Novel agar-based test electrolytes are used to perform electrochemical corrosion investigations on ZnFe and ZnNi binary as well as ZnFeMo ternary zinc coatings. The objectives of the electrochemical investigations include the characterization of the corrosion behavior, the description of the protective effect of the coatings as well as the investigation of the layer formation and degradation under artificial aging. ZnFe and ZnFeMo coatings are applied with varying iron content as well as an additional passivation layer, respectively, to study the effect on corrosion resistance. The results show that the protective effect of the coatings is not negatively influenced by different iron contents or the addition of molybdenum. Additional passivation of the ZnFe-containing coatings by means of a passivating agent leads to a significant improvement in the protective effect. Artificial aging leads to slight degradation of the additional passivation layer whereas coatings without post-treatment enhance their protective effect by the formation of corrosion product layers.
A series of field exposure tests according to ISO 9223 up to 9226 was carried out at different locations to determine the corrosivity and the corrosion progress of different test sites throughout northern and eastern Germany. Standard test specimens of steel, zinc, copper and aluminium were exposed to rural, city and marine atmosphere at test sites of the Bundesanstalt für Materialforschung und -prüfung (BAM). Test sites at city atmosphere comprised exposure on a rooftop, next to a highly frequented road and directly at a motorway. Exposure under marine conditions was carried out at Heligoland in the North Sea. The specimens were stored under sheltered and unsheltered conditions on each test site, respectively. Corrosion rates after the first year of field exposure were determined and used for the classification of the atmospheres and the test sites regarding the corrosivity category.
Results after the first year of exposure were presented at the EUROCORR 2018 in Cracow. The current presentation will present an update of results of the systematic study after five years of exposure. The corrosion progress and the mass loss of the standard metals steel, zinc, copper and aluminium will be presented and discussed with respect to the atmospheric conditions and the time of wetness at the test sites. In addition, the difference between sheltered and unsheltered conditions will be discussed.
The chapter starts with a brief introduction about corrosion, which is defined as the interdependency between a metal, a corrosive environment, and the respective component design. The second section introduces the most important forms of aqueous electrochemical corrosion (uniform corrosion, galvanic corrosion, selective and intergranular corrosion, and finally pitting and crevice corrosion in the case of passive layer forming metals). In addition, electrochemical corrosion under applied mechanical load is introduced (stress corrosion cracking, hydrogen-assisted cracking, corrosion fatigue), as well as special forms of corrosion (erosion, fretting, and microbiologically induced corrosion). The third section of this chapter introduces (mostly dry) chemical corrosion and high-temperature corrosion (oxidation, carburization, high-temperature hydrogen attack, sulfurization, nitriding, halogenation). As in the case of electrochemical corrosion, chemical corrosion can also be superimposed by mechanical loads. Finally, general facts on the testing of corrosion are introduced.
The corrosion resistance of aluminium surfaces is closely linked to the surfacecstate after a grinding process. For years, iron‐containing abrasive materials were suspected to lead to increased corrosion susceptibility after processing of aluminium surfaces. To prove a possible correlation between the iron content of an abrasive and the corrosion behaviour of aluminium components, scientific investigations and experimentally practical corrosion tests are necessary.
For the current investigation, specimens of a technical Al‐Si alloy from the same batch were used. The test specimens were mechanically ground with various resin‐bonded model abrasives containing different iron contents. The performed corrosion tests did not reveal a negative influence of the different iron‐containing abrasives on the corrosion behaviour of the Al–Si alloy.
However, the most sensitive measuring method (electrochemical noise)
showed differences in the surface activity depending on the type of abrasive.
Der Vortrag stellt ein neuartiges Korrosionsprüfverfahren für Zinküberzüge auf Basis gelartiger Elektrolyte vor und führt die Vorteile gegenüber konventionellen Prüfverfahren auf. Basierend auf den Ergebnissen wird die Idee für einen IGF-Projektantrag in Kooperation mit dem Fraunhofer IKTS vorgestellt.
The present work describes the combination of electrochemical investigations by using a gel‐type electrolyte with Fourier‐transformed infrared spectroscopy to investigate partially extremely thin corrosion product films on titanium‐zinc. The gel pad method enables the determination of corrosion relevant parameters such as the potential and the linear polarization resistance without altering the corrosion product layers, which are extremely prone to re‐dissolution when freshly formed. Complementary infrared spectroscopy enables the determination of main compounds of even very thin surface layers of few tenth of nanometers with a certain lateral resolution. It was found that zinc forms mostly zinc carboxy‐hydroxides such as hydrozincite, under various exposure conditions. The protective properties of these hydrozincite layers depend on the structure of the corrosion product film rather than on its thickness. In mid‐term exposure tests, shallow corrosion pits were found even in the absence of corrosive agents such as chloride.
Der Vortrag stellt ein neuartiges Korrosionsprüfverfahren für Zinküberzüge auf Basis gelartiger Elektrolyte vor und führt die Vorteile gegenüber konventionellen Prüfverfahren auf. Basierend auf den Ergebnissen wird die Idee für einen IGF-Projektantrag in Kooperation mit dem Fraunhofer IKTS vorgestellt.
The copper alloyed stainless steel 1.4542 (X5CrNiCuNb16-4) is used in different areas due to its good mechanical properties and corrosion resistance. Strength and corrosion resistance can be adjusted by the heat treatment, which is of importance for the application of this alloy. The mechanical properties (strength and hardness) are attributed to the dispersive precipitation of the copper rich ε–Phase. The additional precipitation of chromi-um carbides can reduce the corrosion resistance. Different ageing states were produced to investigate the precipitation behaviour with various methods. Furthermore, the influence of cold-rolling on the precipitation behaviour was studied in comparison to a solution annealed state without deformation. The microstructure was studied by SEM and the variations of hardness and magnetic proportion were characterised. The electrochemical potentiodynamic reactivation (EPR) was used to determine the corrosion resistance and detect chromium depletion in all heat-treated states. The results show that a work hard-ening accelerates the precipitation rate, while ageing at 600 °C reduces the corrosion resistance due to chromium depletion.
The copper alloyed stainless steel 1.4542 (X5CrNiCuNb16-4) is used in different areas due to its good mechanical properties and corrosion resistance. Strength and corrosion resistance can be adjusted by the heat treatment, which is of importance for the application of this alloy. The mechanical properties (strength and hardness) are attributed to the dispersive precipitation of the copper rich ε–Phase. The additional precipitation of chromi-um carbides can reduce the corrosion resistance. Different ageing states were produced to investigate the precipitation behaviour with various methods. Furthermore, the influence of cold-rolling on the precipitation behaviour was studied in comparison to a solution annealed state without deformation. The microstructure was studied by SEM and the variations of hardness and magnetic proportion were characterised. The electrochemical potentiodynamic reactivation (EPR) was used to determine the corrosion resistance and detect chromium depletion in all heat-treated states. The results show that a work hard-ening accelerates the precipitation rate, while ageing at 600 °C reduces the corrosion resistance due to chromium depletion.
A new approach to the assessment of the corrosion behaviour of zinc coatings under atmospheric conditions can be achieved using gel-type electrolytes as an alternative to standard aqueous test electrolytes. Gel-type electrolytes allow minimally invasive corrosion investigations on zinc coatings. They also provide the possibility to carry out corrosion investigations onsite. By using gel-type electrolytes corrosion-relevant characteristic values such as corrosion currents and polarization resistanc-es can be determined. These allow to describe the formation and the stability of the formed corrosion product layers under various climatic conditions. With this knowledge, a prediction of the zinc coating life cycle is possible. In this contribution, the value of gel-type electrolytes for corrosion research on zinc coatings is presented.
A new approach to the assessment of the corrosion behaviour of zinc coatings under atmospheric conditions can be achieved using gel-type electrolytes as an alternative to standard aqueous test electrolytes. Gel-type electrolytes allow minimally invasive corrosion investigations on zinc coatings. They also provide the possibility to carry out corrosion investigations onsite. By using gel-type electrolytes corrosion-relevant characteristic values such as corrosion currents and polarization resistances can be determined. These allow to describe the formation and the stability of the formed corrosion product layers under various climatic conditions. With this knowledge, a prediction of the zinc coating life cycle is possible. In this contribution, the value of gel-type electrolytes for corrosion research on zinc coatings is presented.
The copper alloyed stainless steel 1.4542 (X5CrNiCuNb16-4) is used in different areas due to its good mechanical properties and corrosion resistance. Strength and corrosion resistance can be adjusted by the heat treatment, which is of importance for the application of this alloy. The mechanical properties (strength and hardness) are attributed to the dispersive precipitation of the copper rich ε–Phase. The additional precipitation of chromium carbides can reduce the corrosion resistance. Different ageing states were produced to investigate the precipitation behaviour with various methods. Furthermore, the influence of cold-rolling on the precipitation behaviour was studied in comparison to a solution annealed state without deformation. The microstructure was studied by SEM and the variations of hardness and magnetic proportion were characterised. The electrochemical potentiodynamic reactivation
(EPR) was used to determine the corrosion resistance and detect chromium depletion in all heattreated states. The results show that a work hardening accelerates the precipitation rate, while ageing at 600 °C reduces the corrosion resistance due to chromium depletion.
The double loop electrochemical potentiodynamic reactivation (EPR) method is a standardised procedure for detecting and quantifying sensitisation on austenitic, ferritic and ferritic-austenitic stainless-steel grades. This sensitisation is caused by microstructural alternations, as the formation of chromium carbides, nitrides or sigma-phases, which generate local chromium depleted zones nearby. The latter strongly influence the corrosion resistance and the electrochemical response of a stainless steel during electrochemical potentiodynamic reactivation, providing important information on the degree of chromium depletion. In case of martensitic stainless steels, which are used for cutlery and surgical instruments, the heat treatment has a strong impact on the microstructure, the material properties and especially on the corrosion resistance. To study this interaction, the EPR method was modified for the application on martensitic stainless steels with about 13 wt.-% chromium. Different H2SO4 concentrations and EPR-parameters were tested and compared on two standard martensitic stainless-steel grades (AISI 420 A / X20Cr13 and AISI 420 C / X46Cr13) to define applicable parameters. Afterwards, these parameters were used to study the effect of austenitisation time and cooling rate on the corrosion resistance of both martensitic stainless steels. The response of both alloys was different due to the different carbon levels, which will be explained by microstructural investigations in detail. All results allow postulating a process window, in which chromium depletion is suppressed and an optimised corrosion resistance is guaranteed. Based on this research, the modified EPR-test is now used to control the heat treatment and its impact on the corrosion resistance of martensitic stainless steels in the cutlery industry. The EPR-test is thus an interesting alternative for manufacturers, processors, users and researchers to the time-consuming exposition test normally used to characterise the corrosion resistance of martensitic stainless steels.
The influence of isothermal ageing on microstructure, sensitisation and pitting corrosion resistance of the lean duplex stainless steel (LDSS) X2CrNiN23-4 was investigated with various electrochemical methods. The aging at 600 °C (from 0.1 h up to 20 h) lead to the formation of precipitations at the ferrite-ferrite (α/α) and ferrite-austenite (α/γ) grain boundaries, inducing sensitisation due to chromium depletion. The degree of sensitisation was evaluated with the double loop electrochemical potentiokinetic reactivation method (DL-EPR) according to ASTM G108 and correlated with critical pitting potentials (Epit) as well as critical pitting temperature (CPT) measured in an electrolyte according to ASTM G48 using electrochemical noise. Up to an ageing time of 1 h, the sensitisation did rise significantly, stabilising at a nearly constant level with a slight drop at 20 h. This behaviour correlated perfectly with the potentiodynamically determined pitting potentials Epit and sensitisation. The CPT showed a higher sensitivity at short ageing times compared to the DL-EPR and Epit. Finally, the KorroPad method was applied to visualise the sensitisation induced reduction of pitting corrosion resistance. The “KorroPad” is an agar-based gel-electrolyte containing 0.1 mol/l sodium chloride (NaCl) and 0.1 mol/l potassium ferricyanide III (K3[Fe(CN)6]), invented at the Federal Institute of Materials Research and Testing in Berlin (Germany) to detect surfaces of stainless steel prone to pitting corrosion. The standard configuration of the KorroPad showed no differentiation for the various aging conditions. Increasing the concentration of both NaCl and potassium ferrocyanide III to 0.5 M shifts the detection limit of the KorroPad method to stainless steels with higher corrosion resistance, producing the same trends detected by standard electrochemical pitting corrosion values (Epit, CPT) and sensitisation (DL-EPR). By that, the KorroPad method was successfully adjusted to the lean-duplex stainless steel X2CrNiN23-4, enabling short-time testing to detect sensitization.
The KorroPad indicator test was invented at the Federal Institute for Materials Research and Testing to detect stainless-steel surfaces susceptible to pitting corrosion. The KorroPad indicator test is thus an interesting alternative for manufacturers, processors, users and researchers to time consuming exposition experiments and complex electrochemical investigations, which are normally used to reveal surface-related processing errors resulting in reduced pitting corrosion resistance. Furthermore, the KorroPad indicator test can be used to visualize alloy- and microstructure-related factors causing susceptibility to pitting corrosion. The detection limit of the KorroPad indicator test was characterized in this work using reference alloys with different chromium content (5 % to 18 %). The alloy-specific detection limit was shifted successfully to higher chromium content by increasing the concentrations of NaCl and K3[Fe(CN)6]. The modified KorroPads can now be used to establish an alloy-specific quality control regarding the pitting corrosion resistance of different stainless steel grades.
The copper alloyed stainless steel 1.4542 (X5CrNiCuNb16-4) is used in different areas due to its good mechanical properties and corrosion resistance. Strength and corrosion re-sistance can be adjusted by the heat treatment, which is of importance for the application of this alloy. The mechanical properties (strength and hardness) are attributed to the dispersive precipitation of the copper rich ε–Phase. The additional precipitation of chromium carbides can reduce the corrosion resistance. Different ageing states were produced to investigate the precipitation behaviour with various methods. Furthermore, the influence of cold-rolling on the precipitation behaviour was studied in comparison to a solution annealed state without deformation. The microstructure was studied by SEM and the variations of hardness and magnetic proportion were characterised. The electrochemical potentiodynamic reactivation (EPR) was used to determine the corrosion resistance and detect chromium depletion in all heat-treated states. The results show that a work hardening accelerates the precipitation rate, while ageing at 600 °C reduces the corrosion re-sistance due to chromium depletion.
The corrosion resistance of stainless-steels grades is of high importance for the technical safety in different environmental conditions. Processing and surface finish influences the corrosion resistance of ferritic stainless steels, which may be considered for some application in marine environment. Three ferritic stainless steel alloys (X2CrNi12, X2CrTiNb18 and X2CrMoTi18-2) were exposed in four different surface finishes (rolled, dry grinding, glass beaded and electro polished) for five years in marine environment to obtain reliable information about the corrosion resistance. All samples were assessed after 22 and 60 months according to DIN EN ISO 10289 in validation degrees from 1 to 10. Complementary investigation using accelerated chamber test (salt spray test followed by four weeks storage at 30 °C / 80 % relative humidity) and short-term electrochemical methods (electrochemical potentiodynamic reactivation, pitting potentials and the KorroPad method) were conducted to compare their results. The presentation gives an overview on all methods and the generated results, which show benefits and restrictions of long-term, accelerated and short-term corrosion tests.
The copper alloyed stainless steel 1.4542 (X5CrNiCuNb16-4) is used in different areas due to its good mechanical properties and corrosion resistance. Strength and corrosion resistance can be adjusted by the heat treatment, which is of importance for the application of this alloy. The mechanical properties (strength and hardness) are attributed to the dispersive precipitation of the copper rich ε–Phase. The additional precipitation of chromium carbides can reduce the corrosion resistance. Different ageing states were produced to investigate the precipitation behaviour with various methods. Furthermore, the influence of cold-rolling on the precipitation behaviour was studied in comparison to a solution annealed state without deformation. The microstructure was studied by SEM and the variations of hardness and magnetic proportion were characterised. The electrochemical potentiodynamic reactivation (EPR) was used to determine the corrosion resistance and detect chromium depletion in all heat-treated states. The results show that a work hardening accelerates the precipitation rate, while ageing at 600 °C reduces the corrosion resistance due to chromium depletion.
Ein neuer Ansatz bei elektrochemischen Korrosionsuntersuchungen kann durch den Einsatz von gelartigen Elektrolyten als Alternative zu wässrigen Prüfelektrolyten beschritten werden. Gelartige Elektrolyte ermöglichen minimalinvasive Untersuchungen an natürlich gebildeten Zinkdeckschichten. Dadurch können korrosionsrelevante Kennwerte ermittelt werden, die Aussagen zur Deckschichtbildung und zur Stabilität der gebildeten Deckschichten unter verschiedenen klimatischen Bedingungen erlauben. In diesem Beitrag wird anhand verschiedener Deckschichtzustände an Zink der Mehrwert von Untersuchungen mit gelartigen Elektrolyten für die Korrosionsforschung verdeutlicht.
Ein neuer Ansatz bei elektrochemischen Korrosionsuntersuchungen kann durch den Einsatz von gelartigen Elektrolyten als Alternative zu wässrigen Prüfelektrolyten beschritten werden. Gelartige Elektrolyte ermöglichen minimalinvasive Untersuchungen an natürlich gebildeten Zinkdeckschichten. Dadurch können korrosionsrelevante Kennwerte ermittelt werden, die Aussagen zur Deckschichtbildung und zur Stabilität der gebildeten Deckschichten unter verschiedenen klimatischen Bedingungen erlauben. In diesem Beitrag wird anhand verschiedener Deckschichtzustände an Zink der Mehrwert von Untersuchungen mit gelartigen Elektrolyten für die Korrosionsforschung verdeutlicht.