4 as pipe steel in corrosive CCS environment
(2017)
Pipe steels suitable for carbon capture and storage technology (CCS) require resistance against the corrosive environment of a potential CCS-site (heat, pressure, salinity of the aquifer, CO2-partial pressure). X5CrNiCuNb16-4 has been proven to be sufficient resistant in corrosive environments, but shows rather unusual corrosion behaviour in CCS environment. Therefore differently heat treated coupons of 1.4542 were kept at T=60 °C and ambient pressure as well as p=100 bar for 700 h - 8000 h in an a) water saturated supercritical CO2 and b) CO2-saturated synthetic aquifer environment similar to on-shore CCS-sites in the Northern German Basin. Additionally fatigue tests were performed via push-pull tests with a series of 30 specimens was tested at stress amplitudes between 150 MPa and 500 MPa (sinusoidal dynamic test loads, R=-1; resonant frequency ~ 30 Hz). Best corrosion resistance in the liquid phase is achieved via normalizing prior to exposure and hardening+tempering at 670 °C leads to lowest corrosion rates in the supercritical phase. With no regard to atmosphere discontinuously ellipsoidal surface corrosion regions appear after exposure of 4000 h and more. The endurance limit of X5CrNiCuNb16-4 measured in air is reduced by more than 50% when exposed to CCS environment (maximum number of cycles (10 x 106) at a stress amplitude of 150 MPa) The scatter range TN = 1:34 is disproportionately large contributing to an overall unusual corrosion behaviour.